Celanese Hostaform® S 27064 XAP2® POM, Impact Modified

Seller in Manila price: $2337 per MT

Celanese Hostaform® S 27064 XAP2® POM, Impact Modified in Polymer, Thermoplastic, Acetal (POM)

  • Physical Properties
  • Density
  • 1.37 g/cc
  • Water Absorption
  • 0.65 %
  • Linear Mold Shrinkage, Flow
  • 0.018 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.0017 cm/cm
  • Melt Flow
  • 18 g/10 min @Load 2.16 kg, Temperature 190 °C
  • Mechanical Properties
  • Tensile Strength, Yield
  • 44.0 MPa
  • Elongation at Break
  • 35 %
  • Elongation at Yield
  • 10 %
  • Tensile Modulus
  • 1.70 GPa
  • Flexural Modulus
  • 1.70 GPa
  • Shear Modulus
  • 100 GPa @Temperature 150 °C
  • Shear Modulus
  • 200 GPa @Temperature 100 °C
  • Shear Modulus
  • 300 GPa @Temperature 50.0 °C
  • Shear Modulus
  • 800 GPa @Temperature 0.000 °C
  • Shear Modulus
  • 1200 GPa @Temperature -50.0 °C
  • Charpy Impact Unnotched
  • 11.0 J/cm² @Temperature -30.0 °C
  • Charpy Impact Unnotched
  • 15.0 J/cm² @Temperature 23.0 °C
  • Charpy Impact, Notched
  • 0.600 J/cm² @Temperature -30.0 °C
  • Charpy Impact, Notched
  • 1.10 J/cm² @Temperature 23.0 °C
  • Tensile Creep Modulus, 1 hour
  • 1400 MPa
  • Tensile Creep Modulus, 1000 hours
  • 800 MPa
  • Thermal Properties
  • CTE, linear, Parallel to Flow
  • 1.30 µm/m-°C
  • Melting Point
  • 166 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 77.0 °C
  • Electrical Properties
  • Volume Resistivity
  • 1.00e+11 ohm-cm
  • Surface Resistance
  • 1.00e+13 ohm
  • Dielectric Constant
  • 4.4 @Frequency 100 Hz
  • Dielectric Constant
  • 4.4 @Frequency 1.00e+6 Hz
  • Dielectric Strength
  • 28.0 kV/mm
  • Dissipation Factor
  • 0.010 @Frequency 100 Hz
  • Dissipation Factor
  • 0.020 @Frequency 1.00e+6 Hz
  • Comparative Tracking Index
  • 600 V
  • Processing Properties
  • Feed Temperature
  • 60.0 - 80.0 °C
  • Nozzle Temperature
  • 190 - 200 °C
  • Zone 1
  • 170 - 180 °C
  • Zone 2
  • 180 - 190 °C
  • Zone 3
  • 190 - 200 °C
  • Zone 4
  • 190 - 200 °C
  • Melt Temperature
  • 190 - 200 °C
  • Mold Temperature
  • 60.0 - 70.0 °C
  • Drying Temperature
  • 100 - 120 °C
  • Dry Time
  • 3 - 4 hour
  • Moisture Content
  • <= 0.15 %
  • Injection Pressure
  • 60.0 - 120 MPa
  • Hold Pressure
  • 60.0 - 120 MPa
  • Back Pressure
  • 0.000 - 2.00 MPa
  • Screw Speed
  • 70 rpm @Diameter 55.0 mm
  • Screw Speed
  • 100 rpm @Diameter 40.0 mm
  • Screw Speed
  • 150 rpm @Diameter 25.0 mm
  • Descriptive Properties
  • Hopper
  • 20-30°C
  • Manifold
  • 190-200°C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, chemical carrier for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Celanese Hostaform® S 27064 XAP2® POM, Impact Modified

Seller from Manila – 2021-07-19:

Seller from Manila work with company: Solvay, Techmer ES, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $2337 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Celanese Hostaform® S 27064 XAP2® POM, Impact Modified?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Tool & die shop in Singapore open-nearme.com