DuPont Performance Polymers Crastin® S600F40 NC010 PBT (Unverified Data**) price 1491 per MT

Physical Properties
Density
1.31 g/cc
Water Absorption
0.20 % @Temperature 23.0 °C
Water Absorption
0.40 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow
0.0225 cm/cm
Linear Mold Shrinkage, Flow
0.0195 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse
0.022 cm/cm
Linear Mold Shrinkage, Transverse
0.018 cm/cm @Thickness 2.00 mm
Melt Flow
32.9 g/10 min @Load 2.16 kg, Temperature 250 °C
Melt Index of Compound
32 g/10 min @Load 2.16 kg, Temperature 250 °C

Mechanical Properties
Tensile Strength, Yield
58.0 MPa @Temperature 23.0 °C
Elongation at Break
30 % @Temperature 23.0 °C
Elongation at Break
>= 50 % @Temperature 23.0 °C
Elongation at Yield
6.0 % @Temperature 23.0 °C
Tensile Modulus
2.60 GPa @Temperature 23.0 °C
Flexural Strength
85.0 MPa @Temperature 23.0 °C
Flexural Modulus
2.40 GPa @Temperature 23.0 °C
Izod Impact, Notched (ISO)
4.00 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
NB @Temperature -30.0 °C
Charpy Impact Unnotched
NB @Temperature 23.0 °C
Charpy Impact, Notched
0.400 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
0.400 J/cm² @Temperature 23.0 °C
Tensile Creep Modulus, 1 hour
2600 MPa @Temperature 23.0 °C
Tensile Creep Modulus, 1000 hours
1800 MPa @Temperature 23.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Transverse to Flow
120 µm/m-°C @Temperature 23.0 - 55.0 °C
Melting Point
225 °C
Deflection Temperature at 0.46 MPa (66 psi)
115 °C
Deflection Temperature at 0.46 MPa (66 psi)
180 °C
Deflection Temperature at 1.8 MPa (264 psi)
50.0 °C
Deflection Temperature at 1.8 MPa (264 psi)
60.0 °C
Glass Transition Temp, Tg
55.0 °C
UL RTI, Electrical
130 °C @Thickness 0.750 mm
UL RTI, Electrical
130 °C @Thickness 1.50 mm
UL RTI, Electrical
130 °C @Thickness 6.00 mm
UL RTI, Electrical
130 °C @Thickness 3.00 mm
UL RTI, Mechanical with Impact
115 °C @Thickness 1.50 mm
UL RTI, Mechanical with Impact
115 °C @Thickness 0.750 mm
UL RTI, Mechanical with Impact
115 °C @Thickness 3.00 mm
UL RTI, Mechanical with Impact
115 °C @Thickness 6.00 mm
UL RTI, Mechanical without Impact
120 °C @Thickness 0.750 mm
UL RTI, Mechanical without Impact
120 °C @Thickness 3.00 mm
UL RTI, Mechanical without Impact
120 °C @Thickness 6.00 mm
UL RTI, Mechanical without Impact
120 °C @Thickness 1.50 mm
Flammability, UL94
HB @Thickness 6.00 mm
Flammability, UL94
HB @Thickness 1.50 mm
Flammability, UL94
HB @Thickness 3.00 mm
Flammability, UL94
HB @Thickness 1.50 mm
Flammability, UL94
HB @Thickness 3.00 mm
Flammability, UL94
HB @Thickness 6.00 mm
Oxygen Index
22 %
Glow Wire Test
750 °C @Thickness 3.00 mm

Electrical Properties
Volume Resistivity
>= 1.00e+15 ohm-cm @Temperature 23.0 °C
Surface Resistance
>= 1.00e+12 ohm @Temperature 23.0 °C
Dielectric Constant
3.2 @Frequency 1.00e+6 Hz, Temperature 23.0 °C
Dielectric Constant
3.8 @Frequency 100 Hz, Temperature 23.0 °C
Dielectric Constant
3.8 @Frequency 50.0 Hz, Temperature 23.0 °C
Dielectric Strength
26.0 kV/mm @Thickness 2.00 mm
Dielectric Strength
26.0 kV/mm @Thickness 1.00 mm, Temperature 23.0 °C
Dissipation Factor
0.0020 @Frequency 100 Hz, Temperature 23.0 °C
Dissipation Factor
0.0020 @Frequency 50.0 Hz, Temperature 23.0 °C
Dissipation Factor
0.020 @Frequency 1.00e+6 Hz, Temperature 23.0 °C
Comparative Tracking Index
250 V @Temperature 23.0 °C
Comparative Tracking Index
600 V @Temperature 23.0 °C

