Lanxess Durethan® A 30 000000 Nylon 66 price 1531 per MT

Physical Properties
Density
1.14 g/cc
Water Absorption
8.5 %
Moisture Absorption at Equilibrium
2.8 %
Viscosity Test
144 cm³/g
Melt Flow
68 g/10 min @Load 5.00 kg, Temperature 270 °C

Mechanical Properties
Tensile Strength, Yield
55.0 MPa
Tensile Strength, Yield
85.0 MPa
Elongation at Break
>= 50 %
Elongation at Yield
4.5 %
Elongation at Yield
20 %
Tensile Modulus
1.30 GPa
Tensile Modulus
3.20 GPa
Charpy Impact Unnotched
NB
Charpy Impact Unnotched
NB @Temperature -30.0 °C
Charpy Impact Unnotched
NB @Temperature 23.0 °C
Charpy Impact Unnotched
NB @Temperature 23.0 °C
Charpy Impact, Notched
<= 1.00 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
<= 1.00 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
<= 1.00 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
2.00 J/cm² @Temperature 23.0 °C
Puncture Energy
108 J
Puncture Energy
19.0 J @Temperature -30.0 °C
Puncture Energy
19.0 J @Temperature -30.0 °C
Tensile Creep Modulus, 1 hour
1000 MPa
Tensile Creep Modulus, 1000 hours
700 MPa

Thermal Properties
CTE, linear, Parallel to Flow
90.0 µm/m-°C
CTE, linear, Transverse to Flow
100 µm/m-°C
Melting Point
263 °C
Deflection Temperature at 0.46 MPa (66 psi)
225 °C
Deflection Temperature at 1.8 MPa (264 psi)
70.0 °C
Deflection Temperature at 8.0 MPa
50.0 °C
Vicat Softening Point
230 °C
Flammability, UL94
V-2 @Thickness 1.60 mm
Flammability, UL94
V-2 @Thickness 3.20 mm
Oxygen Index
27 %

Electrical Properties
Volume Resistivity
1.00e+12 ohm-cm
Volume Resistivity
1.00e+15 ohm-cm
Surface Resistance
1.00e+14 ohm
Dielectric Constant
3.4 @Frequency 1.00e+6 Hz
Dielectric Constant
3.8 @Frequency 100 Hz
Dielectric Constant
4.0 @Frequency 1.00e+6 Hz
Dielectric Constant
10 @Frequency 100 Hz
Dielectric Strength
30.0 kV/mm
Dielectric Strength
35.0 kV/mm
Dissipation Factor
0.0090 @Frequency 100 Hz
Dissipation Factor
0.020 @Frequency 1.00e+6 Hz
Dissipation Factor
0.090 @Frequency 1.00e+6 Hz
Dissipation Factor
0.20 @Frequency 100 Hz
Comparative Tracking Index
600 V

Descriptive Properties
Additives
Release agent
Form
Pellets
ISO Shortname
ISO 1874-PA 66,MR,14-030
Processing
Injection molding
Region
Asia Pacific
Region
Europe
Region
Near East/Africa
Region
North America
Region
South and Central America

Alternative products

Lanxess Durethan® BC 304 H3.0 000000 Nylon 6 accurate 57%

$ 1564/MT

Density: 1.06 g/cc
Water Absorption: 7.5 %
Moisture Absorption at Equilibrium: 2.2 %
Tensile Strength, Yield: 35.0 MPa
Tensile Strength, Yield: 45.0 MPa

Lanxess Durethan® A 30 S 000000 Nylon 66 accurate 57%

$ 1939/MT

Density: 1.136 g/cc
Water Absorption: 8.5 %
Moisture Absorption at Equilibrium: 2.8 %
Viscosity Test: 144 cm³/g
Melt Flow: 75 g/10 min @Load 5.00 kg, Temperature 270 °C

Lanxess Durethan® A 30 H2.0 901510 Nylon 66 accurate 49%

$ 1534/MT

Density: 1.14 g/cc
Water Absorption: 8.0 %
Moisture Absorption at Equilibrium: 2.6 %
Viscosity Test: 144 cm³/g
Melt Flow: 148 g/10 min @Load 5.00 kg, Temperature 280 °C

Lanxess Durethan® AKV 15 H2.0 901510 Nylon 66, 15% Glass Fiber accurate 41%

$ 1858/MT

Density: 1.23 g/cc
Water Absorption: 7.0 %
Moisture Absorption at Equilibrium: 2.4 %
Viscosity Test: 146 cm³/g
Tensile Strength at Break: 90.0 MPa

Lanxess Durethan® B 31 SK 000000 Nylon 6 accurate 57%

$ 1577/MT

Density: 1.14 g/cc
Water Absorption: 10 %
Moisture Absorption at Equilibrium: 3.0 %
Viscosity Test: 138 cm³/g
Melt Flow: 99 g/10 min @Load 5.00 kg, Temperature 260 °C

Lanxess Durethan® BC 40 SR2 000000 Nylon 6 accurate 57%

$ 1785/MT

Density: 1.10 g/cc
Water Absorption: 9.0 %
Moisture Absorption at Equilibrium: 2.7 %
Melt Flow: 27 g/10 min @Load 5.00 kg, Temperature 260 °C
Tensile Strength, Yield: 40.0 MPa

Lanxess Durethan® AC 30 000000 Nylon 66 accurate 57%

$ 1465/MT

Density: 1.10 g/cc
Water Absorption: 8.0 %
Moisture Absorption at Equilibrium: 2.5 %
Tensile Strength, Yield: 48.0 MPa
Tensile Strength, Yield: 80.0 MPa

DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66 (Unverified Data**) accurate 53%

$ 1463/MT

Density: 1.01 g/cc
Density: 1.14 g/cc
Water Absorption: 8.5 % @Thickness 2.00 mm
Moisture Absorption: 2.60 % @Thickness 2.00 mm
Viscosity: 42210 cP @Shear Rate 5000 1/s, Temperature 295 °C

Lanxess Durethan® B 30 S 000000 Nylon 6 accurate 45%

$ 2013/MT

Density: 1.14 g/cc
Water Absorption: 10 %
Moisture Absorption at Equilibrium: 3.0 %
Viscosity Test: 134 cm³/g
Melt Flow: 102 g/10 min @Load 5.00 kg, Temperature 260 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng carrier for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Lanxess Durethan® A 30 000000 Nylon 66

Seller from Porto Alegre – 2021-07-21:

Seller from Porto Alegre work with company: 3M, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2322 per MT

Seller from Melbourne – 2021-08-02:

Seller from Melbourne work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1531 per MT