$ 1550/MT
- Density: 1.05 g/cc
- Melt Flow: 6.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 230 °C
- Tensile Strength, Yield: 38.0 MPa
- Tensile Modulus: 2.00 GPa
$ 1652/MT
- Density: 1.07 g/cc
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Break: 3.0 %
- Elongation at Yield: 3.0 %
- Tensile Modulus: 3.24 GPa
$ 2136/MT
- Density: 1.05 g/cc
- Melt Flow: 7.2 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 42.9 MPa
- Elongation at Break: 35 %
- Elongation at Yield: 4.0 %
$ 2012/MT
- Density: 1.06 g/cc
- Water Absorption: 0.30 %
- Melt Flow: 19 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 40.0 MPa
- Elongation at Break: 30 %
$ 1526/MT
- Density: 1.06 g/cc
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 41.3 MPa
- Elongation at Break: 25 %
- Elongation at Yield: 3.3 %
$ 1941/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 4.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 14.5 g/10 min @Load 10.0 kg, Temperature 230 °C
- Hardness, Rockwell R: 109
$ 1912/MT
- Density: 1.06 g/cc
- Hardness, Rockwell R: 80
- Tensile Strength, Ultimate: 32.0 MPa
- Tensile Strength, Yield: 37.0 MPa
- Elongation at Break: 90 %
$ 1746/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 33.0 MPa
$ 1797/MT
- Density: 1.04 g/cc
- Melt Flow: 17 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 46.0 MPa
- Elongation at Yield: 2.6 %
- Tensile Modulus: 2.50 GPa
$ 1448/MT
- Melt Flow: 14 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength at Break: 68.9 MPa
- Flexural Strength: 75.8 MPa
- Flexural Modulus: 3.45 GPa
- Izod Impact, Unnotched: 3.20 J/cm
$ 1933/MT
- Density: 1.06 g/cc
- Melt Flow: 19 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 46.3 MPa
- Elongation at Break: 19 %
- Elongation at Yield: 3.5 %
$ 1855/MT
- Density: 1.05 g/cc
- Melt Flow: 34 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 44.0 MPa
- Elongation at Yield: 2.4 %
- Tensile Modulus: 2.30 GPa
$ 1887/MT
- Viscosity Measurement: 0.35
- Molecular Weight: 120000 g/mol
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Glass Transition Temp, Tg: 150 °C
- Haze: 2.5 %
$ 1914/MT
- Density: 1.06 g/cc
- Water Absorption: 2.0 %
- Moisture Absorption at Equilibrium: 2.0 %
- Water Absorption at Saturation: 2.0 %
- Linear Mold Shrinkage: 0.010 cm/cm
$ 1571/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0030 cm/cm
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength at Break: 88.0 MPa
- Elongation at Break: 5.0 %
$ 1524/MT
- Density: 1.05 g/cc
- Melt Flow: 3.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 35.1 MPa
- Elongation at Break: 29 %
- Elongation at Yield: 3.3 %
$ 1897/MT
- Density: 1.04 g/cc
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 41.0 MPa
- Elongation at Yield: 2.7 %
- Tensile Modulus: 2.15 GPa
$ 2094/MT
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0080 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 105 MPa
- Tensile Strength, Yield: 45.0 MPa
$ 1535/MT
- Density: 0.995 g/cc
- Density: 1.17 g/cc
- Water Absorption: 3.8 %
- Moisture Absorption at Equilibrium: 1.3 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
$ 1664/MT
- Density: 1.05 g/cc
- Melt Flow: 15 g/10 min @Load 10.0 kg, Temperature 290 °C
- Tensile Strength, Yield: 39.0 MPa
- Tensile Modulus: 2.50 GPa
- Izod Impact, Notched: 0.800 J/cm @Thickness 3.20 mm, Temperature -30.0 °C
$ 2554/MT
- Density: 0.995 g/cc
- Density: 1.17 g/cc
- Water Absorption: 3.8 %
- Moisture Absorption at Equilibrium: 1.3 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
$ 1503/MT
- Density: 1.06 g/cc
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Modulus: 1.52 GPa
- Charpy Impact, Notched: 1.00 J/cm²
- CTE, linear, Parallel to Flow: 97.0 µm/m-°C @Temperature 20.0 °C
$ 2335/MT
- Density: 1.05 g/cc
- Melt Flow: 26 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 47.0 MPa
- Elongation at Yield: 2.5 %
- Tensile Modulus: 2.40 GPa
$ 2153/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 115
- Tensile Strength at Break: 35.0 MPa
$ 1729/MT
- Density: 0.900 g/cc
- Density: 1.06 g/cc
- Water Absorption: 6.0 %
- Moisture Absorption at Equilibrium: 1.7 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 2049/MT
- Tensile Strength, Yield: 34.0 MPa
- Tensile Modulus: 2.00 GPa
- Flexural Yield Strength: 61.0 MPa
- Flexural Modulus: 2.00 GPa
- Izod Impact, Notched: 0.910 J/cm @Thickness 3.20 mm, Temperature -40.0 °C
$ 1592/MT
- Density: 1.07 g/cc
- Melt Flow: 21 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 59.0 MPa
- Elongation at Break: 3.0 %
- Elongation at Yield: 3.0 %
$ 1823/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 108
- Tensile Strength at Break: 30.0 MPa
$ 1929/MT
- Density: 1.05 g/cc
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 36.5 MPa
- Elongation at Break: 14 %
- Elongation at Yield: 3.3 %
