H.C. Starck MP35N® Nickel/Cobalt/Chromium/Molybdenum Alloy

Seller in Bogotá price: $1900 per MT

H.C. Starck MP35N® Nickel/Cobalt/Chromium/Molybdenum Alloy in Nickel Alloy, Cobalt Alloy, Superalloy

  • Physical Properties
  • Density
  • 8.43 g/cc
  • Mechanical Properties
  • Hardness, Rockwell C
  • 7.0
  • Hardness, Rockwell C
  • 44
  • Hardness, Rockwell C
  • 47
  • Hardness, Vickers
  • 220
  • Hardness, Vickers
  • 420
  • Hardness, Vickers
  • 480
  • Tensile Strength, Ultimate
  • 758 MPa
  • Tensile Strength, Ultimate
  • 1520 MPa
  • Tensile Strength, Ultimate
  • 1830 MPa
  • Tensile Strength, Yield
  • 345 MPa
  • Tensile Strength, Yield
  • 1380 MPa
  • Tensile Strength, Yield
  • 1550 MPa
  • Elongation at Break
  • 3.0 %
  • Elongation at Break
  • 10 %
  • Elongation at Break
  • 60 %
  • Modulus of Elasticity
  • 201 GPa @Temperature 482 °C
  • Modulus of Elasticity
  • 201 GPa @Temperature 482 °C
  • Modulus of Elasticity
  • 216 GPa @Temperature 232 °C
  • Modulus of Elasticity
  • 219 GPa @Temperature 232 °C
  • Modulus of Elasticity
  • 233 GPa @Temperature 25.6 °C
  • Modulus of Elasticity
  • 235 GPa @Temperature 25.6 °C
  • Poissons Ratio
  • 0.38 @Temperature 232 °C
  • Poissons Ratio
  • 0.40 @Temperature 25.6 °C
  • Poissons Ratio
  • 0.42 @Temperature 482 °C
  • Poissons Ratio
  • 0.45 @Temperature 25.6 °C
  • Poissons Ratio
  • 0.46 @Temperature 232 °C
  • Poissons Ratio
  • 0.47 @Temperature 482 °C
  • Shear Modulus
  • 68.0 GPa @Temperature 482 °C
  • Shear Modulus
  • 71.0 GPa @Temperature 482 °C
  • Shear Modulus
  • 75.0 GPa @Temperature 232 °C
  • Shear Modulus
  • 78.0 GPa @Temperature 232 °C
  • Shear Modulus
  • 81.0 GPa @Temperature 25.6 °C
  • Shear Modulus
  • 83.0 GPa @Temperature 25.6 °C
  • Thermal Properties
  • CTE, linear
  • 12.8 µm/m-°C @Temperature 21.0 - 93.0 °C
  • CTE, linear
  • 13.7 µm/m-°C @Temperature 21.0 - 204 °C
  • CTE, linear
  • 14.8 µm/m-°C @Temperature 21.0 - 316 °C
  • CTE, linear
  • 14.9 µm/m-°C @Temperature 21.0 - 427 °C
  • CTE, linear
  • 15.7 µm/m-°C @Temperature 21.0 - 538 °C
  • Thermal Conductivity
  • 6.48 W/m-K @Temperature -184 °C
  • Thermal Conductivity
  • 9.08 W/m-K @Temperature -73.0 °C
  • Thermal Conductivity
  • 11.2 W/m-K @Temperature 21.0 °C
  • Thermal Conductivity
  • 12.7 W/m-K @Temperature 93.0 °C
  • Thermal Conductivity
  • 15.0 W/m-K @Temperature 204 °C
  • Thermal Conductivity
  • 17.0 W/m-K @Temperature 316 °C
  • Thermal Conductivity
  • 19.2 W/m-K @Temperature 427 °C
  • Thermal Conductivity
  • 21.3 W/m-K @Temperature 538 °C
  • Thermal Conductivity
  • 23.3 W/m-K @Temperature 649 °C
  • Melting Point
  • 1315 - 1440 °C
  • Solidus
  • 1315 °C
  • Liquidus
  • 1440 °C
  • Component Elements Properties
  • Chromium, Cr
  • 20 %
  • Cobalt, Co
  • 35 %
  • Molybdenum, Mo
  • 10 %
  • Nickel, Ni
  • 35 %
  • Electrical Properties
  • Electrical Resistivity
  • 0.0000990 ohm-cm @Temperature -184 °C
  • Electrical Resistivity
  • 0.000101 ohm-cm @Temperature -73.0 °C
  • Electrical Resistivity
  • 0.000103 ohm-cm @Temperature 21.0 °C
  • Electrical Resistivity
  • 0.000105 ohm-cm @Temperature 93.0 °C
  • Electrical Resistivity
  • 0.000108 ohm-cm @Temperature 204 °C
  • Electrical Resistivity
  • 0.000110 ohm-cm @Temperature 316 °C
  • Electrical Resistivity
  • 0.000113 ohm-cm @Temperature 427 °C
  • Electrical Resistivity
  • 0.000115 ohm-cm @Temperature 538 °C
  • Electrical Resistivity
  • 0.000118 ohm-cm @Temperature 649 °C
  • Magnetic Permeability
  • 1.00085 @Temperature 119 °C
  • Magnetic Permeability
  • 1.00092 @Temperature 25.0 °C
  • Magnetic Permeability
  • 1.00096 @Temperature -27.0 °C
  • Magnetic Permeability
  • 1.00104 @Temperature -73.0 °C
  • Magnetic Permeability
  • 1.00117 @Temperature -140 °C
  • Magnetic Permeability
  • 1.00142 @Temperature -195 °C
  • Magnetic Susceptibility
  • 8.03 @Temperature 119 °C
  • Magnetic Susceptibility
  • 8.7 @Temperature 25.0 °C
  • Magnetic Susceptibility
  • 9.22 @Temperature -27.0 °C
  • Magnetic Susceptibility
  • 9.81 @Temperature -73.0 °C
  • Magnetic Susceptibility
  • 11.07 @Temperature -140 °C
  • Magnetic Susceptibility
  • 13.47 @Temperature -195 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, passenger catamarans for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for H.C. Starck MP35N® Nickel/Cobalt/Chromium/Molybdenum Alloy

Seller from Bogotá – 2021-05-01:

Seller from Bogotá work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1900 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell H.C. Starck MP35N® Nickel/Cobalt/Chromium/Molybdenum Alloy?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or ATV repair shop in Singapore open-nearme.com