DuPont Performance Polymers Delrin® 100AL NC010 Acetal Homopolymer (Unverified Data**) price 2254 per MT

Physical Properties
Density
1.40 g/cc
Linear Mold Shrinkage, Flow
0.020 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse
0.018 cm/cm @Thickness 2.00 mm
Melt Flow
2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound
1.7 g/10 min @Load 2.16 kg, Temperature 190 °C

Mechanical Properties
Tensile Strength, Yield
70.0 MPa @Temperature 23.0 °C
Elongation at Break
45 % @Temperature 23.0 °C
Elongation at Break
65 % @Temperature 23.0 °C
Elongation at Yield
18 % @Temperature 23.0 °C
Tensile Modulus
3.00 GPa @Temperature 23.0 °C
Flexural Modulus
2.80 GPa @Temperature 23.0 °C
Izod Impact, Notched (ISO)
8.00 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
17.0 J/cm² @Temperature -30.0 °C
Charpy Impact Unnotched
25.0 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.700 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
0.900 J/cm² @Temperature 23.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature -40.0 - 23.0 °C
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature 55.0 - 100 °C
CTE, linear, Transverse to Flow
100 µm/m-°C @Temperature -40.0 - 23.0 °C
CTE, linear, Transverse to Flow
110 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Transverse to Flow
150 µm/m-°C @Temperature 55.0 - 100 °C
Melting Point
178 °C
Deflection Temperature at 0.46 MPa (66 psi)
163 °C
Deflection Temperature at 1.8 MPa (264 psi)
97.0 °C
UL RTI, Electrical
50.0 °C @Thickness 3.00 mm
UL RTI, Electrical
50.0 °C @Thickness 0.750 mm
UL RTI, Mechanical with Impact
50.0 °C @Thickness 3.00 mm
UL RTI, Mechanical with Impact
50.0 °C @Thickness 0.750 mm
UL RTI, Mechanical without Impact
50.0 °C @Thickness 0.750 mm
UL RTI, Mechanical without Impact
50.0 °C @Thickness 3.00 mm
Flammability, UL94
HB @Thickness 0.750 mm
Flammability, UL94
HB @Thickness 3.00 mm
Flammability, UL94
HB @Thickness 0.750 mm
Flammability, UL94
HB @Thickness 3.00 mm

Processing Properties
Melt Temperature
215 °C
Melt Temperature
210 - 220 °C
Mold Temperature
90.0 °C
Mold Temperature
80.0 - 100 °C
Drying Temperature
80.0 °C
Dry Time
2.00 - 4.00 hour
Moisture Content
<= 0.20 %

Descriptive Properties
Additive
Lubricant
Appearance
Natural Color
Drying Recommended
Not normally required unless moisture content of resin exceeds recommended level
Features
Creep Resistance, Good
Features
Friction, Low
Features
Homopolymer
Features
Impact Resistance, High
Features
Lubricated
Features
Viscosity, High
Features
Wear Resistance, Good
Forms
Pellets
Generic
Acetal (POM) Homopolymer
Material Status
Current
Part Marking Code
>POM-S<
Polymer Family
POM
Polymer Type
POM Homopolymer
Processing Method
Extrusion
Processing Method
Injection Molding
Product Category
Extrusion Resins
Product Category
Low Wear and Friction Resins
Product Category
Unreinforced Resins
Region Available - Global
Yes
Resin Identification
POM-S
RoHS Compliance
Contact Manufacturer
Ultrasonic Weldable
Yes
Uses
Conveyors
Uses
Gears
Uses
Parts, Engineering

Alternative products

DuPont Performance Polymers Delrin® FG150 NC010 Acetal Homopolymer (Unverified Data**) accurate 93%

$ 1571/MT

Density: 1.42 g/cc
Water Absorption: 0.39 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.018 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.020 cm/cm @Thickness 2.00 mm
Melt Flow: 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® 527UV BK701 Acetal Homopolymer (Unverified Data**) accurate 93%

$ 2249/MT

Density: 1.41 g/cc
Linear Mold Shrinkage, Flow: 0.018 cm/cm @Thickness 4.00 mm
Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 71.0 MPa @Temperature 23.0 °C
Elongation at Break: 23 % @Temperature 23.0 °C

DuPont Performance Polymers Delrin® 911DP BK402 Acetal Homopolymer (Unverified Data**) accurate 93%

$ 2449/MT

Density: 1.42 g/cc
Linear Mold Shrinkage, Flow: 0.018 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.017 cm/cm @Thickness 2.00 mm
Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound: 21 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® FG570 NC000 Acetal Homopolymer accurate 87%

$ 2164/MT

Density: 1.56 g/cc
Water Absorption: 0.10 % @Temperature 23.0 °C
Water Absorption: 0.80 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.016 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.012 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Delrin® 511DP BK402 Acetal Homopolymer (Unverified Data**) accurate 93%

$ 1946/MT

Density: 1.42 g/cc
Linear Mold Shrinkage, Flow: 0.019 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.018 cm/cm @Thickness 2.00 mm
Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound: 13 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® FG511DP NC010 Acetal Homopolymer (Unverified Data**) accurate 93%

$ 1558/MT

Density: 1.42 g/cc
Linear Mold Shrinkage, Flow: 0.019 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.018 cm/cm @Thickness 2.00 mm
Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound: 13 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® 911DP NC010 Acetal Homopolymer (Unverified Data**) accurate 93%

$ 1893/MT

Density: 1.42 g/cc
Linear Mold Shrinkage, Flow: 0.019 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.018 cm/cm @Thickness 2.00 mm
Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound: 21 g/10 min @Load 2.16 kg, Temperature 190 °C

DuPont Performance Polymers Delrin® 100AF Acetal Homopolymer (Unverified Data**) accurate 87%

$ 2118/MT

Specific Gravity: 1.53 g/cc
Density: 1.54 g/cc
Melt Flow: 0.50 g/10 min @Load 1.05 kg, Temperature 190 °C
Tensile Strength at Break: 53.0 MPa @Temperature 23.0 °C
Tensile Strength: 53.0 MPa @Temperature 23.0 °C

DuPont Performance Polymers Delrin® 300CP BK642 Acetal Homopolymer (Unverified Data**) accurate 93%

$ 1948/MT

Density: 1.42 g/cc
Linear Mold Shrinkage, Flow: 0.021 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.018 cm/cm @Thickness 2.00 mm
Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Index of Compound: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng carrier vessel for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for DuPont Performance Polymers Delrin® 100AL NC010 Acetal Homopolymer (Unverified Data**)

Seller from Moscow – 2021-04-30:

Seller from Moscow work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2254 per MT