$ 1807/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
- Ball Indentation Hardness: 85.0 MPa
$ 2275/MT
- Density: 1.05 g/cc
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 45.4 MPa
- Elongation at Break: 25 %
- Elongation at Yield: 3.6 %
$ 1464/MT
- Density: 1.04 g/cc
- Melt Flow: 18 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 42.4 MPa
- Elongation at Break: 33 %
- Elongation at Yield: 3.3 %
$ 1516/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0080 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 65.0 MPa
$ 2034/MT
- Density: 1.05 g/cc
- Melt Flow: 33 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 46.0 MPa
- Elongation at Yield: 2.6 %
- Tensile Modulus: 2.40 GPa
$ 1673/MT
- Density: 1.05 g/cc
- Tensile Strength, Yield: 45.0 MPa
- Tensile Modulus: 2.10 GPa
- Izod Impact, Notched: 1.87 J/cm @Thickness 3.20 mm, Temperature -30.0 °C
- Izod Impact, Notched: 3.74 J/cm @Thickness 3.20 mm, Temperature 23.0 °C
$ 1778/MT
- Specific Gravity: 1.07 g/cc
- Density: 1.08 g/cc
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 230 °C
- Tensile Strength, Yield: 32.0 MPa
- Tensile Modulus: 1.40 GPa
$ 1753/MT
- Density: 1.11 g/cc
- Filler Content: 8 %
- Water Absorption: 1.3 %
- Water Absorption at Saturation: 3.9 %
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm
$ 2345/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0040 cm/cm
- Melt Flow: 19 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength at Break: 74.0 MPa
- Elongation at Break: 5.0 %
$ 1646/MT
- Density: 1.05 g/cc
- Tensile Strength, Yield: 31.0 MPa
- Elongation at Break: 40 %
- Elongation at Yield: 3.5 %
- Tensile Modulus: 1.52 GPa
$ 1570/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 109
$ 1645/MT
- Specific Gravity: 1.06 g/cc
- Hardness, Rockwell R: 82
- Tensile Strength at Break: 28.3 MPa
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Break: 100 %
$ 2293/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Melt Flow: 27 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 113
- Tensile Strength at Break: 34.0 MPa
$ 1475/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Melt Flow: 12 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 75
- Tensile Strength, Ultimate: 62.0 MPa
$ 1628/MT
- Density: 1.04 g/cc
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Yield: 2.6 %
- Tensile Modulus: 2.40 GPa
$ 1802/MT
- Density: 1.03 g/cc
- Melt Flow: 17 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 48.3 MPa
- Elongation at Break: 25 %
- Elongation at Yield: 3.6 %
$ 1531/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 114
- Tensile Strength at Break: 37.0 MPa
$ 1577/MT
- Density: 1.055 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 106 MPa
$ 2077/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0035 cm/cm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Elongation at Break: 1.2 %
- Tensile Modulus: 11.0 GPa
$ 1526/MT
- Density: 1.05 g/cc
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 11 g/10 min @Load 10.0 kg, Temperature 230 °C
- Tensile Strength, Yield: 37.0 MPa
- Tensile Modulus: 2.00 GPa
$ 1572/MT
- Density: 1.06 g/cc
- Hardness, Rockwell R: 95
- Tensile Strength, Ultimate: 39.0 MPa
- Tensile Strength, Yield: 43.0 MPa
- Elongation at Break: 150 %
$ 1608/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.05 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Water Absorption at Saturation: 4.3 %
- Linear Mold Shrinkage: 0.0090 cm/cm
$ 1465/MT
- Specific Gravity: 1.07 g/cc
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 98
- Tensile Strength at Break: 29.1 MPa
- Tensile Strength at Break: 31.0 MPa
$ 1889/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 7.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 21 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 105
$ 1954/MT
- Density: 1.05 g/cc
- Melt Flow: 5.2 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 37.0 MPa
- Elongation at Break: 29 %
- Elongation at Yield: 3.4 %
$ 1467/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 30.0 MPa
- Elongation at Break: 190 %
$ 2008/MT
- Density: 1.05 g/cc
- Melt Flow: 13 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 39.3 MPa
- Elongation at Break: 25 %
- Elongation at Yield: 3.5 %
$ 2465/MT
- Density: 1.05 g/cc
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Yield: 2.9 %
- Tensile Modulus: 2.60 GPa
$ 1662/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Melt Flow: 16 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 33.0 MPa
$ 1601/MT
- Density: 1.04 g/cc
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 48.0 MPa
- Elongation at Yield: 2.6 %
- Tensile Modulus: 2.55 GPa
$ 1956/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 30 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength at Break: 38.0 MPa
