DuPont Performance Polymers Crastin® 6131 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**) price 2063 per MT

Physical Properties
Density
1.11 g/cc
Density
1.30 g/cc
Water Absorption
0.40 % @Thickness 2.00 mm
Moisture Absorption
0.200 % @Thickness 2.00 mm
Viscosity
68390 cP @Shear Rate 5000 1/s, Temperature 260 °C
Viscosity
79240 cP @Shear Rate 5000 1/s, Temperature 250 °C
Viscosity
91390 cP @Shear Rate 5000 1/s, Temperature 240 °C
Viscosity
130000 cP @Shear Rate 500 1/s, Temperature 260 °C
Viscosity
169100 cP @Shear Rate 500 1/s, Temperature 250 °C
Viscosity
222100 cP @Shear Rate 500 1/s, Temperature 240 °C
Viscosity Test
110 cm³/g
Linear Mold Shrinkage, Flow
0.017 cm/cm
Linear Mold Shrinkage, Transverse
0.016 cm/cm
Melt Flow
48 g/10 min @Load 2.16 kg, Temperature 250 °C

Mechanical Properties
Tensile Stress
10.0 MPa @Strain 0.380 %, Time 3600 sec
Tensile Stress
10.0 MPa @Strain 0.550 %, Time 36000 sec
Tensile Stress
10.0 MPa @Strain 0.770 %, Time 360000 sec
Tensile Stress
10.0 MPa @Strain 1.10 %, Time 3.60e+6 sec
Tensile Stress
10.0 MPa @Strain 1.45 %, Time 3.60e+7 sec
Tensile Strength, Yield
59.0 MPa
Elongation at Break
30 %
Elongation at Yield
6.0 %
Tensile Modulus
2.60 GPa
Flexural Strength
85.0 MPa
Shear Modulus
0.110 GPa @Temperature 150 °C
Shear Modulus
0.160 GPa @Temperature 110 °C
Shear Modulus
0.340 GPa @Temperature 60.0 °C
Shear Modulus
1.06 GPa @Temperature 10.0 °C
Shear Modulus
1.12 GPa @Temperature -20.0 °C
Shear Modulus
1.20 GPa @Temperature -50.0 °C
Izod Impact, Notched (ISO)
3.50 kJ/m²
Charpy Impact Unnotched
NB
Charpy Impact Unnotched
NB @Temperature -30.0 °C
Charpy Impact, Notched
0.400 J/cm²
Charpy Impact, Notched
0.400 J/cm² @Temperature -30.0 °C
Tensile Creep Modulus, 1 hour
909 MPa @Pressure 30.0 MPa, Temperature 23.0 °C
Tensile Creep Modulus, 1 hour
975.61 MPa @Pressure 5.00 MPa, Temperature 23.0 °C
Tensile Creep Modulus, 1 hour
1170 MPa @Pressure 25.0 MPa, Temperature 23.0 °C
Tensile Creep Modulus, 1 hour
1670 MPa @Pressure 20.0 MPa, Temperature 23.0 °C
Tensile Creep Modulus, 1 hour
2270 MPa @Pressure 15.0 MPa, Temperature 23.0 °C
Tensile Creep Modulus, 1 hour
2630 MPa @Pressure 10.0 MPa, Temperature 23.0 °C
Tensile Creep Modulus, 1 hour
2810 MPa @Pressure 5.00 MPa, Temperature 23.0 °C
Tensile Creep Modulus, 1000 hours
455 MPa @Pressure 25.0 MPa, Temperature 23.0 °C
Tensile Creep Modulus, 1000 hours
606 MPa @Pressure 20.0 MPa, Temperature 23.0 °C
Tensile Creep Modulus, 1000 hours
789 MPa @Pressure 15.0 MPa, Temperature 23.0 °C
Tensile Creep Modulus, 1000 hours
909 MPa @Pressure 10.0 MPa, Temperature 23.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
108 µm/m-°C
CTE, linear, Transverse to Flow
144 µm/m-°C
Specific Heat Capacity
2.05 J/g-°C
Thermal Conductivity
0.250 W/m-K
Melting Point
225 °C
Deflection Temperature at 0.46 MPa (66 psi)
115 °C
Deflection Temperature at 0.46 MPa (66 psi)
180 °C
Deflection Temperature at 1.8 MPa (264 psi)
50.0 °C
Deflection Temperature at 1.8 MPa (264 psi)
60.0 °C
Vicat Softening Point
175 °C
Flammability, UL94
HB @Thickness 1.50 mm
Flammability, UL94
HB @Thickness 0.900 mm
Oxygen Index
22 %

