$ 2439/MT
- Density: 1.62 g/cc
- Viscosity Test: 120 cm³/g
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 325 °C
$ 1526/MT
- Density: 1.35 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm @Thickness 2.00 mm
- Tensile Strength at Break: 123 MPa @Temperature 23.0 °C
$ 1772/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength at Break: 235 MPa
- Elongation at Break: 2.4 %
$ 2216/MT
- Density: 1.25 g/cc
- Density: 1.40 g/cc
- Water Absorption at Saturation: 0.080 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
$ 2203/MT
- Density: 1.56 g/cc
- Tensile Strength at Break: 142 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 10.6 GPa
- Flexural Strength: 215 MPa
$ 1657/MT
- Density: 1.05 g/cc
- Density: 1.23 g/cc
- Water Absorption: 0.34 % @Thickness 2.00 mm
- Moisture Absorption: 0.110 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.080 %
$ 1650/MT
- Density: 1.07 g/cc
- Water Absorption: 3.3 % @Thickness 2.00 mm
- Moisture Absorption: 1.40 % @Thickness 2.00 mm
- Viscosity Test: 150 cm³/g
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
$ 1673/MT
- Density: 1.09 g/cc
- Water Absorption: 1.07 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.022 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm @Thickness 2.00 mm
- Tensile Strength at Break: 45.0 MPa @Temperature 23.0 °C
$ 1538/MT
- Density: 1.46 g/cc
- Water Absorption: 0.39 % @Thickness 2.00 mm
- Moisture Absorption: 0.150 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Flow: 0.022 cm/cm
$ 1555/MT
- Density: 1.42 g/cc
- Water Absorption: 1.4 % @Thickness 2.00 mm
- Moisture Absorption: 0.300 % @Thickness 2.00 mm
- Viscosity: 73000 cP @Shear Rate 5000 1/s, Temperature 235 °C
- Viscosity: 81000 cP @Shear Rate 5000 1/s, Temperature 215 °C
$ 1726/MT
- Density: 1.18 g/cc
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1497/MT
- Density: 1.42 g/cc
- Tensile Strength, Yield: 73.0 MPa
- Elongation at Break: 35 %
- Elongation at Yield: 16 %
- Tensile Modulus: 3.30 GPa
$ 2458/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.019 cm/cm
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 15 %
$ 1659/MT
- Density: 1.08 g/cc
- Water Absorption: 6.7 % @Thickness 2.00 mm
- Moisture Absorption: 2.20 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.017 cm/cm
- Tensile Strength, Yield: 43.0 MPa
$ 1449/MT
- Density: 1.01 g/cc
- Density: 1.14 g/cc
- Water Absorption: 8.5 % @Thickness 2.00 mm
- Moisture Absorption: 2.70 % @Thickness 2.00 mm
- Viscosity: 64000 cP @Shear Rate 5000 1/s, Temperature 315 °C
$ 2002/MT
- Density: 0.820 g/cc
- Density: 1.00 g/cc
- Viscosity: 74000 cP @Shear Rate 5000 1/s, Temperature 270 °C
- Viscosity: 88000 cP @Shear Rate 5000 1/s, Temperature 250 °C
- Viscosity: 109890 cP @Shear Rate 5000 1/s, Temperature 240 °C
$ 1748/MT
- Density: 1.159 g/cc
- Linear Mold Shrinkage, Flow: 0.00020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0037 cm/cm
- Melt Flow: 5.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 38 @Temperature 23.0 °C, Time 15.0 sec
$ 2225/MT
- Density: 1.24 g/cc
- Density: 1.41 g/cc
- Water Absorption: 5.5 % @Thickness 2.00 mm
- Moisture Absorption: 1.70 % @Thickness 2.00 mm
- Viscosity: 66620 cP @Shear Rate 5000 1/s, Temperature 305 °C
$ 2030/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Tensile Strength, Yield: 65.0 MPa
- Elongation at Break: 7.2 %
$ 2400/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1936/MT
- Specific Gravity: 1.41 g/cc
- Specific Gravity: 1.41 g/cc @Temperature 23.0 °C
- Water Absorption: 0.050 % @Temperature 23.0 °C
- Hardness, Rockwell E: 82 @Temperature 23.0 °C
- Tensile Strength: 117 MPa @Temperature 150 °C
$ 1591/MT
- Specific Gravity: 1.38 g/cc
- Specific Gravity: 1.38 g/cc @Temperature 23.0 °C
- Water Absorption: 0.11 % @Temperature 23.0 °C
- Water Absorption: 0.11 % @Temperature 23.0 °C
- Elongation at Break: 4.0 % @Temperature 23.0 °C
$ 2196/MT
- Specific Gravity: 1.39 g/cc
- Water Absorption: 0.080 % @Temperature 23.0 °C
- Water Absorption: 0.080 % @Temperature 23.0 °C
- Tensile Strength: 119 MPa @Temperature 150 °C
- Elongation at Break: 2.0 % @Temperature 23.0 °C
$ 1575/MT
- Density: 1.73 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Melt Flow: 70 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 110 MPa
$ 1558/MT
- Density: 1.64 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Melt Flow: 16 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 207 MPa
$ 2092/MT
- Density: 1.04 g/cc
- Moisture Absorption: 1.00 % @Thickness 2.00 mm
- Tensile Stress: 0.260 MPa @Strain 0.200 %, Temperature 150 °C
- Tensile Stress: 0.270 MPa @Strain 0.230 %, Temperature 150 °C
- Tensile Stress: 0.350 MPa @Strain 0.210 %, Temperature 90.0 °C
$ 1482/MT
- Density: 1.19 g/cc
- Density: 1.42 g/cc
- Water Absorption: 1.4 % @Thickness 2.00 mm
- Moisture Absorption: 0.300 % @Thickness 2.00 mm
- Viscosity: 138000 cP @Shear Rate 5000 1/s, Temperature 230 °C
$ 1652/MT
- Density: 1.24 g/cc
- Density: 1.40 g/cc
- Water Absorption: 5.5 % @Thickness 2.00 mm
- Moisture Absorption: 1.70 % @Thickness 2.00 mm
- Viscosity: 43638 cP @Shear Rate 5000 1/s, Temperature 305 °C
$ 1877/MT
- Density: 1.28 g/cc
- Density: 1.45 g/cc
- Water Absorption: 5.4 % @Thickness 2.00 mm
- Moisture Absorption: 1.80 % @Thickness 2.00 mm
- Viscosity: 105300 cP @Shear Rate 5000 1/s, Temperature 280 °C
$ 1924/MT
- Density: 1.42 g/cc
- Viscosity: 50400 cP @Shear Rate 5000 1/s, Temperature 300 °C
- Viscosity: 56700 cP @Shear Rate 5000 1/s, Temperature 290 °C
- Viscosity: 58400 cP @Shear Rate 5000 1/s, Temperature 280 °C
- Viscosity: 127400 cP @Shear Rate 500 1/s, Temperature 300 °C
$ 1594/MT
- Melting Point: 154 °C
- Volume Resistivity: >= 1.00e+15 ohm-cm
- Dielectric Strength: 34.0 kV/mm
- Dissipation Factor: 0.0060 @Frequency 100 Hz
- Dissipation Factor: 0.010 @Frequency 1.00e+6 Hz
$ 1777/MT
- Density: 1.00 g/cc
- Density: 1.18 g/cc
- Water Absorption: 0.60 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.60 %
$ 1683/MT
- Regional Availability: Asia Pacific
$ 1556/MT
- Density: 1.69 g/cc
- Viscosity: 110800 cP @Shear Rate 5000 1/s, Temperature 260 °C
- Viscosity: 124700 cP @Shear Rate 5000 1/s, Temperature 250 °C
- Viscosity: 141400 cP @Shear Rate 5000 1/s, Temperature 240 °C
- Viscosity: 348200 cP @Shear Rate 500 1/s, Temperature 260 °C
$ 1479/MT
- Density: 1.16 g/cc
- Density: 1.31 g/cc
- Moisture Absorption: 1.20 % @Thickness 2.00 mm
- Viscosity: 360000 cP @Temperature 250 °C
- Viscosity: 94180 cP @Shear Rate 5000 1/s, Temperature 280 °C
$ 2093/MT
- Density: 1.10 g/cc
- Hardness, Shore D: <= 40
- Tensile Strength at Break: 22.0 MPa
- Elongation at Break: >= 300 %
- Tensile Modulus: 0.0300 GPa
$ 1777/MT
- Density: 1.20 g/cc
- Tensile Strength at Break: 34.0 MPa
- Tensile Stress: 16.6 MPa @Strain 10.0 %
- Elongation at Break: 300 %
- Tensile Modulus: 0.262 GPa
$ 1493/MT
- Density: 1.03 g/cc
- Density: 1.20 g/cc
- Water Absorption: 0.50 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.30 %
$ 1623/MT
- Density: 1.17 g/cc
- Density: 1.34 g/cc
- Moisture Absorption: 0.300 % @Thickness 2.00 mm
- Viscosity: 62350 cP @Shear Rate 5000 1/s, Temperature 260 °C
- Viscosity: 70960 cP @Shear Rate 5000 1/s, Temperature 250 °C
$ 1752/MT
- Density: 1.42 g/cc
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Stress: 16.5 MPa @Strain 0.500 %, Temperature 23.0 °C
- Tensile Stress: 33.4 MPa @Strain 0.900 %, Temperature -40.0 °C
- Tensile Stress: 47.5 MPa @Strain 2.30 %, Temperature 23.0 °C
$ 1643/MT
- Density: 1.36 g/cc
- Filler Content: 30 %
- Water Absorption: 1.9 % @Temperature 23.0 °C
- Water Absorption: 6.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 2.00 mm
$ 1491/MT
- Density: 1.37 g/cc
- Water Absorption: 6.0 % @Thickness 2.00 mm
- Moisture Absorption: 1.90 % @Thickness 2.00 mm
- Viscosity: 46970 cP @Shear Rate 5000 1/s, Temperature 305 °C
- Viscosity: 58620 cP @Shear Rate 5000 1/s, Temperature 295 °C
$ 2319/MT
- Density: 1.03 g/cc
- Density: 1.11 g/cc
- Water Absorption: 0.70 % @Thickness 2.00 mm
- Moisture Absorption: 0.300 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.70 %
$ 2024/MT
- Hardness, Shore D: <= 56
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: >= 300 %
- Tensile Modulus: 0.180 GPa
- Charpy Impact, Notched: NB
$ 2397/MT
- Density: 1.14 g/cc
- Water Absorption: 0.60 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.60 %
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
$ 2086/MT
- Density: 1.19 g/cc
- Water Absorption: 6.3 % @Thickness 2.00 mm
- Moisture Absorption: 1.90 % @Thickness 2.00 mm
- Viscosity Test: 145 cm³/g
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm
$ 1477/MT
- Density: 1.54 g/cc
- Viscosity: 111000 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 128000 cP @Shear Rate 5000 1/s, Temperature 215 °C
- Viscosity: 151000 cP @Shear Rate 5000 1/s, Temperature 200 °C
- Viscosity: 441000 cP @Shear Rate 500 1/s, Temperature 230 °C
$ 1953/MT
- Density: 1.42 g/cc
- Filler Content: 35 %
- Water Absorption: 1.8 % @Temperature 23.0 °C
- Water Absorption: 6.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 2.00 mm
$ 1901/MT
- Density: 1.12 g/cc
- Density: 1.30 g/cc
- Water Absorption: 0.40 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Viscosity Test: 150 cm³/g
$ 1711/MT
- Density: 1.49 g/cc
- Filler Content: 30 %
- Tensile Strength at Break: 55.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 71.0 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 127 MPa @Temperature 23.0 °C
$ 1599/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption at Saturation: 3.4 %
- Hardness, Rockwell R: 71
- Tensile Strength: 52.0 MPa
- Additives: Release agent
$ 1445/MT
- Density: 1.28 g/cc
- Density: 1.45 g/cc
- Water Absorption: 5.4 % @Thickness 2.00 mm
- Moisture Absorption: 1.40 % @Thickness 2.00 mm
- Water Absorption at Saturation: 1.0 %
$ 2339/MT
- Density: 1.51 g/cc
- Water Absorption: 0.45 % @Thickness 2.00 mm
- Moisture Absorption: 0.180 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
$ 2598/MT
- Density: 1.08 g/cc
