Physical Properties
Density
1.42 g/cc
Melt Flow
15 g/10 min @Load 2.16 kg, Temperature 190 °C

Mechanical Properties
Tensile Strength, Yield
71.0 MPa @Temperature 23.0 °C
Elongation at Break
25 % @Temperature 23.0 °C
Elongation at Break
35 % @Temperature 23.0 °C
Elongation at Yield
14 % @Temperature 23.0 °C
Tensile Modulus
3.10 GPa @Temperature 23.0 °C
Flexural Modulus
3.00 GPa @Temperature 23.0 °C
Izod Impact, Notched (ISO)
8.00 kJ/m² @Temperature -40.0 °C
Izod Impact, Notched (ISO)
8.00 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
18.0 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.700 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
0.800 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.900 J/cm² @Temperature -40.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature -40.0 - 23.0 °C
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature 55.0 - 100 °C
CTE, linear, Transverse to Flow
98.0 µm/m-°C @Temperature -40.0 - 23.0 °C
CTE, linear, Transverse to Flow
115 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Transverse to Flow
167 µm/m-°C @Temperature 55.0 - 100 °C
Melting Point
178 °C
Deflection Temperature at 0.46 MPa (66 psi)
162 °C
Deflection Temperature at 1.8 MPa (264 psi)
96.0 °C
UL RTI, Electrical
50.0 °C @Thickness 0.750 mm
UL RTI, Electrical
110 °C @Thickness 3.00 mm
UL RTI, Electrical
110 °C @Thickness 1.50 mm
UL RTI, Mechanical with Impact
50.0 °C @Thickness 0.750 mm
UL RTI, Mechanical with Impact
85.0 °C @Thickness 1.50 mm
UL RTI, Mechanical with Impact
90.0 °C @Thickness 3.00 mm
UL RTI, Mechanical without Impact
50.0 °C @Thickness 0.750 mm
UL RTI, Mechanical without Impact
90.0 °C @Thickness 1.50 mm
UL RTI, Mechanical without Impact
95.0 °C @Thickness 3.00 mm
Flammability, UL94
HB @Thickness 1.50 mm
Flammability, UL94
HB @Thickness 3.00 mm
Flammability, UL94
HB @Thickness 0.750 mm
Flammability, UL94
HB @Thickness 0.750 mm
Flammability, UL94
HB @Thickness 0.800 mm
Flammability, UL94
HB @Thickness 1.50 mm
Flammability, UL94
HB @Thickness 3.00 mm

Electrical Properties
Comparative Tracking Index
600 V @Temperature 23.0 °C

Processing Properties
Melt Temperature
215 °C
Melt Temperature
210 - 220 °C
Mold Temperature
90.0 °C
Mold Temperature
80.0 - 100 °C
Drying Temperature
80.0 °C
Dry Time
2.00 - 4.00 hour
Moisture Content
<= 0.20 %

Descriptive Properties
Appearance
Black Color
Drying Recommended
Not normally required unless moisture content of resin exceeds recommended level
Extrudable - Cast Film
Yes
Extrudable - Sheet
Yes
Extrudable - Tubing
Yes
Extrudable - Wire and Cable
Yes
Features
Creep Resistance, Good
Features
Dimensional Stability, Good
Features
Fatigue Resistant
Features
Homopolymer
Features
Impact Resistance, Good
Features
Stiffness, High
Features
Strength, High
Features
Viscosity, Medium
Forms
Pellets
Generic
Acetal (POM) Homopolymer
Material Status
Current
Part Marking Code
>POM<
Polymer Family
POM
Polymer Type
POM Homopolymer
Processing Method
Extrusion
Processing Method
Extrusion
Processing Method
Injection Molding
Product Category
Unreinforced Resins
Region Available - Global
Yes
Resin Identification
POM
RoHS Compliance
Contact Manufacturer
Ultrasonic Weldable
Yes
Uses
Automotive Applications
Uses
Fasteners
Uses
Gears
Uses
General Purpose
Uses
Parts, Engineering

Alternative products

DuPont Performance Polymers Delrin® FG100P NC010 Acetal Homopolymer (Unverified Data**) accurate 86%

$ 1688/MT

Density: 1.42 g/cc
Water Absorption: 0.30 % @Temperature 23.0 °C
Water Absorption: 1.4 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.022 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.020 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® 900P BK602 Acetal Homopolymer (Unverified Data**) accurate 86%

$ 2005/MT

Density: 1.42 g/cc
Linear Mold Shrinkage, Flow: 0.018 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.017 cm/cm @Thickness 2.00 mm
Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 70.0 MPa @Temperature 23.0 °C

DuPont Performance Polymers Delrin® FG900P NC010 Acetal Homopolymer (Unverified Data**) accurate 92%

$ 1448/MT

Density: 1.42 g/cc
Water Absorption: 0.26 % @Temperature 23.0 °C
Water Absorption: 0.56 % @Temperature 23.0 °C
Water Absorption: 1.4 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.019 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® FG150 NC010 Acetal Homopolymer (Unverified Data**) accurate 92%

$ 1571/MT

Density: 1.42 g/cc
Water Absorption: 0.39 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.018 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.020 cm/cm @Thickness 2.00 mm
Melt Flow: 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® 911DP BK402 Acetal Homopolymer (Unverified Data**) accurate 86%

$ 2449/MT

Density: 1.42 g/cc
Linear Mold Shrinkage, Flow: 0.018 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.017 cm/cm @Thickness 2.00 mm
Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound: 21 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® 300CP NC010 Acetal Homopolymer (Unverified Data**) accurate 86%

$ 1777/MT

Density: 1.42 g/cc
Water Absorption: 0.17 % @Temperature 23.0 °C
Water Absorption: 0.40 % @Temperature 23.0 °C
Water Absorption: 0.90 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.021 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® 511DP BK402 Acetal Homopolymer (Unverified Data**) accurate 86%

$ 1946/MT

Density: 1.42 g/cc
Linear Mold Shrinkage, Flow: 0.019 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.018 cm/cm @Thickness 2.00 mm
Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound: 13 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® 911DP NC010 Acetal Homopolymer (Unverified Data**) accurate 86%

$ 1893/MT

Density: 1.42 g/cc
Linear Mold Shrinkage, Flow: 0.019 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.018 cm/cm @Thickness 2.00 mm
Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound: 21 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® 100AF Acetal Homopolymer (Unverified Data**) accurate 92%

$ 2118/MT

Specific Gravity: 1.53 g/cc
Density: 1.54 g/cc
Melt Flow: 0.50 g/10 min @Load 1.05 kg, Temperature 190 °C
Tensile Strength at Break: 53.0 MPa @Temperature 23.0 °C
Tensile Strength: 53.0 MPa @Temperature 23.0 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cargo ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for DuPont Performance Polymers Delrin® 500P BK602 Acetal Homopolymer (Unverified Data**)

Seller from Guadalajara – 2021-04-15:

Seller from Guadalajara work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1565 per MT

Seller from Ho Chi Minh City – 2021-06-23:

Seller from Ho Chi Minh City work with company: Solvay, Fainplast Compounds, Exxon Chemical, SABIC Innovative Plastics (GE Plastics)

Price: $1886 per MT

Seller from Ahmadābād – 2021-04-15:

Seller from Ahmadābād work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2470 per MT