Physical Properties
Specific Gravity
1.53 g/cc
Density
1.54 g/cc
Melt Flow
0.50 g/10 min @Load 1.05 kg, Temperature 190 °C

Mechanical Properties
Tensile Strength at Break
53.0 MPa @Temperature 23.0 °C
Tensile Strength
53.0 MPa @Temperature 23.0 °C
Tensile Strength, Yield
53.0 MPa @Temperature 23.0 °C
Elongation at Break
15 % @Temperature 23.0 °C
Elongation at Break
19 % @Temperature 23.0 °C
Elongation at Yield
15 % @Temperature 23.0 °C
Tensile Modulus
2.70 GPa @Temperature 23.0 °C
Tensile Modulus
2.75 GPa @Temperature 23.0 °C
Flexural Modulus
2.50 GPa @Temperature 23.0 °C
Flexural Modulus
2.51 GPa @Temperature 23.0 °C
Izod Impact, Notched
0.500 J/cm @Temperature 23.0 °C
Izod Impact, Notched (ISO)
5.00 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
7.00 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.500 J/cm² @Temperature 23.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature -40.0 - 23.0 °C
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature 55.0 - 100 °C
CTE, linear, Transverse to Flow
100 µm/m-°C @Temperature -40.0 - 23.0 °C
CTE, linear, Transverse to Flow
110 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Transverse to Flow
110 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Transverse to Flow
130 µm/m-°C @Temperature 55.0 - 100 °C
Melting Point
178 °C
Melting Point
178 °C
Deflection Temperature at 1.8 MPa (264 psi)
87.0 °C
UL RTI, Electrical
105 °C @Thickness 3.00 mm
UL RTI, Electrical
105 °C @Thickness 1.50 mm
UL RTI, Mechanical with Impact
85.0 °C @Thickness 1.50 mm
UL RTI, Mechanical with Impact
85.0 °C @Thickness 3.00 mm
UL RTI, Mechanical without Impact
90.0 °C @Thickness 1.50 mm
UL RTI, Mechanical without Impact
90.0 °C @Thickness 3.00 mm
Flammability, UL94
HB @Thickness 1.50 mm
Flammability, UL94
HB @Thickness 3.00 mm
Flammability, UL94
HB @Thickness 1.50 mm
Flammability, UL94
HB @Thickness 3.00 mm

Electrical Properties
Comparative Tracking Index
600 V @Thickness 3.00 mm, Temperature 23.0 °C

Processing Properties
Melt Temperature
215 °C
Melt Temperature
210 - 220 °C
Mold Temperature
90.0 °C
Mold Temperature
80.0 - 100 °C
Drying Temperature
80.0 °C
Dry Time
2.00 - 4.00 hour
Moisture Content
<= 0.20 %

Descriptive Properties
Additive
Lubricant, PTFE, 20%
Appearance
Brown Color
Drying Recommended
Not normally required unless moisture content of resin exceeds recommended level
Features
Friction, Low
Features
Viscosity, High
Features
Wear Resistance, Good
Forms
Pellets
Generic
Acetal (POM) Homopolymer
Material Status
Current
Part Marking Code
>POM-SF20<
Polymer Family
POM
Polymer Type
POM Homopolymer
Processing Method
Extrusion
Processing Method
Injection Molding
Product Category
Extrusion Resins
Product Category
Low Wear and Friction Resins
Region Available - Global
Yes
Resin Identification
POM-SF20
RoHS Compliance
Contact Manufacturer
Uses
Bushings
Uses
Parts, Engineering

Alternative products

DuPont Performance Polymers Delrin® FG100P NC010 Acetal Homopolymer (Unverified Data**) accurate 77%

$ 1688/MT

Density: 1.42 g/cc
Water Absorption: 0.30 % @Temperature 23.0 °C
Water Absorption: 1.4 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.022 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.020 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® 900P BK602 Acetal Homopolymer (Unverified Data**) accurate 77%

$ 2005/MT

Density: 1.42 g/cc
Linear Mold Shrinkage, Flow: 0.018 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.017 cm/cm @Thickness 2.00 mm
Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 70.0 MPa @Temperature 23.0 °C

DuPont Performance Polymers Delrin® FG500P NC010 Acetal Homopolymer (Unverified Data**) accurate 77%

$ 1702/MT

Density: 1.42 g/cc
Water Absorption: 0.30 % @Temperature 23.0 °C
Water Absorption: 0.60 % @Temperature 23.0 °C
Water Absorption: 1.4 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.020 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® FG150 NC010 Acetal Homopolymer (Unverified Data**) accurate 82%

$ 1571/MT

Density: 1.42 g/cc
Water Absorption: 0.39 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.018 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.020 cm/cm @Thickness 2.00 mm
Melt Flow: 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® 527UV BK701 Acetal Homopolymer (Unverified Data**) accurate 77%

$ 2249/MT

Density: 1.41 g/cc
Linear Mold Shrinkage, Flow: 0.018 cm/cm @Thickness 4.00 mm
Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 71.0 MPa @Temperature 23.0 °C
Elongation at Break: 23 % @Temperature 23.0 °C

DuPont Performance Polymers Delrin® 500P BK602 Acetal Homopolymer (Unverified Data**) accurate 77%

$ 1565/MT

Density: 1.42 g/cc
Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 71.0 MPa @Temperature 23.0 °C
Elongation at Break: 25 % @Temperature 23.0 °C
Elongation at Break: 35 % @Temperature 23.0 °C

DuPont Performance Polymers Delrin® 911DP BK402 Acetal Homopolymer (Unverified Data**) accurate 77%

$ 2449/MT

Density: 1.42 g/cc
Linear Mold Shrinkage, Flow: 0.018 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.017 cm/cm @Thickness 2.00 mm
Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound: 21 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® 300CP NC010 Acetal Homopolymer (Unverified Data**) accurate 77%

$ 1777/MT

Density: 1.42 g/cc
Water Absorption: 0.17 % @Temperature 23.0 °C
Water Absorption: 0.40 % @Temperature 23.0 °C
Water Absorption: 0.90 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.021 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® 911DP NC010 Acetal Homopolymer (Unverified Data**) accurate 77%

$ 1893/MT

Density: 1.42 g/cc
Linear Mold Shrinkage, Flow: 0.019 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.018 cm/cm @Thickness 2.00 mm
Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound: 21 g/10 min @Load 2.16 kg, Temperature 190 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for DuPont Performance Polymers Delrin® 100AF Acetal Homopolymer (Unverified Data**)

Seller from Hāora – 2021-08-10:

Seller from Hāora work with company: Solvay, SABIC Innovative Plastics (GE Plastics), LG Chemical, ALIMEX GmbH

Price: $2118 per MT