BASF Ultrason S 3010 PSU

Seller in Washington price: $1754 per MT
Seller in Shenyang price: $2408 per MT
Seller in Shanghai price: $1769 per MT

BASF Ultrason S 3010 PSU in Polymer, Thermoplastic, Polysulfone (PSU)

  • Physical Properties
  • Density
  • 1.24 g/cc
  • Water Absorption
  • 0.80 %
  • Moisture Absorption at Equilibrium
  • 0.30 %
  • Viscosity Test
  • 72 cm³/g
  • Linear Mold Shrinkage, Flow
  • 0.0070 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.0074 cm/cm
  • Melt Flow
  • 40 g/10 min @Load 10.0 kg, Temperature 360 °C
  • Mechanical Properties
  • Ball Indentation Hardness
  • 135 MPa
  • Tensile Strength at Break
  • 75.0 MPa
  • Tensile Stress
  • 20.0 MPa @Strain 1.00 %, Temperature 160 °C
  • Tensile Stress
  • 27.0 MPa @Strain 1.00 %, Temperature 23.0 °C
  • Tensile Stress
  • 35.0 MPa @Strain 2.00 %, Temperature 160 °C
  • Tensile Stress
  • 47.0 MPa @Strain 2.00 %, Temperature 23.0 °C
  • Tensile Stress
  • 70.0 MPa @Strain 4.00 %, Temperature 23.0 °C
  • Tensile Strength, Yield
  • 75.0 MPa
  • Tensile Strength, Yield
  • 40.0 MPa @Temperature 140 °C
  • Tensile Strength, Yield
  • 58.0 MPa @Temperature 100 °C
  • Tensile Strength, Yield
  • 68.0 MPa @Temperature 60.0 °C
  • Tensile Strength, Yield
  • 75.0 MPa @Temperature 20.0 °C
  • Elongation at Break
  • 5.7 %
  • Elongation at Yield
  • 5.7 %
  • Elongation at Yield
  • 0.50 % @Time 3600 sec, Pressure 10.0 MPa
  • Elongation at Yield
  • 0.55 % @Pressure 10.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 0.56 % @Pressure 10.0 MPa, Time 3.60e+7 sec
  • Elongation at Yield
  • 0.80 % @Time 3600 sec, Pressure 20.0 MPa
  • Elongation at Yield
  • 0.90 % @Pressure 20.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 1.3 % @Time 3600 sec, Pressure 30.0 MPa
  • Elongation at Yield
  • 1.4 % @Pressure 30.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 1.5 % @Pressure 30.0 MPa, Time 3.60e+7 sec
  • Elongation at Yield
  • 1.9 % @Time 3600 sec, Pressure 40.0 MPa
  • Elongation at Yield
  • 2.0 % @Pressure 20.0 MPa, Time 3.60e+7 sec
  • Elongation at Yield
  • 2.0 % @Pressure 40.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 2.0 % @Time 3600 sec, Pressure 42.0 MPa
  • Elongation at Yield
  • 2.2 % @Pressure 42.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 2.4 % @Pressure 40.0 MPa, Time 3.60e+7 sec
  • Elongation at Yield
  • 2.5 % @Pressure 42.0 MPa, Time 3.60e+7 sec
  • Creep Strength
  • 17.0 MPa @Time 3.60e+7 sec
  • Creep Strength
  • 20.0 MPa @Time 3.60e+6 sec
  • Creep Strength
  • 25.0 MPa @Time 360000 sec
  • Creep Strength
  • 32.0 MPa @Time 36000 sec
  • Modulus of Elasticity
  • 2.00 GPa @Temperature 140 °C
  • Modulus of Elasticity
  • 2.30 GPa @Temperature 100 °C
  • Modulus of Elasticity
  • 2.49 GPa @Temperature 60.0 °C
  • Modulus of Elasticity
  • 2.51 GPa @Temperature 20.0 °C
  • Tensile Modulus
  • 2.60 GPa
  • Fatigue Strength
  • 25.0 MPa @# of Cycles 1.00e+7
  • Fatigue Strength
  • 30.0 MPa @# of Cycles 1.00e+6
  • Fatigue Strength
  • 40.0 MPa @# of Cycles 100000
  • Fatigue Strength
  • 50.0 MPa @# of Cycles 10000
  • Shear Modulus
  • 0.0250 GPa @Temperature 200 °C
  • Shear Modulus
  • 0.800 GPa @Temperature 175 °C
  • Shear Modulus
  • 0.900 GPa @Temperature 100 °C
  • Shear Modulus
  • 0.950 GPa @Temperature 50.0 °C
  • Izod Impact, Notched (ISO)
  • 5.50 kJ/m²
  • Izod Impact, Notched (ISO)
  • 5.00 kJ/m² @Temperature 120 °C
  • Izod Impact, Notched (ISO)
  • 6.00 kJ/m² @Temperature -30.0 °C
  • Izod Impact, Notched (ISO)
  • 10.0 kJ/m² @Temperature 50.0 °C
  • Izod Impact, Notched (ISO)
  • 13.0 kJ/m² @Temperature -25.0 °C
  • Charpy Impact Unnotched
  • NB
  • Charpy Impact Unnotched
  • NB @Temperature -30.0 °C
  • Charpy Impact, Notched
  • 0.550 J/cm²
  • Charpy Impact, Notched
  • 0.600 J/cm² @Temperature -30.0 °C
  • Tensile Creep Modulus, 1000 hours
  • 2500 MPa
  • Thermal Properties
  • CTE, linear, Parallel to Flow
  • 53.0 µm/m-°C @Temperature 23.0 - 80.0 °C
  • CTE, linear, Parallel to Flow
  • 60.0 µm/m-°C @Temperature 140 - 180 °C
  • Electrical Properties
  • Volume Resistivity
  • >= 1.00e+13 ohm-cm
  • Surface Resistance
  • >= 1.00e+14 ohm
  • Dielectric Constant
  • 3.1 @Frequency 100 Hz
  • Dielectric Constant
  • 3.1 @Frequency 1.00e+6 Hz
  • Dielectric Strength
  • 37.0 kV/mm
  • Dissipation Factor
  • 0.00080 @Frequency 100 Hz
  • Dissipation Factor
  • 0.0064 @Frequency 1.00e+6 Hz
  • Comparative Tracking Index
  • 125 V

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, chemical tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for BASF Ultrason S 3010 PSU

Seller from Washington – 2021-04-21:

Seller from Washington work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1754 per MT

Seller from Shenyang – 2021-06-03:

Seller from Shenyang work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2408 per MT

Seller from Shanghai – 2021-08-15:

Seller from Shanghai work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1769 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell BASF Ultrason S 3010 PSU?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Custom home builder in Singapore open-nearme.com