Eurostar Staramide A28N PA66, Nucleated, Injection Molding price 1655 per MT

Physical Properties
Density
1.14 g/cc
Moisture Absorption
2.00 % @Temperature 23.0 °C
Water Absorption at Saturation
8.5 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow
0.016 - 0.020 cm/cm

Mechanical Properties
Hardness, Rockwell L
118
Tensile Strength, Yield
85.0 MPa
Elongation at Break
>= 20 %
Elongation at Yield
3.8 %
Tensile Modulus
3.00 GPa
Flexural Yield Strength
105 MPa
Flexural Modulus
2.80 GPa
Izod Impact, Notched (ISO)
3.00 kJ/m² @Temperature -30.0 °C
Izod Impact, Notched (ISO)
3.00 kJ/m² @Temperature -40.0 °C
Izod Impact, Notched (ISO)
4.00 kJ/m² @Temperature -20.0 °C
Izod Impact, Notched (ISO)
5.00 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
>= 10.0 J/cm² @Temperature -30.0 °C
Charpy Impact Unnotched
>= 27.0 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.300 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
0.500 J/cm² @Temperature 23.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
80.0 µm/m-°C @Temperature 23.0 - 60.0 °C
CTE, linear, Transverse to Flow
80.0 µm/m-°C @Temperature 23.0 - 60.0 °C
Thermal Conductivity
0.290 W/m-K
Hot Ball Pressure Test
123 - 127 °C
Deflection Temperature at 0.46 MPa (66 psi)
210 °C
Deflection Temperature at 1.8 MPa (264 psi)
90.0 °C
Vicat Softening Point
240 °C
Vicat Softening Point
243 °C
UL RTI, Electrical
65.0 °C
UL RTI, Mechanical with Impact
65.0 °C
UL RTI, Mechanical without Impact
65.0 °C
Flammability, UL94
V-2 @Thickness 1.60 mm
Oxygen Index
26 %

Electrical Properties
Volume Resistivity
>= 1.00e+16 ohm-cm
Surface Resistance
>= 1.00e+16 ohm
Dielectric Constant
2.9 @Frequency 1.00e+6 Hz
Dielectric Constant
3.2 @Frequency 50.0 - 60.0 Hz
Dielectric Strength
16.0 kV/mm @Thickness 3.20 mm
Dissipation Factor
0.0055 @Frequency 50.0 - 60.0 Hz
Dissipation Factor
0.017 @Frequency 1.00e+6 Hz
Comparative Tracking Index
600 V
Comparative Tracking Index
600 V

Processing Properties
Zone 1
260 - 270 °C
Zone 2
270 - 280 °C
Zone 3
270 - 290 °C
Melt Temperature
270 - 290 °C
Mold Temperature
60.0 - 90.0 °C
Drying Temperature
75.0 - 85.0 °C @Time 14400 - 21600 sec
Moisture Content
0.20 %

Alternative products

Eurostar Staramide A28K PA66, Heat Stabilized, Injection Molding accurate 82%

$ 2443/MT

Density: 1.14 g/cc
Moisture Absorption: 2.00 % @Temperature 23.0 °C
Water Absorption at Saturation: 8.5 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.016 - 0.020 cm/cm
Hardness, Rockwell L: 118

Eurostar Staramide B40 PA6, Extrusion accurate 70%

$ 2478/MT

Density: 1.13 g/cc
Moisture Absorption: 2.35 % @Temperature 23.0 °C
Water Absorption at Saturation: 10 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm
Hardness, Rockwell R: 121

Eurostar Staramide B28 PA6, Injection Molded accurate 70%

$ 1552/MT

Density: 1.14 g/cc
Moisture Absorption: 2.60 % @Temperature 23.0 °C
Water Absorption at Saturation: 10 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm
Hardness, Rockwell R: 120

Eurostar Staramide B28H PA6, Heat Stabilized, Injection Molded accurate 70%

$ 2256/MT

Density: 1.14 g/cc
Moisture Absorption: 2.60 % @Temperature 23.0 °C
Water Absorption at Saturation: 10 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm
Hardness, Rockwell R: 120

Eurostar Staramide B28N PA6, Nucleated, Injection Molded accurate 70%

$ 2120/MT

Density: 1.14 g/cc
Moisture Absorption: 2.60 % @Temperature 23.0 °C
Water Absorption at Saturation: 10 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm
Hardness, Rockwell R: 120

BASF Ultramid® 8202 HS PA6 (Dry) accurate 57%

$ 1640/MT

Density: 0.932 g/cc
Density: 1.13 g/cc
Water Absorption: 1.6 %
Water Absorption: 9.5 %
Moisture Absorption at Equilibrium: 2.7 %

BASF Ultramid® 8202 PA6 (Dry) accurate 57%

$ 1824/MT

Density: 0.932 g/cc
Density: 1.13 g/cc
Water Absorption: 1.6 %
Water Absorption: 9.5 %
Moisture Absorption at Equilibrium: 2.7 %

DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66 (Unverified Data**) accurate 57%

$ 1463/MT

Density: 1.01 g/cc
Density: 1.14 g/cc
Water Absorption: 8.5 % @Thickness 2.00 mm
Moisture Absorption: 2.60 % @Thickness 2.00 mm
Viscosity: 42210 cP @Shear Rate 5000 1/s, Temperature 295 °C

Eurostar Staramide A28 PA66, Injection Molding accurate 66%

$ 1896/MT

Density: 1.14 g/cc
Moisture Absorption: 2.00 % @Temperature 23.0 °C
Water Absorption at Saturation: 8.5 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.016 - 0.020 cm/cm
Tensile Strength, Yield: 85.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, vessels for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Eurostar Staramide A28N PA66, Nucleated, Injection Molding

Seller from Madrid – 2021-08-03:

Seller from Madrid work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1816 per MT

Seller from Lahore – 2021-08-04:

Seller from Lahore work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1655 per MT