- Tensile Strength, Yield: 62.0 MPa @Temperature 23.0 °C
- Tensile Modulus: 2.25 GPa @Temperature 23.0 °C
- Flexural Modulus: 2.10 GPa @Temperature 23.0 °C
- Izod Impact, Notched (ISO): 5.00 kJ/m² @Temperature 23.0 °C
$ 2050/MT
- Density: 1.01 g/cc
- Viscosity: 82000 cP @Shear Rate 5000 1/s, Temperature 270 °C
- Viscosity: 98500 cP @Shear Rate 5000 1/s, Temperature 250 °C
- Viscosity: 110700 cP @Shear Rate 5000 1/s, Temperature 240 °C
- Viscosity: 292700 cP @Shear Rate 500 1/s, Temperature 270 °C
$ 1999/MT
- Density: 1.42 g/cc
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 71.5 MPa
- Elongation at Break: 37 %
- Elongation at Yield: 22 %
$ 2261/MT
- Density: 1.43 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm @Thickness 2.00 mm
- Tensile Strength at Break: 97.0 MPa @Temperature 23.0 °C
$ 1796/MT
- Density: 1.31 g/cc
- Density: 1.53 g/cc
- Viscosity: 74660 cP @Shear Rate 5000 1/s, Temperature 270 °C
- Viscosity: 85140 cP @Shear Rate 5000 1/s, Temperature 260 °C
- Viscosity: 98010 cP @Shear Rate 5000 1/s, Temperature 250 °C
$ 2177/MT
- Density: 1.07 g/cc
- Water Absorption: 3.0 % @Thickness 2.00 mm
- Moisture Absorption: 1.30 % @Thickness 2.00 mm
- Viscosity Test: 95 cm³/g
- Linear Mold Shrinkage, Flow: 0.013 cm/cm
$ 2166/MT
- Specific Gravity: 1.79 g/cc
- Density: 1.79 g/cc
- Filler Content: 43 %
- Water Absorption: 0.060 % @Temperature 23.0 °C
- Water Absorption: 0.11 % @Temperature 23.0 °C
$ 1933/MT
- Density: 1.02 g/cc
- Density: 1.16 g/cc
- Water Absorption: 0.70 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.60 %
$ 1670/MT
- Density: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
$ 1474/MT
- Density: 1.19 g/cc
- Water Absorption: 6.2 % @Thickness 2.00 mm
- Moisture Absorption: 1.80 % @Thickness 2.00 mm
- Viscosity Test: 137 cm³/g
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1704/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 75.0 MPa
- Tensile Strength at Break: 120 MPa
$ 1844/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 120 MPa
- Tensile Stress: 7.27 MPa @Strain 0.100 %, Temperature 23.0 °C
$ 2561/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength at Break: 220 MPa
- Tensile Stress: 8.88 MPa @Strain 0.190 %, Temperature 150 °C
$ 1520/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength at Break: 200 MPa
- Tensile Strength at Break: 210 MPa
$ 1634/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength at Break: 210 MPa
- Tensile Strength at Break: 220 MPa
$ 1812/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Ball Indentation Hardness: 310 MPa
- Tensile Strength at Break: 190 MPa
$ 1551/MT
- Density: 1.46 g/cc
- Tensile Strength at Break: 215 MPa
- Elongation at Break: 2.6 %
- Tensile Modulus: 11.5 GPa
- Flexural Modulus: 10.3 GPa
$ 1539/MT
- Density: 1.47 g/cc
- Filler Content: 35 %
- Tensile Strength at Break: 215 MPa @Temperature 23.0 °C
- Elongation at Break: 2.3 % @Temperature 23.0 °C
- Tensile Modulus: 11.5 GPa @Temperature 23.0 °C
$ 1849/MT
- Density: 1.57 g/cc
- Water Absorption: 3.6 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength at Break: 230 MPa
$ 1812/MT
- Specific Gravity: 1.47 g/cc
- Density: 1.45 g/cc
- Filler Content: 35 %
- Linear Mold Shrinkage: 0.0025 cm/cm @Thickness 1.60 mm
- Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 3.20 mm
$ 1646/MT
- Density: 1.56 g/cc
- Filler Content: 45 %
- Tensile Strength at Break: 240 MPa @Temperature 23.0 °C
- Tensile Stress: 11.26 MPa @Strain 0.100 %, Temperature 150 °C
- Tensile Stress: 11.39 MPa @Strain 0.100 %, Temperature 100 °C
$ 1782/MT
- Density: 1.59 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 cm/cm
- Tensile Strength at Break: 215 MPa
- Tensile Strength at Break: 250 MPa
$ 1659/MT
- Density: 1.58 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm
- Tensile Strength at Break: 210 MPa
- Tensile Strength at Break: 270 MPa
$ 1470/MT
- Density: 1.72 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Tensile Strength at Break: 225 MPa
- Tensile Strength at Break: 265 MPa
$ 2149/MT
- Density: 1.25 g/cc
- Viscosity Test: 82 cm³/g
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 118 MPa
$ 1814/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 100 MPa
- Tensile Strength at Break: 130 MPa
$ 1467/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Tensile Strength at Break: 185 MPa
- Tensile Stress: 1.39 MPa @Strain 0.0300 %, Temperature -20.0 °C
$ 1938/MT
- Density: 1.38 g/cc
- Tensile Strength at Break: 189 MPa
- Elongation at Break: 2.7 %
- Tensile Modulus: 11.7 GPa
- Charpy Impact Unnotched: 9.00 J/cm²
$ 1514/MT
- Density: 1.40 g/cc
- Tensile Strength at Break: 175 MPa
- Elongation at Break: 3.1 %
- Tensile Modulus: 10.5 GPa
- Charpy Impact Unnotched: 9.00 J/cm²
$ 2488/MT
- Density: 1.68 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0010 cm/cm
- Tensile Strength at Break: 270 MPa
- Elongation at Break: 1.9 %
$ 1501/MT
- Density: 1.44 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 157 MPa
- Tensile Strength at Break: 200 MPa
$ 1547/MT
- Density: 1.54 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 168 MPa
- Tensile Strength at Break: 214 MPa
$ 1862/MT
- Density: 1.42 g/cc
- Tensile Strength at Break: 200 MPa
- Elongation at Break: 2.9 %
- Tensile Modulus: 10.2 GPa
- Flexural Strength: 280 MPa
$ 1478/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Tensile Strength at Break: 162 MPa
- Tensile Strength at Break: 168 MPa
$ 1751/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength, Yield: 69.0 MPa
- Elongation at Break: 14 %
$ 1559/MT
- Density: 1.13 g/cc
- Water Absorption: 6.3 % @Thickness 2.00 mm
- Moisture Absorption: 1.90 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
$ 1569/MT
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 185 MPa
- Tensile Strength at Break: 205 MPa
- Elongation at Break: 2.2 %
$ 2043/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 120 MPa
- Tensile Strength at Break: 135 MPa
$ 1454/MT
- Density: 1.62 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 160 MPa
- Elongation at Break: 2.0 %
$ 1452/MT
- Density: 1.44 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 150 MPa
- Tensile Stress: 0.150 MPa @Strain 0.000 %, Temperature 175 °C
$ 1585/MT
- Density: 1.44 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 130 MPa
- Tensile Strength at Break: 150 MPa
$ 1550/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 135 MPa
- Tensile Strength at Break: 145 MPa
$ 2032/MT
- Density: 1.76 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength at Break: 155 MPa
- Tensile Strength at Break: 175 MPa
$ 2120/MT
- Density: 1.65 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 cm/cm
- Tensile Strength at Break: 195 MPa
- Elongation at Break: 1.6 %
$ 1486/MT
- Density: 1.42 g/cc
- Tensile Strength at Break: 187 MPa @Temperature 23.0 °C
- Elongation at Break: 2.7 % @Temperature 23.0 °C
- Tensile Modulus: 10.0 GPa @Temperature 23.0 °C
- Charpy Impact Unnotched: 8.20 J/cm² @Temperature 23.0 °C
$ 1804/MT
- Density: 1.42 g/cc
- Water Absorption: 1.4 % @Thickness 2.00 mm
- Moisture Absorption: 0.300 % @Thickness 2.00 mm
- Viscosity: 73000 cP @Shear Rate 5000 1/s, Temperature 235 °C
- Viscosity: 81000 cP @Shear Rate 5000 1/s, Temperature 215 °C
$ 1864/MT
- Melting Point: 147 °C
- Delivery Form: Pellets
- Regional Availability: Asia Pacific
- Regional Availability: Europe
- Regional Availability: Global
$ 2270/MT
- Specific Gravity: 1.64 g/cc
- Density: 1.64 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Hardness, Rockwell M: 75
$ 1519/MT
- Density: 1.64 g/cc
- Water Absorption: 0.75 % @Thickness 2.00 mm
- Moisture Absorption: 0.100 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
$ 2046/MT
- Specific Gravity: 1.60 g/cc
- Tensile Strength at Break: 94.0 MPa
- Elongation at Break: 2.0 %
- Izod Impact, Unnotched (ISO): 500 kJ/m²
- Izod Impact Resistance: 5.90 J/cm²
$ 2325/MT
- Density: 1.40 g/cc
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 2.3 %
- Tensile Modulus: 6.20 GPa
- Flexural Strength: 170 MPa
$ 2364/MT
- Density: 1.40 g/cc
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 2.3 %
- Tensile Modulus: 6.20 GPa
- Flexural Strength: 170 MPa
$ 1521/MT
- Density: 1.40 g/cc
- Water Absorption at Saturation: 0.080 %
- Tensile Strength at Break: 125 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 6.50 GPa
$ 1546/MT
- Density: 1.56 g/cc
- Tensile Strength at Break: 142 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 10.6 GPa
- Flexural Strength: 215 MPa
$ 1916/MT
- Density: 1.56 g/cc
- Water Absorption at Saturation: 0.080 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 165 MPa
$ 1681/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 15 %
$ 1688/MT
- Density: 1.12 g/cc
- Density: 1.32 g/cc
- Viscosity: 66880 cP @Shear Rate 5000 1/s, Temperature 270 °C
- Viscosity: 77790 cP @Shear Rate 5000 1/s, Temperature 260 °C
- Viscosity: 90760 cP @Shear Rate 5000 1/s, Temperature 250 °C
$ 1588/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 15 %
$ 2499/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 15 %
$ 1916/MT
- Density: 1.51 g/cc
- Density: 1.74 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 280 °C
$ 2064/MT
- Density: 1.35 g/cc
- Density: 1.56 g/cc
- Water Absorption at Saturation: 0.080 %
- Viscosity: 80700 cP @Shear Rate 5000 1/s, Temperature 270 °C
- Viscosity: 91200 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 1624/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 15 %
$ 1454/MT
- Density: 1.47 g/cc
- Density: 1.66 g/cc
- Water Absorption: 0.30 % @Thickness 2.00 mm
- Moisture Absorption: 0.100 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
DuPont Performance Polymers Rynite® 415HP BK503 Polyethylene Terephthalate (PET) (Unverified Data**)
$ 2229/MT
- Density: 1.39 g/cc
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 4.50 GPa
- Flexural Modulus: 4.00 GPa
$ 1720/MT
- Density: 1.03 g/cc
- Moisture Absorption: 1.20 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Tensile Stress: 0.480 MPa @Strain 0.260 %, Temperature 150 °C
$ 1499/MT
