DuPont Performance Polymers Hytrel® 4053FG NC010 Polyester Elastomer TPC-ET (Unverified Data**) price 1593 per MT

Physical Properties
Density
1.02 g/cc
Density
1.16 g/cc
Water Absorption
0.70 % @Thickness 2.00 mm
Moisture Absorption
0.200 % @Thickness 2.00 mm
Linear Mold Shrinkage, Flow
0.0020 cm/cm
Linear Mold Shrinkage, Transverse
0.0040 cm/cm
Melt Flow
5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Flow
5.3 g/10 min @Load 2.16 kg, Temperature 190 °C

Mechanical Properties
Hardness, Shore D
38
Tensile Strength at Break
26.0 MPa
Tensile Stress
2.40 MPa @Strain 5.00 %
Tensile Stress
4.10 MPa @Strain 10.0 %
Tensile Stress
7.30 MPa @Strain 50.0 %
Elongation at Break
>= 300 %
Tensile Modulus
0.0560 GPa
Charpy Impact Unnotched
NB
Charpy Impact Unnotched
NB @Temperature -30.0 °C
Charpy Impact, Notched
NB
Charpy Impact, Notched
NB @Temperature -30.0 °C
Charpy Impact, Notched
NB @Temperature -40.0 °C
Tensile Impact Strength
230 kJ/m²
Tensile Creep Modulus, 1 hour
50.0 MPa @Time 3600 sec
Tensile Creep Modulus, 1000 hours
40.0 MPa @Time 3.60e+6 sec
Tear Strength
110 kN/m

Thermal Properties
CTE, linear, Parallel to Flow
220 µm/m-°C
CTE, linear, Transverse to Flow
220 µm/m-°C
Melting Point
150 °C
Glass Transition Temp, Tg
-50.0 °C
Flammability, UL94
HB @Thickness 1.50 mm
Oxygen Index
20 %

Electrical Properties
Volume Resistivity
7.00e+12 ohm-cm
Surface Resistance
2.00e+14 ohm
Dielectric Constant
4.7 @Frequency 1.00e+6 Hz
Dielectric Constant
5.2 @Frequency 100 Hz
Dielectric Strength
18.0 kV/mm
Dissipation Factor
0.011 @Frequency 100 Hz
Dissipation Factor
0.0525 @Frequency 1.00e+6 Hz
Comparative Tracking Index
600 V

Descriptive Properties
Delivery Form
Pellets
Eff. thermal diffusivity
5.44E-08 m²/s
Part Marking Code
>TPC-ET<
Processing
Calandering
Processing
Casting
Processing
Coatable
Processing
Film Extrusion
Processing
Injection Moulding
Processing
Other Extrusion
Processing
Profile Extrusion
Processing
Sheet Extrusion
Processing
Thermoforming
Regional Availability
Asia Pacific
Regional Availability
Europe
Regional Availability
Global
Regional Availability
Near East/Africa
Regional Availability
North America
Regional Availability
South and Central America
Resin Identification
TPC-ET
Special Characteristics
Light stabilised or stable to light
UL recognition
UL

Alternative products

SABIC Innovative Plastics SABIC PPCOMPOUND 8620A PP accurate 49%

$ 1688/MT

Specific Gravity: 1.03 g/cc
Density: 1.03 g/cc
Linear Mold Shrinkage, Flow: 0.0040 cm/cm
Linear Mold Shrinkage, Flow: 0.0050 cm/cm
Linear Mold Shrinkage, Flow: 0.0060 cm/cm

DuPont Performance Polymers Hytrel® RS 40F3 NC010 Polyester Elastomer TPC-ET (Unverified Data**) accurate 55%

$ 1670/MT

Density: 1.11 g/cc
Linear Mold Shrinkage, Flow: 0.0080 cm/cm
Linear Mold Shrinkage, Flow: 0.0090 cm/cm
Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm

DuPont Performance Polymers Crastin® LW9030 NC010 PBT+ASA (Unverified Data**) accurate 49%

$ 1680/MT

Density: 1.28 g/cc
Density: 1.44 g/cc
Water Absorption: 0.72 % @Thickness 2.00 mm
Moisture Absorption: 0.240 % @Thickness 2.00 mm
Viscosity: 67000 cP @Shear Rate 5000 1/s, Temperature 260 °C

Thermal Ceramics Cerafelt accurate 60%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

DuPont Performance Polymers Zytel® FE5382 BK276 Nylon 612 (Unverified Data**) accurate 55%

$ 1446/MT

Density: 1.12 g/cc
Density: 1.32 g/cc
Water Absorption: 1.8 % @Thickness 2.00 mm
Moisture Absorption: 0.700 % @Thickness 2.00 mm
Viscosity: 29770 cP @Shear Rate 5000 1/s, Temperature 300 °C

Celanese FORTRON 214 PPS (Unverified Data**) accurate 60%

$ 2311/MT

Specific Gravity: 1.35 g/cc
Specific Gravity: 1.36 g/cc
Density: 1.35 g/cc
Density: 1.35 g/cc
Density of Compound: 1.15 g/cc

DuPont Performance Polymers Hytrel® HTR8223 BK320 Polyester Elastomer TPC-ET (Unverified Data**) accurate 55%

$ 2207/MT

Density: 1.00 g/cc
Density: 1.13 g/cc
Water Absorption: 0.80 % @Thickness 2.00 mm
Moisture Absorption: 0.200 % @Thickness 2.00 mm
Water Absorption at Saturation: 0.60 %

DuPont Performance Polymers Hytrel® 4069 Polyester Elastomer TPC-ET (Unverified Data**) accurate 71%

$ 1737/MT

Density: 1.10 g/cc
Density: 1.11 g/cc
Water Absorption: 0.70 % @Thickness 2.00 mm
Moisture Absorption: 0.300 % @Thickness 2.00 mm
Water Absorption at Saturation: 0.70 %

Celanese FORTRON 214 PPS, Unfilled accurate 55%

$ 2385/MT

Specific Gravity: 1.35 g/cc
Density: 0.000782 g/cc
Density: 1.35 g/cc
Density of Compound: 1.15 g/cc
Water Absorption: 0.0300 % @Temperature 22.8 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale nl. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for DuPont Performance Polymers Hytrel® 4053FG NC010 Polyester Elastomer TPC-ET (Unverified Data**)

Seller from Monterrey – 2021-04-08:

Seller from Monterrey work with company: 3M, Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $1593 per MT