Lanxess Pocan® B 3225 000000 PBT, 20% Glass Fiber price 1839 per MT

Physical Properties
Density
1.46 g/cc
Water Absorption
0.40 %
Moisture Absorption at Equilibrium
0.20 %
Viscosity Test
100 cm³/g
Melt Flow
26 g/10 min @Load 2.16 kg, Temperature 260 °C

Mechanical Properties
Tensile Strength at Break
120 MPa
Elongation at Break
2.6 %
Tensile Modulus
7.00 GPa
Charpy Impact Unnotched
4.50 J/cm² @Temperature -30.0 °C
Charpy Impact Unnotched
5.00 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
<= 1.00 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
<= 1.00 J/cm² @Temperature 23.0 °C
Impact
635
Impact
626 @Temperature -30.0 °C
Puncture Energy
10.6 J
Puncture Energy
1.80 J @Temperature -30.0 °C
Tensile Creep Modulus, 1 hour
6900 MPa
Tensile Creep Modulus, 1000 hours
6300 MPa

Thermal Properties
CTE, linear, Parallel to Flow
30.0 µm/m-°C
CTE, linear, Transverse to Flow
110 µm/m-°C
Melting Point
225 °C
Deflection Temperature at 0.46 MPa (66 psi)
220 °C
Deflection Temperature at 1.8 MPa (264 psi)
210 °C
Deflection Temperature at 8.0 MPa
140 °C
Vicat Softening Point
215 °C
Flammability, UL94
HB @Thickness 0.800 mm
Flammability, UL94
HB @Thickness 1.60 mm
Oxygen Index
20 %

Electrical Properties
Volume Resistivity
>= 1.00e+15 ohm-cm
Surface Resistance
>= 1.00e+15 ohm
Dielectric Constant
3.6 @Frequency 1.00e+6 Hz
Dielectric Constant
3.8 @Frequency 100 Hz
Dielectric Strength
30.0 kV/mm
Dissipation Factor
0.0015 @Frequency 100 Hz
Dissipation Factor
0.020 @Frequency 1.00e+6 Hz
Comparative Tracking Index
350 V

Processing Properties
Melt Temperature
260 °C
Mold Temperature
80.0 °C

Descriptive Properties
Additives
Release agent
Form
Pellets
ISO Shortname
ISO 7792-1-PBT,GHMR,09-070,GF20
Processing
Injection molding
Region
Asia Pacific
Region
Europe
Region
Near East/Africa
Region
North America
Region
South and Central America

Alternative products

Celanese CELANEX 2300 GV1/20 PBT, 20% Glass Reinforced accurate 56%

$ 1794/MT

Density: 1.45 g/cc
Density of Compound: 1.23 g/cc
Moisture Absorption: 0.150 %
Viscosity Test: 80.0 cm³/g
Melt Flow: 14.0 g/10 min @Load 2.16 kg, Temperature 250 °C

Lanxess Pocan® B 3235 901510 PBT, 30% Glass Fiber accurate 73%

$ 1663/MT

Density: 1.55 g/cc
Water Absorption: 0.40 %
Moisture Absorption at Equilibrium: 0.10 %
Viscosity Test: 95 cm³/g
Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 260 °C

Lanxess Pocan® B 3235 000000 PBT, 30% Glass Fiber accurate 73%

$ 2156/MT

Density: 1.55 g/cc
Water Absorption: 0.40 %
Moisture Absorption at Equilibrium: 0.10 %
Viscosity Test: 95 cm³/g
Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 260 °C

Lanxess Pocan® B 3225 901510 PBT, 20% Glass Fiber accurate 86%

$ 1463/MT

Density: 1.46 g/cc
Water Absorption: 0.40 %
Moisture Absorption at Equilibrium: 0.20 %
Viscosity Test: 100 cm³/g
Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 260 °C

Celanese Celanex® 3200-2 PBT, 15% Glass Reinforced (Unverified Data**) accurate 56%

$ 2151/MT

Specific Gravity: 1.41 g/cc
Density: 1.41 g/cc
Moisture Absorption: 0.200 %
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm

Celanese Celanex® 5300-2 PBT, 30% Glass Reinforced (Unverified Data**) accurate 64%

$ 2032/MT

Specific Gravity: 1.54 g/cc
Density: 1.54 g/cc
Water Absorption: 0.050 %
Moisture Absorption: 0.200 %
Viscosity Test: 68 cm³/g

Celanese Celanex® 2300 GV1/20 PBT, 20% Glass Reinforced (Unverified Data**) accurate 56%

$ 2210/MT

Density: 1.45 g/cc
Density of Compound: 1.23 g/cc
Moisture Absorption: 0.150 %
Viscosity Test: 80 cm³/g
Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 250 °C

Celanese CELANEX 5300-2 PBT, 30% Glass Reinforced accurate 60%

$ 2095/MT

Specific Gravity: 1.54 g/cc
Density: 1.54 g/cc
Water Absorption: 0.0500 % @Temperature 22.8 °C
Moisture Absorption: 0.200 %
Viscosity Test: 68.0 cm³/g

Celanese Celanex® 3200-2FC PBT, 15% Glass Reinforced (Unverified Data**) accurate 56%

$ 2078/MT

Specific Gravity: 1.41 g/cc
Density: 1.41 g/cc
Moisture Absorption: 0.200 %
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ship for sales. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Lanxess Pocan® B 3225 000000 PBT, 20% Glass Fiber

Seller from Los Angeles – 2021-07-05:

Seller from Los Angeles work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1839 per MT

Seller from Chennai – 2021-03-23:

Seller from Chennai work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2577 per MT

Seller from Shenyang – 2021-08-02:

Seller from Shenyang work with company: 3M, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co., ALIMEX GmbH

Price: $2308 per MT