- Density: 0.970 g/cc
- Density: 1.14 g/cc
- Water Absorption: 8.5 % @Thickness 2.00 mm
- Moisture Absorption: 2.60 % @Thickness 2.00 mm
- Viscosity: 42820 cP @Shear Rate 5000 1/s, Temperature 300 °C
$ 1639/MT
- Density: 1.31 g/cc
- Filler Content: 33 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Thickness 2.00 mm
- Tensile Strength at Break: 104 MPa @Temperature 23.0 °C
$ 1879/MT
- Density: 1.12 g/cc
- Density: 1.32 g/cc
- Water Absorption at Saturation: 0.83 %
- Viscosity Test: 165 cm³/g
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
$ 1510/MT
- Density: 1.19 g/cc
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.022 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2131/MT
- Density: 1.36 g/cc
- Water Absorption: 6.3 % @Thickness 2.00 mm
- Moisture Absorption: 1.90 % @Thickness 2.00 mm
- Viscosity Test: 150 cm³/g
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
$ 2452/MT
- Specific Gravity: 1.04 g/cc
- Density: 1.04 g/cc
- Water Absorption: 1.5 % @Temperature 23.0 °C
- Water Absorption: 2.3 % @Temperature 23.0 °C
- Water Absorption: 6.8 % @Temperature 23.0 °C
$ 1531/MT
- Specific Gravity: 1.32 g/cc
- Density: 1.32 g/cc
- Filler Content: 33 %
- Water Absorption: 0.16 % @Temperature 23.0 °C
- Water Absorption: 2.0 % @Temperature 23.0 °C
$ 1617/MT
- Density: 1.68 g/cc
- Water Absorption: 0.75 % @Thickness 2.00 mm
- Moisture Absorption: 0.150 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
$ 1635/MT
- Density: 1.25 g/cc
- Hardness, Shore D: 66
- Hardness, Shore D: <= 70
- Tensile Strength at Break: 52.0 MPa
- Tensile Stress: 23.0 MPa @Strain 10.0 %
$ 1497/MT
- Density: 1.08 g/cc
- Water Absorption: 3.8 % @Thickness 2.00 mm
- Moisture Absorption: 1.70 % @Thickness 2.00 mm
- Viscosity: 77500 cP @Shear Rate 5000 1/s, Temperature 270 °C
- Viscosity: 94600 cP @Shear Rate 5000 1/s, Temperature 250 °C
$ 1456/MT
- Density: 1.42 g/cc
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: 30 %
- Elongation at Yield: 17 %
- Tensile Modulus: 3.10 GPa
$ 2181/MT
- Density: 1.36 g/cc
- Density: 1.53 g/cc
- Water Absorption: 0.35 % @Thickness 2.00 mm
- Moisture Absorption: 0.150 % @Thickness 2.00 mm
- Viscosity: 91150 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 1674/MT
- Density: 1.42 g/cc
- Melt Flow: 21 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 72.0 MPa
- Elongation at Yield: 12 %
- Tensile Modulus: 3.20 GPa
$ 1500/MT
- Density: 1.42 g/cc
- Water Absorption: 1.2 % @Thickness 2.00 mm
- Moisture Absorption: 0.300 % @Thickness 2.00 mm
- Viscosity: 138000 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 147000 cP @Shear Rate 5000 1/s, Temperature 215 °C
$ 1719/MT
- Density: 1.42 g/cc
- Water Absorption: 0.90 % @Thickness 2.00 mm
- Moisture Absorption: 0.170 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.021 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
$ 2388/MT
- Density: 1.53 g/cc
- Water Absorption: 1.0 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Viscosity: 100000 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 107000 cP @Shear Rate 5000 1/s, Temperature 215 °C
$ 1551/MT
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 67.0 MPa
- Elongation at Break: 18 %
- Elongation at Yield: 13 %
- Tensile Modulus: 3.20 GPa
$ 1543/MT
- Density: 1.43 g/cc
- Water Absorption: 0.90 % @Thickness 2.00 mm
- Moisture Absorption: 0.170 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
$ 2044/MT
- Density: 1.42 g/cc
- Water Absorption: 0.30 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1731/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Melt Flow: 21 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 24 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1910/MT
- Density: 1.42 g/cc
- Water Absorption: 1.4 % @Thickness 2.00 mm
- Moisture Absorption: 0.300 % @Thickness 2.00 mm
- Viscosity: 138000 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 153500 cP @Shear Rate 5000 1/s, Temperature 215 °C
$ 1514/MT
- Melt Flow: 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 72.0 MPa
- Elongation at Break: 40 %
- Elongation at Yield: 20 %
- Tensile Modulus: 3.15 GPa
$ 1723/MT
- Density: 1.39 g/cc
- Tensile Strength, Yield: 65.0 MPa
- Elongation at Break: 23 %
- Elongation at Yield: 11 %
- Tensile Modulus: 3.00 GPa
$ 1543/MT
- Density: 1.42 g/cc
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: 30 %
- Elongation at Yield: 17 %
- Tensile Modulus: 3.10 GPa
$ 1768/MT
- Density: 1.42 g/cc
- Tensile Strength, Yield: 71.0 MPa
- Elongation at Break: 23 %
- Elongation at Yield: 12 %
- Tensile Modulus: 3.30 GPa
$ 1664/MT
- Density: 1.43 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 71.0 MPa
$ 1628/MT
- Density: 1.42 g/cc
- Water Absorption: 1.7 % @Thickness 2.00 mm
- Moisture Absorption: 0.700 % @Thickness 2.00 mm
- Viscosity Test: 145 cm³/g
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
$ 2284/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm @Thickness 2.00 mm
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 240 °C
- Hardness, Shore D: 65 @Time 15.0 sec
- Tensile Strength at Break: 30.0 MPa @Temperature 23.0 °C
$ 1479/MT
- Density: 1.08 g/cc
- Water Absorption: 1.1 % @Temperature 23.0 °C
- Water Absorption: 6.7 % @Temperature 23.0 °C
- Water Absorption: 2.0 % @Thickness 1.00 mm, Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.020 cm/cm @Thickness 2.00 mm
$ 2381/MT
- Density: 1.44 g/cc
- Tensile Strength at Break: 125 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 9.20 GPa
- Flexural Strength: 180 MPa
$ 1966/MT
- Density: 1.23 g/cc
- Melt Flow: 4.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: <= 65
- Hardness, Shore D: 63 @Time 15.0 sec
- Tensile Strength at Break: 31.0 MPa @Temperature 23.0 °C
$ 1446/MT
- Density: 1.03 g/cc
- Density: 1.20 g/cc
- Water Absorption: 0.60 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.60 %
$ 1961/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 21
$ 1810/MT
- Specific Gravity: 1.15 g/cc
- Density: 1.16 g/cc
- Water Absorption: 1.8 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0080 cm/cm @Thickness 1.60 mm
- Linear Mold Shrinkage: 0.0080 cm/cm @Thickness 1.60 mm
$ 2251/MT
- Density: 1.42 g/cc
- Water Absorption: 0.90 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
$ 1668/MT
- Density: 1.33 g/cc
- Water Absorption at Saturation: 0.91 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 112 MPa
$ 2396/MT
- Density: 1.18 g/cc
- Water Absorption: 5.8 % @Thickness 2.00 mm
- Viscosity: 44000 cP @Shear Rate 5000 1/s, Temperature 320 °C
- Viscosity: 70000 cP @Shear Rate 500 1/s, Temperature 320 °C
- Viscosity: 72000 cP @Shear Rate 5000 1/s, Temperature 300 °C
$ 1465/MT
- Density: 1.19 g/cc
- Density: 1.35 g/cc
- Water Absorption: 0.78 % @Thickness 2.00 mm
- Moisture Absorption: 0.260 % @Thickness 2.00 mm
- Viscosity: 64000 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 1542/MT
- Density: 1.32 g/cc
- Tensile Strength at Break: 120 MPa
- Tensile Strength at Break: 180 MPa
- Elongation at Break: 3.0 %
- Elongation at Break: 6.0 %
$ 1691/MT
- Density: 1.39 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 140 MPa
- Tensile Strength at Break: 200 MPa
$ 1811/MT
- Density: 1.19 g/cc
- Water Absorption: 6.8 % @Thickness 2.00 mm
- Moisture Absorption: 2.70 % @Thickness 2.00 mm
- Viscosity Test: 135 cm³/g
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
$ 1458/MT
- Density: 1.40 g/cc
- Density: 1.60 g/cc
- Moisture Absorption: 0.700 % @Thickness 2.00 mm
- Viscosity: 79440 cP @Shear Rate 5000 1/s, Temperature 280 °C
- Viscosity: 101000 cP @Shear Rate 5000 1/s, Temperature 270 °C
$ 1763/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 72.0 MPa
- Tensile Strength at Break: 120 MPa
$ 1583/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.021 cm/cm
- Linear Mold Shrinkage, Transverse: 0.019 cm/cm
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1786/MT
- Density: 1.40 g/cc
- Filler Content: 35 %
- Water Absorption: 2.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 2.00 mm
$ 2090/MT
- Density: 1.46 g/cc
- Density: 1.67 g/cc
- Viscosity: 75510 cP @Shear Rate 5000 1/s, Temperature 270 °C
- Viscosity: 91440 cP @Shear Rate 5000 1/s, Temperature 260 °C
- Viscosity: 112800 cP @Shear Rate 5000 1/s, Temperature 250 °C
$ 1538/MT
- Density: 1.07 g/cc
- Density: 1.25 g/cc
- Water Absorption: 6.8 % @Thickness 2.00 mm
- Moisture Absorption: 2.10 % @Thickness 2.00 mm
- Viscosity: 330000 cP @Temperature 280 °C
$ 2141/MT
- Density: 1.25 g/cc
- Viscosity Test: 140 cm³/g
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Tensile Strength at Break: 87.0 MPa
- Tensile Strength at Break: 122 MPa
$ 1659/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.019 cm/cm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1629/MT
- Density: 1.36 g/cc
- Density: 1.52 g/cc
- Water Absorption: 0.78 % @Thickness 2.00 mm
- Moisture Absorption: 0.230 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
$ 1985/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Tensile Strength, Yield: 36.0 MPa
- Elongation at Break: >= 50 %
$ 1829/MT
- Density: 1.56 g/cc
- Viscosity: 99000 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 105000 cP @Shear Rate 5000 1/s, Temperature 215 °C
- Viscosity: 111000 cP @Shear Rate 5000 1/s, Temperature 200 °C
- Viscosity: 365000 cP @Shear Rate 500 1/s, Temperature 230 °C
$ 2091/MT
- Density: 1.49 g/cc
- Water Absorption: 7.6 % @Thickness 2.00 mm
- Moisture Absorption: 2.20 % @Thickness 2.00 mm
- Viscosity Test: 120 cm³/g
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
$ 1540/MT
- Density: 1.07 g/cc
- Density: 1.23 g/cc
- Water Absorption: 7.6 % @Thickness 2.00 mm
- Moisture Absorption: 2.50 % @Thickness 2.00 mm
- Viscosity Test: 150 cm³/g
$ 1601/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption at Saturation: 3.1 %
- Hardness, Rockwell R: 71
- Tensile Strength: 51.0 MPa
- Melting Point: 156 °C
$ 2448/MT
- Density: 1.42 g/cc
- Water Absorption: 0.90 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
$ 1616/MT
- Density: 1.43 g/cc
