Celanese Hostaform® C 9021 GV3/30 POM, 30% Glass Reinforced price 2043 per MT

Physical Properties
Density
1.59 g/cc
Density of Compound
1.37 g/cc
Water Absorption at Saturation
0.900 %
Melt Flow
7.50 g/10 min @Load 2.16 kg, Temperature 190 °C

Mechanical Properties
Tensile Strength, Yield
38.0 MPa
Elongation at Break
12.0 %
Elongation at Yield
6.00 %
Tensile Modulus
3.90 GPa
Flexural Modulus
3.50 GPa
Charpy Impact Unnotched
4.00 J/cm²
Charpy Impact Unnotched
4.00 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
0.300 J/cm²
Charpy Impact, Notched
0.300 J/cm² @Temperature -30.0 °C
Tensile Creep Modulus, 1 hour
3300 MPa
Tensile Creep Modulus, 1000 hours
2100 MPa

Thermal Properties
CTE, linear, Parallel to Flow
90.0 µm/m-°C
CTE, linear, Transverse to Flow
90.0 µm/m-°C
Specific Heat Capacity
1.78 J/g-°C
Thermal Conductivity
0.225 W/m-K
Melting Point
166 °C
Deflection Temperature at 1.8 MPa (264 psi)
112 °C
Flammability, UL94
HB @Thickness 1.57 mm
Flammability, UL94
HB @Thickness 0.810 mm

Electrical Properties
Volume Resistivity
1.00e+14 ohm-cm
Surface Resistance
1.00e+14 ohm
Dielectric Constant
4.50 @Frequency 1.00e+6 Hz
Dielectric Constant
5.00 @Frequency 100 Hz
Dielectric Strength
40.0 kV/mm
Dissipation Factor
0.00800 @Frequency 1.00e+6 Hz
Dissipation Factor
0.0300 @Frequency 100 Hz
Comparative Tracking Index
600 V

Processing Properties
Processing Temperature
80.0 - 120 °C
Processing Temperature
190 - 210 °C
Feed Temperature
60.0 - 80.0 °C
Middle Barrel Temperature
20.0 - 30.0 °C
Zone 1
170 - 180 °C
Zone 2
180 - 190 °C
Zone 3
190 - 200 °C
Zone 4
190 - 210 °C
Die Temperature
190 - 210 °C
Melt Temperature
190 - 210 °C
Ejection Temperature
140 °C
Drying Temperature
100 - 120 °C
Dry Time
3.00 - 4.00 hour
Moisture Content
<= 0.150 %
Injection Pressure
60.0 - 120 MPa
Hold Pressure
60.0 - 120 MPa
Back Pressure
<= 2.00 MPa
Screw Speed
70.0 rpm @Diameter 55.0 mm
Screw Speed
100 rpm @Diameter 40.0 mm
Screw Speed
150 rpm @Diameter 25.0 mm

Descriptive Properties
Eff. thermal diffusivity
7.3E-08
Injection molding
Yes
Injection Speed
slow
Processing conditions acc. ISO
9988

Alternative products

Celanese Hostaform® C 9021 GV1/10 POM, 10% Glass Reinforced accurate 72%

$ 1567/MT

Density: 1.48 g/cc
Water Absorption at Saturation: 0.850 %
Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 90.0 MPa
Elongation at Break: 4.00 %

Celanese Hostaform® C 9021 GV1/30 POM, 30% Glass Reinforced accurate 63%

$ 1792/MT

Density: 1.60 g/cc
Density of Compound: 1.35 g/cc
Water Absorption at Saturation: 0.900 %
Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 135 MPa

Celanese Hostaform® C 27021 GV3/30 POM, 30% Glass Reinforced accurate 78%

$ 1494/MT

Density: 1.59 g/cc
Water Absorption at Saturation: 0.900 %
Melt Flow: 16.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 38.0 MPa
Elongation at Break: 12.0 %

Celanese Hostaform® C 9021 K POM, Tribological accurate 63%

$ 1523/MT

Density: 1.44 g/cc
Density of Compound: 1.23 g/cc
Water Absorption at Saturation: 0.650 %
Linear Mold Shrinkage, Flow: 0.0200 cm/cm
Linear Mold Shrinkage, Transverse: 0.0180 cm/cm

Celanese Hostaform® C 9021 GV1/10 POM, 10% Glass Reinforced (Unverified Data**) accurate 66%

$ 1641/MT

Density: 1.48 g/cc
Water Absorption: 0.85 %
Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 90.0 MPa
Elongation at Break: 4.0 %

Celanese Hostaform® C 9021 GV3/20 POM, 20% Glass Reinforced accurate 63%

$ 1749/MT

Density: 1.53 g/cc
Water Absorption at Saturation: 0.800 %
Melt Flow: 8.50 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 46.0 MPa
Elongation at Break: 15.0 %

Celanese Hostaform® C 9021 GV3/30 POM, 30% Glass Reinforced (Unverified Data**) accurate 87%

$ 1845/MT

Density: 1.59 g/cc
Density of Compound: 1.37 g/cc
Water Absorption: 0.90 %
Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 38.0 MPa

Celanese Hostaform® C 9021 GV1/20 POM, 20% Glass Reinforced accurate 66%

$ 2503/MT

Density: 1.57 g/cc
Water Absorption at Saturation: 0.850 %
Melt Flow: 4.50 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 120 MPa
Elongation at Break: 3.00 %

Celanese Hostaform® C 9021 GV3/10 POM, 10% Glass Reinforced accurate 63%

$ 2502/MT

Density: 1.47 g/cc
Density of Compound: 1.25 g/cc
Water Absorption at Saturation: 0.800 %
Melt Flow: 9.00 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 52.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale ru. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Celanese Hostaform® C 9021 GV3/30 POM, 30% Glass Reinforced

Seller from Lima – 2021-04-22:

Seller from Lima work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2150 per MT

Seller from Madrid – 2021-04-29:

Seller from Madrid work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2043 per MT