Celanese Zenite® 6140L WT010 LCP

Seller in Toronto price: $2282 per MT
Seller in Delhi price: $2340 per MT

Celanese Zenite® 6140L WT010 LCP in Polymer, Thermoplastic, 40% Glass Fiber Filled, Liquid Crystal Polymer (LCP)

  • Physical Properties
  • Density
  • 1.77 g/cc
  • Filler Content
  • 40 %
  • Linear Mold Shrinkage, Flow
  • 0.00050 cm/cm @Thickness 2.00 mm
  • Linear Mold Shrinkage, Transverse
  • 0.0050 cm/cm @Thickness 2.00 mm
  • Mechanical Properties
  • Tensile Strength at Break
  • 125 MPa
  • Elongation at Break
  • 1.3 %
  • Tensile Modulus
  • 17.3 GPa @Temperature 23.0 °C
  • Flexural Strength
  • 200 MPa @Temperature 23.0 °C
  • Flexural Modulus
  • 14.5 GPa @Temperature 23.0 °C
  • Izod Impact, Notched (ISO)
  • 10.0 kJ/m² @Temperature 23.0 °C
  • Izod Impact, Unnotched (ISO)
  • 20.0 kJ/m² @Temperature -30.0 °C
  • Izod Impact, Unnotched (ISO)
  • 20.0 kJ/m² @Temperature 23.0 °C
  • Charpy Impact Unnotched
  • 1.80 J/cm² @Temperature -30.0 °C
  • Charpy Impact Unnotched
  • 2.00 J/cm² @Temperature 23.0 °C
  • Charpy Impact, Notched
  • 1.40 J/cm² @Temperature 23.0 °C
  • Charpy Impact, Notched
  • 1.50 J/cm² @Temperature -30.0 °C
  • Thermal Properties
  • CTE, linear
  • 0.000 µm/m-°C @Thickness 2.00 mm, Temperature 160 - 260 °C
  • CTE, linear
  • 2.00 µm/m-°C @Thickness 4.00 mm, Temperature 160 - 260 °C
  • CTE, linear
  • 3.00 µm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 23.0 °C
  • CTE, linear
  • 3.00 µm/m-°C @Thickness 2.00 mm, Temperature -40.0 - 23.0 °C
  • CTE, linear
  • 3.00 µm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 260 °C
  • CTE, linear
  • 3.00 µm/m-°C @Thickness 2.00 mm, Temperature -40.0 - 260 °C
  • CTE, linear
  • 3.00 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C
  • CTE, linear
  • 3.00 µm/m-°C @Thickness 2.00 mm, Temperature 55.0 - 160 °C
  • CTE, linear
  • 4.00 µm/m-°C @Thickness 4.00 mm, Temperature 23.0 - 55.0 °C
  • CTE, linear
  • 5.00 µm/m-°C @Thickness 4.00 mm, Temperature 55.0 - 160 °C
  • CTE, linear, Transverse to Flow
  • 55.0 µm/m-°C @Temperature -40.0 - 23.0 °C
  • CTE, linear, Transverse to Flow
  • 56.0 µm/m-°C @Temperature -40.0 - 23.0 °C
  • CTE, linear, Transverse to Flow
  • 77.0 µm/m-°C @Temperature -40.0 - 260 °C
  • CTE, linear, Transverse to Flow
  • 79.0 µm/m-°C @Temperature -40.0 - 260 °C
  • CTE, linear, Transverse to Flow
  • 62.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C
  • CTE, linear, Transverse to Flow
  • 64.0 µm/m-°C @Thickness 4.00 mm, Temperature 23.0 - 55.0 °C
  • CTE, linear, Transverse to Flow
  • 80.0 µm/m-°C @Thickness 2.00 mm, Temperature 55.0 - 160 °C
  • CTE, linear, Transverse to Flow
  • 82.0 µm/m-°C @Thickness 4.00 mm, Temperature 55.0 - 160 °C
  • CTE, linear, Transverse to Flow
  • 90.0 µm/m-°C @Thickness 2.00 mm, Temperature 160 - 260 °C
  • CTE, linear, Transverse to Flow
  • 94.0 µm/m-°C @Thickness 4.00 mm, Temperature 160 - 260 °C
  • Melting Point
  • 335 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 280 °C
  • UL RTI, Electrical
  • 240 °C @Thickness 1.50 mm
  • UL RTI, Electrical
  • 240 °C @Thickness 3.00 mm
  • UL RTI, Mechanical with Impact
  • 220 °C @Thickness 1.50 mm
  • UL RTI, Mechanical with Impact
  • 220 °C @Thickness 3.00 mm
  • UL RTI, Mechanical without Impact
  • 240 °C @Thickness 1.50 mm
  • UL RTI, Mechanical without Impact
  • 240 °C @Thickness 3.00 mm
  • Flammability, UL94
  • V-0 @Thickness 1.50 mm
  • Flammability, UL94
  • V-0 @Thickness 1.50 mm
  • Flammability, UL94
  • V-0 @Thickness 3.00 mm
  • Flammability, UL94
  • V-0 @Thickness 3.00 mm
  • Electrical Properties
  • Comparative Tracking Index
  • 175 - 249 V
  • Processing Properties
  • Melt Temperature
  • 355 °C
  • Melt Temperature
  • 350 - 360 °C
  • Mold Temperature
  • 80.0 °C
  • Mold Temperature
  • 40.0 - 150 °C
  • Drying Temperature
  • 150 °C
  • Dry Time
  • 3 hour
  • Moisture Content
  • <= 0.010 %
  • Descriptive Properties
  • Color
  • White
  • Drying Recommended
  • Yes
  • Filler
  • Glass Reinforced
  • Flame Retardant - Halogen/Red Phosphorus Free
  • Yes
  • Forms
  • Pellets
  • Generic
  • LCP
  • Part Marking Code
  • >LCP-GF40<
  • Polymer Family
  • LCP
  • Polymer Type
  • LCP
  • Processing
  • Injection Moldable
  • Processing Method
  • Injection Molding
  • Product Category
  • Electrical Resins
  • Product Category
  • Electrical Resins
  • Product Category
  • Flame Retardant Resins
  • Product Category
  • Flame Retardant Resins
  • Product Category
  • Glass Reinforced Resins
  • Product Category
  • Glass Reinforced Resins
  • Region Available
  • Americas
  • Region Available
  • Asia/Pacific
  • Region Available
  • Europe
  • Resin Identification
  • LCP-GF40

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Celanese Zenite® 6140L WT010 LCP

Seller from Toronto – 2021-07-12:

Seller from Toronto work with company: Solvay, Dow Corning, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2282 per MT

Seller from Delhi – 2021-06-18:

Seller from Delhi work with company: Hexcel, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2340 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Celanese Zenite® 6140L WT010 LCP?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Glass manufacturer in Singapore open-nearme.com