- Viscosity: 98000 cP @Shear Rate 5000 1/s, Temperature 220 °C
- Viscosity: 108000 cP @Shear Rate 5000 1/s, Temperature 205 °C
- Viscosity: 120000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 372000 cP @Shear Rate 500 1/s, Temperature 220 °C
$ 1578/MT
- Specific Gravity: 1.58 g/cc
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 280 °C
- Hardness, Rockwell M: 100
- Hardness, Rockwell R: 120
- Tensile Strength at Break: 170 MPa
$ 1666/MT
- Density: 1.15 g/cc
- Water Absorption: 12 % @Thickness 2.00 mm
- Moisture Absorption: 0.800 % @Thickness 2.00 mm
- Water Absorption at Saturation: 6.9 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1566/MT
- Density: 1.23 g/cc
- Filler Content: 15 %
- Water Absorption: 2.1 % @Temperature 23.0 °C
- Water Absorption: 7.7 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 2.00 mm
$ 1487/MT
- Density: 1.39 g/cc
- Tensile Strength, Yield: 65.0 MPa
- Elongation at Break: 23 %
- Elongation at Yield: 11 %
- Tensile Modulus: 3.00 GPa
$ 1880/MT
- Density: 1.11 g/cc
- Density: 1.31 g/cc
- Water Absorption: 0.40 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Viscosity: 88500 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 1619/MT
- Density: 1.39 g/cc
- Water Absorption: 5.7 % @Thickness 2.00 mm
- Moisture Absorption: 1.80 % @Thickness 2.00 mm
- Water Absorption at Saturation: 1.2 %
- Viscosity Test: 145 cm³/g
$ 1445/MT
- Specific Gravity: 1.09 g/cc
- Tensile Strength, Yield: 60.0 MPa @Temperature 23.0 °C
- Elongation at Break: 160 % @Temperature 23.0 °C
- Elongation at Break: >= 160 % @Temperature 23.0 °C
- Elongation at Yield: 4.4 % @Temperature 23.0 °C
DuPont Performance Polymers Crastin® 6131 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)
$ 2063/MT
- Density: 1.11 g/cc
- Density: 1.30 g/cc
- Water Absorption: 0.40 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Viscosity: 68390 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 2146/MT
- Density: 1.25 g/cc
- Hardness, Shore D: 66
- Hardness, Shore D: <= 70
- Tensile Strength at Break: 53.0 MPa
- Tensile Stress: 23.0 MPa @Strain 10.0 %
$ 2186/MT
- Density: 1.01 g/cc
- Density: 1.19 g/cc
- Water Absorption at Saturation: 2.5 %
- Viscosity: 47110 cP @Shear Rate 5000 1/s, Temperature 250 °C
- Viscosity: 51280 cP @Shear Rate 5000 1/s, Temperature 240 °C
$ 1481/MT
- Density: 1.14 g/cc
- Water Absorption: 2.7 % @Temperature 23.0 °C
- Water Absorption: 8.5 % @Temperature 23.0 °C
- Viscosity: 109000 cP @Shear Rate 7000 1/s, Temperature 305 °C
- Viscosity: 119000 cP @Shear Rate 7000 1/s, Temperature 295 °C
$ 2167/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.019 cm/cm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2382/MT
- Density: 1.41 g/cc
- Tensile Strength at Break: 140 MPa @Temperature 23.0 °C
- Tensile Strength at Break: 220 MPa @Temperature 23.0 °C
- Elongation at Break: 3.0 % @Temperature 23.0 °C
- Elongation at Break: 5.0 % @Temperature 23.0 °C
$ 1570/MT
- Density: 1.41 g/cc
- Tensile Strength, Yield: 66.0 MPa
- Elongation at Break: 40 %
- Elongation at Yield: 21 %
- Tensile Modulus: 3.00 GPa
$ 1566/MT
- Density: 1.19 g/cc
- Hardness, Shore D: <= 55
- Tensile Strength at Break: 44.0 MPa
- Elongation at Break: >= 300 %
- Charpy Impact, Notched: NB
$ 1878/MT
- Hardness, Shore D: <= 72
- Tensile Strength at Break: 53.0 MPa
- Elongation at Break: >= 300 %
- Tensile Modulus: 0.525 GPa
- Charpy Impact, Notched: 3.30 J/cm²
$ 2337/MT
- Density: 1.49 g/cc
- Water Absorption: 1.1 % @Thickness 2.00 mm
- Moisture Absorption: 0.160 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
$ 1460/MT
- Density: 1.42 g/cc
- Density: 1.57 g/cc
- Water Absorption: 0.72 % @Thickness 2.00 mm
- Moisture Absorption: 0.210 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
$ 1837/MT
- Density: 1.50 g/cc
- Water Absorption: 5.0 % @Thickness 2.00 mm
- Moisture Absorption: 1.60 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
$ 1551/MT
- Density: 0.995 g/cc
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 240 °C
$ 1600/MT
- Density: 1.39 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 140 MPa
- Tensile Strength at Break: 200 MPa
$ 1598/MT
- Density: 1.35 g/cc
- Density: 1.49 g/cc
- Water Absorption: 3.4 % @Thickness 2.00 mm
- Moisture Absorption: 0.900 % @Thickness 2.00 mm
- Viscosity: 85370 cP @Shear Rate 5000 1/s, Temperature 280 °C
$ 1829/MT
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Modulus: 6.00 GPa
- Tensile Modulus: 10.0 GPa
- Charpy Impact Unnotched: 8.50 J/cm²
$ 1532/MT
- Density: 1.03 g/cc
- Density: 1.18 g/cc
- Water Absorption: 3.7 % @Thickness 2.00 mm
- Moisture Absorption: 0.400 % @Thickness 2.00 mm
- Water Absorption at Saturation: 2.1 %
$ 1884/MT
- Density: 1.41 g/cc
- Water Absorption: 1.0 % @Thickness 2.00 mm
- Moisture Absorption: 0.250 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
$ 1787/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.021 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Melt Flow: 1.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1663/MT
- Density: 1.11 g/cc
- Density: 1.30 g/cc
- Water Absorption: 0.50 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Viscosity: 116000 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 1883/MT
- Density: 1.13 g/cc
- Density: 1.28 g/cc
- Water Absorption: 0.60 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.30 %
$ 1680/MT
- Density: 1.28 g/cc
- Density: 1.44 g/cc
- Water Absorption: 0.72 % @Thickness 2.00 mm
- Moisture Absorption: 0.240 % @Thickness 2.00 mm
- Viscosity: 67000 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 1445/MT
- Specific Gravity: 1.51 g/cc
- Density: 1.49 g/cc
- Filler Content: 30 %
- Water Absorption: 0.060 % @Temperature 23.0 °C
- Viscosity: 110000 cP @Shear Rate 3090 1/s, Temperature 305 °C
$ 1678/MT
- Density: 1.57 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 80.0 MPa
- Tensile Stress: 1.94 MPa @Strain 0.0700 %, Temperature 150 °C
$ 1523/MT
- Density: 1.42 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C
- Water Absorption: 0.60 % @Temperature 23.0 °C
- Water Absorption: 1.4 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.019 cm/cm @Thickness 2.00 mm
$ 2161/MT
- Density: 1.38 g/cc
- Filler Content: 20 %
- Water Absorption: 0.40 % @Temperature 23.0 °C
- Tensile Strength at Break: 95.0 MPa @Temperature 23.0 °C
- Elongation at Break: 2.9 % @Temperature 23.0 °C
$ 1536/MT
- Density: 1.25 g/cc
- Density: 1.45 g/cc
- Water Absorption: 0.35 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Viscosity: 157000 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 1679/MT
- Specific Gravity: 1.15 g/cc
- Density: 1.16 g/cc
- Water Absorption: 2.4 % @Thickness 1.00 mm, Temperature 23.0 °C
- Water Absorption: 8.0 % @Thickness 1.00 mm, Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Thickness 2.00 mm
$ 1692/MT
- Density: 1.48 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 2.00 mm
- Tensile Strength at Break: 138 MPa @Temperature 23.0 °C
- Elongation at Break: 2.6 % @Temperature 23.0 °C
$ 1562/MT
- Density: 1.28 g/cc
- Hardness, Shore D: <= 82
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: >= 300 %
- Charpy Impact, Notched: 1.50 J/cm²
$ 1973/MT
- Density: 1.40 g/cc
- Density: 1.62 g/cc
- Water Absorption: 4.0 % @Thickness 2.00 mm
- Moisture Absorption: 1.30 % @Thickness 2.00 mm
- Viscosity: 67650 cP @Shear Rate 5000 1/s, Temperature 280 °C
$ 1610/MT
- Density: 1.63 g/cc
- Water Absorption: 0.32 % @Thickness 2.00 mm
- Moisture Absorption: 0.130 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
$ 1606/MT
- Density: 1.37 g/cc
- Density: 1.58 g/cc
- Water Absorption: 0.33 % @Thickness 2.00 mm
- Moisture Absorption: 0.140 % @Thickness 2.00 mm
- Viscosity: 102700 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 1527/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.98 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.015 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage: 0.023 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 70
DuPont Performance Polymers Crastin® 6130 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)
$ 1969/MT
- Density: 1.11 g/cc
- Density: 1.30 g/cc
- Viscosity: 102200 cP @Shear Rate 5000 1/s, Temperature 260 °C
- Viscosity: 113100 cP @Shear Rate 5000 1/s, Temperature 250 °C
- Viscosity: 125300 cP @Shear Rate 5000 1/s, Temperature 240 °C
$ 1489/MT
- Density: 1.42 g/cc
- Water Absorption: 0.90 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
$ 1618/MT
- Density: 1.64 g/cc
- Water Absorption: 0.60 % @Thickness 2.00 mm
- Moisture Absorption: 0.150 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
$ 1589/MT
- Density: 1.49 g/cc
- Density: 1.71 g/cc
- Water Absorption: 0.30 % @Thickness 2.00 mm
- Moisture Absorption: 0.100 % @Thickness 2.00 mm
- Viscosity: 110800 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 1603/MT
- Density: 1.22 g/cc
- Hardness, Shore D: <= 63
- Tensile Strength at Break: 41.0 MPa
- Elongation at Break: >= 300 %
- Tensile Modulus: 0.260 GPa
$ 1657/MT
- Density: 1.15 g/cc
- Hardness, Shore D: <= 40
- Tensile Strength at Break: 26.0 MPa
- Elongation at Break: >= 300 %
- Charpy Impact, Notched: NB
$ 1530/MT
- Density: 1.71 g/cc
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 1.7 %
- Tensile Modulus: 15.7 GPa
- Flexural Strength: 210 MPa
$ 1545/MT
- Density: 1.00 g/cc
- Density: 1.17 g/cc
- Water Absorption: 0.50 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.50 %
$ 1710/MT
- Density: 1.14 g/cc
- Water Absorption: 0.50 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 37
$ 2345/MT
- Density: 1.26 g/cc
- Density: 1.45 g/cc
- Water Absorption: 0.40 % @Thickness 2.00 mm
- Moisture Absorption: 0.150 % @Thickness 2.00 mm
- Viscosity: 80120 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 1684/MT
- Density: 1.02 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm @Thickness 2.00 mm
- Tensile Strength at Break: 28.0 MPa @Temperature 23.0 °C
- Elongation at Break: >= 50 % @Temperature 23.0 °C
$ 1497/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1460/MT