Processing Properties
Melt Temperature
250 °C
Melt Temperature
240 - 260 °C
Mold Temperature
80.0 °C
Mold Temperature
30.0 - 130 °C
Drying Temperature
110 - 130 °C
Dry Time
2.00 - 4.00 hour
Moisture Content
<= 0.040 %

Descriptive Properties
Additive
Lubricant
Appearance
Natural Color

Alternative products

DuPont Performance Polymers Crastin® FG6129 NC010 PBT (Unverified Data**) accurate 93%

$ 1581/MT

Density: 1.30 g/cc
Water Absorption: 0.20 % @Temperature 23.0 °C
Water Absorption: 0.40 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.017 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.015 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Crastin® 6134 NC010 PBT (Unverified Data**) accurate 93%

$ 1467/MT

Density: 1.30 g/cc
Melt Flow: 33 g/10 min @Load 2.16 kg, Temperature 250 °C
Melt Flow: 33.5 g/10 min @Load 2.16 kg, Temperature 250 °C
Tensile Strength, Yield: 59.0 MPa @Temperature 23.0 °C
Elongation at Break: 45 % @Temperature 23.0 °C

DuPont Performance Polymers Crastin® S650FR BK851 PBT (Unverified Data**) accurate 64%

$ 2393/MT

Density: 1.46 g/cc
Linear Mold Shrinkage, Flow: 0.018 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.016 cm/cm @Thickness 2.00 mm
Tensile Strength, Yield: 65.0 MPa @Temperature 23.0 °C
Elongation at Break: 7.2 % @Temperature 23.0 °C

DuPont Performance Polymers Crastin® S600F40 BK851 PBT (Unverified Data**) accurate 75%

$ 1695/MT

Density: 1.31 g/cc
Tensile Strength, Yield: 58.0 MPa @Temperature 23.0 °C
Elongation at Break: 20 % @Temperature 23.0 °C
Elongation at Break: 30 % @Temperature 23.0 °C
Elongation at Yield: 6.0 % @Temperature 23.0 °C

DuPont Performance Polymers Crastin® CE2056 NC010 PBT accurate 70%

$ 1759/MT

Density: 1.272 g/cc
Linear Mold Shrinkage, Flow: 0.026 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.023 cm/cm @Thickness 2.00 mm
Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 250 °C
Melt Flow: 6.5 g/10 min @Load 2.16 kg, Temperature 250 °C

DuPont Performance Polymers Crastin® S600LF NC010 PBT accurate 70%

$ 1448/MT

Density: 1.32 g/cc
Water Absorption: 0.20 % @Temperature 23.0 °C
Water Absorption: 0.40 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.022 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.022 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Crastin® S620F20 BK851 PBT (Unverified Data**) accurate 75%

$ 1519/MT

Density: 1.31 g/cc
Tensile Strength, Yield: 59.0 MPa @Temperature 23.0 °C
Elongation at Break: 30 % @Temperature 23.0 °C
Elongation at Break: >= 50 % @Temperature 23.0 °C
Elongation at Yield: 8.0 % @Temperature 23.0 °C

DuPont Performance Polymers Crastin® S600F10 BK851 PBT (Unverified Data**) accurate 75%

$ 1444/MT

Density: 1.30 g/cc
Tensile Strength, Yield: 57.0 MPa @Temperature 23.0 °C
Elongation at Break: >= 50 % @Temperature 23.0 °C
Elongation at Break: >= 50 % @Temperature 23.0 °C
Elongation at Yield: 6.0 % @Temperature 23.0 °C

DuPont Performance Polymers Crastin® S600F20 BK851 PBT (Unverified Data**) accurate 75%

$ 2451/MT

Density: 1.31 g/cc
Tensile Strength, Yield: 57.0 MPa @Temperature 23.0 °C
Elongation at Break: 40 % @Temperature 23.0 °C
Elongation at Break: >= 50 % @Temperature 23.0 °C
Elongation at Yield: 6.0 % @Temperature 23.0 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships on sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for DuPont Performance Polymers Crastin® S600F40 NC010 PBT (Unverified Data**)

Seller from Bogotá – 2021-08-14:

Seller from Bogotá work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $1491 per MT