DuPont Performance Polymers Hytrel® HTR8223 BK320 TPC-ET (Unverified Data**) price 1489 per MT

Physical Properties
Density
1.13 g/cc
Water Absorption
0.60 % @Temperature 23.0 °C
Water Absorption
0.60 % @Temperature 23.0 °C, Time 86400 sec
Melt Flow
0.60 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Flow
2.3 g/10 min @Load 5.00 kg, Temperature 230 °C

Mechanical Properties
Hardness, Shore D
<= 42
Hardness, Shore D
<= 45
Hardness, Shore D
38 @Time 15.0 sec
Tensile Strength at Break
27.0 MPa @Temperature 23.0 °C
Tensile Stress
3.50 MPa @Strain 5.00 %, Temperature 23.0 °C
Tensile Stress
5.50 MPa @Strain 10.0 %, Temperature 23.0 °C
Tensile Stress
6.80 MPa @Strain 50.0 %, Temperature 23.0 °C
Elongation at Break
>= 300 % @Temperature 23.0 °C
Elongation at Break
450 % @Temperature 23.0 °C
Tensile Modulus
0.0740 GPa @Temperature 23.0 °C
Flexural Modulus
0.0440 GPa @Temperature 100 °C
Flexural Modulus
0.0790 GPa @Temperature 23.0 °C
Flexural Modulus
0.210 GPa @Temperature -40.0 °C
Izod Impact, Notched (ISO)
NB @Temperature -50.0 °C
Izod Impact, Notched (ISO)
NB @Temperature 23.0 °C
Charpy Impact, Notched
NB @Temperature 23.0 °C

Thermal Properties
Melting Point
195 °C
Brittleness Temperature
-100 °C

Processing Properties
Melt Temperature
225 °C
Mold Temperature
45.0 °C
Mold Temperature
40.0 - 50.0 °C
Drying Temperature
110 °C
Drying Temperature
110 °C
Dry Time
3.00 - 4.00 hour
Dry Time
3.00 - 4.00 hour
Moisture Content
<= 0.020 %
Moisture Content
<= 0.020 %

Descriptive Properties
Appearance
Black Color
Extrudable - Blown Film
Yes
Extrudable - Cast Film
Yes
Extrudable - Coating
Yes
Extrudable - Filament
Yes
Extrudable - Hose
Yes
Extrudable - Sheet
Yes
Extrudable - Tubing
Yes
Extrudable - Wire and Cable
Yes
Extrusion Blow Moldable
Yes
Forms
Pellets
Generic
TPC-ET
Heat Stabilized
Yes
Material Status
Preliminary Data
Melt Castable
Yes
Part Marking Code
>TPC-ET<
Polymer Family
TPC-ET
Polymer Type
TPC-ET
Processing Method
Blow Molding
Product Category
Blow Moldable Resins
Region Available - Global
Yes
Resin Identification
TPC-ET
RoHS Compliance
Contact Manufacturer

Alternative products

BASF Ultramid® KR 4355 G5 BK 00564 25% Glass Filled PA6/6T (Dry) accurate 46%

$ 2404/MT

Bulk Density: 0.500 - 0.800 g/cc
Density: 1.35 g/cc
Water Absorption: 5.0 - 6.0 %
Moisture Absorption at Equilibrium: 1.1 - 1.5 %
Viscosity Measurement: 130

DuPont Performance Polymers Hytrel® HTR8685 BK022A TPC-ET (Unverified Data**) accurate 58%

$ 2596/MT

Density: 1.15 g/cc
Linear Mold Shrinkage, Flow: 0.017 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.016 cm/cm @Thickness 2.00 mm
Hardness, Shore D: <= 44 @Temperature 23.0 °C
Hardness, Shore D: 41 @Time 15.0 sec

BASF Ultramid® KR 4357 G6 BK 00564 30% Glass Filled PA6/6T (Dry) accurate 46%

$ 2007/MT

Bulk Density: 0.500 - 0.800 g/cc
Density: 1.37 g/cc
Water Absorption: 4.0 - 5.0 %
Moisture Absorption at Equilibrium: 0.60 - 1.0 %
Viscosity Measurement: 130

DuPont Performance Polymers Hytrel® 7246HS BK320 TPC-ET (Unverified Data**) accurate 58%

$ 1460/MT

Density: 1.25 g/cc
Hardness, Shore D: 66
Hardness, Shore D: <= 70
Tensile Strength at Break: 53.0 MPa @Temperature 23.0 °C
Tensile Stress: 23.0 MPa @Strain 10.0 %, Temperature 23.0 °C

DuPont Performance Polymers Hytrel® HTR237BG BK320 TPC-ET (Unverified Data**) accurate 46%

$ 1965/MT

Density: 1.15 g/cc
Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 220 °C
Hardness, Shore D: <= 45
Tensile Strength at Break: 31.0 MPa @Temperature 23.0 °C
Tensile Stress: 7.60 MPa @Strain 10.0 %, Temperature 23.0 °C

BASF Ultramid® KR 4355 G5 25% Glass Filled PA6/6T (Conditioned) accurate 46%

$ 1663/MT

Bulk Density: 0.500 - 0.800 g/cc
Density: 1.35 g/cc
Water Absorption: 5.0 - 6.0 %
Moisture Absorption at Equilibrium: >= 1.3 %
Moisture Absorption at Equilibrium: 1.1 - 1.5 %

DuPont Performance Polymers Hytrel® HTR8136BK TPC-ET (Unverified Data**) accurate 64%

$ 2199/MT

Specific Gravity: 1.16 g/cc
Density: 1.16 g/cc
Water Absorption: 0.20 % @Temperature 23.0 °C
Water Absorption: 0.70 % @Temperature 23.0 °C
Water Absorption: 0.70 % @Temperature 23.0 °C

DuPont Performance Polymers Hytrel® 7246HS NC010 TPC-ET (Unverified Data**) accurate 58%

$ 1599/MT

Density: 1.25 g/cc
Hardness, Shore D: 66
Hardness, Shore D: <= 70
Tensile Strength at Break: 52.0 MPa @Temperature 23.0 °C
Tensile Stress: 23.0 MPa @Strain 10.0 %, Temperature 23.0 °C

DuPont Performance Polymers Hytrel® HTR5612BK TPC-ET (Unverified Data**) accurate 64%

$ 1470/MT

Density: 1.16 g/cc
Water Absorption: 0.20 % @Temperature 23.0 °C
Water Absorption: 0.60 % @Temperature 23.0 °C
Water Absorption: 0.40 % @Thickness 1.00 mm, Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 2.00 mm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, bulk cargo ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for DuPont Performance Polymers Hytrel® HTR8223 BK320 TPC-ET (Unverified Data**)

Seller from Rangoon – 2021-08-04:

Seller from Rangoon work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1489 per MT