- Density: 1.02 g/cc
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 30 %
- Tensile Modulus: 0.800 GPa
$ 2096/MT
- Density: 1.31 g/cc
- Tensile Strength, Yield: 58.0 MPa
- Elongation at Break: 30 %
- Elongation at Yield: 6.0 %
- Tensile Modulus: 2.60 GPa
$ 1444/MT
- Density: 1.39 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1555/MT
- Tensile Strength at Break: 100 MPa
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 3.1 %
- Elongation at Break: 4.5 %
- Tensile Modulus: 6.00 GPa
$ 1526/MT
- Density: 1.31 g/cc
- Tensile Strength, Yield: 58.0 MPa
- Elongation at Break: 30 %
- Elongation at Yield: 6.0 %
- Tensile Modulus: 2.60 GPa
$ 1777/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 13 %
$ 1550/MT
- Density: 1.61 g/cc
- Melt Flow: 17 g/10 min @Load 2.16 kg, Temperature 280 °C
- Tensile Strength at Break: 145 MPa
- Tensile Stress: 6.65 MPa @Strain 0.190 %, Temperature 150 °C
- Tensile Stress: 11.36 MPa @Strain 0.230 %, Temperature 90.0 °C
$ 1953/MT
- Density: 1.40 g/cc
- Water Absorption: 4.0 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength at Break: 90.0 MPa
$ 2085/MT
- Density: 1.12 g/cc
- Density: 1.30 g/cc
- Water Absorption: 0.40 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Viscosity Test: 130 cm³/g
$ 1619/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 57.0 MPa
$ 1715/MT
- Density: 1.13 g/cc
- Water Absorption: 3.0 % @Temperature 23.0 °C
- Water Absorption: 9.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.010 cm/cm @Thickness 3.00 mm
- Tensile Strength, Yield: 50.0 MPa @Temperature 23.0 °C
$ 1631/MT
- Density: 1.04 g/cc
- Density: 1.22 g/cc
- Water Absorption: 0.60 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Viscosity: 94540 cP @Shear Rate 5000 1/s, Temperature 250 °C
$ 1595/MT
- Density: 0.900 g/cc
- Density: 1.06 g/cc
- Water Absorption: 3.0 % @Thickness 2.00 mm
- Moisture Absorption: 1.30 % @Thickness 2.00 mm
- Viscosity: 54050 cP @Shear Rate 5000 1/s, Temperature 290 °C
DuPont Performance Polymers Rynite® 415HP NC010 Polyethylene Terephthalate (PET) (Unverified Data**)
$ 1724/MT
- Specific Gravity: 1.39 g/cc
- Density: 1.39 g/cc
- Water Absorption: 2.5 % @Thickness 2.00 mm
- Moisture Absorption: 0.250 % @Thickness 2.00 mm
- Viscosity: 57000 cP @Shear Rate 5000 1/s, Temperature 315 °C
$ 1698/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.021 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1488/MT
- Density: 1.60 g/cc
- Water Absorption: 1.26 % @Thickness 2.00 mm
- Moisture Absorption: 0.170 % @Thickness 2.00 mm
- Viscosity: 84000 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 94000 cP @Shear Rate 5000 1/s, Temperature 215 °C
$ 1831/MT
- Density: 1.42 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 72.5 MPa
- Elongation at Break: 40 %
$ 1611/MT
- Density: 1.24 g/cc
- Density: 1.40 g/cc
- Water Absorption: 2.0 % @Thickness 2.00 mm
- Viscosity: 63230 cP @Shear Rate 5000 1/s, Temperature 280 °C
- Viscosity: 75340 cP @Shear Rate 5000 1/s, Temperature 270 °C
$ 1459/MT
- Density: 1.07 g/cc
- Hardness, Shore D: <= 30
- Tensile Strength at Break: 24.0 MPa
- Elongation at Break: >= 300 %
- Charpy Impact, Notched: NB
$ 1759/MT
- Density: 1.37 g/cc
- Water Absorption at Saturation: 0.080 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Hardness, Rockwell R: 117
$ 1584/MT
- Density: 1.11 g/cc
- Water Absorption: 0.70 % @Thickness 2.00 mm
- Moisture Absorption: 0.300 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
DuPont Performance Polymers Rynite® FG530 NC011 Polyethylene Terephthalate (PET) (Unverified Data**)
$ 1534/MT
- Density: 1.57 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 162 MPa
- Elongation at Break: 2.1 %
$ 1661/MT
- Density: 1.29 g/cc
- Density: 1.50 g/cc
- Water Absorption: 0.35 % @Thickness 2.00 mm
- Moisture Absorption: 0.150 % @Thickness 2.00 mm
- Viscosity: 68560 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 2151/MT
- Density: 0.940 g/cc
- Density: 1.07 g/cc
- Water Absorption: 0.80 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.50 %
$ 1593/MT
- Density: 1.02 g/cc
- Density: 1.16 g/cc
- Water Absorption: 0.70 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
$ 2278/MT
- Density: 1.04 g/cc
- Tensile Strength at Break: 40.0 MPa @Temperature 23.0 °C
- Elongation at Break: >= 50 % @Temperature 23.0 °C
- Elongation at Break: 125 % @Temperature 23.0 °C
- Elongation at Break: 150 % @Temperature 23.0 °C
$ 1744/MT
- Density: 1.19 g/cc
- Density: 1.37 g/cc
- Water Absorption: 0.40 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Viscosity: 78230 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 1748/MT
- Density: 1.20 g/cc
- Melt Flow: 7.5 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore D: 70 @Time 15.0 sec
- Tensile Strength at Break: 40.0 MPa @Temperature 23.0 °C
- Tensile Stress: 30.0 MPa @Strain 10.0 %, Temperature 23.0 °C
$ 1702/MT
- Density: 1.22 g/cc
- Hardness, Shore D: <= 63
- Tensile Strength at Break: 43.0 MPa
- Elongation at Break: >= 300 %
- Charpy Impact, Notched: 12.0 J/cm²
$ 2590/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm @Thickness 2.00 mm
- Tensile Strength at Break: 82.0 MPa @Temperature 23.0 °C
- Elongation at Break: 5.0 % @Temperature 23.0 °C
$ 1886/MT
- Density: 1.42 g/cc
- Tensile Strength at Break: 133 MPa
- Elongation at Break: 2.2 %
- Tensile Modulus: 9.60 GPa
- Izod Impact, Notched (ISO): 7.00 kJ/m²
$ 1861/MT
- Density: 1.35 g/cc
- Tensile Strength at Break: 108 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 7.00 GPa
- Flexural Strength: 160 MPa
$ 1631/MT
- Density: 1.02 g/cc
- Tensile Strength, Yield: 32.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 32 %
- Flexural Modulus: 0.850 GPa
$ 1879/MT
- Density: 1.42 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C
- Water Absorption: 0.50 % @Temperature 23.0 °C
- Water Absorption: 1.4 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.019 cm/cm @Thickness 2.00 mm
$ 2397/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Tensile Strength at Break: 166 MPa
- Tensile Strength at Break: 180 MPa
$ 1759/MT
- Density: 1.272 g/cc
- Linear Mold Shrinkage, Flow: 0.026 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.023 cm/cm @Thickness 2.00 mm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Melt Flow: 6.5 g/10 min @Load 2.16 kg, Temperature 250 °C
$ 2146/MT
- Density: 1.54 g/cc
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Tensile Stress: 32.4 MPa @Strain 1.80 %, Temperature 23.0 °C
- Tensile Stress: 33.3 MPa @Strain 1.10 %, Temperature -40.0 °C
$ 1466/MT
- Density: 1.40 g/cc
- Density: 1.57 g/cc
- Water Absorption: 4.2 % @Thickness 2.00 mm
- Moisture Absorption: 1.20 % @Thickness 2.00 mm
- Viscosity: 31200 cP @Shear Rate 5000 1/s, Temperature 305 °C
$ 2399/MT
- Specific Gravity: 1.44 g/cc
- Tensile Strength: 170 MPa @Temperature 23.0 °C
- Elongation at Break: 5.0 % @Temperature 23.0 °C
- Flexural Strength: 230 MPa @Temperature 23.0 °C
- Flexural Modulus: 10.8 GPa @Temperature 23.0 °C
$ 1504/MT
- Density: 1.42 g/cc
- Water Absorption: 1.2 % @Thickness 2.00 mm
- Moisture Absorption: 0.170 % @Thickness 2.00 mm
- Viscosity: 84000 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 90000 cP @Shear Rate 5000 1/s, Temperature 215 °C
$ 1483/MT
- Density: 1.10 g/cc
- Hardness, Shore D: <= 40
- Tensile Strength at Break: 22.0 MPa
- Elongation at Break: >= 300 %
- Charpy Impact, Notched: NB
$ 2237/MT
- Specific Gravity: 1.15 g/cc
- Density: 1.15 g/cc
- Water Absorption: 5.0 % @Temperature 23.0 °C
- Water Absorption: 5.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0050 cm/cm
$ 2048/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 91.0 MPa
- Elongation at Break: 2.8 %
$ 2273/MT
- Density: 1.58 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 82.0 MPa
- Elongation at Break: 2.0 %
$ 1469/MT
- Density: 1.11 g/cc
- Density: 1.31 g/cc
- Water Absorption: 0.40 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Viscosity: 92000 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 2200/MT
- Density: 1.43 g/cc
- Water Absorption: 4.9 % @Thickness 2.00 mm
- Moisture Absorption: 1.50 % @Thickness 2.00 mm
- Viscosity Test: 137 cm³/g
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
$ 1948/MT
- Specific Gravity: 1.18 g/cc
- Density: 1.18 g/cc
- Water Absorption: 0.20 % @Temperature 23.0 °C
- Water Absorption: 0.60 % @Temperature 23.0 °C
- Water Absorption: 0.60 % @Temperature 23.0 °C
$ 1958/MT
- Density: 1.29 g/cc
- Density: 1.49 g/cc
- Water Absorption: 4.7 % @Thickness 2.00 mm
- Moisture Absorption: 1.50 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.90 %
$ 1603/MT
- Density: 0.950 g/cc
- Density: 1.09 g/cc
- Water Absorption: 7.0 % @Thickness 2.00 mm
- Moisture Absorption: 2.20 % @Thickness 2.00 mm
- Viscosity Test: 150 cm³/g
$ 1458/MT
- Density: 1.37 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 54.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 27 %
$ 1521/MT
- Density: 1.04 g/cc
- Tensile Strength at Break: 36.0 MPa @Temperature 23.0 °C
- Elongation at Break: >= 50 % @Temperature 23.0 °C
- Elongation at Break: 170 % @Temperature 23.0 °C
- Elongation at Break: 200 % @Temperature 23.0 °C
$ 1506/MT
- Density: 1.46 g/cc
- Density: 1.67 g/cc
- Viscosity: 75510 cP @Shear Rate 5000 1/s, Temperature 270 °C
- Viscosity: 91440 cP @Shear Rate 5000 1/s, Temperature 260 °C
- Viscosity: 112800 cP @Shear Rate 5000 1/s, Temperature 250 °C
$ 1504/MT
- Density: 1.35 g/cc
- Water Absorption: 6.3 % @Thickness 2.00 mm
- Moisture Absorption: 2.10 % @Thickness 2.00 mm
- Viscosity Test: 145 cm³/g
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
$ 1527/MT
- Density: 0.870 g/cc
- Density: 1.02 g/cc
- Viscosity: 57470 cP @Shear Rate 5000 1/s, Temperature 280 °C
- Viscosity: 81230 cP @Shear Rate 5000 1/s, Temperature 245 °C
- Viscosity: 96410 cP @Shear Rate 5000 1/s, Temperature 230 °C
$ 2395/MT
- Specific Gravity: 1.13 g/cc
- Density: 1.13 g/cc
- Water Absorption: 3.0 % @Temperature 23.0 °C
- Water Absorption: 9.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.010 cm/cm @Thickness 3.00 mm
