DuPont Performance Polymers Crastin® CE2056 NC010 PBT price 1759 per MT

Physical Properties
Density
1.272 g/cc
Linear Mold Shrinkage, Flow
0.026 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse
0.023 cm/cm @Thickness 2.00 mm
Melt Flow
2.0 g/10 min @Load 2.16 kg, Temperature 250 °C
Melt Flow
6.5 g/10 min @Load 2.16 kg, Temperature 250 °C

Mechanical Properties
Tensile Strength at Break
37.0 MPa @Temperature 23.0 °C
Tensile Strength, Yield
50.0 MPa @Temperature 23.0 °C
Elongation at Break
16 % @Temperature 23.0 °C
Elongation at Break
20 % @Temperature 23.0 °C
Elongation at Yield
6.0 % @Temperature 23.0 °C
Tensile Modulus
2.30 GPa @Temperature 23.0 °C
Flexural Strength
65.0 MPa @Temperature 23.0 °C
Flexural Modulus
2.015 GPa @Temperature 23.0 °C
Izod Impact, Notched (ISO)
16.9 kJ/m² @Temperature 23.0 °C
Izod Impact, Unnotched (ISO)
209 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
28.0 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
1.50 J/cm² @Temperature 23.0 °C

Thermal Properties
Melting Point
225 °C
Deflection Temperature at 0.46 MPa (66 psi)
135 °C
Deflection Temperature at 1.8 MPa (264 psi)
50.0 °C

Processing Properties
Melt Temperature
250 °C
Melt Temperature
240 - 260 °C
Mold Temperature
80.0 °C
Mold Temperature
30.0 - 130 °C
Drying Temperature
110 - 130 °C
Dry Time
2.00 - 4.00 hour
Moisture Content
<= 0.040 %

Descriptive Properties
Drying Recommended
Yes
Generic
PBT
Product Category
Unreinforced Resins
Product Category
Unreinforced Resins

Alternative products

DuPont Performance Polymers Crastin® FG6129 NC010 PBT (Unverified Data**) accurate 91%

$ 1581/MT

Density: 1.30 g/cc
Water Absorption: 0.20 % @Temperature 23.0 °C
Water Absorption: 0.40 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.017 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.015 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Crastin® 6134 NC010 PBT (Unverified Data**) accurate 91%

$ 1467/MT

Density: 1.30 g/cc
Melt Flow: 33 g/10 min @Load 2.16 kg, Temperature 250 °C
Melt Flow: 33.5 g/10 min @Load 2.16 kg, Temperature 250 °C
Tensile Strength, Yield: 59.0 MPa @Temperature 23.0 °C
Elongation at Break: 45 % @Temperature 23.0 °C

DuPont Performance Polymers Crastin® S650FR BK851 PBT (Unverified Data**) accurate 82%

$ 2393/MT

Density: 1.46 g/cc
Linear Mold Shrinkage, Flow: 0.018 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.016 cm/cm @Thickness 2.00 mm
Tensile Strength, Yield: 65.0 MPa @Temperature 23.0 °C
Elongation at Break: 7.2 % @Temperature 23.0 °C

DuPont Performance Polymers Crastin® CE2055 NC010 PBT (Unverified Data**) accurate 82%

$ 1816/MT

Density: 1.31 g/cc
Linear Mold Shrinkage, Flow: 0.020 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.018 cm/cm @Thickness 2.00 mm
Melt Flow: 50 g/10 min @Load 2.16 kg, Temperature 250 °C
Tensile Strength, Yield: 60.0 MPa @Temperature 23.0 °C

DuPont Performance Polymers Crastin® S600F40 NC010 PBT (Unverified Data**) accurate 91%

$ 1491/MT

Density: 1.31 g/cc
Water Absorption: 0.20 % @Temperature 23.0 °C
Water Absorption: 0.40 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.0225 cm/cm
Linear Mold Shrinkage, Flow: 0.0195 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Crastin® HR5315HF BK503 PBT (Unverified Data**) accurate 82%

$ 1689/MT

Density: 1.37 g/cc
Filler Content: 15 %
Water Absorption: 0.080 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.011 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Crastin® SK605 BK851 PBT (Unverified Data**) accurate 82%

$ 1559/MT

Density: 1.52 g/cc
Filler Content: 30 %
Tensile Strength at Break: 130 MPa @Temperature 23.0 °C
Elongation at Break: 2.5 % @Temperature 23.0 °C
Tensile Modulus: 9.60 GPa @Temperature 23.0 °C

DuPont Performance Polymers Crastin® S600F10 BK851 PBT (Unverified Data**) accurate 82%

$ 1444/MT

Density: 1.30 g/cc
Tensile Strength, Yield: 57.0 MPa @Temperature 23.0 °C
Elongation at Break: >= 50 % @Temperature 23.0 °C
Elongation at Break: >= 50 % @Temperature 23.0 °C
Elongation at Yield: 6.0 % @Temperature 23.0 °C

DuPont Performance Polymers Crastin® SK603 BK851 PBT (Unverified Data**) accurate 82%

$ 1647/MT

Density: 1.45 g/cc
Filler Content: 20 %
Tensile Strength at Break: 113 MPa @Temperature 23.0 °C
Elongation at Break: 3.0 % @Temperature 23.0 °C
Tensile Modulus: 6.90 GPa @Temperature 23.0 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cruise ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for DuPont Performance Polymers Crastin® CE2056 NC010 PBT

Seller from Montréal – 2021-07-15:

Seller from Montréal work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2052 per MT

Seller from Yokohama – 2021-07-08:

Seller from Yokohama work with company: Solvay, RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $1759 per MT

Seller from Yokohama – 2021-06-07:

Seller from Yokohama work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2360 per MT

Seller from Philadelphia – 2021-05-20:

Seller from Philadelphia work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2591 per MT