Lanxess Durethan® AC 30 000000 Nylon 66 price 1465 per MT

Physical Properties
Density
1.10 g/cc
Water Absorption
8.0 %
Moisture Absorption at Equilibrium
2.5 %

Mechanical Properties
Tensile Strength, Yield
48.0 MPa
Tensile Strength, Yield
80.0 MPa
Elongation at Break
14 %
Elongation at Break
>= 50 %
Elongation at Yield
5.0 %
Elongation at Yield
21 %
Tensile Modulus
1.20 GPa
Tensile Modulus
2.90 GPa
Charpy Impact Unnotched
20.0 J/cm² @Temperature -30.0 °C
Charpy Impact Unnotched
NB @Temperature -30.0 °C
Charpy Impact Unnotched
NB @Temperature 23.0 °C
Charpy Impact Unnotched
NB @Temperature 23.0 °C
Charpy Impact, Notched
<= 1.00 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
<= 1.00 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
1.00 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
1.50 J/cm² @Temperature 23.0 °C
Impact
4314
Impact
5050
Impact
5977 @Temperature -30.0 °C
Puncture Energy
26.0 J
Puncture Energy
32.0 J
Puncture Energy
33.0 J @Temperature -30.0 °C
Puncture Energy
33.0 J @Temperature -30.0 °C
Tensile Creep Modulus, 1 hour
1100 MPa
Tensile Creep Modulus, 1000 hours
800 MPa

Thermal Properties
CTE, linear, Parallel to Flow
90.0 µm/m-°C
CTE, linear, Transverse to Flow
110 µm/m-°C
Melting Point
260 °C
Deflection Temperature at 0.46 MPa (66 psi)
160 °C
Deflection Temperature at 1.8 MPa (264 psi)
70.0 °C
Deflection Temperature at 8.0 MPa
53.0 °C
Vicat Softening Point
200 °C
Flammability, UL94
HB @Thickness 1.60 mm
Flammability, UL94
HB @Thickness 3.20 mm
Oxygen Index
21 %

Electrical Properties
Volume Resistivity
1.00e+13 ohm-cm
Volume Resistivity
1.00e+15 ohm-cm
Surface Resistance
1.00e+14 ohm
Dielectric Constant
3.4 @Frequency 1.00e+6 Hz
Dielectric Constant
3.6 @Frequency 100 Hz
Dielectric Constant
3.8 @Frequency 1.00e+6 Hz
Dielectric Constant
7.0 @Frequency 100 Hz
Dielectric Strength
30.0 kV/mm
Dielectric Strength
30.0 kV/mm
Dissipation Factor
0.0090 @Frequency 100 Hz
Dissipation Factor
0.020 @Frequency 1.00e+6 Hz
Dissipation Factor
0.070 @Frequency 1.00e+6 Hz
Dissipation Factor
0.14 @Frequency 100 Hz
Comparative Tracking Index
600 V

Descriptive Properties
Additives
Release agent
Features
High impact or high impact modified
Form
Pellets
ISO Shortname
ISO 1874-PA 66-I, MR, -030
Processing
Injection molding
Region
Asia Pacific
Region
Europe
Region
Near East/Africa
Region
North America
Region
South and Central America

Alternative products

Covestro Makroblend® DP UT6003 Polycarbonate + PBT, Impact Grade accurate 42%

$ 1844/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 260 °C
Water Absorption: 0.50 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 18 g/10 min @Load 5.00 kg, Temperature 260 °C

Lanxess Durethan® BC 304 H3.0 000000 Nylon 6 accurate 45%

$ 1564/MT

Density: 1.06 g/cc
Water Absorption: 7.5 %
Moisture Absorption at Equilibrium: 2.2 %
Tensile Strength, Yield: 35.0 MPa
Tensile Strength, Yield: 45.0 MPa

Covestro Makroblend® DP UT6005 Polycarbonate + PBT, Impact Grade accurate 42%

$ 1557/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 260 °C
Water Absorption: 0.50 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 18 g/10 min @Load 5.00 kg, Temperature 260 °C

Lanxess Durethan® A 30 S 000000 Nylon 66 accurate 49%

$ 1939/MT

Density: 1.136 g/cc
Water Absorption: 8.5 %
Moisture Absorption at Equilibrium: 2.8 %
Viscosity Test: 144 cm³/g
Melt Flow: 75 g/10 min @Load 5.00 kg, Temperature 270 °C

Lanxess Durethan® A 30 000000 Nylon 66 accurate 53%

$ 1531/MT

Density: 1.14 g/cc
Water Absorption: 8.5 %
Moisture Absorption at Equilibrium: 2.8 %
Viscosity Test: 144 cm³/g
Melt Flow: 68 g/10 min @Load 5.00 kg, Temperature 270 °C

Lanxess Durethan® B 31 SK 000000 Nylon 6 accurate 56%

$ 1577/MT

Density: 1.14 g/cc
Water Absorption: 10 %
Moisture Absorption at Equilibrium: 3.0 %
Viscosity Test: 138 cm³/g
Melt Flow: 99 g/10 min @Load 5.00 kg, Temperature 260 °C

DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66 (Unverified Data**) accurate 45%

$ 1463/MT

Density: 1.01 g/cc
Density: 1.14 g/cc
Water Absorption: 8.5 % @Thickness 2.00 mm
Moisture Absorption: 2.60 % @Thickness 2.00 mm
Viscosity: 42210 cP @Shear Rate 5000 1/s, Temperature 295 °C

Covestro Makroblend® DP UT6007 Polycarbonate + PBT, Impact Grade accurate 42%

$ 2178/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 260 °C
Water Absorption: 0.50 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 18 g/10 min @Load 5.00 kg, Temperature 260 °C

Lanxess Durethan® B 30 S 000000 Nylon 6 accurate 60%

$ 2013/MT

Density: 1.14 g/cc
Water Absorption: 10 %
Moisture Absorption at Equilibrium: 3.0 %
Viscosity Test: 134 cm³/g
Melt Flow: 102 g/10 min @Load 5.00 kg, Temperature 260 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng carrier for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Lanxess Durethan® AC 30 000000 Nylon 66

Seller from Hong Kong – 2021-05-28:

Seller from Hong Kong work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2407 per MT

Seller from Kolkata – 2021-04-22:

Seller from Kolkata work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1465 per MT