$ 1664/MT
- Density: 1.06 g/cc
- Density: 1.18 g/cc
- Water Absorption: 6.5 % @Thickness 2.00 mm
- Moisture Absorption: 0.700 % @Thickness 2.00 mm
- Water Absorption at Saturation: 3.4 %
$ 2581/MT
- Density: 1.25 g/cc
- Density: 1.47 g/cc
- Water Absorption: 5.0 % @Thickness 2.00 mm
- Moisture Absorption: 1.50 % @Thickness 2.00 mm
- Viscosity: 40000 cP @Shear Rate 5000 1/s, Temperature 315 °C
$ 1508/MT
- Density: 1.36 g/cc
- Density: 1.54 g/cc
- Water Absorption: 0.35 % @Thickness 2.00 mm
- Moisture Absorption: 0.150 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
$ 1519/MT
- Density: 1.06 g/cc
- Density: 1.22 g/cc
- Water Absorption: 0.60 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.50 %
$ 2118/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 40.0 MPa
$ 1819/MT
- Density: 1.34 g/cc
- Water Absorption: 0.90 % @Thickness 2.00 mm
- Moisture Absorption: 0.350 % @Thickness 2.00 mm
- Viscosity: 148000 cP @Shear Rate 5000 1/s, Temperature 220 °C
- Viscosity: 171000 cP @Shear Rate 5000 1/s, Temperature 205 °C
$ 2546/MT
- Density: 1.33 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 43.0 MPa
- Elongation at Break: >= 50 %
$ 2476/MT
- Density: 1.37 g/cc
- Water Absorption: 0.90 % @Thickness 2.00 mm
- Moisture Absorption: 0.300 % @Thickness 2.00 mm
- Viscosity: 165000 cP @Shear Rate 5000 1/s, Temperature 220 °C
- Viscosity: 187000 cP @Shear Rate 5000 1/s, Temperature 205 °C
$ 1642/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1840/MT
- Density: 1.39 g/cc
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 54.0 MPa
$ 1618/MT
- Density: 1.38 g/cc
- Water Absorption: 0.82 % @Thickness 2.00 mm
- Moisture Absorption: 0.210 % @Thickness 2.00 mm
- Viscosity: 69000 cP @Shear Rate 5000 1/s, Temperature 220 °C
- Viscosity: 83000 cP @Shear Rate 5000 1/s, Temperature 205 °C
$ 1588/MT
- Density: 1.38 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 54.0 MPa
- Elongation at Break: 33 %
- Elongation at Yield: 20 %
$ 1487/MT
- Density: 1.38 g/cc
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 54.0 MPa
$ 1516/MT
- Specific Gravity: 1.42 g/cc
- Tensile Strength: 144 MPa @Temperature 150 °C
- Elongation at Break: 2.0 % @Temperature 23.0 °C
- Elongation at Break: 4.0 % @Temperature 150 °C
- Flexural Strength: 314 MPa @Temperature 23.0 °C
$ 2594/MT
- Specific Gravity: 1.35 g/cc @Temperature 23.0 °C
- Water Absorption: 0.070 % @Temperature 23.0 °C
- Water Absorption: 0.16 % @Temperature 23.0 °C
- Tensile Strength: 80.0 MPa @Temperature 23.0 °C
- Elongation at Break: 3.0 % @Temperature 23.0 °C
$ 2276/MT
- Specific Gravity: 1.32 g/cc
- Water Absorption: 0.090 % @Temperature 23.0 °C
- Water Absorption: 0.23 % @Temperature 23.0 °C
- Tensile Strength: 91.0 MPa @Temperature 23.0 °C
- Elongation at Break: 31 % @Temperature 23.0 °C
$ 1603/MT
- Specific Gravity: 1.56 g/cc @Temperature 23.0 °C
- Water Absorption: 0.10 % @Temperature 23.0 °C
- Water Absorption: 0.23 % @Temperature 23.0 °C
- Tensile Strength: 106 MPa @Temperature 150 °C
- Tensile Strength: 165 MPa @Temperature 23.0 °C
$ 1883/MT
- Specific Gravity: 1.38 g/cc
- Water Absorption: 0.20 % @Temperature 23.0 °C
- Tensile Strength: 73.0 MPa @Temperature 23.0 °C
- Flexural Strength: 117 MPa @Temperature 23.0 °C
- Flexural Modulus: 0.00260 GPa @Temperature 23.0 °C
$ 1742/MT
- Tensile Strength: 144 MPa @Temperature 150 °C
- Tensile Strength: 229 MPa @Temperature 23.0 °C
- Flexural Modulus: 17.2 GPa @Temperature 23.0 °C
- Izod Impact, Notched: 1.10 J/cm @Temperature 23.0 °C
- CTE, linear, Parallel to Flow: 47.0 µm/m-°C @Temperature 23.0 - 150 °C
$ 2026/MT
- Specific Gravity: 1.46 g/cc @Temperature 23.0 °C
- Water Absorption: 0.20 % @Temperature 23.0 °C
- Water Absorption: 0.20 % @Temperature 23.0 °C
- Tensile Strength: 106 MPa @Temperature 150 °C
- Tensile Strength: 142 MPa @Temperature 23.0 °C
$ 1490/MT
- Specific Gravity: 1.42 g/cc
- Density: 1.42 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C
- Water Absorption: 1.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.017 - 0.020 cm/cm @Thickness 3.20 mm
$ 1446/MT
- Density: 1.12 g/cc
- Density: 1.32 g/cc
- Water Absorption: 1.8 % @Thickness 2.00 mm
- Moisture Absorption: 0.700 % @Thickness 2.00 mm
- Viscosity: 29770 cP @Shear Rate 5000 1/s, Temperature 300 °C
$ 1602/MT
- Density: 1.12 g/cc
- Density: 1.33 g/cc
- Water Absorption: 4.5 % @Thickness 2.00 mm
- Moisture Absorption: 1.50 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.85 %
$ 1498/MT
- Density: 1.38 g/cc
- Water Absorption: 0.40 % @Thickness 2.00 mm
- Moisture Absorption: 0.150 % @Thickness 2.00 mm
- Viscosity: 175000 cP @Temperature 250 °C
- Viscosity: 55600 cP @Shear Rate 5000 1/s, Temperature 270 °C
$ 1756/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Melt Flow: 10.1 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 57.0 MPa
$ 1595/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 13 %
$ 1650/MT
- Density: 1.54 g/cc
- Water Absorption: 0.35 % @Thickness 2.00 mm
- Moisture Absorption: 0.150 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
$ 2532/MT
- Density: 1.02 g/cc
- Tensile Strength at Break: 29.0 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 29.0 MPa @Temperature 23.0 °C
- Elongation at Break: >= 50 % @Temperature 23.0 °C
- Elongation at Break: 190 % @Temperature 23.0 °C
$ 1792/MT
- Density: 1.50 g/cc
- Water Absorption: 0.35 % @Thickness 2.00 mm
- Moisture Absorption: 0.150 % @Thickness 2.00 mm
- Viscosity: 230000 cP @Temperature 250 °C
- Viscosity: 68400 cP @Shear Rate 5000 1/s, Temperature 270 °C
$ 2164/MT
- Density: 1.56 g/cc
- Water Absorption: 0.10 % @Temperature 23.0 °C
- Water Absorption: 0.80 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.016 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm @Thickness 2.00 mm
$ 2280/MT
- Density: 1.63 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 280 °C
- Tensile Strength at Break: 110 MPa
$ 1931/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 40.0 MPa @Temperature 23.0 °C
- Tensile Strength at Break: 43.0 MPa @Temperature 23.0 °C
$ 1794/MT
- Density: 1.17 g/cc
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Tensile Stress: 5.62 MPa @Strain 1.20 %, Temperature 90.0 °C
$ 2009/MT
- Density: 1.16 g/cc
- Density: 1.31 g/cc
- Moisture Absorption: 1.20 % @Thickness 2.00 mm
- Viscosity: 93100 cP @Shear Rate 5000 1/s, Temperature 280 °C
- Viscosity: 123000 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 2248/MT
- Density: 1.30 g/cc
- Density: 1.43 g/cc
- Water Absorption at Saturation: 1.9 %
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
$ 2523/MT
- Density: 1.14 g/cc
- Density: 1.37 g/cc
- Water Absorption: 0.40 % @Thickness 2.00 mm
- Moisture Absorption: 0.150 % @Thickness 2.00 mm
- Viscosity: 55190 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 1587/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Stress: 16.6 MPa @Strain 0.500 %, Temperature 23.0 °C
$ 1727/MT
- Density: 1.07 g/cc
- Water Absorption: 1.1 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.020 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm @Thickness 2.00 mm
- Tensile Stress: 44.0 MPa @Strain 50.0 %, Temperature 23.0 °C
$ 1861/MT
- Density: 1.35 g/cc @Temperature 23.0 °C
- Tensile Strength at Break: 163 MPa @Temperature 23.0 °C
- Elongation at Break: 3.3 % @Temperature 23.0 °C
- Tensile Modulus: 9.40 GPa @Temperature 23.0 °C
- Flexural Strength: 260 MPa @Temperature 23.0 °C
$ 2199/MT
- Specific Gravity: 1.16 g/cc
- Density: 1.16 g/cc
- Water Absorption: 0.20 % @Temperature 23.0 °C
- Water Absorption: 0.70 % @Temperature 23.0 °C
- Water Absorption: 0.70 % @Temperature 23.0 °C
$ 1567/MT
- Density: 1.42 g/cc
- Water Absorption: 0.90 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
$ 1454/MT
- Density: 1.15 g/cc
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 220 °C
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Shore D: 41
- Hardness, Shore D: <= 45
$ 1586/MT
- Density: 1.05 g/cc
- Water Absorption: 1.5 % @Thickness 2.00 mm
- Moisture Absorption: 0.750 % @Thickness 2.00 mm
- Viscosity: 210000 cP @Temperature 250 °C
- Viscosity: 104300 cP @Shear Rate 5000 1/s, Temperature 240 °C
$ 1623/MT
- Density: 1.42 g/cc
- Water Absorption: 0.20 % @Temperature 23.0 °C
- Water Absorption: 1.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.017 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm @Thickness 2.00 mm
$ 1602/MT
- Density: 1.14 g/cc
- Water Absorption: 8.5 % @Thickness 2.00 mm
- Moisture Absorption: 2.60 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
$ 1478/MT
- Density: 1.42 g/cc
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: 20 %
- Elongation at Yield: 10 %
- Tensile Modulus: 3.40 GPa
$ 1791/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm @Diameter 4.00 mm
- Linear Mold Shrinkage: 0.017 cm/cm @Diameter 4.00 mm
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 50.0 MPa @Temperature 23.0 °C
$ 1578/MT
- Density: 1.42 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C
- Water Absorption: 0.60 % @Temperature 23.0 °C
- Water Absorption: 1.4 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.020 cm/cm @Thickness 2.00 mm
$ 1559/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm @Thickness 2.00 mm
- Tensile Strength: 70.0 MPa @Temperature 23.0 °C
- Tensile Stress: 1.14 MPa @Strain 0.100 %, Temperature 80.0 °C
$ 2242/MT
- Density: 1.24 g/cc
- Density: 1.41 g/cc
- Water Absorption: 5.5 % @Thickness 2.00 mm
- Moisture Absorption: 1.70 % @Thickness 2.00 mm
- Viscosity: 69000 cP @Shear Rate 5000 1/s, Temperature 305 °C
$ 1603/MT
- Density: 1.22 g/cc
- Density: 1.42 g/cc
- Water Absorption: 0.40 % @Thickness 2.00 mm
- Moisture Absorption: 0.150 % @Thickness 2.00 mm
- Viscosity: 54480 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 2249/MT
- Density: 1.43 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 cm/cm
- Tensile Strength at Break: 175 MPa @Temperature 23.0 °C
$ 2071/MT
- Density: 1.23 g/cc
- Water Absorption: 7.6 % @Thickness 2.00 mm
- Moisture Absorption: 2.20 % @Thickness 2.00 mm
