DuPont Performance Polymers Hytrel® HTR8685 BK022A TPC-ET (Unverified Data**) price 2596 per MT

Physical Properties
Density
1.15 g/cc
Linear Mold Shrinkage, Flow
0.017 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse
0.016 cm/cm @Thickness 2.00 mm

Mechanical Properties
Hardness, Shore D
<= 44 @Temperature 23.0 °C
Hardness, Shore D
41 @Time 15.0 sec
Tensile Strength at Break
30.0 MPa @Temperature 23.0 °C
Tensile Stress
8.40 MPa @Strain 10.0 %, Temperature 23.0 °C
Tensile Stress
14.0 MPa @Strain 50.0 %, Temperature 23.0 °C
Elongation at Break
320 % @Temperature 23.0 °C
Elongation at Break
350 % @Temperature 23.0 °C
Tensile Modulus
0.100 GPa @Temperature 23.0 °C
Flexural Modulus
0.100 GPa @Temperature 23.0 °C
Charpy Impact, Notched
NB @Temperature 23.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
500 µm/m-°C @Temperature 23.0 - 55.0 °C
CTE, linear, Transverse to Flow
200 µm/m-°C @Temperature 23.0 - 55.0 °C
Melting Point
206 °C
Deflection Temperature at 0.46 MPa (66 psi)
62.0 °C

Processing Properties
Melt Temperature
240 °C
Mold Temperature
45.0 °C
Mold Temperature
40.0 - 50.0 °C
Drying Temperature
110 °C
Drying Temperature
110 °C
Dry Time
3.00 - 4.00 hour
Dry Time
3.00 - 4.00 hour
Moisture Content
<= 0.020 %
Moisture Content
<= 0.020 %

Descriptive Properties
Appearance
Black Color
Forms
Pellets
Generic
TPC-ET
Material Status
Preliminary Data
Part Marking Code
>TPC-ET<
Processing Method
Blow Molding
Product Category
Blow Moldable Resins
Region Available - Global
Yes
Resin Identification
TPC-ET
RoHS Compliance
Contact Manufacturer

Alternative products

DuPont Performance Polymers Hytrel® HTR8223 BK320 TPC-ET (Unverified Data**) accurate 82%

$ 1489/MT

Density: 1.13 g/cc
Water Absorption: 0.60 % @Temperature 23.0 °C
Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Flow: 2.3 g/10 min @Load 5.00 kg, Temperature 230 °C

DuPont Performance Polymers Hytrel® 7246HS BK320 TPC-ET (Unverified Data**) accurate 99%

$ 1460/MT

Density: 1.25 g/cc
Hardness, Shore D: 66
Hardness, Shore D: <= 70
Tensile Strength at Break: 53.0 MPa @Temperature 23.0 °C
Tensile Stress: 23.0 MPa @Strain 10.0 %, Temperature 23.0 °C

DuPont Performance Polymers Zytel® ST7301 BK356 Nylon 6 (Unverified Data**) accurate 66%

$ 1467/MT

Density: 1.06 g/cc
Linear Mold Shrinkage, Flow: 0.013 cm/cm @Thickness 2.00 mm
Tensile Strength, Yield: 30.0 MPa @Temperature 23.0 °C
Tensile Strength, Yield: 48.0 MPa @Temperature 23.0 °C
Elongation at Break: 45 % @Temperature 23.0 °C

DuPont Performance Polymers Hytrel® HTR8136BK TPC-ET (Unverified Data**) accurate 82%

$ 2199/MT

Specific Gravity: 1.16 g/cc
Density: 1.16 g/cc
Water Absorption: 0.20 % @Temperature 23.0 °C
Water Absorption: 0.70 % @Temperature 23.0 °C
Water Absorption: 0.70 % @Temperature 23.0 °C

DuPont Performance Polymers Hytrel® 7246HS NC010 TPC-ET (Unverified Data**) accurate 99%

$ 1599/MT

Density: 1.25 g/cc
Hardness, Shore D: 66
Hardness, Shore D: <= 70
Tensile Strength at Break: 52.0 MPa @Temperature 23.0 °C
Tensile Stress: 23.0 MPa @Strain 10.0 %, Temperature 23.0 °C

DuPont Performance Polymers Zytel® ST811HS BK038 Nylon 6 (Unverified Data**) accurate 66%

$ 1610/MT

Density: 1.05 g/cc
Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.014 cm/cm @Thickness 2.00 mm
Tensile Strength at Break: 44.0 MPa @Temperature 23.0 °C
Elongation at Break: 200 % @Temperature 23.0 °C

BASF Ultramid® KR 4355 G10 BK 23215 50% Glass Filled PA6/6T (Dry) accurate 57%

$ 2293/MT

Bulk Density: 0.500 - 0.800 g/cc
Density: 1.62 g/cc
Water Absorption: 3.5 - 4.5 %
Moisture Absorption at Equilibrium: 0.40 - 0.80 %
Viscosity Measurement: 135

DuPont Performance Polymers Hytrel® HTR5612BK TPC-ET (Unverified Data**) accurate 82%

$ 1470/MT

Density: 1.16 g/cc
Water Absorption: 0.20 % @Temperature 23.0 °C
Water Absorption: 0.60 % @Temperature 23.0 °C
Water Absorption: 0.40 % @Thickness 1.00 mm, Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Zytel® ST7301 NC010 Nylon 6 (Unverified Data**) accurate 66%

$ 1727/MT

Density: 1.06 g/cc
Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 2.00 mm
Tensile Strength, Yield: 29.0 MPa @Temperature 23.0 °C
Tensile Strength, Yield: 48.0 MPa @Temperature 23.0 °C
Elongation at Break: >= 50 % @Temperature 23.0 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, commercial ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for DuPont Performance Polymers Hytrel® HTR8685 BK022A TPC-ET (Unverified Data**)

Seller from Chengdu – 2021-04-05:

Seller from Chengdu work with company: Solvay, RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $2596 per MT