DuPont Performance Polymers Rynite® 515CS BK575M PET price 2261 per MT

Physical Properties
Density
1.43 g/cc
Filler Content
15 %
Linear Mold Shrinkage, Flow
0.0020 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse
0.0090 cm/cm @Thickness 2.00 mm

Mechanical Properties
Tensile Strength at Break
97.0 MPa @Temperature 23.0 °C
Elongation at Break
2.4 % @Temperature 23.0 °C
Tensile Modulus
6.20 GPa @Temperature 23.0 °C
Flexural Modulus
5.60 GPa @Temperature 23.0 °C
Izod Impact, Notched (ISO)
5.00 kJ/m² @Temperature 23.0 °C
Izod Impact, Notched (ISO)
5.00 kJ/m² @Temperature -40.0 °C
Charpy Impact Unnotched
2.00 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.500 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.500 J/cm² @Temperature -40.0 °C

Thermal Properties
Melting Point
250 °C
Deflection Temperature at 0.46 MPa (66 psi)
245 °C
Deflection Temperature at 1.8 MPa (264 psi)
200 °C
UL RTI, Electrical
75.0 °C @Thickness 0.750 mm
UL RTI, Mechanical with Impact
75.0 °C @Thickness 0.750 mm
UL RTI, Mechanical without Impact
75.0 °C @Thickness 0.750 mm
Flammability, UL94
HB @Thickness 0.750 mm
Flammability, UL94
HB @Thickness 0.750 mm
Oxygen Index
20 %

Processing Properties
Melt Temperature
270 - 290 °C
Melt Temperature
280 °C
Mold Temperature
130 - 140 °C
Mold Temperature
135 °C
Drying Temperature
120 °C
Dry Time
4.00 hour
Moisture Content
<= 0.020 %

Descriptive Properties
Appearance
Black Color
Drying Recommended
Yes
Filler
Glass Reinforced
Generic
PET
Material Status
Current
Part Marking Code
>PET-GF15<
Polymer Family
Polyester
Polymer Type
PET
Product Category
Color Stable Resins
Product Category
Glass Reinforced Resins
Resin Identification
PET-GF15
RoHS Compliance
Contact Manufacturer

Alternative products

DuPont Performance Polymers Rynite® 408 BK515 PET accurate 53%

$ 1711/MT

Density: 1.49 g/cc
Filler Content: 30 %
Tensile Strength at Break: 55.0 MPa @Temperature 150 °C
Tensile Strength at Break: 71.0 MPa @Temperature 90.0 °C
Tensile Strength at Break: 127 MPa @Temperature 23.0 °C

Solvay Specialty Polymers Amodel® A-1240 L Polyphthalamide (PPA) (discontinued **) accurate 37%

$ 1715/MT

Specific Gravity: 1.54 g/cc
Density: 1.54 g/cc
Filler Content: 40 %
Water Absorption: 0.10 % @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.010 cm/cm

DuPont Performance Polymers Sorona® FG3015G NC010 Polytrimethylene Terephthalate (PTT) (Unverified Data** accurate 45%

$ 2127/MT

Density: 1.44 g/cc
Filler Content: 15 %
Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 2.00 mm
Tensile Strength at Break: 120 MPa @Temperature 23.0 °C

BASF Ultramid® B3ZG8 BK 20560 40% Glass Filled PA6-1 (Conditioned) accurate 37%

$ 1625/MT

Density: 1.40 g/cc
Water Absorption: 4.7 - 5.3 %
Moisture Absorption at Equilibrium: 1.4 - 1.8 %
Viscosity Measurement: 160
Linear Mold Shrinkage: 0.0035 cm/cm

Plastcom SLOVASTER® B GF 15 Polybutylene Terephthalate, 15% Glass Fiber accurate 37%

$ 1510/MT

Density: 1.41 g/cc
Linear Mold Shrinkage: 0.0089 cm/cm
Linear Mold Shrinkage, Transverse: 0.0135 cm/cm
Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
Tensile Strength at Break: 105 MPa

DuPont Performance Polymers Rynite® 415HP BK503 PET (Unverified Data**) accurate 61%

$ 1674/MT

Density: 1.39 g/cc
Filler Content: 15 %
Tensile Strength at Break: 80.0 MPa @Temperature 23.0 °C
Elongation at Break: 5.0 % @Temperature 23.0 °C
Tensile Modulus: 4.50 GPa @Temperature 23.0 °C

DuPont Performance Polymers Rynite® GW520CS NC010 PET (Unverified Data**) accurate 45%

$ 1518/MT

Density: 1.61 g/cc
Filler Content: 20 %
Melt Index of Compound: 17 g/10 min @Load 2.16 kg, Temperature 280 °C
Tensile Strength at Break: 145 MPa @Temperature 23.0 °C
Elongation at Break: 2.5 % @Temperature 23.0 °C

DuPont Performance Polymers Rynite® FR530L BK507 PET (Unverified Data**) accurate 45%

$ 1597/MT

Density: 1.68 g/cc
Filler Content: 30 %
Tensile Strength at Break: 133 MPa @Temperature 23.0 °C
Elongation at Break: 1.9 % @Temperature 23.0 °C
Tensile Modulus: 11.3 GPa @Temperature 23.0 °C

DuPont Performance Polymers Rynite® FR515 BK507 PET (Unverified Data**) accurate 68%

$ 1720/MT

Density: 1.55 g/cc
Filler Content: 15 %
Tensile Strength at Break: 100 MPa @Temperature 23.0 °C
Tensile Strength at Break: 125 MPa @Temperature -40.0 °C
Elongation at Break: 2.0 % @Temperature -40.0 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, sales ship. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for DuPont Performance Polymers Rynite® 515CS BK575M PET

Seller from Luanda – 2021-05-11:

Seller from Luanda work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2261 per MT