Lanxess Pocan® B 3225 901510 PBT, 20% Glass Fiber price 1463 per MT

Physical Properties
Density
1.46 g/cc
Water Absorption
0.40 %
Moisture Absorption at Equilibrium
0.20 %
Viscosity Test
100 cm³/g
Melt Flow
26 g/10 min @Load 2.16 kg, Temperature 260 °C

Mechanical Properties
Tensile Strength at Break
120 MPa
Elongation at Break
2.6 %
Tensile Modulus
7.00 GPa
Charpy Impact Unnotched
4.50 J/cm² @Temperature -30.0 °C
Charpy Impact Unnotched
5.00 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
<= 1.00 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
<= 1.00 J/cm² @Temperature 23.0 °C
Puncture Energy
2.10 J
Tensile Creep Modulus, 1 hour
6900 MPa
Tensile Creep Modulus, 1000 hours
6300 MPa

Thermal Properties
CTE, linear, Parallel to Flow
30.0 µm/m-°C
CTE, linear, Transverse to Flow
90.0 µm/m-°C
Melting Point
225 °C
Deflection Temperature at 0.46 MPa (66 psi)
220 °C
Deflection Temperature at 1.8 MPa (264 psi)
210 °C
Deflection Temperature at 8.0 MPa
140 °C
Vicat Softening Point
215 °C
Flammability, UL94
HB @Thickness 0.800 mm
Flammability, UL94
HB @Thickness 1.60 mm
Oxygen Index
20 %

Electrical Properties
Volume Resistivity
>= 1.00e+15 ohm-cm
Surface Resistance
>= 1.00e+15 ohm
Dielectric Constant
3.6 @Frequency 1.00e+6 Hz
Dielectric Constant
3.8 @Frequency 100 Hz
Dielectric Strength
28.0 kV/mm
Dissipation Factor
0.0030 @Frequency 100 Hz
Dissipation Factor
0.021 @Frequency 1.00e+6 Hz
Comparative Tracking Index
350 V

Processing Properties
Melt Temperature
260 °C
Mold Temperature
80.0 °C

Descriptive Properties
Additives
Release agent
Form
Pellets
ISO Shortname
ISO 7792-PBT,MHMR,11-070,GF20
Processing
Injection molding
Region
Asia Pacific
Region
Europe
Region
Near East/Africa
Region
North America
Region
South and Central America

Alternative products

Lanxess Pocan® B 3235 901510 PBT, 30% Glass Fiber accurate 77%

$ 1663/MT

Density: 1.55 g/cc
Water Absorption: 0.40 %
Moisture Absorption at Equilibrium: 0.10 %
Viscosity Test: 95 cm³/g
Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 260 °C

Lanxess Pocan® B 3235 000000 PBT, 30% Glass Fiber accurate 77%

$ 2156/MT

Density: 1.55 g/cc
Water Absorption: 0.40 %
Moisture Absorption at Equilibrium: 0.10 %
Viscosity Test: 95 cm³/g
Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 260 °C

Lanxess Pocan® B 4225 000000 PBT, 20% Glass Fiber accurate 56%

$ 2162/MT

Density: 1.57 g/cc
Water Absorption: 0.30 %
Moisture Absorption at Equilibrium: 0.10 %
Viscosity Test: 97 cm³/g
Linear Mold Shrinkage, Flow: 0.0049 cm/cm

Lanxess Pocan® B 3225 000000 PBT, 20% Glass Fiber accurate 86%

$ 1839/MT

Density: 1.46 g/cc
Water Absorption: 0.40 %
Moisture Absorption at Equilibrium: 0.20 %
Viscosity Test: 100 cm³/g
Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 260 °C

Celanese Celanex® 5200-2 PBT, 15% Glass Reinforced (Unverified Data**) accurate 60%

$ 2074/MT

Specific Gravity: 1.41 g/cc
Density: 1.41 g/cc
Water Absorption: 0.050 %
Moisture Absorption: 0.200 %
Viscosity Test: 69 cm³/g

Covestro Bayblend® T88 GF-20* Polycarbonate + SAN Glass Filled Impact Grade accurate 56%

$ 1603/MT

Density: 1.29 g/cc
Density: 1.07 g/cc @Temperature 260 °C
Water Absorption: 0.60 %
Moisture Absorption at Equilibrium: 0.20 %
Tensile Strength at Break: 120 MPa

Celanese Celanex® 5300-2 PBT, 30% Glass Reinforced (Unverified Data**) accurate 56%

$ 2032/MT

Specific Gravity: 1.54 g/cc
Density: 1.54 g/cc
Water Absorption: 0.050 %
Moisture Absorption: 0.200 %
Viscosity Test: 68 cm³/g

Celanese Celanex® 2300 GV1/20 PBT, 20% Glass Reinforced (Unverified Data**) accurate 56%

$ 2210/MT

Density: 1.45 g/cc
Density of Compound: 1.23 g/cc
Moisture Absorption: 0.150 %
Viscosity Test: 80 cm³/g
Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 250 °C

Lanxess Pocan® KL 1-7033 000000 PBT, 30% Glass Fiber accurate 56%

$ 1968/MT

Density: 1.46 g/cc
Water Absorption: 0.40 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 17 g/10 min @Load 5.00 kg, Temperature 260 °C
Tensile Strength at Break: 100 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale listing. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

6 prices for Lanxess Pocan® B 3225 901510 PBT, 20% Glass Fiber

Seller from Xi’an – 2021-06-18:

Seller from Xi’an work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1463 per MT

Seller from Tehran – 2021-03-10:

Seller from Tehran work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2227 per MT

Seller from Dongguan – 2021-06-04:

Seller from Dongguan work with company: Solvay, RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $2483 per MT

Seller from Taipei – 2021-03-13:

Seller from Taipei work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2323 per MT

Seller from Los Angeles – 2021-05-16:

Seller from Los Angeles work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2383 per MT

Seller from Karachi – 2021-03-16:

Seller from Karachi work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1581 per MT