Ineos ABS Lustran® LK197 ABS, Extrusion Grade price 1470 per MT

Physical Properties
Density
1.06 g/cc
Water Absorption
0.40 % @Time 86400 sec
Melt Flow
9.2 g/10 min @Load 10.0 kg, Temperature 230 °C

Mechanical Properties
Hardness, Rockwell R
113
Tensile Strength, Yield
22.1 MPa @Temperature 71.0 °C
Tensile Strength, Yield
40.0 MPa @Temperature 23.0 °C
Tensile Strength, Yield
59.3 MPa @Temperature -18.0 °C
Tensile Modulus
1.50 GPa @Temperature 71.0 °C
Tensile Modulus
2.30 GPa @Temperature 23.0 °C
Tensile Modulus
2.60 GPa @Temperature -18.0 °C
Flexural Yield Strength
49.6 MPa @Temperature 71.0 °C
Flexural Yield Strength
63.4 MPa @Temperature 23.0 °C
Flexural Yield Strength
113.8 MPa @Temperature -40.0 °C
Flexural Modulus
1.90 GPa @Temperature 71.0 °C
Flexural Modulus
2.50 GPa @Temperature 23.0 °C
Flexural Modulus
2.80 GPa @Temperature -40.0 °C
Izod Impact, Notched
0.910 J/cm @Thickness 3.20 mm, Temperature -40.0 °C
Izod Impact, Notched
1.33 J/cm @Thickness 3.20 mm, Temperature -18.0 °C
Izod Impact, Notched
2.40 J/cm @Thickness 3.20 mm, Temperature 23.0 °C
Impact Test
11.0 J @Temperature -40.0 °C
Impact Test
14.0 J @Temperature -40.0 °C
Impact Test
19.0 J @Temperature -18.0 °C
Impact Test
22.0 J @Temperature 23.0 °C
Impact Test
24.0 J @Temperature -18.0 °C
Impact Test
30.0 J @Temperature 23.0 °C

Thermal Properties
CTE, linear
90.0 µm/m-°C
Deflection Temperature at 0.46 MPa (66 psi)
93.0 °C
Deflection Temperature at 0.46 MPa (66 psi)
101 °C
Deflection Temperature at 1.8 MPa (264 psi)
85.0 °C
Deflection Temperature at 1.8 MPa (264 psi)
94.0 °C
UL RTI, Electrical
60.0 °C @Thickness 1.50 mm
UL RTI, Mechanical with Impact
60.0 °C @Thickness 1.50 mm
UL RTI, Mechanical without Impact
60.0 °C @Thickness 1.50 mm
Flammability, UL94
HB @Thickness 1.47 mm
Flame Spread
35.6 mm/min @Thickness 3.20 mm

Optical Properties
Gloss
90 %

Processing Properties
Rear Barrel Temperature
215 - 240 °C
Middle Barrel Temperature
215 - 240 °C
Front Barrel Temperature
215 - 240 °C
Die Temperature
210 - 240 °C
Melt Temperature
215 - 249 °C
Roll Temperature
63.0 - 85.0 °C
Roll Temperature
71.0 - 93.0 °C
Roll Temperature
77.0 - 99.0 °C
Roll Temperature
82.0 - 105 °C
Roll Temperature
82.0 - 105 °C
Roll Temperature
82.0 - 105 °C
Drying Temperature
82.0 - 93.0 °C @Time 10800 - 14400 sec
Moisture Content
<= 0.030 %
Dew Point
<= -29.0 °C

Descriptive Properties
Pump Ratio
1.5-2.0
Screw Compression Ratio
2.5-2.7

Alternative products

LG Chemical B240 EPS, Non-Flame Retardant accurate 35%

$ 1551/MT

Water Absorption: 0.45 %
Water Absorption: 0.50 %
Water Absorption: 0.75 %
Water Absorption: 0.83 %
Flexural Yield Strength: 0.186 MPa

Thermal Ceramics Cerafelt accurate 54%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

Axion Polymers Axpoly® PP06 5001 Enhanced Black General Purpose Polypropylene accurate 35%

$ 2010/MT

Density: 0.930 g/cc
Density: 0.922 - 1.00 g/cc
Particle Size: 2000 - 4000 µm
Particle Size: 3000 µm
Melt Index of Compound: 12 g/10 min @Load 2.16 kg, Temperature 230 °C

DuPont Performance Polymers Zytel® 7301 NC010 Nylon 6 (Unverified Data**) accurate 35%

$ 2395/MT

Specific Gravity: 1.13 g/cc
Density: 1.13 g/cc
Water Absorption: 3.0 % @Temperature 23.0 °C
Water Absorption: 9.5 % @Temperature 23.0 °C
Linear Mold Shrinkage: 0.010 cm/cm @Thickness 3.00 mm

Thermal Ceramics Pyro-Packing R accurate 35%

$ 1496/MT

Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.240 g/cc
Thermal Conductivity: 0.0706 W/m-K @Temperature 260 °C

SABIC Innovative Plastics LNP THERMOCOMP TF006 PU accurate 35%

$ 2545/MT

Density: 1.47 g/cc
Density: 1.47 g/cc
Moisture Absorption: 0.360 %
Moisture Absorption: 0.500 %
Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Time 86400 sec

Bhansali Engineering Abstron IM-11 ABS Injection Molding Grade accurate 35%

$ 2086/MT

Density: 1.045 g/cc
Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
Hardness, Rockwell R: 113
Tensile Strength, Yield: 43.1 MPa @Thickness 3.20 mm

Thermal Ceramics Superwool 607 Max Blanket accurate 35%

$ 1545/MT

Density: 0.0640 g/cc
Density: 0.0960 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Thermal Conductivity: 0.0605 W/m-K @Temperature 260 °C

Propex Fabrics Curv™ C100A Polypropylene/Polypropylene Thermoformable Composite accurate 44%

$ 2111/MT

Density: 0.920 g/cc
Density: 0.920 g/cc
Water Absorption: <= 0.10 %
Water Absorption: <= 0.10 %
Water Absorption: <= 0.10 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lpg tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Ineos ABS Lustran® LK197 ABS, Extrusion Grade

Seller from Hong Kong – 2021-07-19:

Seller from Hong Kong work with company: Techmer ES, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1470 per MT

Seller from Rio de Janeiro – 2021-06-17:

Seller from Rio de Janeiro work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2276 per MT