Celanese FORTRON ICE 716A PPS, 65% Mineral / Glass Reinforced (Unverified Data**) price 1562 per MT

Physical Properties
Specific Gravity
1.99 g/cc
Specific Gravity
2.00 g/cc
Density
1.95 g/cc
Density
2.00 g/cc
Water Absorption
0.020 %
Water Absorption
0.030 %
Linear Mold Shrinkage, Flow
0.0010 - 0.0020 cm/cm
Linear Mold Shrinkage, Flow
0.0020 - 0.0050 cm/cm
Linear Mold Shrinkage, Transverse
0.0030 - 0.0050 cm/cm
Linear Mold Shrinkage, Transverse
0.0030 - 0.0060 cm/cm

Mechanical Properties
Hardness, Rockwell M
100
Hardness, Rockwell M
100
Tensile Strength at Break
114 MPa
Tensile Strength at Break
130 MPa
Elongation at Break
1.2 %
Elongation at Break
1.3 % @Temperature 22.8 °C
Tensile Modulus
19.0 GPa
Flexural Strength
1.45 MPa
Flexural Strength
207 MPa
Flexural Modulus
18.8 GPa
Flexural Modulus
19.3 GPa @Temperature 22.8 °C
Izod Impact, Notched
0.641 J/cm
Izod Impact, Unnotched
2.46 J/cm
Izod Impact, Notched (ISO)
6.00 kJ/m²
Izod Impact, Notched (ISO)
6.00 kJ/m² @Temperature -30.0 °C
Izod Impact, Unnotched (ISO)
20.0 kJ/m²
Charpy Impact Unnotched
2.00 J/cm²
Charpy Impact Unnotched
2.00 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
0.700 J/cm²
Charpy Impact, Notched
0.700 J/cm² @Temperature -30.0 °C

Thermal Properties
CTE, linear
19.0 µm/m-°C
CTE, linear, Transverse to Flow
24.0 µm/m-°C
Specific Heat Capacity
1.60 J/g-°C
Melting Point
280 °C
Transformation Temperature, Tg
90.0 °C
Deflection Temperature at 0.46 MPa (66 psi)
280 °C
Deflection Temperature at 1.8 MPa (264 psi)
266 °C
Deflection Temperature at 1.8 MPa (264 psi)
270 °C
Deflection Temperature at 8.0 MPa
215 °C
Flammability, UL94
V-0 @Thickness 1.60 mm
Flammability, UL94
V-0 @Thickness 0.750 mm

Electrical Properties
Volume Resistivity
>= 1.00e+15 ohm-cm
Volume Resistivity
1.00e+16 ohm-cm
Surface Resistance
>= 1.00e+15 ohm
Dielectric Constant
4.5 @Frequency 1000 Hz
Dielectric Constant
4.5 @Frequency 1.00e+6 Hz
Dielectric Constant
5.6 @Frequency 1.00e+6 Hz
Dielectric Strength
25.0 kV/mm
Dissipation Factor
0.00090 @Frequency 1.00e+6 Hz
Dissipation Factor
0.0010 @Frequency 1000 Hz
Dissipation Factor
0.0020 @Frequency 1.00e+6 Hz
Arc Resistance
182 sec
Comparative Tracking Index
175 V

Processing Properties
Processing Temperature
20.0 - 30.0 °C
Processing Temperature
140 - 160 °C
Feed Temperature
60.0 - 80.0 °C
Zone 1
290 - 300 °C
Zone 2
310 - 320 °C
Zone 3
330 - 340 °C
Zone 4
330 - 340 °C
Die Temperature
310 - 330 °C
Melt Temperature
310 - 340 °C
Melt Temperature
330 - 340 °C
Mold Temperature
135 - 160 °C
Drying Temperature
130 - 140 °C
Dry Time
3.00 - 4.00 hour

Alternative products

Celanese FORTRON 6165A6 PPS, 65% Mineral / Glass Reinforced (Unverified Data**) accurate 99%

$ 1878/MT

Specific Gravity: 1.99 g/cc
Specific Gravity: 2.00 g/cc
Density: 1.95 g/cc
Density: 2.00 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 11400000000 PPS, 40% Glass Reinforced (Unverified Data**) accurate 70%

$ 1868/MT

Specific Gravity: 1.60 g/cc
Specific Gravity: 1.66 g/cc
Density: 1.63 g/cc
Density: 1.65 g/cc
Water Absorption: 0.020 %

Celanese FORTRON ICE 506L PPS, 40% Glass Reinforced (Unverified Data**) accurate 64%

$ 1730/MT

Specific Gravity: 1.60 g/cc
Specific Gravity: 1.61 g/cc
Density: 1.60 g/cc
Density: 1.65 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 1140L6 PPS, 40% Glass Reinforced (Unverified Data**) accurate 64%

$ 1551/MT

Specific Gravity: 1.60 g/cc
Specific Gravity: 1.61 g/cc
Density: 1.60 g/cc
Density: 1.65 g/cc
Water Absorption: 0.020 %

Celanese FORTRON ICE 716A PPS, 65% Mineral / Glass Reinforced accurate 74%

$ 1657/MT

Specific Gravity: 2.00 g/cc
Density: 0.00116 g/cc
Density: 1.95 g/cc
Water Absorption: 0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON ICE 714A PPS, 65% Mineral / Glass Reinforced accurate 70%

$ 1563/MT

Specific Gravity: 2.00 g/cc
Density: 0.00115 g/cc
Density: 1.95 g/cc
Water Absorption: 0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON 4184L6 PPS, 53% Mineral / Glass Reinforced (Unverified Data**) accurate 74%

$ 1475/MT

Specific Gravity: 1.80 g/cc
Specific Gravity: 1.80 g/cc
Density: 1.80 g/cc
Density: 1.80 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 4184L4 PPS, 53% Mineral / Glass Reinforced (Unverified Data**) accurate 70%

$ 1910/MT

Specific Gravity: 1.80 g/cc
Specific Gravity: 1.80 g/cc
Density: 1.80 g/cc
Density: 1.80 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 1140L4 PPS, 40% Glass Reinforced (Unverified Data**) accurate 66%

$ 1642/MT

Specific Gravity: 1.60 g/cc
Specific Gravity: 1.66 g/cc
Density: 1.64 g/cc
Density: 1.64 g/cc
Density: 1.65 g/cc

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cargo ship sales. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Celanese FORTRON ICE 716A PPS, 65% Mineral / Glass Reinforced (Unverified Data**)

Seller from Hyderabad – 2021-04-30:

Seller from Hyderabad work with company: PolyOne Corporation, Exxon Chemical, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1562 per MT

Seller from Shenzhen – 2021-05-22:

Seller from Shenzhen work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2121 per MT