Carlson C 800AT Nickel-Iron-Chromium Alloy price 1480 per MT

Physical Properties
Density
7.94 g/cc

Mechanical Properties
Tensile Strength at Break
>= 448 MPa
Tensile Strength, Yield
>= 172 MPa @Strain 0.200 %
Elongation at Break
>= 30 %
Modulus of Elasticity
197 GPa
Poissons Ratio
0.339
Shear Modulus
73.6 GPa

Thermal Properties
CTE, linear
18.4 µm/m-°C @Temperature 21.1 - 871 °C
Melting Point
1357 - 1385 °C
Solidus
1357 °C
Liquidus
1385 °C

Component Elements Properties
Aluminum, Al
0.15 - 0.60 %
Carbon, C
0.060 - 0.10 %
Chromium, Cr
19 - 23 %
Copper, Cu
<= 0.75 %
Iron, Fe
>= 39.5 %
Manganese, Mn
<= 1.5 %
Nickel, Ni
30 - 35 %
Silicon, Si
<= 1.0 %
Sulfur, S
<= 0.015 %
Titanium, Ti
0.15 - 0.60 %

Electrical Properties
Magnetic Permeability
1.014
Curie Temperature
-115 °C

Alternative products

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 95% - 16) accurate 77%

$ 1562/MT

Particle Size: 6.7 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 90% - 16) accurate 77%

$ 1714/MT

Particle Size: 8.4 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals Co212-e Cobalt Alloy Powder (Grade 90% - 22) accurate 66%

$ 1490/MT

Particle Size: 10 µm
Carbon, C: 0.050 %
Carbon, C: <= 0.20 %
Chromium, Cr: 27 - 30 %
Cobalt, Co: 62.85 %

Special Metals NIMONIC® Alloy 80A accurate 66%

$ 2344/MT

Density: 8.19 g/cc
Tensile Strength, Ultimate: 1030 MPa @Temperature 650 °C
Tensile Strength, Ultimate: 1250 MPa @Temperature 23.0 °C
Tensile Strength, Yield: 780 MPa @Strain 0.200 %
Tensile Strength, Yield: 710 MPa @Strain 0.200 %, Temperature 650 °C

Carlson C 800 Nickel-Iron-Chromium Alloy accurate 99%

$ 1951/MT

Density: 7.94 g/cc
Tensile Strength at Break: >= 517 MPa
Tensile Strength, Yield: >= 207 MPa @Strain 0.200 %
Elongation at Break: >= 30 %
Modulus of Elasticity: 197 GPa

Osprey Metals 310S Stainless Steel Powder (Grade 90% - 22) accurate 66%

$ 2107/MT

Particle Size: 10 µm
Carbon, C: 0.010 %
Carbon, C: <= 0.080 %
Chromium, Cr: 24 - 26 %
Iron, Fe: 51.99 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 80% - 22) accurate 77%

$ 1507/MT

Particle Size: 12 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 90% - 22) accurate 77%

$ 1515/MT

Particle Size: 10 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Carlson C 800H Nickel-Iron-Chromium Alloy accurate 99%

$ 1751/MT

Density: 7.94 g/cc
Tensile Strength at Break: >= 448 MPa
Tensile Strength, Ultimate: 378 MPa @Temperature 649 °C
Tensile Strength, Ultimate: 465 MPa @Temperature 427 °C
Tensile Strength, Yield: 93.1 MPa @Temperature 649 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, freighter ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Carlson C 800AT Nickel-Iron-Chromium Alloy

Seller from Sydney – 2021-06-30:

Seller from Sydney work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1480 per MT