Celanese CELANEX 2500 PBT, Unfilled price 2268 per MT

Physical Properties
Density
1.31 g/cc
Density of Compound
1.11 g/cc
Moisture Absorption
0.200 %
Viscosity Test
85.0 cm³/g
Linear Mold Shrinkage, Flow
0.0180 - 0.0200 cm/cm
Melt Flow
40.0 g/10 min @Load 2.16 kg, Temperature 250 °C

Mechanical Properties
Tensile Strength at Break
60.0 MPa
Tensile Strength, Yield
60.0 MPa
Elongation at Break
15.0 %
Elongation at Yield
4.00 %
Tensile Modulus
2.70 GPa
Flexural Strength
90.0 MPa
Charpy Impact Unnotched
13.5 J/cm²
Charpy Impact Unnotched
13.0 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
0.500 J/cm²
Charpy Impact, Notched
0.450 J/cm² @Temperature -30.0 °C
Tensile Creep Modulus, 1 hour
2400 MPa
Tensile Creep Modulus, 1000 hours
1600 MPa

Thermal Properties
CTE, linear, Parallel to Flow
110 µm/m-°C
Specific Heat Capacity
1.92 J/g-°C
Thermal Conductivity
0.133 W/m-K
Melting Point
225 °C
Deflection Temperature at 0.46 MPa (66 psi)
160 °C
Deflection Temperature at 1.8 MPa (264 psi)
60.0 °C
Vicat Softening Point
190 °C
Flammability, UL94
HB @Thickness 1.49 mm
Flammability, UL94
HB @Thickness 1.00 mm
Oxygen Index
22.0 %

Electrical Properties
Volume Resistivity
>= 1.00e+15 ohm-cm
Surface Resistance
>= 1.00e+15 ohm
Dielectric Constant
3.80 @Frequency 1.00e+6 Hz
Dielectric Constant
3.90 @Frequency 100 Hz
Dielectric Strength
23.0 kV/mm
Dissipation Factor
0.00130 @Frequency 100 Hz
Dissipation Factor
0.0200 @Frequency 1.00e+6 Hz
Comparative Tracking Index
600 V

Processing Properties
Processing Temperature
75.0 - 85.0 °C
Processing Temperature
250 - 260 °C
Feed Temperature
190 - 200 °C
Middle Barrel Temperature
20.0 - 50.0 °C
Zone 1
240 - 250 °C
Zone 2
240 - 250 °C
Zone 3
245 - 255 °C
Zone 4
245 - 255 °C
Die Temperature
250 - 260 °C
Melt Temperature
250 - 260 °C
Melt Temperature
265 °C
Mold Temperature
80.0 °C
Ejection Temperature
219 °C
Injection Velocity
200 mm/sec
Drying Temperature
120 - 140 °C
Dry Time
2.00 - 4.00 hour
Moisture Content
<= 0.0200 %
Hold Pressure
70.0 MPa

Descriptive Properties
Injection molding
Yes
Injection Speed
fast
Processing conditions acc. ISO
7792
pvT (Generic Grade reference)
PBT, M, A14-03

Alternative products

Celanese CELANEX 1700A PBT, Unfilled accurate 64%

$ 1560/MT

Specific Gravity: 1.31 g/cc
Density: 1.31 g/cc
Water Absorption: 0.0800 % @Temperature 22.8 °C
Moisture Absorption: 0.200 %
Viscosity Test: 130 cm³/g

Celanese CELANEX 1700FC PBT, Unfilled accurate 64%

$ 1457/MT

Specific Gravity: 1.31 g/cc
Density: 1.31 g/cc
Water Absorption: 0.0800 % @Temperature 22.8 °C
Moisture Absorption: 0.200 %
Viscosity Test: 130 cm³/g

Celanese CELANEX 1602Z PBT, Unfilled accurate 64%

$ 1960/MT

Specific Gravity: 1.31 g/cc
Density: 1.31 g/cc
Water Absorption: 0.0800 % @Temperature 22.8 °C
Linear Mold Shrinkage, Flow: 0.0180 - 0.0200 cm/cm
Linear Mold Shrinkage, Flow: 0.0200 cm/cm

Celanese Celanex® 2002UV PBT, Unfilled accurate 64%

$ 1552/MT

Specific Gravity: 1.31 g/cc
Density: 1.31 g/cc
Water Absorption: 0.090 % @Temperature 22.8 °C
Linear Mold Shrinkage, Flow: 0.018 - 0.020 cm/cm
Linear Mold Shrinkage, Flow: 0.018 - 0.020 cm/cm

Celanese CELANEX 2401 MT PBT, Medical Technology accurate 67%

$ 1562/MT

Density: 1.31 g/cc
Linear Mold Shrinkage, Flow: 0.0180 - 0.0200 cm/cm
Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 250 °C
Tensile Strength, Yield: 60.0 MPa
Tensile Strength, Yield: 30.0 MPa @Strain 50.0 %

Celanese CELANEX 2401 MT PBT, Medical Technology accurate 67%

$ 1591/MT

Density: 1.31 g/cc
Linear Mold Shrinkage, Flow: 0.0180 - 0.0200 cm/cm
Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 250 °C
Tensile Strength, Yield: 60.0 MPa
Tensile Strength, Yield: 30.0 MPa @Strain 50.0 %

Celanese Celanex® 2500 PBT (Unverified Data**) accurate 93%

$ 1669/MT

Density: 1.31 g/cc
Density of Compound: 1.11 g/cc
Moisture Absorption: 0.200 %
Viscosity Test: 85 cm³/g
Linear Mold Shrinkage, Flow: 0.018 - 0.020 cm/cm

Celanese CELANEX 2002 PBT, Unfilled accurate 86%

$ 1521/MT

Specific Gravity: 1.31 g/cc
Density: 1.31 g/cc
Water Absorption: 0.0900 % @Temperature 22.8 °C
Moisture Absorption: 0.190 %
Linear Mold Shrinkage, Flow: 0.0180 - 0.0200 cm/cm

Celanese Celanex® 2002-2 PBT (Unverified Data**) accurate 76%

$ 1547/MT

Specific Gravity: 1.31 g/cc
Density: 1.31 g/cc
Water Absorption: 0.090 %
Linear Mold Shrinkage, Flow: 0.018 - 0.020 cm/cm
Linear Mold Shrinkage, Flow: 0.018 - 0.020 cm/cm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, vessels for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Celanese CELANEX 2500 PBT, Unfilled

Seller from Dallas – 2021-07-18:

Seller from Dallas work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2568 per MT

Seller from Chongqing – 2021-04-23:

Seller from Chongqing work with company: Celanese Corporation, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2268 per MT

Seller from Delhi – 2021-03-18:

Seller from Delhi work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2350 per MT