DuPont Performance Polymers Delrin® 527UVE RD402 Acetal Homopolymer (Unverified Data**) price 2176 per MT

Physical Properties
Density
1.42 g/cc
Water Absorption
0.40 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow
0.020 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse
0.019 cm/cm @Thickness 2.00 mm
Melt Flow
15 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound
13 g/10 min

Mechanical Properties
Tensile Strength, Yield
73.0 MPa @Temperature 23.0 °C
Elongation at Break
30 % @Temperature 23.0 °C
Elongation at Break
35 % @Temperature 23.0 °C
Elongation at Yield
15 % @Temperature 23.0 °C
Tensile Modulus
3.20 GPa @Temperature 23.0 °C
Flexural Modulus
3.10 GPa @Temperature 23.0 °C
Charpy Impact Unnotched
30.0 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.700 J/cm² @Temperature 23.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature -40.0 - 23.0 °C
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature 55.0 - 100 °C
CTE, linear, Transverse to Flow
90.0 µm/m-°C @Temperature -40.0 - 23.0 °C
CTE, linear, Transverse to Flow
110 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Transverse to Flow
140 µm/m-°C @Temperature 55.0 - 100 °C
Melting Point
178 °C
Deflection Temperature at 1.8 MPa (264 psi)
94.0 °C

Processing Properties
Melt Temperature
205 °C
Melt Temperature
200 - 210 °C
Mold Temperature
90.0 °C
Mold Temperature
80.0 - 100 °C
Drying Temperature
80.0 °C
Dry Time
2.00 - 4.00 hour
Moisture Content
<= 0.20 %

Descriptive Properties
Appearance
Red Color
Forms
Pellets
Generic
POM
Material Status
Preliminary Data
Part Marking Code
>POM<
Polymer Family
POM
Polymer Type
POM Homopolymer
Processing Method
Injection Molding
Product Category
Low Emissions Resins
Product Category
Unreinforced Resins
Product Category
UV Resistant/Weatherable Resins
Region Available - Global
Yes
Resin Identification
POM
RoHS Compliance
Contact Manufacturer
Uses
automotive interior applications

Alternative products

DuPont Performance Polymers Delrin® FG500P NC010 Acetal Homopolymer (Unverified Data**) accurate 72%

$ 1702/MT

Density: 1.42 g/cc
Water Absorption: 0.30 % @Temperature 23.0 °C
Water Absorption: 0.60 % @Temperature 23.0 °C
Water Absorption: 1.4 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.020 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® 300PE NC010A Acetal Homopolymer accurate 92%

$ 1523/MT

Density: 1.42 g/cc
Water Absorption: 0.30 % @Temperature 23.0 °C
Water Absorption: 0.60 % @Temperature 23.0 °C
Water Absorption: 1.4 % @Temperature 23.0 °C
Linear Mold Shrinkage: 0.019 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® 527UVE NC010 Acetal Homopolymer (Unverified Data**) accurate 92%

$ 1552/MT

Density: 1.42 g/cc
Water Absorption: 0.40 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.020 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.019 cm/cm @Thickness 2.00 mm
Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® 500PE NC010A Acetal Homopolymer accurate 92%

$ 1879/MT

Density: 1.42 g/cc
Water Absorption: 0.30 % @Temperature 23.0 °C
Water Absorption: 0.50 % @Temperature 23.0 °C
Water Absorption: 1.4 % @Temperature 23.0 °C
Linear Mold Shrinkage: 0.019 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® 327UVE NC010 Acetal Homopolymer (Unverified Data**) accurate 86%

$ 1544/MT

Density: 1.42 g/cc
Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound: 6.0 g/10 min
Tensile Strength, Yield: 71.0 MPa @Temperature 23.0 °C
Elongation at Break: 40 % @Temperature 23.0 °C

DuPont Performance Polymers Delrin® 300ATB BK000 Acetal Homopolymer (Unverified Data**) accurate 86%

$ 1791/MT

Density: 1.41 g/cc
Linear Mold Shrinkage: 0.015 cm/cm @Diameter 4.00 mm
Linear Mold Shrinkage: 0.017 cm/cm @Diameter 4.00 mm
Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 50.0 MPa @Temperature 23.0 °C

DuPont Performance Polymers Delrin® 100PE NC010A Acetal Homopolymer accurate 92%

$ 1578/MT

Density: 1.42 g/cc
Water Absorption: 0.30 % @Temperature 23.0 °C
Water Absorption: 0.60 % @Temperature 23.0 °C
Water Absorption: 1.4 % @Temperature 23.0 °C
Linear Mold Shrinkage: 0.020 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® 127UVE RD402 Acetal Homopolymer (Unverified Data**) accurate 92%

$ 2114/MT

Density: 1.42 g/cc
Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound: 2.1 g/10 min
Tensile Strength, Yield: 71.5 MPa @Temperature 23.0 °C
Elongation at Break: 50 % @Temperature 23.0 °C

DuPont Performance Polymers Delrin® 127UVE NC010 Acetal Homopolymer (Unverified Data**) accurate 92%

$ 2271/MT

Density: 1.42 g/cc
Water Absorption: 0.50 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.021 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.019 cm/cm @Thickness 2.00 mm
Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale vessel. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for DuPont Performance Polymers Delrin® 527UVE RD402 Acetal Homopolymer (Unverified Data**)

Seller from Bogotá – 2021-06-24:

Seller from Bogotá work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), BASF

Price: $2176 per MT