DuPont Performance Polymers Rynite® 530 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**)

Seller in Santiago price: $1580 per MT
Seller in Bangkok price: $1600 per MT

DuPont Performance Polymers Rynite® 530 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**) in Polymer, Thermoplastic, Polyester, TP, Polyethylene Terephthalate (PET), 30% Glass Reinforced

  • Physical Properties
  • Specific Gravity
  • 1.56 g/cc
  • Density
  • 1.56 g/cc
  • Water Absorption
  • 0.70 % @Thickness 2.00 mm
  • Moisture Absorption
  • 0.200 % @Thickness 2.00 mm
  • Viscosity
  • 44000 cP @Shear Rate 5000 1/s, Temperature 300 °C
  • Viscosity
  • 60000 cP @Shear Rate 5000 1/s, Temperature 290 °C
  • Viscosity
  • 82000 cP @Shear Rate 5000 1/s, Temperature 280 °C
  • Viscosity
  • 130000 cP @Shear Rate 500 1/s, Temperature 300 °C
  • Viscosity
  • 174000 cP @Shear Rate 500 1/s, Temperature 290 °C
  • Viscosity
  • 232000 cP @Shear Rate 500 1/s, Temperature 280 °C
  • Linear Mold Shrinkage, Flow
  • 0.0020 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.0080 cm/cm
  • Melt Flow
  • 5.0 g/10 min @Load 2.16 kg, Temperature 280 °C
  • Mechanical Properties
  • Hardness, Rockwell M
  • 100
  • Hardness, Rockwell R
  • 120
  • Tensile Strength at Break
  • 158 MPa
  • Tensile Stress
  • 16.7 MPa @Strain 0.460 %, Temperature 150 °C
  • Tensile Stress
  • 23.95 MPa @Strain 0.490 %, Temperature 90.0 °C
  • Tensile Stress
  • 25.5 MPa @Strain 0.260 %, Temperature 40.0 °C
  • Tensile Stress
  • 27.0 MPa @Strain 0.250 %, Temperature 23.0 °C
  • Tensile Stress
  • 27.4 MPa @Strain 0.240 %, Temperature 0.000 °C
  • Tensile Stress
  • 28.9 MPa @Strain 0.230 %, Temperature -40.0 °C
  • Tensile Stress
  • 45.0 MPa @Strain 1.84 %, Temperature 150 °C
  • Tensile Stress
  • 57.0 MPa @Strain 3.21 %, Temperature 150 °C
  • Tensile Stress
  • 62.0 MPa @Strain 4.59 %, Temperature 150 °C
  • Tensile Stress
  • 62.15 MPa @Strain 1.90 %, Temperature 90.0 °C
  • Tensile Stress
  • 78.2 MPa @Strain 3.30 %, Temperature 90.0 °C
  • Tensile Stress
  • 82.65 MPa @Strain 4.71 %, Temperature 90.0 °C
  • Tensile Stress
  • 82.95 MPa @Strain 1.04 %, Temperature 40.0 °C
  • Tensile Stress
  • 90.0 MPa @Strain 0.970 %, Temperature 23.0 °C
  • Tensile Stress
  • 97.0 MPa @Strain 0.950 %, Temperature 0.000 °C
  • Tensile Stress
  • 105 MPa @Strain 0.940 %, Temperature -40.0 °C
  • Tensile Stress
  • 117.1 MPa @Strain 1.82 %, Temperature 40.0 °C
  • Tensile Stress
  • 131.5 MPa @Strain 2.60 %, Temperature 40.0 °C
  • Tensile Stress
  • 134 MPa @Strain 1.69 %, Temperature 23.0 °C
  • Tensile Stress
  • 151 MPa @Strain 1.67 %, Temperature 0.000 °C
  • Tensile Stress
  • 155 MPa @Strain 2.42 %, Temperature 23.0 °C
  • Tensile Stress
  • 164 MPa @Strain 1.60 %, Temperature -40.0 °C
  • Tensile Stress
  • 185 MPa @Strain 2.38 %, Temperature 0.000 °C
  • Tensile Stress
  • 211 MPa @Strain 2.29 %, Temperature -40.0 °C
  • Tensile Stress
  • 20.0 MPa @Strain 0.222 %, Time 3.60e+6 sec
  • Tensile Stress
  • 20.0 MPa @Strain 0.190 %, Time 36000 sec
  • Tensile Stress
  • 20.0 MPa @Strain 0.201 %, Time 360000 sec
  • Tensile Stress
  • 20.0 MPa @Strain 0.247 %, Time 1.80e+7 sec
  • Tensile Stress
  • 20.0 MPa @Strain 0.260 %, Time 3.60e+7 sec
  • Tensile Stress
  • 20.0 MPa @Strain 0.183 %, Time 3600 sec
  • Tensile Stress
  • 60.0 MPa @Strain 0.574 %, Time 3600 sec
  • Tensile Stress
  • 60.0 MPa @Strain 0.831 %, Time 3.60e+7 sec
  • Tensile Stress
  • 60.0 MPa @Strain 0.785 %, Time 1.80e+7 sec
  • Tensile Stress
  • 60.0 MPa @Strain 0.638 %, Time 360000 sec
  • Tensile Stress
  • 60.0 MPa @Strain 0.599 %, Time 36000 sec
  • Tensile Stress
  • 60.0 MPa @Strain 0.709 %, Time 3.60e+6 sec
  • Elongation at Break
  • 2.5 %
  • Tensile Modulus
  • 11.0 GPa
  • Flexural Strength
  • 230 MPa
  • Flexural Modulus
  • 8.95 GPa
  • Shear Modulus
  • 0.548 GPa @Temperature 160 °C
  • Shear Modulus
  • 0.637 GPa @Temperature 120 °C
  • Shear Modulus
  • 1.33 GPa @Temperature 70.0 °C
  • Shear Modulus
  • 2.101 GPa @Temperature 20.0 °C
  • Shear Modulus
  • 2.288 GPa @Temperature -20.0 °C
  • Shear Modulus
  • 2.487 GPa @Temperature -50.0 °C
  • Shear Strength
  • 0.0650 MPa @Shear Rate 500 1/s, Temperature 300 °C
  • Shear Strength
  • 0.0870 MPa @Shear Rate 500 1/s, Temperature 290 °C
  • Shear Strength
  • 0.116 MPa @Shear Rate 500 1/s, Temperature 280 °C
  • Secant Modulus
  • 5.97 GPa @Strain 2.08 %, Temperature 40.0 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, crude oil tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for DuPont Performance Polymers Rynite® 530 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**)

Seller from Santiago – 2021-06-16:

Seller from Santiago work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1580 per MT

Seller from Bangkok – 2021-06-18:

Seller from Bangkok work with company: Solvay, Techmer ES, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1600 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell DuPont Performance Polymers Rynite® 530 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**)?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Equestrian store in Singapore open-nearme.com