Carlson C 800 Nickel-Iron-Chromium Alloy price 1951 per MT

Physical Properties
Density
7.94 g/cc

Mechanical Properties
Tensile Strength at Break
>= 517 MPa
Tensile Strength, Yield
>= 207 MPa @Strain 0.200 %
Elongation at Break
>= 30 %
Modulus of Elasticity
197 GPa
Modulus of Elasticity
132 GPa @Temperature 871 °C
Modulus of Elasticity
169.9 GPa @Temperature 427 °C

Thermal Properties
CTE, linear
18.4 µm/m-°C @Temperature 21.1 - 871 °C
Melting Point
1357 - 1385 °C
Solidus
1357 °C
Liquidus
1385 °C

Component Elements Properties
Aluminum, Al
0.15 - 0.60 %
Carbon, C
<= 0.010 %
Chromium, Cr
19 - 23 %
Copper, Cu
<= 0.75 %
Iron, Fe
>= 39.5 %
Manganese, Mn
<= 1.5 %
Nickel, Ni
30 - 35 %
Silicon, Si
<= 1.0 %
Sulfur, S
<= 0.015 %
Titanium, Ti
0.15 - 0.60 %

Electrical Properties
Magnetic Permeability
1.014
Curie Temperature
-115 °C

Alternative products

Schmolz + Bickenbach UGIMA® 630 Stainless Steel Bar accurate 70%

$ 1880/MT

Density: 7.75 g/cc
Hardness, Brinell: >= 277
Hardness, Brinell: 320 - 340 @Thickness <=25.4 mm
Hardness, Brinell: 320 - 340 @Thickness >=25.4 mm
Hardness, Brinell: >= 255 @Treatment Temp. 579.4 °C, Time 14400 sec

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 95% - 16) accurate 70%

$ 1562/MT

Particle Size: 6.7 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 90% - 16) accurate 70%

$ 1714/MT

Particle Size: 8.4 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals Co212-e Cobalt Alloy Powder (Grade 90% - 16) accurate 63%

$ 1849/MT

Particle Size: 8.4 µm
Carbon, C: 0.050 %
Carbon, C: <= 0.20 %
Chromium, Cr: 27 - 30 %
Cobalt, Co: 62.85 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 80% - 22) accurate 70%

$ 1507/MT

Particle Size: 12 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 90% - 22) accurate 70%

$ 1515/MT

Particle Size: 10 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals Co212-e Cobalt Alloy Powder (Grade 80% - 22) accurate 63%

$ 2148/MT

Particle Size: 12 µm
Carbon, C: 0.050 %
Carbon, C: <= 0.20 %
Chromium, Cr: 27 - 30 %
Cobalt, Co: 62.85 %

Carlson C 800AT Nickel-Iron-Chromium Alloy accurate 63%

$ 1480/MT

Density: 7.94 g/cc
Tensile Strength at Break: >= 448 MPa
Tensile Strength, Yield: >= 172 MPa @Strain 0.200 %
Elongation at Break: >= 30 %
Modulus of Elasticity: 197 GPa

Carlson C 800H Nickel-Iron-Chromium Alloy accurate 78%

$ 1751/MT

Density: 7.94 g/cc
Tensile Strength at Break: >= 448 MPa
Tensile Strength, Ultimate: 378 MPa @Temperature 649 °C
Tensile Strength, Ultimate: 465 MPa @Temperature 427 °C
Tensile Strength, Yield: 93.1 MPa @Temperature 649 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Carlson C 800 Nickel-Iron-Chromium Alloy

Seller from Brasília – 2021-08-06:

Seller from Brasília work with company: Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1951 per MT