- Water Absorption at Saturation: 1.7 %
- Viscosity Test: 150 cm³/g
$ 1786/MT
- Density: 1.06 g/cc
- Tensile Strength, Yield: 54.0 MPa
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Yield: 4.5 %
- Elongation at Yield: 18 %
$ 1821/MT
- Density: 1.45 g/cc
- Viscosity Test: 140 cm³/g
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 72.0 MPa
$ 1610/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm @Thickness 2.00 mm
- Tensile Strength at Break: 44.0 MPa @Temperature 23.0 °C
- Elongation at Break: 200 % @Temperature 23.0 °C
$ 1623/MT
- Density: 0.950 g/cc
- Density: 1.14 g/cc
- Water Absorption: 8.5 % @Thickness 2.00 mm
- Moisture Absorption: 2.80 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
$ 1667/MT
- Density: 1.07 g/cc
- Hardness, Shore D: <= 30
- Tensile Strength at Break: 24.0 MPa
- Elongation at Break: >= 300 %
- Charpy Impact, Notched: NB
$ 1731/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm @Thickness 2.00 mm
- Tensile Strength, Yield: 58.0 MPa @Temperature 23.0 °C
- Tensile Modulus: 2.25 GPa @Temperature 23.0 °C
$ 1463/MT
- Density: 1.01 g/cc
- Density: 1.14 g/cc
- Water Absorption: 8.5 % @Thickness 2.00 mm
- Moisture Absorption: 2.60 % @Thickness 2.00 mm
- Viscosity: 42210 cP @Shear Rate 5000 1/s, Temperature 295 °C
$ 2061/MT
- Density: 1.39 g/cc
- Tensile Strength at Break: 200 MPa
- Elongation at Break: 3.5 %
- Tensile Modulus: 10.5 GPa
- Flexural Strength: 290 MPa
$ 1902/MT
- Density: 1.09 g/cc
- Moisture Absorption: 2.00 % @Thickness 2.00 mm
- Water Absorption at Saturation: 1.1 %
- Linear Mold Shrinkage, Flow: 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
$ 1618/MT
- Density: 1.07 g/cc
- Density: 1.23 g/cc
- Water Absorption: 0.60 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
$ 1735/MT
- Density: 1.08 g/cc
- Water Absorption: 3.3 % @Thickness 2.00 mm
- Moisture Absorption: 1.40 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.58 %
- Viscosity Test: 170 cm³/g
$ 1702/MT
- Density: 1.40 g/cc
- Tensile Strength, Yield: 63.0 MPa
- Elongation at Break: 30 %
- Elongation at Yield: 12 %
- Tensile Modulus: 3.05 GPa
$ 1837/MT
- Density: 1.11 g/cc
- Density: 1.31 g/cc
- Water Absorption: 0.40 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Viscosity: 75900 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 2012/MT
- Density: 1.61 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 117 MPa
- Elongation at Break: 2.6 %
$ 1544/MT
- Density: 1.21 g/cc
- Water Absorption: 0.50 % @Temperature 23.0 °C
- Water Absorption: 1.5 % @Temperature 23.0 °C
- Water Absorption: 2.2 % @Temperature 23.0 °C
- Hardness, Shore D: 54 @Time 15.0 sec
$ 1445/MT
- Density: 1.38 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2171/MT
- Density: 1.42 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Stress: 16.3 MPa @Strain 0.400 %, Temperature -40.0 °C
- Tensile Stress: 20.4 MPa @Strain 0.600 %, Temperature 23.0 °C
- Tensile Stress: 56.4 MPa @Strain 2.50 %, Temperature 23.0 °C
$ 1542/MT
- Density: 1.39 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 125 MPa
- Tensile Strength at Break: 185 MPa
$ 1454/MT
- Density: 1.16 g/cc
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.019 cm/cm
- Melt Flow: 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1470/MT
- Density: 1.16 g/cc
- Water Absorption: 0.20 % @Temperature 23.0 °C
- Water Absorption: 0.60 % @Temperature 23.0 °C
- Water Absorption: 0.40 % @Thickness 1.00 mm, Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 2.00 mm
$ 2172/MT
- Density: 1.28 g/cc
- Hardness, Shore D: <= 82
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: >= 300 %
- Tensile Modulus: 1.18 GPa
$ 1461/MT
- Density: 1.06 g/cc
- Water Absorption: 3.0 % @Thickness 2.00 mm
- Moisture Absorption: 1.30 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
$ 1622/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C
- Water Absorption: 1.3 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.017 cm/cm @Thickness 2.00 mm
$ 2369/MT
- Density: 1.37 g/cc
- Viscosity: 43340 cP @Shear Rate 5000 1/s, Temperature 305 °C
- Viscosity: 54070 cP @Shear Rate 5000 1/s, Temperature 295 °C
- Viscosity: 68870 cP @Shear Rate 5000 1/s, Temperature 285 °C
- Viscosity: 127100 cP @Shear Rate 500 1/s, Temperature 305 °C
$ 2202/MT
- Density: 1.20 g/cc
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 130 MPa
$ 1602/MT
- Density: 1.00 g/cc
- Density: 1.17 g/cc
- Water Absorption: 0.50 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
$ 1593/MT
- Density: 1.42 g/cc
- Water Absorption: 0.90 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
$ 1517/MT
- Density: 1.11 g/cc
- Density: 1.31 g/cc
- Water Absorption: 0.40 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Viscosity: 66530 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 2050/MT
- Density: 1.04 g/cc
- Viscosity: 260000 cP @Temperature 250 °C
- Linear Mold Shrinkage, Flow: 0.026 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Stress: 27.0 MPa @Strain 50.0 %
$ 1682/MT
- Density: 0.900 g/cc
- Density: 1.06 g/cc
- Water Absorption: 3.0 % @Thickness 2.00 mm
- Moisture Absorption: 1.30 % @Thickness 2.00 mm
- Viscosity Test: 95 cm³/g
$ 1478/MT
- Density: 1.11 g/cc
- Density: 1.31 g/cc
- Water Absorption: 0.40 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Viscosity: 88500 cP @Shear Rate 5000 1/s, Temperature 260 °C
DuPont Performance Polymers Rynite® FR515 BK507 Polyethylene Terephthalate (PET) (Unverified Data**)
$ 1483/MT
- Density: 1.55 g/cc
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 2.2 %
- Tensile Modulus: 6.135 GPa
- Flexural Strength: 160 MPa
$ 1580/MT
- Density: 1.05 g/cc
- Density: 1.22 g/cc
- Water Absorption: 2.2 % @Thickness 2.00 mm
- Moisture Absorption: 0.400 % @Thickness 2.00 mm
- Water Absorption at Saturation: 1.6 %
$ 1631/MT
- Density: 1.69 g/cc
- Water Absorption: 0.62 % @Thickness 2.00 mm
- Moisture Absorption: 0.140 % @Thickness 2.00 mm
- Viscosity: 43000 cP @Shear Rate 5000 1/s, Temperature 305 °C
- Viscosity: 55000 cP @Shear Rate 5000 1/s, Temperature 295 °C
$ 1562/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2378/MT
- Density: 1.01 g/cc
- Density: 1.14 g/cc
- Water Absorption: 8.5 % @Thickness 2.00 mm
- Moisture Absorption: 2.60 % @Thickness 2.00 mm
- Viscosity: 84550 cP @Shear Rate 5000 1/s, Temperature 300 °C
$ 1685/MT
- Density: 1.48 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 138 MPa
- Elongation at Break: 2.6 %
$ 1446/MT
- Density: 1.50 g/cc
- Water Absorption: 0.35 % @Thickness 2.00 mm
- Moisture Absorption: 0.150 % @Thickness 2.00 mm
- Viscosity: 230000 cP @Temperature 250 °C
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
$ 2023/MT
- Density: 1.68 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 1.9 %
$ 1493/MT
- Density: 0.970 g/cc
- Density: 1.14 g/cc
- Water Absorption: 8.5 % @Thickness 2.00 mm
- Moisture Absorption: 2.60 % @Thickness 2.00 mm
- Viscosity Test: 150 cm³/g
$ 1937/MT
- Tensile Modulus: 0.550 GPa
- Charpy Impact, Notched: 1.60 J/cm²
- Melting Point: 220 °C
- Glass Transition Temp, Tg: 30.0 °C
- Additives: Plasticiser
$ 1501/MT
- Density: 1.29 g/cc
- Water Absorption: 2.1 % @Temperature 23.0 °C
- Water Absorption: 6.8 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm @Thickness 2.00 mm
$ 1783/MT
- Density: 1.14 g/cc
- Water Absorption: 8.5 % @Thickness 2.00 mm
- Moisture Absorption: 2.70 % @Thickness 2.00 mm
- Viscosity Test: 300 cm³/g
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
$ 2027/MT
- Density: 1.40 g/cc
- Density: 1.57 g/cc
- Water Absorption: 4.2 % @Thickness 2.00 mm
- Moisture Absorption: 1.20 % @Thickness 2.00 mm
- Viscosity Test: 100 cm³/g
$ 2087/MT
- Density: 1.31 g/cc
- Melt Flow: 32.9 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 58.0 MPa
- Elongation at Break: 20 %
- Elongation at Yield: 6.0 %
$ 1810/MT
- Density: 1.05 g/cc
- Moisture Absorption: 1.00 % @Thickness 2.00 mm
- Viscosity Test: 130 cm³/g
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
$ 1556/MT
- Density: 1.40 g/cc
- Viscosity: 111000 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 129000 cP @Shear Rate 5000 1/s, Temperature 215 °C
- Viscosity: 152000 cP @Shear Rate 5000 1/s, Temperature 200 °C
- Viscosity: 432000 cP @Shear Rate 500 1/s, Temperature 230 °C
$ 1636/MT
- Density: 1.42 g/cc
- Viscosity: 102500 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 104400 cP @Shear Rate 5000 1/s, Temperature 215 °C
- Viscosity: 112500 cP @Shear Rate 5000 1/s, Temperature 200 °C
- Viscosity: 369800 cP @Shear Rate 500 1/s, Temperature 230 °C
$ 1578/MT
- Density: 1.52 g/cc
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 9.60 GPa
- Flexural Strength: 200 MPa
$ 1680/MT
- Density: 1.18 g/cc
- Water Absorption: 6.8 % @Thickness 2.00 mm
- Moisture Absorption: 0.700 % @Thickness 2.00 mm
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
$ 1467/MT
- Density: 1.19 g/cc
- Density: 1.42 g/cc
- Water Absorption: 0.90 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Viscosity: 143400 cP @Shear Rate 5000 1/s, Temperature 230 °C
$ 1827/MT
- Density: 1.01 g/cc
- Density: 1.14 g/cc
- Water Absorption: 8.5 % @Thickness 2.00 mm
- Moisture Absorption: 2.60 % @Thickness 2.00 mm
- Viscosity Test: 280 cm³/g
$ 1645/MT
- Density: 1.70 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 175 MPa
- Elongation at Break: 1.9 %
$ 1695/MT
- Density: 1.07 g/cc
- Water Absorption: 0.80 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
$ 1522/MT
- Density: 1.34 g/cc
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 2.3 %
- Tensile Modulus: 7.30 GPa
- Izod Impact, Notched (ISO): 6.50 kJ/m²
$ 1833/MT
- Density: 1.58 g/cc
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 3.4 %
- Tensile Modulus: 7.20 GPa
- Flexural Strength: 155 MPa
$ 2127/MT
- Density: 1.42 g/cc
- Water Absorption: 1.4 % @Thickness 2.00 mm
- Moisture Absorption: 0.300 % @Thickness 2.00 mm
- Viscosity: 92857 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 100600 cP @Shear Rate 5000 1/s, Temperature 215 °C
$ 1448/MT
- Density: 1.32 g/cc
- Water Absorption: 0.20 % @Temperature 23.0 °C
