Celanese Hostaform® C 9021 GV1/20 POM, 20% Glass Reinforced (Unverified Data**) price 1669 per MT

Physical Properties
Density
1.57 g/cc
Water Absorption
0.85 %
Melt Flow
4.5 g/10 min @Load 2.16 kg, Temperature 190 °C

Mechanical Properties
Tensile Strength at Break
120 MPa
Elongation at Break
3.0 %
Tensile Modulus
7.20 GPa
Flexural Modulus
6.90 GPa
Charpy Impact Unnotched
3.50 J/cm²
Charpy Impact Unnotched
4.00 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
0.800 J/cm²
Charpy Impact, Notched
0.800 J/cm² @Temperature -30.0 °C
Tensile Creep Modulus, 1 hour
6500 MPa
Tensile Creep Modulus, 1000 hours
4000 MPa

Thermal Properties
CTE, linear
50.0 µm/m-°C
CTE, linear, Transverse to Flow
80.0 µm/m-°C
Melting Point
166 °C
Deflection Temperature at 1.8 MPa (264 psi)
159 °C
Deflection Temperature at 8.0 MPa
105 °C
Flammability, UL94
HB @Thickness 1.60 mm
Flammability, UL94
HB @Thickness 3.00 mm
Flame Spread
<= 100 mm/min

Electrical Properties
Volume Resistivity
1.00e+14 ohm-cm
Surface Resistance
1.00e+14 ohm
Dielectric Constant
4.3 @Frequency 100 Hz
Dielectric Constant
4.3 @Frequency 1.00e+6 Hz
Dielectric Strength
35.0 kV/mm
Dissipation Factor
0.0030 @Frequency 100 Hz
Dissipation Factor
0.0060 @Frequency 1.00e+6 Hz
Comparative Tracking Index
600 V

Processing Properties
Processing Temperature
20.0 - 30.0 °C
Processing Temperature
80.0 - 120 °C
Feed Temperature
60.0 - 80.0 °C
Zone 1
170 - 180 °C
Zone 2
180 - 190 °C
Zone 3
190 - 200 °C
Zone 4
190 - 210 °C
Die Temperature
190 - 210 °C
Melt Temperature
190 - 230 °C
Mold Temperature
80.0 - 120 °C
Drying Temperature
100 - 120 °C
Dry Time
3.00 - 4.00 hour
Moisture Content
0.15 %
Injection Pressure
60.0 - 120 MPa
Hold Pressure
60.0 - 120 MPa
Back Pressure
2.00 MPa
Screw Speed
70 rpm @Diameter 55.0 mm
Screw Speed
100 rpm @Diameter 40.0 mm
Screw Speed
150 rpm @Diameter 25.0 mm
Hot-Working Temperature
190 - 210 °C

Descriptive Properties
Injection molding
Yes
Injection Speed
slow
Longer pre-drying times/storage
The product can then be stored in standard conditions until processed.
Pre-drying
Drying is not normally required with proper storage
Processing conditions
ISO 9988

Alternative products

Celanese Hostaform® C 9021 GV1/10 POM, 10% Glass Reinforced accurate 69%

$ 1567/MT

Density: 1.48 g/cc
Water Absorption at Saturation: 0.850 %
Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 90.0 MPa
Elongation at Break: 4.00 %

Celanese Hostaform® C 9021 GV1/30 POM, 30% Glass Reinforced accurate 72%

$ 1792/MT

Density: 1.60 g/cc
Density of Compound: 1.35 g/cc
Water Absorption at Saturation: 0.900 %
Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 135 MPa

Celanese Hostaform® C 9021 G POM, Tribological (Unverified Data**) accurate 72%

$ 1718/MT

Density: 1.34 g/cc
Water Absorption: 0.80 %
Linear Mold Shrinkage, Flow: 0.023 cm/cm
Linear Mold Shrinkage, Transverse: 0.018 cm/cm
Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 190 °C

Celanese Hostaform® C 9021 G POM, Tribological accurate 69%

$ 1561/MT

Density: 1.34 g/cc
Water Absorption at Saturation: 0.800 %
Linear Mold Shrinkage, Flow: 0.0230 cm/cm
Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
Melt Flow: 5.50 g/10 min @Load 2.16 kg, Temperature 190 °C

Celanese Hostaform® C 9021 GV1/10 POM, 10% Glass Reinforced (Unverified Data**) accurate 72%

$ 1641/MT

Density: 1.48 g/cc
Water Absorption: 0.85 %
Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 90.0 MPa
Elongation at Break: 4.0 %

Celanese Hostaform® C 9021 GV3/30 POM, 30% Glass Reinforced (Unverified Data**) accurate 66%

$ 1845/MT

Density: 1.59 g/cc
Density of Compound: 1.37 g/cc
Water Absorption: 0.90 %
Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 38.0 MPa

SABIC Innovative Plastics Valox® 4022 PBT (Europe-Africa-Middle East) accurate 69%

$ 2528/MT

Specific Gravity: 1.45 g/cc
Density: 1.45 g/cc
Filler Content: 20 %
Moisture Absorption: 0.0300 %
Water Absorption at Saturation: 0.15 %

Celanese Hostaform® C 9021 GV1/20 POM, 20% Glass Reinforced accurate 92%

$ 2503/MT

Density: 1.57 g/cc
Water Absorption at Saturation: 0.850 %
Melt Flow: 4.50 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 120 MPa
Elongation at Break: 3.00 %

Celanese Hostaform® C 9021 GV1/30 POM, 30% Glass Reinforced (Unverified Data**) accurate 76%

$ 2317/MT

Density: 1.60 g/cc
Density of Compound: 1.35 g/cc
Water Absorption: 0.90 %
Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 135 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, vessels for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Celanese Hostaform® C 9021 GV1/20 POM, 20% Glass Reinforced (Unverified Data**)

Seller from Rangoon – 2021-04-08:

Seller from Rangoon work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2092 per MT

Seller from New York – 2021-08-15:

Seller from New York work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1669 per MT

Seller from Barcelona – 2021-08-14:

Seller from Barcelona work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1975 per MT