Electrical Properties
Volume Resistivity
>= 1.00e+15 ohm-cm
Surface Resistance
1.00e+12 ohm
Dielectric Strength
26.0 kV/mm
Comparative Tracking Index
600 V

Descriptive Properties
Delivery Form
Pellets
Part Marking Code
>PBT<
Processing
Casting
Processing
Coatable
Processing
Film Extrusion
Processing
Injection Moulding
Processing
Other Extrusion
Processing
Profile Extrusion
Processing
Sheet Extrusion
Regional Availability
Europe
Regional Availability
Near East/Africa
Resin Identification
PBT
UL recognition
UL

Alternative products

DuPont Performance Polymers Crastin® S650FR NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)< accurate 57%

$ 1538/MT

Density: 1.46 g/cc
Water Absorption: 0.39 % @Thickness 2.00 mm
Moisture Absorption: 0.150 % @Thickness 2.00 mm
Linear Mold Shrinkage, Flow: 0.018 cm/cm
Linear Mold Shrinkage, Flow: 0.022 cm/cm

DuPont Performance Polymers Crastin® FG6129 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)< accurate 86%

$ 1901/MT

Density: 1.12 g/cc
Density: 1.30 g/cc
Water Absorption: 0.40 % @Thickness 2.00 mm
Moisture Absorption: 0.200 % @Thickness 2.00 mm
Viscosity Test: 150 cm³/g

DuPont Performance Polymers Crastin® SO653 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**) accurate 57%

$ 1536/MT

Density: 1.25 g/cc
Density: 1.45 g/cc
Water Absorption: 0.35 % @Thickness 2.00 mm
Moisture Absorption: 0.200 % @Thickness 2.00 mm
Viscosity: 157000 cP @Shear Rate 5000 1/s, Temperature 260 °C

DuPont Performance Polymers Crastin® FG6130 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)< accurate 89%

$ 2085/MT

Density: 1.12 g/cc
Density: 1.30 g/cc
Water Absorption: 0.40 % @Thickness 2.00 mm
Moisture Absorption: 0.200 % @Thickness 2.00 mm
Viscosity Test: 130 cm³/g

DuPont Performance Polymers Crastin® S620F20 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)&l accurate 80%

$ 1469/MT

Density: 1.11 g/cc
Density: 1.31 g/cc
Water Absorption: 0.40 % @Thickness 2.00 mm
Moisture Absorption: 0.200 % @Thickness 2.00 mm
Viscosity: 92000 cP @Shear Rate 5000 1/s, Temperature 260 °C

DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66 (Unverified Data**) accurate 57%

$ 1463/MT

Density: 1.01 g/cc
Density: 1.14 g/cc
Water Absorption: 8.5 % @Thickness 2.00 mm
Moisture Absorption: 2.60 % @Thickness 2.00 mm
Viscosity: 42210 cP @Shear Rate 5000 1/s, Temperature 295 °C

DuPont Performance Polymers Crastin® S600F40 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)&l accurate 89%

$ 1837/MT

Density: 1.11 g/cc
Density: 1.31 g/cc
Water Absorption: 0.40 % @Thickness 2.00 mm
Moisture Absorption: 0.200 % @Thickness 2.00 mm
Viscosity: 75900 cP @Shear Rate 5000 1/s, Temperature 260 °C

DuPont Performance Polymers Crastin® S610SF NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)< accurate 57%

$ 1517/MT

Density: 1.11 g/cc
Density: 1.31 g/cc
Water Absorption: 0.40 % @Thickness 2.00 mm
Moisture Absorption: 0.200 % @Thickness 2.00 mm
Viscosity: 66530 cP @Shear Rate 5000 1/s, Temperature 260 °C

DuPont Performance Polymers Crastin® FGS600F10 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**) accurate 64%

$ 1868/MT

Density: 1.11 g/cc
Density: 1.30 g/cc
Water Absorption: 0.50 % @Thickness 2.00 mm
Moisture Absorption: 0.200 % @Thickness 2.00 mm
Linear Mold Shrinkage, Flow: 0.017 cm/cm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, vessels for sale norway. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for DuPont Performance Polymers Crastin® 6131 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)

Seller from Delhi – 2021-08-11:

Seller from Delhi work with company: Solvay, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co., ALIMEX GmbH

Price: $2338 per MT

Seller from Mexico City – 2021-04-29:

Seller from Mexico City work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2063 per MT

Seller from Jakarta – 2021-05-09:

Seller from Jakarta work with company: Solvay, RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $2517 per MT