CP-Polymer-Technik Wellamid® 6000 GV 20 HWCP 20% Glass Fiber Nylon 6, Heat Stabilized, Conditioned price 2224 per MT

Physical Properties
Density
1.29 g/cc
Moisture Absorption at Equilibrium
2.0 - 2.5 %
Linear Mold Shrinkage
0.0030 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse
0.0090 cm/cm @Thickness 4.00 mm

Mechanical Properties
Tensile Strength at Break
90.0 MPa
Elongation at Break
8.0 %
Tensile Modulus
4.50 GPa
Charpy Impact Unnotched
10.5 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
2.30 J/cm² @Temperature 23.0 °C

Thermal Properties
Melting Point
215 °C

Electrical Properties
Volume Resistivity
1.00e+12 ohm-cm
Surface Resistance
1.00e+10 ohm
Dielectric Constant
7.0 @Frequency 1e+6 Hz
Dielectric Strength
35.0 kV/mm
Dielectric Loss Index
0.24

Processing Properties
Melt Temperature
250 - 280 °C
Mold Temperature
60.0 - 90.0 °C

Descriptive Properties
Back Pressure
Low
Holding Pressure
High
Injection Speed
Medium to High
Screw Speed
High

Alternative products

CP-Polymer-Technik Wellamid® 6000 MRGV 20/10 HWCP 20% Mineral and 10% Glass Fiber Nylon 6, Heat Stabilized, Conditioned accurate 89%

$ 2183/MT

Density: 1.38 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0060 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 60.0 MPa

CP-Polymer-Technik Wellamid® 6000 GVS 10/30 HWCP 10% Glass Fiber and 30% Glass Sphere Nylon 6, Heat Stabilized, Conditioned accurate 79%

$ 1835/MT

Density: 1.46 g/cc
Moisture Absorption at Equilibrium: 1.5 - 2.0 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 65.0 MPa

CP-Polymer-Technik Wellamid® 6600 MF30 HWCP 30% Milled Glass Fiber Nylon 66, Heat Stabilized, Conditioned accurate 79%

$ 2353/MT

Density: 1.36 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 90.0 MPa

CP-Polymer-Technik Wellamid® 6600/58 GV 30 HWCP 30% Glass Fiber Nylon 66, Impact Modified Until -40°C, Heat Stabilized, Conditioned accurate 79%

$ 2451/MT

Density: 1.27 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0020 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 90.0 MPa

CP-Polymer-Technik Wellamid® 6000 MRGV 25/15 HWCP 25% Mineral and 15% Glass Fiber Nylon 6, Heat Stabilized, Conditioned accurate 79%

$ 1655/MT

Density: 1.47 g/cc
Moisture Absorption at Equilibrium: 1.5 - 2.0 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 70.0 MPa

CP-Polymer-Technik Wellamid® 6000 MF 30 HWCP 30% Milled Glass Fiber Nylon 6, Heat Stabilized, Conditioned accurate 79%

$ 1826/MT

Density: 1.32 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 80.0 MPa

CP-Polymer-Technik Wellamid® 6600/50 GV 30 HWCP 30% Glass Fiber Nylon 66, Impact Modified Until 0°C, Heat Stabilized, Conditioned accurate 69%

$ 1739/MT

Density: 1.29 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0020 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 90.0 MPa

CP-Polymer-Technik Wellamid® 6000 GVS 10/20 HWCP 10% Glass Fiber and 20% Glass Sphere Nylon 6, Heat Stabilized, Conditioned accurate 79%

$ 2523/MT

Density: 1.38 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 60.0 MPa

CP-Polymer-Technik Wellamid® 6000 MRGV 25/15 HWUVCP 25% Mineral and 15% Glass Fiber Nylon 6, UV Stabilized, Heat Stabilized, Conditioned accurate 79%

$ 1967/MT

Density: 1.47 g/cc
Moisture Absorption at Equilibrium: 1.5 - 2.0 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 70.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cargo ship for sale in india. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for CP-Polymer-Technik Wellamid® 6000 GV 20 HWCP 20% Glass Fiber Nylon 6, Heat Stabilized, Conditioned

Seller from Taipei – 2021-04-02:

Seller from Taipei work with company: Solvay, RTP Company, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics)

Price: $2224 per MT