DuPont Performance Polymers Rynite® 415HP NC010 Polyethylene Terephthalate (PET)  (Unverified Data**)

Seller in Montréal price: $1724 per MT

DuPont Performance Polymers Rynite® 415HP NC010 Polyethylene Terephthalate (PET)  (Unverified Data**) in Polymer, Thermoplastic, Polyester, TP, Polyethylene Terephthalate (PET), 20% Glass Reinforced

  • Physical Properties
  • Specific Gravity
  • 1.39 g/cc
  • Density
  • 1.39 g/cc
  • Water Absorption
  • 2.5 % @Thickness 2.00 mm
  • Moisture Absorption
  • 0.250 % @Thickness 2.00 mm
  • Viscosity
  • 57000 cP @Shear Rate 5000 1/s, Temperature 315 °C
  • Viscosity
  • 71000 cP @Shear Rate 5000 1/s, Temperature 295 °C
  • Viscosity
  • 92000 cP @Shear Rate 5000 1/s, Temperature 275 °C
  • Viscosity
  • 200000 cP @Shear Rate 500 1/s, Temperature 315 °C
  • Viscosity
  • 248000 cP @Shear Rate 500 1/s, Temperature 295 °C
  • Viscosity
  • 312000 cP @Shear Rate 500 1/s, Temperature 275 °C
  • Linear Mold Shrinkage, Flow
  • 0.0030 cm/cm
  • Linear Mold Shrinkage, Flow
  • 0.0050 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.0080 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.012 cm/cm
  • Melt Flow
  • 4.0 g/10 min @Load 2.16 kg, Temperature 280 °C
  • Mechanical Properties
  • Hardness, Rockwell M
  • 58
  • Hardness, Rockwell R
  • 111
  • Tensile Strength at Break
  • 79.0 MPa
  • Tensile Stress
  • 13.4 MPa @Strain 1.00 %, Temperature 150 °C
  • Tensile Stress
  • 16.4 MPa @Strain 0.450 %, Temperature 40.0 °C
  • Tensile Stress
  • 18.2 MPa @Strain 0.350 %, Temperature 23.0 °C
  • Tensile Stress
  • 19.7 MPa @Strain 0.300 %, Temperature 0.000 °C
  • Tensile Stress
  • 21.1 MPa @Strain 1.00 %, Temperature 90.0 °C
  • Tensile Stress
  • 27.9 MPa @Strain 0.350 %, Temperature -20.0 °C
  • Tensile Stress
  • 34.1 MPa @Strain 4.00 %, Temperature 150 °C
  • Tensile Stress
  • 40.0 MPa @Strain 7.00 %, Temperature 150 °C
  • Tensile Stress
  • 41.9 MPa @Strain 10.0 %, Temperature 150 °C
  • Tensile Stress
  • 44.7 MPa @Strain 4.00 %, Temperature 90.0 °C
  • Tensile Stress
  • 49.9 MPa @Strain 7.00 %, Temperature 90.0 °C
  • Tensile Stress
  • 50.2 MPa @Strain 1.80 %, Temperature 40.0 °C
  • Tensile Stress
  • 51.9 MPa @Strain 10.0 %, Temperature 90.0 °C
  • Tensile Stress
  • 57.4 MPa @Strain 1.40 %, Temperature 23.0 °C
  • Tensile Stress
  • 63.8 MPa @Strain 1.20 %, Temperature 0.000 °C
  • Tensile Stress
  • 67.5 MPa @Strain 3.15 %, Temperature 40.0 °C
  • Tensile Stress
  • 71.3 MPa @Strain 4.50 %, Temperature 40.0 °C
  • Tensile Stress
  • 77.6 MPa @Strain 2.45 %, Temperature 23.0 °C
  • Tensile Stress
  • 84.5 MPa @Strain 3.50 %, Temperature 23.0 °C
  • Tensile Stress
  • 86.3 MPa @Strain 1.40 %, Temperature -20.0 °C
  • Tensile Stress
  • 91.6 MPa @Strain 2.10 %, Temperature 0.000 °C
  • Tensile Stress
  • 109 MPa @Strain 3.00 %, Temperature 0.000 °C
  • Tensile Stress
  • 116 MPa @Strain 2.45 %, Temperature -20.0 °C
  • Tensile Stress
  • 128 MPa @Strain 3.33 %, Temperature -20.0 °C
  • Elongation at Break
  • 5.0 %
  • Tensile Modulus
  • 4.70 GPa
  • Tensile Modulus
  • 0.161 GPa @Temperature 230 °C
  • Tensile Modulus
  • 0.296 GPa @Temperature 170 °C
  • Tensile Modulus
  • 0.404 GPa @Temperature 90.0 °C
  • Tensile Modulus
  • 0.779 GPa @Temperature 40.0 °C
  • Tensile Modulus
  • 1.314 GPa @Temperature -20.0 °C
  • Tensile Modulus
  • 1.657 GPa @Temperature -50.0 °C
  • Flexural Modulus
  • 3.55 GPa
  • Shear Modulus
  • 0.303 GPa @Temperature 160 °C
  • Shear Modulus
  • 0.333 GPa @Temperature 120 °C
  • Shear Modulus
  • 0.486 GPa @Temperature 70.0 °C
  • Shear Modulus
  • 0.992 GPa @Temperature 20.0 °C
  • Shear Modulus
  • 1.314 GPa @Temperature -20.0 °C
  • Shear Modulus
  • 1.657 GPa @Temperature -50.0 °C
  • Shear Strength
  • 0.100 MPa @Shear Rate 500 1/s, Temperature 315 °C
  • Shear Strength
  • 0.124 MPa @Shear Rate 500 1/s, Temperature 295 °C
  • Shear Strength
  • 0.156 MPa @Shear Rate 500 1/s, Temperature 275 °C
  • Secant Modulus
  • 1.94 GPa @Strain 3.60 %, Temperature 40.0 °C
  • Secant Modulus
  • 2.79 GPa @Strain 1.80 %, Temperature 40.0 °C
  • Secant Modulus
  • 2.89 GPa @Strain 2.80 %, Temperature 23.0 °C
  • Secant Modulus
  • 3.64 GPa @Strain 0.450 %, Temperature 40.0 °C
  • Secant Modulus
  • 4.09 GPa @Strain 2.40 %, Temperature 0.000 °C
  • Secant Modulus
  • 4.10 GPa @Strain 1.40 %, Temperature 23.0 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, container ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for DuPont Performance Polymers Rynite® 415HP NC010 Polyethylene Terephthalate (PET)  (Unverified Data**)

Seller from Montréal – 2021-06-11:

Seller from Montréal work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1724 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell DuPont Performance Polymers Rynite® 415HP NC010 Polyethylene Terephthalate (PET)  (Unverified Data**)?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Property maintenance in Singapore open-nearme.com