Celanese Hostaform® C 9021 GV1/10 POM, 10% Glass Reinforced price 1567 per MT

Physical Properties
Density
1.48 g/cc
Water Absorption at Saturation
0.850 %
Melt Flow
6.00 g/10 min @Load 2.16 kg, Temperature 190 °C

Mechanical Properties
Tensile Strength at Break
90.0 MPa
Elongation at Break
4.00 %
Tensile Modulus
4.80 GPa
Flexural Modulus
4.50 GPa
Charpy Impact Unnotched
4.00 J/cm²
Charpy Impact Unnotched
5.00 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
0.650 J/cm²
Charpy Impact, Notched
0.650 J/cm² @Temperature -30.0 °C
Tensile Creep Modulus, 1 hour
3700 MPa
Tensile Creep Modulus, 1000 hours
2500 MPa

Thermal Properties
CTE, linear, Parallel to Flow
80.0 µm/m-°C
CTE, linear, Transverse to Flow
90.0 µm/m-°C
Melting Point
166 °C
Deflection Temperature at 1.8 MPa (264 psi)
154 °C
Deflection Temperature at 8.0 MPa
64.0 °C
Flammability, UL94
HB @Thickness 1.50 mm
Flammability, UL94
HB @Thickness 3.00 mm

Electrical Properties
Volume Resistivity
1.00e+14 ohm-cm
Surface Resistance
1.00e+14 ohm
Dielectric Constant
4.10 @Frequency 100 Hz
Dielectric Constant
4.10 @Frequency 1.00e+6 Hz
Dielectric Strength
35.0 kV/mm
Dissipation Factor
0.00300 @Frequency 100 Hz
Dissipation Factor
0.00600 @Frequency 1.00e+6 Hz
Comparative Tracking Index
600 V

Processing Properties
Processing Temperature
80.0 - 120 °C
Processing Temperature
190 - 210 °C
Feed Temperature
60.0 - 80.0 °C
Middle Barrel Temperature
20.0 - 30.0 °C
Zone 1
170 - 180 °C
Zone 2
180 - 190 °C
Zone 3
190 - 200 °C
Zone 4
190 - 210 °C
Die Temperature
190 - 210 °C
Melt Temperature
190 - 210 °C
Drying Temperature
100 - 120 °C
Dry Time
3.00 - 4.00 hour
Moisture Content
<= 0.150 %
Injection Pressure
60.0 - 120 MPa
Hold Pressure
60.0 - 120 MPa
Back Pressure
<= 2.00 MPa
Screw Speed
70.0 rpm @Diameter 55.0 mm
Screw Speed
100 rpm @Diameter 40.0 mm
Screw Speed
150 rpm @Diameter 25.0 mm

Descriptive Properties
Injection molding
Yes
Injection Speed
slow
Processing conditions acc. ISO
9988

Alternative products

Celanese Hostaform® C 9021 GV1/20 POM, 20% Glass Reinforced (Unverified Data**) accurate 71%

$ 1669/MT

Density: 1.57 g/cc
Water Absorption: 0.85 %
Melt Flow: 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 120 MPa
Elongation at Break: 3.0 %

Celanese Hostaform® C 9021 GV3/30 POM, 30% Glass Reinforced accurate 75%

$ 2043/MT

Density: 1.59 g/cc
Density of Compound: 1.37 g/cc
Water Absorption at Saturation: 0.900 %
Melt Flow: 7.50 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 38.0 MPa

SABIC Innovative Plastics Valox® VX5011 PBT (Europe-Africa-Middle East) accurate 61%

$ 2138/MT

Specific Gravity: 1.31 g/cc
Density: 1.31 g/cc
Filler Content: 10 %
Moisture Absorption: 0.100 %
Water Absorption at Saturation: 0.15 %

Celanese Hostaform® C 9021 AW XAP² ™ LS POM, Tribological accurate 61%

$ 2399/MT

Density: 1.38 g/cc
Water Absorption at Saturation: 0.650 %
Linear Mold Shrinkage, Flow: 0.0180 cm/cm
Linear Mold Shrinkage, Transverse: 0.0160 cm/cm
Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C

Celanese Hostaform® C 9021 GV1/10 POM, 10% Glass Reinforced (Unverified Data**) accurate 92%

$ 1641/MT

Density: 1.48 g/cc
Water Absorption: 0.85 %
Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 90.0 MPa
Elongation at Break: 4.0 %

Celanese Hostaform® C 9021 GV3/30 POM, 30% Glass Reinforced (Unverified Data**) accurate 71%

$ 1845/MT

Density: 1.59 g/cc
Density of Compound: 1.37 g/cc
Water Absorption: 0.90 %
Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 38.0 MPa

Celanese Hostaform® C 9021 AW POM, Tribological accurate 61%

$ 1452/MT

Density: 1.38 g/cc
Water Absorption at Saturation: 0.650 %
Linear Mold Shrinkage, Flow: 0.0210 cm/cm
Linear Mold Shrinkage, Transverse: 0.0190 cm/cm
Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C

Celanese Hostaform® C 9021 GV1/20 POM, 20% Glass Reinforced accurate 75%

$ 2503/MT

Density: 1.57 g/cc
Water Absorption at Saturation: 0.850 %
Melt Flow: 4.50 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 120 MPa
Elongation at Break: 3.00 %

Celanese Hostaform® C 9021 GV3/10 POM, 10% Glass Reinforced accurate 61%

$ 2502/MT

Density: 1.47 g/cc
Density of Compound: 1.25 g/cc
Water Absorption at Saturation: 0.800 %
Melt Flow: 9.00 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 52.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cruise ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Celanese Hostaform® C 9021 GV1/10 POM, 10% Glass Reinforced

Seller from Delhi – 2021-04-11:

Seller from Delhi work with company: 3M, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2218 per MT

Seller from Bogotá – 2021-07-26:

Seller from Bogotá work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1567 per MT

Seller from Los Angeles – 2021-06-03:

Seller from Los Angeles work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1683 per MT