Physical Properties
Density
1.57 g/cc
Viscosity Test
136 cm³/g

Mechanical Properties
Tensile Strength at Break
220 MPa
Tensile Strength
140 MPa @Temperature 80.0 °C
Elongation at Break
1.60 %
Elongation at Break
1.80 % @Temperature 80.0 °C
Tensile Modulus
16.8 GPa
Tensile Modulus
10.0 GPa @Temperature 80.0 °C
Flexural Strength
330 MPa
Flexural Strength
260 MPa @Temperature 80.0 °C
Flexural Modulus
15.5 GPa
Flexural Modulus
10.5 GPa @Temperature 80.0 °C
Izod Impact, Notched (ISO)
47.0 kJ/m² @Temperature -30.0 °C
Izod Impact, Notched (ISO)
54.0 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
6.00 J/cm²
Charpy Impact Unnotched
5.80 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
3.00 J/cm²
Charpy Impact, Notched
3.00 J/cm² @Temperature -30.0 °C
Puncture Energy
23.8 J

Thermal Properties
Melting Point
260 °C
Deflection Temperature at 1.8 MPa (264 psi)
258 °C
Deflection Temperature at 8.0 MPa
240 °C

Processing Properties
Processing Temperature
80.0 - 100 °C
Feed Temperature
20.0 - 50.0 °C
Middle Barrel Temperature
70.0 - 80.0 °C
Zone 1
285 - 295 °C
Zone 2
290 - 300 °C
Zone 3
300 - 310 °C
Zone 4
300 - 315 °C
Die Temperature
300 - 315 °C
Melt Temperature
305 °C
Melt Temperature
300 - 315 °C
Mold Temperature
90.0 °C
Injection Velocity
80.0 mm/sec
Drying Temperature
70.0 - 80.0 °C
Dry Time
2.00 - 4.00 hour
Moisture Content
<= 0.150 %
Injection Pressure
120 - 150 MPa
Hold Pressure
50.0 - 80.0 MPa
Hold Pressure
83.0 MPa
Back Pressure
<= 3.00 MPa
Screw Speed
25.0 rpm @Diameter 75.0 mm
Screw Speed
35.0 rpm @Diameter 55.0 mm
Screw Speed
50.0 rpm @Diameter 40.0 mm

Descriptive Properties
Heat stabilized/stable to heat
Yes
Injection molding
Yes
Sheet extrusion
Yes

Alternative products

Celanese Celstran® PA66-GF50-0112P7,5/10 Nylon 6/66, 50% Glass Reinforced accurate 81%

$ 2519/MT

Density: 1.55 g/cc
Tensile Strength at Break: 220 MPa
Tensile Strength: 140 MPa @Temperature 80.0 °C
Elongation at Break: 1.60 %
Elongation at Break: 2.40 % @Temperature 80.0 °C

Celanese Celstran® PP-GF30-0405 P10/10 PP, 30% Glass Reinforced accurate 76%

$ 1711/MT

Density: 1.13 g/cc
Tensile Strength at Break: 110 MPa
Tensile Strength: 70.0 MPa @Temperature 80.0 °C
Elongation at Break: 2.20 %
Elongation at Break: 2.30 % @Temperature 80.0 °C

Celanese Celstran® PP-GF50-0453P10/10 PP, 50% Glass Reinforced accurate 76%

$ 1640/MT

Density: 1.34 g/cc
Tensile Strength at Break: 140 MPa
Tensile Strength: 85.0 MPa @Temperature 80.0 °C
Elongation at Break: 1.8 %
Elongation at Break: 2.3 % @Temperature 80.0 °C

Celanese Celstran® PP-GF50-0453 P10/10 PP, 50% Glass Reinforced accurate 76%

$ 1474/MT

Density: 1.34 g/cc
Tensile Strength at Break: 140 MPa
Tensile Strength: 85.0 MPa @Temperature 80.0 °C
Elongation at Break: 1.80 %
Elongation at Break: 2.30 % @Temperature 80.0 °C

Celanese Celstran® PP-GF30-0553 Black PP, 30% Glass Reinforced accurate 76%

$ 2244/MT

Density: 1.12 g/cc
Tensile Strength at Break: 100 MPa
Tensile Strength: 63.0 MPa @Temperature 80.0 °C
Elongation at Break: 2.50 %
Elongation at Break: 3.30 % @Temperature 80.0 °C

Celanese Celstran® PP-GF30-0453 P10/10 PP, 30% Glass Reinforced accurate 76%

$ 2026/MT

Density: 1.12 g/cc
Tensile Strength at Break: 110 MPa
Tensile Strength: 70.0 MPa @Temperature 80.0 °C
Elongation at Break: 2.20 %
Elongation at Break: 2.30 % @Temperature 80.0 °C

Celanese Celstran® PP-GF50-0403 P10/10 PP, 50% Glass Reinforced accurate 76%

$ 2401/MT

Density: 1.34 g/cc
Tensile Strength at Break: 140 MPa
Tensile Strength: 85.0 MPa @Temperature 80.0 °C
Elongation at Break: 1.80 %
Elongation at Break: 2.30 % @Temperature 80.0 °C

Celanese Celstran® +PP-GF60-04CN15/10 PP, 60% Glass Reinforced accurate 76%

$ 1891/MT

Density: 1.43 g/cc
Tensile Strength at Break: 135 MPa
Tensile Strength: 80.0 MPa @Temperature 80.0 °C
Elongation at Break: 1.80 %
Elongation at Break: 2.00 % @Temperature 80.0 °C

Celanese Celstran® +PP-GF40-04CN03/10 PP, 40% Glass Reinforced accurate 76%

$ 1901/MT

Density: 1.22 g/cc
Tensile Strength at Break: 125 MPa
Tensile Strength: 80.0 MPa @Temperature 80.0 °C
Elongation at Break: 1.80 %
Elongation at Break: 2.00 % @Temperature 80.0 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cruise ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

5 prices for Celanese Celstran® PA66-GF50-02 P11/14 Nylon 66, 50% Glass Reinforced

Seller from Luanda – 2021-07-14:

Seller from Luanda work with company: Celanese Corporation, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $1794 per MT

Seller from Cairo – 2021-06-27:

Seller from Cairo work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2349 per MT

Seller from Hechi – 2021-04-15:

Seller from Hechi work with company: 3M, Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $1835 per MT

Seller from Dongguan – 2021-08-05:

Seller from Dongguan work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2183 per MT

Seller from London – 2021-07-08:

Seller from London work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1818 per MT