Eurostar Staramide AG3K PA66, 15% Glass Filled, Injection Molded price 1703 per MT

Physical Properties
Density
1.23 g/cc
Water Absorption at Saturation
7.0 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow
0.0040 - 0.0080 cm/cm

Mechanical Properties
Tensile Strength at Break
125 MPa
Elongation at Break
3.0 %
Tensile Modulus
6.50 GPa
Flexural Strength
175 MPa
Flexural Modulus
6.00 GPa
Izod Impact, Notched (ISO)
6.00 kJ/m²
Charpy Impact Unnotched
5.50 J/cm²

Thermal Properties
CTE, linear, Parallel to Flow
35.0 µm/m-°C @Temperature 23.0 - 60.0 °C
CTE, linear, Transverse to Flow
100 µm/m-°C @Temperature 23.0 - 60.0 °C
Thermal Conductivity
0.330 W/m-K
Deflection Temperature at 1.8 MPa (264 psi)
230 °C
Vicat Softening Point
253 °C
UL RTI, Electrical
65.0 °C @Thickness 0.750 mm
UL RTI, Electrical
65.0 °C @Thickness 3.00 mm
UL RTI, Mechanical with Impact
65.0 °C @Thickness 0.750 mm
UL RTI, Mechanical with Impact
65.0 °C @Thickness 3.00 mm
UL RTI, Mechanical without Impact
65.0 °C @Thickness 0.750 mm
UL RTI, Mechanical without Impact
65.0 °C @Thickness 3.00 mm
Flammability, UL94
HB @Thickness 0.750 mm
Flammability, UL94
HB @Thickness 3.00 mm
Flame Spread
5.00 mm/min @Thickness 3.00 mm
Flame Spread
10.0 mm/min @Thickness 2.00 mm
Glow Wire Test
650 °C @Thickness 2.00 mm

Electrical Properties
Volume Resistivity
>= 1.00e+16 ohm-cm
Surface Resistance
>= 1.00e+16 ohm
Dielectric Constant
3.2 @Frequency 1.00e+6 Hz
Dielectric Constant
3.4 @Frequency 50.0 - 60.0 Hz
Dielectric Strength
19.0 kV/mm @Thickness 3.20 mm
Dissipation Factor
0.0068 @Frequency 50.0 - 60.0 Hz
Dissipation Factor
0.015 @Frequency 1.00e+6 Hz
Comparative Tracking Index
450 V
Comparative Tracking Index
550 V

Processing Properties
Rear Barrel Temperature
260 - 280 °C
Middle Barrel Temperature
270 - 280 °C
Front Barrel Temperature
270 - 290 °C
Melt Temperature
270 - 290 °C
Mold Temperature
60.0 - 90.0 °C
Drying Temperature
75.0 - 85.0 °C
Dry Time
4.00 - 6.00 hour
Moisture Content
0.20 %

Descriptive Properties
UL f1
f1

Alternative products

Eurostar Staramide BG3 PA6, 15% Glass Filled, Injection Molded accurate 68%

$ 1682/MT

Density: 1.23 g/cc
Water Absorption at Saturation: 8.0 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.0045 - 0.0085 cm/cm
Hardness, Rockwell L: 110
Tensile Strength at Break: 125 MPa

BASF Styrodur® 3035 CS Extruded Rigid Polystyrene Foam (Europe) accurate 68%

$ 2271/MT

Density: 0.0330 g/cc
Water Absorption: 0.20 %
Water Absorption: <= 3.0 %
Water Vapor Transmission: 50.0 - 150 g/m²/day
Deformation: <= 5.0 % @Pressure 0.0400 MPa, Temperature 70.0 °C

Celanese Celstran® PP-GF30-02 AD 3002 PP, 30% Glass Reinforced accurate 68%

$ 2015/MT

Specific Gravity: 1.12 g/cc
Density: 1.12 g/cc
Tensile Strength at Break: 92.0 MPa
Tensile Strength at Break: 108 MPa
Tensile Strength at Break: 66.9 MPa @Temperature 93.3 °C

SABIC Innovative Plastics LNP Faradex EX06464 PEI (Asia Pacific) accurate 80%

$ 1957/MT

Specific Gravity: 1.50 g/cc
Density: 1.46 g/cc
Density: 1.46 g/cc
Linear Mold Shrinkage, Flow: 0.0055 cm/cm
Linear Mold Shrinkage, Flow: 0.0055 cm/cm @Time 86400 sec

Celanese Celstran® PP-GF30-02 AF 3001 PP, 30% Glass Reinforced accurate 68%

$ 1557/MT

Specific Gravity: 1.12 g/cc
Density: 1.12 g/cc
Tensile Strength at Break: 108 MPa
Tensile Strength at Break: 130 MPa
Tensile Strength at Break: 66.9 MPa @Temperature 93.3 °C

Eurostar Staramide AG4 PA66, 20% Glass Filled, Injection Molded accurate 80%

$ 1456/MT

Density: 1.26 g/cc
Water Absorption at Saturation: 5.5 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
Hardness, Rockwell L: 112
Tensile Strength at Break: 130 MPa

SABIC Innovative Plastics LNP LUBRICOMP DCP32 PC (Asia Pacific) accurate 68%

$ 1599/MT

Density: 1.30 g/cc
Density: 1.30 g/cc
Moisture Absorption: 0.100 %
Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0043 cm/cm @Time 86400 sec

Eurostar Staramide AG3 PA66, 15% Glass Filled, Injection Molded accurate 99%

$ 1914/MT

Density: 1.23 g/cc
Water Absorption at Saturation: 7.0 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm
Tensile Strength at Break: 125 MPa
Elongation at Break: 3.0 %

Celanese Celstran® PP-GF30-02 AD 3019 PP, 30% Glass Reinforced accurate 68%

$ 1742/MT

Specific Gravity: 1.12 g/cc
Density: 1.12 g/cc
Tensile Strength at Break: 100 MPa
Tensile Strength at Break: 108 MPa
Tensile Strength at Break: 66.9 MPa @Temperature 93.3 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, oil tanker ship sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Eurostar Staramide AG3K PA66, 15% Glass Filled, Injection Molded

Seller from Toronto – 2021-07-01:

Seller from Toronto work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1703 per MT

Seller from Karachi – 2021-04-15:

Seller from Karachi work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2121 per MT