Celanese Hostaform® S 9362 XAP2 ™ POM, Impact Modified price 1570 per MT

Physical Properties
Density
1.39 g/cc
Water Absorption at Saturation
0.80 %

Mechanical Properties
Tensile Strength, Yield
55.0 MPa
Elongation at Yield
10 %
Tensile Modulus
2.30 GPa
Flexural Modulus
2.20 GPa
Charpy Impact Unnotched
NB
Charpy Impact Unnotched
19.0 J/cm² @Temperature 30.0 °C
Charpy Impact, Notched
1.00 J/cm²
Charpy Impact, Notched
0.600 J/cm² @Temperature 30.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
110 µm/m-°C
CTE, linear, Transverse to Flow
110 µm/m-°C
Melting Point
166 °C
Deflection Temperature at 0.46 MPa (66 psi)
151 °C
Deflection Temperature at 1.8 MPa (264 psi)
87.0 °C

Processing Properties
Processing Temperature
80.0 - 120 °C
Zone 1
170 - 180 °C
Zone 2
180 - 190 °C
Zone 3
180 - 190 °C
Zone 4
180 - 200 °C
Die Temperature
180 - 200 °C
Melt Temperature
180 - 200 °C
Drying Temperature
80.0 - 100 °C
Dry Time
3 hour
Injection Pressure
60.0 - 120 MPa
Hold Pressure
60.0 - 120 MPa
Back Pressure
<= 0.500 MPa

Descriptive Properties
Injection molding
Yes
Injection Speed
slow
Melt volume rate (MVR), cm³/10min
6.5
MVR test load, kg
2.16
MVR test temperature, °C
190
Processing conditions acc. ISO
9988-2
Profile extrusion
Yes
Remarks
Do not heat over 205 C (~400 F) to avoid burning and discoloring product.

Alternative products

Celanese Hostaform® S 9362 POM, Impact Modified accurate 94%

$ 1660/MT

Density: 1.39 g/cc
Water Absorption at Saturation: 0.800 %
Linear Mold Shrinkage, Flow: 0.0190 cm/cm
Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
Melt Flow: 6.50 g/10 min @Load 2.16 kg, Temperature 190 °C

Celanese Celcon® LW90-S2 POM, Tribological accurate 73%

$ 2066/MT

Specific Gravity: 1.40 g/cc
Density: 1.38 g/cc
Linear Mold Shrinkage, Flow: 0.0190 cm/cm
Linear Mold Shrinkage, Flow: 0.0220 cm/cm
Linear Mold Shrinkage, Transverse: 0.0160 cm/cm

Celanese Hostaform® S 9362 POM, Impact Modified (Unverified Data**) accurate 83%

$ 1618/MT

Density: 1.39 g/cc
Water Absorption: 0.80 %
Linear Mold Shrinkage, Flow: 0.019 cm/cm
Linear Mold Shrinkage, Transverse: 0.018 cm/cm
Melt Flow: 6.5 g/10 min @Load 2.16 kg, Temperature 190 °C

Celanese Hostaform® S 9362 XAP² ™ POM, Impact Modified accurate 94%

$ 1749/MT

Density: 1.39 g/cc
Water Absorption at Saturation: 0.800 %
Linear Mold Shrinkage, Flow: 0.0190 cm/cm
Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
Melt Flow: 6.50 g/10 min @Load 2.16 kg, Temperature 190 °C

Celanese Hostaform® S 9363 POM, Impact Modified accurate 73%

$ 1471/MT

Density: 1.38 g/cc
Water Absorption at Saturation: 0.800 %
Linear Mold Shrinkage, Flow: 0.0180 cm/cm
Linear Mold Shrinkage, Transverse: 0.0160 cm/cm
Melt Flow: 5.50 g/10 min @Load 2.16 kg, Temperature 190 °C

Celanese Hostaform® S 9363 XAP² ™ POM, Impact Modified accurate 73%

$ 1658/MT

Density: 1.38 g/cc
Water Absorption at Saturation: 0.800 %
Linear Mold Shrinkage, Flow: 0.0180 cm/cm
Linear Mold Shrinkage, Transverse: 0.0160 cm/cm
Melt Flow: 5.50 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66 (Unverified Data**) accurate 78%

$ 1463/MT

Density: 1.01 g/cc
Density: 1.14 g/cc
Water Absorption: 8.5 % @Thickness 2.00 mm
Moisture Absorption: 2.60 % @Thickness 2.00 mm
Viscosity: 42210 cP @Shear Rate 5000 1/s, Temperature 295 °C

Celanese Hostaform® S 9363 XAP2 ™ POM, Impact Modified accurate 78%

$ 2152/MT

Density: 1.38 g/cc
Water Absorption at Saturation: 0.80 %
Tensile Strength, Yield: 50.0 MPa
Elongation at Yield: 12 %
Tensile Modulus: 2.00 GPa

Celanese Hostaform® S 9362 XAP² ™ POM, Impact Modified (Unverified Data**) accurate 83%

$ 1975/MT

Density: 1.39 g/cc
Water Absorption: 0.80 %
Linear Mold Shrinkage, Flow: 0.019 cm/cm
Linear Mold Shrinkage, Transverse: 0.018 cm/cm
Melt Flow: 6.5 g/10 min @Load 2.16 kg, Temperature 190 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ship tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

7 prices for Celanese Hostaform® S 9362 XAP2 ™ POM, Impact Modified

Seller from Kinshasa – 2021-08-11:

Seller from Kinshasa work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2324 per MT

Seller from Montréal – 2021-04-05:

Seller from Montréal work with company: 3M, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co., ALIMEX GmbH

Price: $2188 per MT

Seller from Shanghai – 2021-04-20:

Seller from Shanghai work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1570 per MT

Seller from Hāora – 2021-05-16:

Seller from Hāora work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1789 per MT

Seller from Alexandria – 2021-03-31:

Seller from Alexandria work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2106 per MT

Seller from Chennai – 2021-07-13:

Seller from Chennai work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2164 per MT

Seller from Dallas – 2021-06-24:

Seller from Dallas work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1771 per MT