Ineos ABS Lustran® 433 ABS, General-Purpose Injection Molding Grade price 1570 per MT

Physical Properties
Specific Gravity
1.05 g/cc
Linear Mold Shrinkage
0.0040 - 0.0060 cm/cm
Melt Flow
5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
Melt Flow
12 g/10 min @Load 10.0 kg, Temperature 220 °C

Mechanical Properties
Hardness, Rockwell R
109
Tensile Strength, Yield
42.0 MPa
Elongation at Break
>= 30 %
Tensile Modulus
2.55 GPa
Flexural Yield Strength
72.0 MPa
Flexural Modulus
2.60 GPa
Izod Impact, Notched
0.640 J/cm @Thickness 3.20 mm, Temperature -40.0 °C
Izod Impact, Notched
2.08 J/cm @Thickness 12.7 mm, Temperature 23.0 °C
Izod Impact, Notched
3.75 J/cm @Thickness 3.20 mm, Temperature 23.0 °C

Thermal Properties
CTE, linear
90.0 µm/m-°C
Deflection Temperature at 0.46 MPa (66 psi)
92.0 °C @Thickness 12.7 mm
Deflection Temperature at 0.46 MPa (66 psi)
99.0 °C @Thickness 12.7 mm
Deflection Temperature at 1.8 MPa (264 psi)
85.0 °C @Thickness 12.7 mm
Deflection Temperature at 1.8 MPa (264 psi)
94.0 °C @Thickness 12.7 mm
Deflection Temperature at 1.8 MPa (264 psi)
102 °C @Thickness 12.7 mm
Vicat Softening Point
106 °C
Flammability, UL94
HB @Thickness 1.50 mm
Flammability, UL94
HB @Thickness 3.00 mm

Processing Properties
Rear Barrel Temperature
235 - 249 °C
Middle Barrel Temperature
241 - 254 °C
Front Barrel Temperature
246 - 260 °C
Nozzle Temperature
246 - 260 °C
Melt Temperature
246 - 274 °C
Mold Temperature
43.0 - 66.0 °C
Drying Temperature
71.0 - 77.0 °C @Time 14400 sec
Drying Temperature
82.0 - 88.0 °C @Time 7200 sec
Moisture Content
<= 0.10 %
Dew Point
<= -29.0 °C
Injection Pressure
68.9 - 110 MPa
Back Pressure
0.000 - 0.172 MPa
Clamp Pressure
30.8 - 61.6 MPa
Cushion
<= 0.635 cm

Descriptive Properties
Hold Pressure
50-75% of Injection Pressure, Injection Molding
Injection Speed
High
Screw Compression Ratio
2.5:1
Screw Length-to-Diameter Ratio
>= 20:1
Screw Speed
Moderate, Injection Molding
Shot Weight-to-Machine Capacity Ratio
0.5-0.75

Alternative products

Ineos ABS Lustran® 633 ABS, Injection Molding Grade accurate 72%

$ 1941/MT

Density: 1.05 g/cc
Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
Melt Flow: 4.5 g/10 min @Load 3.80 kg, Temperature 230 °C
Melt Flow: 14.5 g/10 min @Load 10.0 kg, Temperature 230 °C
Hardness, Rockwell R: 109

Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded (discontinued **) accurate 66%

$ 1589/MT

Specific Gravity: 1.13 g/cc
Specific Gravity: 1.15 g/cc
Moisture Absorption at Equilibrium: 0.70 %
Tensile Strength at Break: 55.0 MPa
Tensile Strength at Break: 31.0 MPa @Temperature 100 °C

Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded (discontinued **) accurate 66%

$ 2169/MT

Specific Gravity: 1.13 g/cc
Specific Gravity: 1.15 g/cc
Moisture Absorption at Equilibrium: 0.70 %
Tensile Strength at Break: 55.0 MPa
Tensile Strength at Break: 31.0 MPa @Temperature 100 °C

Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded (discontinued **) accurate 66%

$ 2396/MT

Specific Gravity: 1.13 g/cc
Specific Gravity: 1.15 g/cc
Moisture Absorption at Equilibrium: 0.70 %
Tensile Strength at Break: 55.0 MPa
Tensile Strength at Break: 31.0 MPa @Temperature 100 °C

Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded (discontinued **) accurate 66%

$ 1948/MT

Specific Gravity: 1.13 g/cc
Specific Gravity: 1.15 g/cc
Moisture Absorption at Equilibrium: 0.70 %
Tensile Strength at Break: 55.0 MPa
Tensile Strength at Break: 31.0 MPa @Temperature 100 °C

Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded (discontinued **) accurate 66%

$ 2526/MT

Specific Gravity: 1.13 g/cc
Specific Gravity: 1.15 g/cc
Moisture Absorption at Equilibrium: 0.70 %
Tensile Strength at Break: 55.0 MPa
Tensile Strength at Break: 31.0 MPa @Temperature 100 °C

Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded (discontinued **) accurate 66%

$ 2525/MT

Specific Gravity: 1.13 g/cc
Specific Gravity: 1.15 g/cc
Moisture Absorption at Equilibrium: 0.70 %
Tensile Strength at Break: 55.0 MPa
Tensile Strength at Break: 31.0 MPa @Temperature 100 °C

Ineos ABS Lustran® 308 ABS, Medical Grade accurate 66%

$ 1889/MT

Density: 1.06 g/cc
Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
Melt Flow: 7.0 g/10 min @Load 3.80 kg, Temperature 230 °C
Melt Flow: 21 g/10 min @Load 10.0 kg, Temperature 220 °C
Hardness, Rockwell R: 105

SABIC Innovative Plastics NORYL HN731A PPE+PS accurate 59%

$ 1875/MT

Specific Gravity: 1.06 g/cc
Density: 1.06 g/cc
Water Absorption: 0.060 % @Time 86400 sec
Moisture Absorption: 0.0600 %
Water Absorption at Saturation: 0.23 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Ineos ABS Lustran® 433 ABS, General-Purpose Injection Molding Grade

Seller from Chennai – 2021-07-22:

Seller from Chennai work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2066 per MT

Seller from Philadelphia – 2021-03-14:

Seller from Philadelphia work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $1570 per MT