DuPont Performance Polymers Crastin® LW9030 NC010 PBT+ASA  (Unverified Data**)

Seller in Tianjin price: $1680 per MT

DuPont Performance Polymers Crastin® LW9030 NC010 PBT+ASA  (Unverified Data**) in Polymer, Thermoplastic, Polyester, TP, Polybutylene Terephthalate (PBT), Glass Fiber Reinforced, PBT + ASA Blend

  • Physical Properties
  • Density
  • 1.28 g/cc
  • Density
  • 1.44 g/cc
  • Water Absorption
  • 0.72 % @Thickness 2.00 mm
  • Moisture Absorption
  • 0.240 % @Thickness 2.00 mm
  • Viscosity
  • 67000 cP @Shear Rate 5000 1/s, Temperature 260 °C
  • Viscosity
  • 77000 cP @Shear Rate 5000 1/s, Temperature 250 °C
  • Viscosity
  • 89000 cP @Shear Rate 5000 1/s, Temperature 240 °C
  • Viscosity
  • 278000 cP @Shear Rate 500 1/s, Temperature 260 °C
  • Viscosity
  • 325000 cP @Shear Rate 500 1/s, Temperature 250 °C
  • Viscosity
  • 383000 cP @Shear Rate 500 1/s, Temperature 240 °C
  • Linear Mold Shrinkage, Flow
  • 0.0015 cm/cm
  • Linear Mold Shrinkage, Flow
  • 0.0020 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.0020 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.0070 cm/cm
  • Mechanical Properties
  • Tensile Strength at Break
  • 130 MPa
  • Tensile Stress
  • 3.26 MPa @Strain 0.250 %, Temperature 160 °C
  • Tensile Stress
  • 13.4 MPa @Strain 1.50 %, Temperature 160 °C
  • Tensile Stress
  • 17.0 MPa @Strain 3.00 %, Temperature 160 °C
  • Tensile Stress
  • 21.8 MPa @Strain 0.250 %, Temperature 40.0 °C
  • Tensile Stress
  • 23.9 MPa @Strain 0.250 %, Temperature 23.0 °C
  • Tensile Stress
  • 25.6 MPa @Strain 0.250 %, Temperature 0.000 °C
  • Tensile Stress
  • 25.9 MPa @Strain 0.250 %, Temperature -20.0 °C
  • Tensile Stress
  • 27.3 MPa @Strain 0.250 %, Temperature -40.0 °C
  • Tensile Stress
  • 95.9 MPa @Strain 1.50 %, Temperature 40.0 °C
  • Tensile Stress
  • 111 MPa @Strain 1.50 %, Temperature 23.0 °C
  • Tensile Stress
  • 125 MPa @Strain 1.50 %, Temperature 0.000 °C
  • Tensile Stress
  • 132 MPa @Strain 1.50 %, Temperature -20.0 °C
  • Tensile Stress
  • 138 MPa @Strain 1.50 %, Temperature -40.0 °C
  • Tensile Stress
  • 10.0 MPa @Strain 0.105 %, Time 3600 sec
  • Tensile Stress
  • 10.0 MPa @Strain 0.110 %, Time 36000 sec
  • Tensile Stress
  • 10.0 MPa @Strain 0.120 %, Time 360000 sec
  • Tensile Stress
  • 20.0 MPa @Strain 0.274 %, Time 3.60e+6 sec
  • Tensile Stress
  • 50.0 MPa @Strain 0.778 %, Time 3.60e+6 sec
  • Tensile Stress
  • 50.0 MPa @Strain 0.684 %, Time 360000 sec
  • Tensile Stress
  • 60.0 MPa @Strain 0.715 %, Time 3600 sec
  • Tensile Stress
  • 60.0 MPa @Strain 0.757 %, Time 36000 sec
  • Elongation at Break
  • 2.5 %
  • Tensile Modulus
  • 9.50 GPa
  • Tensile Modulus
  • 1.441 GPa @Temperature 160 °C
  • Tensile Modulus
  • 6.071 GPa @Temperature 80.0 °C
  • Tensile Modulus
  • 8.992 GPa @Temperature 30.0 °C
  • Tensile Modulus
  • 9.489 GPa @Temperature -20.0 °C
  • Tensile Modulus
  • 9.77 GPa @Temperature -50.0 °C
  • Flexural Strength
  • 190 MPa
  • Flexural Modulus
  • 8.50 GPa
  • Secant Modulus
  • 2.85 GPa @Strain 1.50 %, Temperature 100 °C
  • Secant Modulus
  • 4.03 GPa @Strain 1.50 %, Temperature 80.0 °C
  • Secant Modulus
  • 4.40 GPa @Strain 0.250 %, Temperature 100 °C
  • Secant Modulus
  • 6.04 GPa @Strain 0.250 %, Temperature 80.0 °C
  • Secant Modulus
  • 6.39 GPa @Strain 1.50 %, Temperature 40.0 °C
  • Secant Modulus
  • 7.40 GPa @Strain 1.50 %, Temperature 23.0 °C
  • Secant Modulus
  • 8.33 GPa @Strain 1.50 %, Temperature 0.000 °C
  • Secant Modulus
  • 8.72 GPa @Strain 0.250 %, Temperature 40.0 °C
  • Secant Modulus
  • 8.80 GPa @Strain 1.50 %, Temperature -20.0 °C
  • Secant Modulus
  • 9.20 GPa @Strain 1.50 %, Temperature -40.0 °C
  • Secant Modulus
  • 9.56 GPa @Strain 0.250 %, Temperature 23.0 °C
  • Secant Modulus
  • 10.24 GPa @Strain 0.250 %, Temperature 0.000 °C
  • Secant Modulus
  • 10.36 GPa @Strain 0.250 %, Temperature -20.0 °C
  • Secant Modulus
  • 10.92 GPa @Strain 0.250 %, Temperature -40.0 °C
  • Izod Impact, Notched (ISO)
  • 8.00 kJ/m²
  • Izod Impact, Notched (ISO)
  • 8.00 kJ/m² @Temperature -30.0 °C
  • Izod Impact, Unnotched (ISO)
  • 50.0 kJ/m²
  • Izod Impact, Unnotched (ISO)
  • 50.0 kJ/m² @Temperature -30.0 °C
  • Charpy Impact Unnotched
  • 6.00 J/cm²
  • Charpy Impact Unnotched
  • 6.50 J/cm² @Temperature -30.0 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for DuPont Performance Polymers Crastin® LW9030 NC010 PBT+ASA  (Unverified Data**)

Seller from Tianjin – 2021-07-22:

Seller from Tianjin work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1680 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit