DuPont Performance Polymers Crastin® SK605 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)

Seller in Hāora price: $2181 per MT

DuPont Performance Polymers Crastin® SK605 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**) in Polymer, Thermoplastic, 30% Glass Fiber Filled, Polyester, TP, Polybutylene Terephthalate (PBT)

  • Physical Properties
  • Density
  • 1.36 g/cc
  • Density
  • 1.53 g/cc
  • Water Absorption
  • 0.35 % @Thickness 2.00 mm
  • Moisture Absorption
  • 0.150 % @Thickness 2.00 mm
  • Viscosity
  • 91150 cP @Shear Rate 5000 1/s, Temperature 260 °C
  • Viscosity
  • 107900 cP @Shear Rate 5000 1/s, Temperature 250 °C
  • Viscosity
  • 129480 cP @Shear Rate 5000 1/s, Temperature 240 °C
  • Viscosity
  • 274700 cP @Shear Rate 500 1/s, Temperature 260 °C
  • Viscosity
  • 340700 cP @Shear Rate 500 1/s, Temperature 250 °C
  • Viscosity
  • 424600 cP @Shear Rate 500 1/s, Temperature 240 °C
  • Viscosity Test
  • 100 cm³/g
  • Linear Mold Shrinkage, Flow
  • 0.0030 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.011 cm/cm
  • Melt Flow
  • 10 g/10 min
  • Melt Flow
  • 7.0 g/10 min @Load 2.16 kg, Temperature 250 °C
  • Mechanical Properties
  • Tensile Strength at Break
  • 140 MPa
  • Tensile Stress
  • 8.08 MPa @Strain 0.250 %, Temperature 160 °C
  • Tensile Stress
  • 22.5 MPa @Strain 0.250 %, Temperature 40.0 °C
  • Tensile Stress
  • 24.9 MPa @Strain 0.250 %, Temperature 23.0 °C
  • Tensile Stress
  • 28.9 MPa @Strain 0.250 %, Temperature 0.000 °C
  • Tensile Stress
  • 30.0 MPa @Strain 0.250 %, Temperature -20.0 °C
  • Tensile Stress
  • 30.7 MPa @Strain 0.250 %, Temperature -40.0 °C
  • Tensile Stress
  • 30.7 MPa @Strain 1.50 %, Temperature 160 °C
  • Tensile Stress
  • 41.3 MPa @Strain 3.00 %, Temperature 160 °C
  • Tensile Stress
  • 91.7 MPa @Strain 1.50 %, Temperature 40.0 °C
  • Tensile Stress
  • 114 MPa @Strain 3.00 %, Temperature 40.0 °C
  • Tensile Stress
  • 122 MPa @Strain 1.50 %, Temperature 23.0 °C
  • Tensile Stress
  • 138 MPa @Strain 1.50 %, Temperature 0.000 °C
  • Tensile Stress
  • 149 MPa @Strain 1.50 %, Temperature -20.0 °C
  • Tensile Stress
  • 159 MPa @Strain 1.50 %, Temperature -40.0 °C
  • Tensile Stress
  • 10.0 MPa @Strain 0.175 %, Time 3.60e+7 sec
  • Tensile Stress
  • 10.0 MPa @Strain 0.126 %, Time 36000 sec
  • Tensile Stress
  • 10.0 MPa @Strain 0.115 %, Time 3600 sec
  • Tensile Stress
  • 10.0 MPa @Strain 0.142 %, Time 360000 sec
  • Tensile Stress
  • 10.0 MPa @Strain 0.159 %, Time 3.60e+6 sec
  • Tensile Stress
  • 40.0 MPa @Strain 0.603 %, Time 360000 sec
  • Tensile Stress
  • 50.0 MPa @Strain 0.889 %, Time 3.60e+6 sec
  • Tensile Stress
  • 50.0 MPa @Strain 0.682 %, Time 36000 sec
  • Tensile Stress
  • 50.0 MPa @Strain 1.02 %, Time 3.60e+7 sec
  • Tensile Stress
  • 60.0 MPa @Strain 0.768 %, Time 3600 sec
  • Tensile Stress
  • 80.0 MPa @Strain 1.53 %, Time 360000 sec
  • Elongation at Break
  • 2.7 %
  • Tensile Modulus
  • 10.0 GPa
  • Tensile Modulus
  • 3.59 GPa @Temperature 150 °C
  • Tensile Modulus
  • 4.20 GPa @Temperature 90.0 °C
  • Tensile Modulus
  • 4.78 GPa @Temperature 90.0 °C
  • Tensile Modulus
  • 7.65 GPa @Temperature 40.0 °C
  • Tensile Modulus
  • 10.5 GPa @Temperature -40.0 °C
  • Tensile Modulus
  • 10.66 GPa @Temperature -40.0 °C
  • Flexural Strength
  • 200 MPa
  • Flexural Modulus
  • 9.00 GPa
  • Shear Modulus
  • 0.550 GPa @Temperature 160 °C
  • Shear Modulus
  • 0.696 GPa @Temperature 120 °C
  • Shear Modulus
  • 1.00 GPa @Temperature 70.0 °C
  • Shear Modulus
  • 1.94 GPa @Temperature 20.0 °C
  • Shear Modulus
  • 2.09 GPa @Temperature -20.0 °C
  • Shear Modulus
  • 2.21 GPa @Temperature -50.0 °C
  • Secant Modulus
  • 1.82 GPa @Strain 3.50 %, Temperature 100 °C
  • Secant Modulus
  • 1.99 GPa @Strain 3.50 %, Temperature 80.0 °C
  • Secant Modulus
  • 2.95 GPa @Strain 1.50 %, Temperature 100 °C
  • Secant Modulus
  • 3.29 GPa @Strain 3.50 %, Temperature 40.0 °C
  • Secant Modulus
  • 3.30 GPa @Strain 1.50 %, Temperature 80.0 °C
  • Secant Modulus
  • 4.44 GPa @Strain 0.250 %, Temperature 100 °C
  • Secant Modulus
  • 4.84 GPa @Strain 0.250 %, Temperature 80.0 °C
  • Secant Modulus
  • 6.11 GPa @Strain 1.50 %, Temperature 40.0 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, used cruise ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for DuPont Performance Polymers Crastin® SK605 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)

Seller from Hāora – 2021-06-16:

Seller from Hāora work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2181 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell DuPont Performance Polymers Crastin® SK605 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Video conferencing equipment supplier in Singapore open-nearme.com