Physical Properties
Density
1.41 g/cc
Linear Mold Shrinkage
0.015 cm/cm @Diameter 4.00 mm
Linear Mold Shrinkage
0.017 cm/cm @Diameter 4.00 mm
Melt Flow
2.3 g/10 min @Load 2.16 kg, Temperature 190 °C

Mechanical Properties
Tensile Strength at Break
50.0 MPa @Temperature 23.0 °C
Elongation at Break
16 % @Temperature 23.0 °C
Tensile Modulus
2.30 GPa @Temperature 23.0 °C
Flexural Modulus
2.10 GPa @Temperature 23.0 °C
Izod Impact, Notched (ISO)
7.70 kJ/m² @Temperature 23.0 °C
Charpy Impact, Notched
0.800 J/cm² @Temperature 23.0 °C

Thermal Properties
Melting Point
178 °C
Deflection Temperature at 0.46 MPa (66 psi)
135 °C
Deflection Temperature at 1.8 MPa (264 psi)
70.0 °C

Electrical Properties
Volume Resistivity
1e+05 @Temperature 23.0 °C
Surface Resistance
1e+05 @Temperature 23.0 °C

Processing Properties
Melt Temperature
205 °C
Melt Temperature
200 - 210 °C
Mold Temperature
90.0 °C
Mold Temperature
80.0 - 100 °C
Drying Temperature
80.0 °C
Dry Time
2.00 - 4.00 hour
Moisture Content
<= 0.050 %

Descriptive Properties
Appearance
Black Color
Forms
Pellets
Generic
Acetal (POM) Homopolymer
Material Status
Preliminary Data
Polymer Family
POM
Polymer Type
POM Homopolymer
Processing Method
Injection Molding
Product Category
Static Dissipative Resins
Product Category
Toughened Resins
Region Available - Global
Yes
RoHS Compliance
Contact Manufacturer

Alternative products

DuPont Performance Polymers Delrin® 300PE NC010A Acetal Homopolymer accurate 80%

$ 1523/MT

Density: 1.42 g/cc
Water Absorption: 0.30 % @Temperature 23.0 °C
Water Absorption: 0.60 % @Temperature 23.0 °C
Water Absorption: 1.4 % @Temperature 23.0 °C
Linear Mold Shrinkage: 0.019 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® 527UVE NC010 Acetal Homopolymer (Unverified Data**) accurate 80%

$ 1552/MT

Density: 1.42 g/cc
Water Absorption: 0.40 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.020 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.019 cm/cm @Thickness 2.00 mm
Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® FG400XRD NC010 Acetal (Unverified Data**) accurate 68%

$ 1541/MT

Tensile Strength, Yield: 51.0 MPa @Temperature 23.0 °C
Elongation at Yield: 7.0 % @Temperature 23.0 °C
Tensile Modulus: 3.20 GPa @Temperature 23.0 °C
Charpy Impact Unnotched: 8.00 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched: 0.400 J/cm² @Temperature 23.0 °C

DuPont Performance Polymers Delrin® 500PE NC010A Acetal Homopolymer accurate 80%

$ 1879/MT

Density: 1.42 g/cc
Water Absorption: 0.30 % @Temperature 23.0 °C
Water Absorption: 0.50 % @Temperature 23.0 °C
Water Absorption: 1.4 % @Temperature 23.0 °C
Linear Mold Shrinkage: 0.019 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® 327UVE NC010 Acetal Homopolymer (Unverified Data**) accurate 80%

$ 1544/MT

Density: 1.42 g/cc
Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound: 6.0 g/10 min
Tensile Strength, Yield: 71.0 MPa @Temperature 23.0 °C
Elongation at Break: 40 % @Temperature 23.0 °C

DuPont Performance Polymers Delrin® 527UVE RD402 Acetal Homopolymer (Unverified Data**) accurate 80%

$ 2176/MT

Density: 1.42 g/cc
Water Absorption: 0.40 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.020 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.019 cm/cm @Thickness 2.00 mm
Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® 100PE NC010A Acetal Homopolymer accurate 80%

$ 1578/MT

Density: 1.42 g/cc
Water Absorption: 0.30 % @Temperature 23.0 °C
Water Absorption: 0.60 % @Temperature 23.0 °C
Water Absorption: 1.4 % @Temperature 23.0 °C
Linear Mold Shrinkage: 0.020 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® 127UVE RD402 Acetal Homopolymer (Unverified Data**) accurate 80%

$ 2114/MT

Density: 1.42 g/cc
Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound: 2.1 g/10 min
Tensile Strength, Yield: 71.5 MPa @Temperature 23.0 °C
Elongation at Break: 50 % @Temperature 23.0 °C

DuPont Performance Polymers Delrin® 127UVE NC010 Acetal Homopolymer (Unverified Data**) accurate 80%

$ 2271/MT

Density: 1.42 g/cc
Water Absorption: 0.50 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.021 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.019 cm/cm @Thickness 2.00 mm
Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, oil tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for DuPont Performance Polymers Delrin® 300ATB BK000 Acetal Homopolymer (Unverified Data**)

Seller from Ahmadābād – 2021-04-02:

Seller from Ahmadābād work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2223 per MT

Seller from Delhi – 2021-05-24:

Seller from Delhi work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2314 per MT

Seller from Yokohama – 2021-08-12:

Seller from Yokohama work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1791 per MT