- Tensile Modulus: 2.80 GPa
$ 2018/MT
- Density: 1.04 g/cc
- Melt Flow: 17 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 48.2 MPa
- Elongation at Break: 25 %
- Elongation at Yield: 3.5 %
$ 2012/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 6.0 g/10 min
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 42.1 MPa
$ 1717/MT
- Density: 1.11 g/cc
- Filler Content: 8 %
- Water Absorption: 1.3 %
- Water Absorption at Saturation: 3.9 %
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm
$ 2040/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
- Tensile Strength at Break: 31.0 MPa
$ 1541/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0040 cm/cm
- Melt Flow: 23 g/10 min @Load 10.0 kg, Temperature 220 °C
- Elongation at Break: 3.2 %
- Tensile Modulus: 3.70 GPa
$ 2453/MT
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0090 cm/cm
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 74.0 MPa
- Tensile Strength at Break: 29.0 MPa
$ 1608/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0080 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 100 MPa
$ 1448/MT
- Density: 1.05 g/cc
- Melt Flow: 13 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Yield: 2.5 %
- Tensile Modulus: 2.30 GPa
$ 1468/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 4.4 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 107
- Tensile Strength, Yield: 42.7 MPa
$ 1470/MT
- Density: 1.06 g/cc
- Water Absorption: 0.40 % @Time 86400 sec
- Melt Flow: 9.2 g/10 min @Load 10.0 kg, Temperature 230 °C
- Hardness, Rockwell R: 113
- Tensile Strength, Yield: 22.1 MPa @Temperature 71.0 °C
$ 1472/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Melt Flow: 28 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 112
- Tensile Strength at Break: 34.0 MPa
$ 2324/MT
- Density: 1.05 g/cc
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 35.8 MPa
- Elongation at Break: 14 %
- Elongation at Yield: 3.3 %
$ 1578/MT
- Density: 1.05 g/cc
- Melt Flow: 5.7 g/10 min @Load 10.0 kg, Temperature 230 °C
- Hardness, Rockwell R: 111
- Tensile Strength, Yield: 36.0 MPa
- Tensile Modulus: 1.70 GPa
$ 1512/MT
- Density: 1.05 g/cc
- Water Absorption: 2.0 %
- Moisture Absorption at Equilibrium: 2.0 %
- Water Absorption at Saturation: 2.0 %
- Linear Mold Shrinkage: 0.0045 cm/cm
$ 1490/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0045 cm/cm
- Hardness, Rockwell R: 69
- Tensile Strength, Ultimate: 32.0 MPa
- Tensile Strength, Yield: 27.0 MPa
$ 1857/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Melt Flow: 30 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 90.0 MPa
$ 1493/MT
- Density: 1.05 g/cc
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 51.0 MPa
- Elongation at Yield: 2.8 %
- Tensile Modulus: 2.70 GPa
$ 1589/MT
- Tensile Strength, Yield: 42.7 MPa
- Tensile Modulus: 2.69 GPa
- Izod Impact, Notched: 2.14 J/cm
- Melt Instron Rheology (lb): 380
$ 2568/MT
- Density: 0.900 g/cc
- Density: 1.06 g/cc
- Water Absorption: 6.0 %
- Moisture Absorption at Equilibrium: 1.7 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 2475/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.05 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Water Absorption at Saturation: 4.3 %
- Linear Mold Shrinkage: 0.0090 cm/cm
$ 1791/MT
- Density: 1.05 g/cc
- Melt Flow: 19 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 47.0 MPa
- Elongation at Yield: 2.5 %
- Tensile Modulus: 2.40 GPa
$ 2392/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 112
- Tensile Strength at Break: 34.0 MPa
$ 1657/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 0.70 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 5.2 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 230 °C
$ 1602/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
- Ball Indentation Hardness: 100 MPa
$ 1694/MT
- Density: 1.11 g/cc
- Water Absorption: 3.9 %
- Moisture Absorption at Equilibrium: 1.3 %
- Melt Flow: 9.0 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 39.0 MPa
$ 1556/MT
- Density: 1.04 g/cc
- Melt Flow: 16 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 46.0 MPa
- Elongation at Yield: 2.5 %
- Tensile Modulus: 2.40 GPa
$ 1661/MT
- Tensile Strength, Yield: 31.0 MPa
- Elongation at Break: 40 %
- Elongation at Yield: 3.5 %
- Tensile Modulus: 1.52 GPa
$ 1472/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Melt Flow: 25 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength at Break: 58.0 MPa
- Tensile Modulus: 4.71 GPa
$ 2199/MT
- Density: 0.900 g/cc
- Density: 1.06 g/cc
- Water Absorption: 6.0 %
- Moisture Absorption at Equilibrium: 1.7 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
Delivery Polymer Ineos ABS
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
small lng carrier for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.