DuPont Performance Polymers Delrin® 327UVE NC010 Acetal Homopolymer (Unverified Data**) price 1544 per MT

Physical Properties
Density
1.42 g/cc
Melt Flow
7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound
6.0 g/10 min

Mechanical Properties
Tensile Strength, Yield
71.0 MPa @Temperature 23.0 °C
Elongation at Break
40 % @Temperature 23.0 °C
Elongation at Break
50 % @Temperature 23.0 °C
Elongation at Yield
22 % @Temperature 23.0 °C
Tensile Modulus
3.00 GPa @Temperature 23.0 °C
Charpy Impact Unnotched
35.0 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
1.00 J/cm² @Temperature 23.0 °C

Thermal Properties
Melting Point
178 °C
Deflection Temperature at 1.8 MPa (264 psi)
91.0 °C

Processing Properties
Melt Temperature
205 °C
Melt Temperature
200 - 210 °C
Mold Temperature
90.0 °C
Mold Temperature
80.0 - 100 °C
Drying Temperature
80.0 °C
Dry Time
2.00 - 4.00 hour
Moisture Content
<= 0.20 %

Descriptive Properties
Forms
Pellets
Generic
Acetal (POM) Homopolymer
Material Status
Preliminary Data
Part Marking Code
>POM<
Polymer Family
POM
Polymer Type
POM Homopolymer
Processing Method
Injection Molding
Product Category
Low Emissions Resins
Product Category
Unreinforced Resins
Product Category
UV Resistant/Weatherable Resins
Region Available - Global
Yes
Resin Identification
POM
RoHS Compliance
Contact Manufacturer

Alternative products

DuPont Performance Polymers Delrin® 300PE NC010A Acetal Homopolymer accurate 92%

$ 1523/MT

Density: 1.42 g/cc
Water Absorption: 0.30 % @Temperature 23.0 °C
Water Absorption: 0.60 % @Temperature 23.0 °C
Water Absorption: 1.4 % @Temperature 23.0 °C
Linear Mold Shrinkage: 0.019 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® 527UVE NC010 Acetal Homopolymer (Unverified Data**) accurate 92%

$ 1552/MT

Density: 1.42 g/cc
Water Absorption: 0.40 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.020 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.019 cm/cm @Thickness 2.00 mm
Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® FG400XRD NC010 Acetal (Unverified Data**) accurate 78%

$ 1541/MT

Tensile Strength, Yield: 51.0 MPa @Temperature 23.0 °C
Elongation at Yield: 7.0 % @Temperature 23.0 °C
Tensile Modulus: 3.20 GPa @Temperature 23.0 °C
Charpy Impact Unnotched: 8.00 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched: 0.400 J/cm² @Temperature 23.0 °C

DuPont Performance Polymers Delrin® 500PE NC010A Acetal Homopolymer accurate 92%

$ 1879/MT

Density: 1.42 g/cc
Water Absorption: 0.30 % @Temperature 23.0 °C
Water Absorption: 0.50 % @Temperature 23.0 °C
Water Absorption: 1.4 % @Temperature 23.0 °C
Linear Mold Shrinkage: 0.019 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® 527UVE RD402 Acetal Homopolymer (Unverified Data**) accurate 92%

$ 2176/MT

Density: 1.42 g/cc
Water Absorption: 0.40 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.020 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.019 cm/cm @Thickness 2.00 mm
Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® 300ATB BK000 Acetal Homopolymer (Unverified Data**) accurate 92%

$ 1791/MT

Density: 1.41 g/cc
Linear Mold Shrinkage: 0.015 cm/cm @Diameter 4.00 mm
Linear Mold Shrinkage: 0.017 cm/cm @Diameter 4.00 mm
Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 50.0 MPa @Temperature 23.0 °C

DuPont Performance Polymers Delrin® 100PE NC010A Acetal Homopolymer accurate 92%

$ 1578/MT

Density: 1.42 g/cc
Water Absorption: 0.30 % @Temperature 23.0 °C
Water Absorption: 0.60 % @Temperature 23.0 °C
Water Absorption: 1.4 % @Temperature 23.0 °C
Linear Mold Shrinkage: 0.020 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® 127UVE RD402 Acetal Homopolymer (Unverified Data**) accurate 92%

$ 2114/MT

Density: 1.42 g/cc
Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound: 2.1 g/10 min
Tensile Strength, Yield: 71.5 MPa @Temperature 23.0 °C
Elongation at Break: 50 % @Temperature 23.0 °C

DuPont Performance Polymers Delrin® 127UVE NC010 Acetal Homopolymer (Unverified Data**) accurate 99%

$ 2271/MT

Density: 1.42 g/cc
Water Absorption: 0.50 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.021 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.019 cm/cm @Thickness 2.00 mm
Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for DuPont Performance Polymers Delrin® 327UVE NC010 Acetal Homopolymer (Unverified Data**)

Seller from Kolkata – 2021-04-16:

Seller from Kolkata work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1544 per MT

Seller from Dhaka – 2021-03-05:

Seller from Dhaka work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2404 per MT