- Water Absorption: 0.40 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.022 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.022 cm/cm @Thickness 2.00 mm
$ 2251/MT
- Density: 1.55 g/cc
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 1.7 %
- Tensile Modulus: 10.2 GPa
- Flexural Strength: 160 MPa
$ 1699/MT
- Density: 1.31 g/cc
- Tensile Strength, Yield: 59.0 MPa
- Elongation at Break: 30 %
- Elongation at Yield: 8.0 %
- Tensile Modulus: 2.60 GPa
$ 2016/MT
- Density: 1.38 g/cc
- Water Absorption: 0.40 % @Thickness 2.00 mm
- Moisture Absorption: 0.150 % @Thickness 2.00 mm
- Viscosity: 175000 cP @Temperature 250 °C
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
$ 1676/MT
- Density: 1.19 g/cc
- Density: 1.42 g/cc
- Viscosity: 135800 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 156200 cP @Shear Rate 5000 1/s, Temperature 215 °C
- Viscosity: 164900 cP @Shear Rate 5000 1/s, Temperature 200 °C
$ 1526/MT
- Density: 1.41 g/cc
- Tensile Strength at Break: 102 MPa
- Elongation at Break: 3.4 %
- Tensile Modulus: 5.70 GPa
- Izod Impact, Notched (ISO): 5.00 kJ/m²
$ 2334/MT
- Specific Gravity: 1.58 g/cc
- Density: 1.58 g/cc
- Water Absorption: 0.83 % @Thickness 2.00 mm
- Moisture Absorption: 0.130 % @Thickness 2.00 mm
- Viscosity: 37000 cP @Shear Rate 5000 1/s, Temperature 315 °C
$ 1580/MT
- Specific Gravity: 1.56 g/cc
- Density: 1.56 g/cc
- Water Absorption: 0.70 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Viscosity: 44000 cP @Shear Rate 5000 1/s, Temperature 300 °C
$ 1492/MT
- Density: 1.39 g/cc
- Water Absorption: 5.7 % @Thickness 2.00 mm
- Moisture Absorption: 1.80 % @Thickness 2.00 mm
- Water Absorption at Saturation: 1.2 %
- Viscosity: 198170 cP @Shear Rate 500 1/s, Temperature 295 °C
$ 2458/MT
- Density: 1.03 g/cc
- Density: 1.21 g/cc
- Water Absorption: 6.5 % @Thickness 2.00 mm
- Moisture Absorption: 2.20 % @Thickness 2.00 mm
- Viscosity: 54330 cP @Shear Rate 5000 1/s, Temperature 305 °C
DuPont Performance Polymers Rynite® FR531 NC010 Polyethylene Terephthalate (PET) (Unverified Data**)
$ 1630/MT
- Density: 1.83 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 129 MPa
$ 1518/MT
- Density: 1.08 g/cc
- Water Absorption: 1.17 % @Temperature 23.0 °C
- Water Absorption: 1.9 % @Thickness 1.00 mm, Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.020 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm @Thickness 2.00 mm
$ 1606/MT
- Density: 1.72 g/cc
- Filler Content: 50 %
- Water Absorption: 0.10 % @Temperature 23.0 °C
- Water Absorption: 0.20 % @Temperature 23.0 °C
- Viscosity: 62000 cP @Shear Rate 10000 1/s, Temperature 270 °C
$ 1476/MT
- Density: 1.43 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 71.0 MPa
$ 1469/MT
- Density: 1.37 g/cc
- Filler Content: 30 %
- Water Absorption: 1.9 % @Temperature 23.0 °C
- Water Absorption: 6.0 % @Temperature 23.0 °C
- Viscosity: 58000 cP @Shear Rate 7000 1/s, Temperature 305 °C
$ 1708/MT
- Density: 1.06 g/cc
- Water Absorption: 3.0 % @Thickness 2.00 mm
- Moisture Absorption: 1.30 % @Thickness 2.00 mm
- Viscosity: 66500 cP @Shear Rate 5000 1/s, Temperature 270 °C
- Viscosity: 71900 cP @Shear Rate 5000 1/s, Temperature 250 °C
$ 1844/MT
- Density: 1.56 g/cc
- Water Absorption: 0.80 % @Thickness 2.00 mm
- Moisture Absorption: 0.100 % @Thickness 2.00 mm
- Viscosity: 96000 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 102000 cP @Shear Rate 5000 1/s, Temperature 215 °C
$ 2501/MT
- Density: 1.44 g/cc
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 9.50 GPa
- Charpy Impact Unnotched: 6.00 J/cm²
$ 1483/MT
- Density: 1.43 g/cc
- Water Absorption: 0.90 % @Thickness 2.00 mm
- Moisture Absorption: 0.170 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
$ 2282/MT
- Density: 1.14 g/cc
- Water Absorption: 0.40 % @Temperature 23.0 °C
- Melt Flow: 4.5 g/10 min @Load 10.0 kg, Temperature 250 °C
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Shore D: 62 @Time 15.0 sec
$ 2207/MT
- Density: 1.00 g/cc
- Density: 1.13 g/cc
- Water Absorption: 0.80 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.60 %
$ 1529/MT
- Density: 1.42 g/cc
- Viscosity: 88855 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 90970 cP @Shear Rate 5000 1/s, Temperature 215 °C
- Viscosity: 99370 cP @Shear Rate 5000 1/s, Temperature 200 °C
- Viscosity: 254390 cP @Shear Rate 500 1/s, Temperature 230 °C
$ 1868/MT
- Density: 1.11 g/cc
- Density: 1.30 g/cc
- Water Absorption: 0.50 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.017 cm/cm
$ 2429/MT
- Density: 1.14 g/cc
- Water Absorption: 0.50 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2173/MT
- Density: 1.01 g/cc
- Density: 1.19 g/cc
- Viscosity: 114600 cP @Shear Rate 5000 1/s, Temperature 240 °C
- Viscosity: 143100 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 511800 cP @Shear Rate 500 1/s, Temperature 240 °C
$ 1519/MT
- Density: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
$ 2474/MT
- Density: 2.10 g/cc
- Melting Point: 200 °C
- Delivery Form: Pellets
- Processing: Casting
- Processing: Coatable
$ 1737/MT
- Density: 1.10 g/cc
- Density: 1.11 g/cc
- Water Absorption: 0.70 % @Thickness 2.00 mm
- Moisture Absorption: 0.300 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.70 %
$ 1626/MT
- Density: 1.56 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 2.1 %
$ 2362/MT
- Density: 1.03 g/cc
- Density: 1.21 g/cc
- Viscosity: 169000 cP @Shear Rate 5000 1/s, Temperature 260 °C
- Viscosity: 226000 cP @Shear Rate 5000 1/s, Temperature 250 °C
- Viscosity: 312000 cP @Shear Rate 5000 1/s, Temperature 240 °C
$ 1490/MT
- Density: 1.40 g/cc
- Moisture Absorption: 2.00 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 120 MPa
$ 1658/MT
- Density: 1.05 g/cc
- Moisture Absorption: 1.10 % @Thickness 2.00 mm
- Viscosity: 230000 cP @Temperature 250 °C
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
$ 2044/MT
- Density: 1.40 g/cc
- Viscosity: 111000 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 129000 cP @Shear Rate 5000 1/s, Temperature 215 °C
- Viscosity: 152000 cP @Shear Rate 5000 1/s, Temperature 200 °C
- Viscosity: 432000 cP @Shear Rate 500 1/s, Temperature 230 °C
$ 1685/MT
- Density: 1.50 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 3.1 %
$ 1702/MT
- Density: 1.45 g/cc
- Tensile Strength at Break: 113 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 6.90 GPa
- Flexural Strength: 175 MPa
$ 1782/MT
- Density: 1.04 g/cc
- Viscosity: 215000 cP @Temperature 250 °C
- Viscosity Test: 108 cm³/g
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
DuPont Performance Polymers Rynite® FR530 NC010 Polyethylene Terephthalate (PET) (Unverified Data**)
$ 1727/MT
- Density: 1.68 g/cc
- Water Absorption: 0.75 % @Thickness 2.00 mm
- Moisture Absorption: 0.150 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
$ 1912/MT
- Density: 1.19 g/cc
- Density: 1.42 g/cc
- Viscosity: 134900 cP @Shear Rate 5000 1/s, Temperature 230 °C
- Viscosity: 151800 cP @Shear Rate 5000 1/s, Temperature 215 °C
- Viscosity: 167300 cP @Shear Rate 5000 1/s, Temperature 200 °C
$ 1475/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.25 g/cc
- Water Absorption: 0.20 % @Temperature 23.0 °C
- Water Absorption: 0.20 % @Temperature 23.0 °C
- Melt Flow: 5.2 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1634/MT
- Density: 1.50 g/cc
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 7.80 GPa
- Flexural Strength: 140 MPa
$ 1859/MT
- Density: 1.03 g/cc
- Density: 1.22 g/cc
- Water Absorption: 0.31 % @Thickness 2.00 mm
- Moisture Absorption: 0.120 % @Thickness 2.00 mm
- Viscosity: 219200 cP @Shear Rate 5000 1/s, Temperature 250 °C
$ 1483/MT
- Density: 0.960 g/cc
- Density: 1.15 g/cc
- Water Absorption: 0.70 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.70 %
$ 2207/MT
- Density: 1.14 g/cc
- Water Absorption: 8.5 % @Thickness 2.00 mm
- Moisture Absorption: 2.70 % @Thickness 2.00 mm
- Viscosity Test: 350 cm³/g
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
$ 1450/MT
- Density: 1.43 g/cc
- Filler Content: 5.0 %
- Linear Mold Shrinkage: 0.013 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage: 0.014 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 60.0 MPa @Temperature 23.0 °C
$ 1606/MT
- Density: 1.41 g/cc
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 71.0 MPa
- Elongation at Break: 23 %
- Elongation at Yield: 14 %
$ 1652/MT
- Density: 1.27 g/cc
- Density: 1.42 g/cc
- Water Absorption: 1.0 % @Thickness 2.00 mm
- Moisture Absorption: 0.250 % @Thickness 2.00 mm
- Viscosity: 72620 cP @Shear Rate 5000 1/s, Temperature 260 °C
$ 2049/MT
- Density: 1.03 g/cc
- Density: 1.19 g/cc
- Water Absorption: 0.60 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Water Absorption at Saturation: 0.60 %
$ 1966/MT
- Density: 1.23 g/cc
- Water Absorption: 7.6 % @Thickness 2.00 mm
- Moisture Absorption: 2.20 % @Thickness 2.00 mm
- Water Absorption at Saturation: 1.7 %
- Viscosity Test: 150 cm³/g
DuPont Performance Polymers Crastin® 6134 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)
$ 1585/MT
- Density: 1.30 g/cc
- Melt Flow: 33.5 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 59.0 MPa
- Elongation at Break: 45 %
- Elongation at Yield: 4.0 %
$ 1930/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Hardness, Rockwell M: 53
- Hardness, Rockwell M: 81
$ 2114/MT
- Density: 1.42 g/cc
- Water Absorption: 0.90 % @Thickness 2.00 mm
- Moisture Absorption: 0.200 % @Thickness 2.00 mm
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
$ 1786/MT
- Density: 1.04 g/cc
- Density: 1.23 g/cc
- Viscosity: 91910 cP @Shear Rate 5000 1/s, Temperature 245 °C
- Viscosity: 99440 cP @Shear Rate 5000 1/s, Temperature 235 °C
- Viscosity: 108100 cP @Shear Rate 5000 1/s, Temperature 225 °C
$ 2409/MT
- Density: 1.22 g/cc
- Density: 1.41 g/cc
- Water Absorption: 0.42 % @Thickness 2.00 mm
- Moisture Absorption: 0.170 % @Thickness 2.00 mm
- Viscosity: 77750 cP @Shear Rate 5000 1/s, Temperature 260 °C
Delivery Polymer DuPont Performance Polymers
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.