Lanxess Pocan® T 7391 POS151 000000 PBT + PET, 45% Glass Fiber (discontinued **) price 1867 per MT

Physical Properties
Density
1.68 g/cc
Water Absorption
0.30 %
Moisture Absorption at Equilibrium
0.10 %
Viscosity Test
80 cm³/g
Melt Flow
42 g/10 min @Load 5.00 kg, Temperature 260 °C

Mechanical Properties
Tensile Strength at Break
165 MPa
Elongation at Break
2.0 %
Tensile Modulus
16.5 GPa
Charpy Impact Unnotched
7.00 J/cm² @Temperature -30.0 °C
Charpy Impact Unnotched
7.00 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
1.10 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
1.20 J/cm² @Temperature 23.0 °C
Tensile Creep Modulus, 1 hour
16500 MPa
Tensile Creep Modulus, 1000 hours
15000 MPa

Thermal Properties
CTE, linear, Parallel to Flow
20.0 µm/m-°C
CTE, linear, Transverse to Flow
50.0 µm/m-°C
Melting Point
225 - 250 °C
Deflection Temperature at 0.46 MPa (66 psi)
225 °C
Deflection Temperature at 1.8 MPa (264 psi)
210 °C
Deflection Temperature at 8.0 MPa
150 °C
Vicat Softening Point
210 °C
Flammability, UL94
HB @Thickness 0.800 mm
Flammability, UL94
HB @Thickness 1.60 mm
Oxygen Index
21 %

Electrical Properties
Volume Resistivity
>= 1.00e+15 ohm-cm
Surface Resistance
>= 1.00e+15 ohm
Dielectric Constant
4.2 @Frequency 1.00e+6 Hz
Dielectric Constant
4.3 @Frequency 100 Hz
Dielectric Strength
28.0 kV/mm
Dissipation Factor
0.0020 @Frequency 100 Hz
Dissipation Factor
0.014 @Frequency 1.00e+6 Hz
Comparative Tracking Index
275 V

Processing Properties
Melt Temperature
270 °C
Mold Temperature
90.0 °C

Descriptive Properties
Additives
Release agent
Features
U.V. stabilized or stable to weather
Form
Pellets
ISO Shortname
ISO 7792-1-PBT+PET,GHLMR,09-160,GF45
Processing
Injection molding
Region
Asia Pacific
Region
Europe
Region
Near East/Africa
Region
North America
Region
South and Central America

Alternative products

Celanese Celanex® 2302 GV1/15 PBT, 15% Glass Reinforced (Unverified Data**) accurate 51%

$ 1483/MT

Density: 1.43 g/cc
Density of Compound: 1.22 g/cc
Moisture Absorption: 0.150 %
Viscosity Test: 76 cm³/g
Melt Flow: 21 g/10 min @Load 2.16 kg, Temperature 265 °C

Lanxess Pocan® BF 4235 000000 PBT, 30% Glass Fiber accurate 51%

$ 1558/MT

Density: 1.65 g/cc
Water Absorption: 0.40 %
Moisture Absorption at Equilibrium: 0.10 %
Viscosity Test: 93 cm³/g
Linear Mold Shrinkage, Flow: 0.0030 cm/cm

Lanxess Pocan® B 4235 000000 PBT, 30% Glass Fiber accurate 56%

$ 1734/MT

Density: 1.65 g/cc
Water Absorption: 0.40 %
Moisture Absorption at Equilibrium: 0.10 %
Viscosity Test: 93 cm³/g
Linear Mold Shrinkage, Flow: 0.0040 cm/cm

Lanxess Pocan® T 7331 000000 PBT + PET, 30% Glass Fiber accurate 56%

$ 1445/MT

Density: 1.55 g/cc
Water Absorption: 0.30 %
Moisture Absorption at Equilibrium: 0.10 %
Viscosity Test: 91 cm³/g
Melt Flow: 38 g/10 min @Load 5.00 kg, Temperature 260 °C

Lanxess Pocan® T 7391 000000 PBT + PET, 45% Glass Fiber accurate 99%

$ 1660/MT

Density: 1.67 g/cc
Water Absorption: 0.30 %
Moisture Absorption at Equilibrium: 0.10 %
Viscosity Test: 80 cm³/g
Melt Flow: 42 g/10 min @Load 5.00 kg, Temperature 260 °C

Celanese FORTRON 1140L6 PPS, 40% Glass Reinforced (Unverified Data**) accurate 51%

$ 1551/MT

Specific Gravity: 1.60 g/cc
Specific Gravity: 1.61 g/cc
Density: 1.60 g/cc
Density: 1.65 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 4184L6 PPS, 53% Mineral / Glass Reinforced (Unverified Data**) accurate 56%

$ 1475/MT

Specific Gravity: 1.80 g/cc
Specific Gravity: 1.80 g/cc
Density: 1.80 g/cc
Density: 1.80 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 4184L4 PPS, 53% Mineral / Glass Reinforced (Unverified Data**) accurate 56%

$ 1910/MT

Specific Gravity: 1.80 g/cc
Specific Gravity: 1.80 g/cc
Density: 1.80 g/cc
Density: 1.80 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 1140L4 PPS, 40% Glass Reinforced (Unverified Data**) accurate 56%

$ 1642/MT

Specific Gravity: 1.60 g/cc
Specific Gravity: 1.66 g/cc
Density: 1.64 g/cc
Density: 1.64 g/cc
Density: 1.65 g/cc

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, used lng tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Lanxess Pocan® T 7391 POS151 000000 PBT + PET, 45% Glass Fiber (discontinued **)

Seller from Dhaka – 2021-03-12:

Seller from Dhaka work with company: RTP Company, PolyOne Corporation, Parker Chomerics, SABIC Innovative Plastics (GE Plastics)

Price: $2031 per MT

Seller from Dallas – 2021-03-02:

Seller from Dallas work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1867 per MT

Seller from Monterrey – 2021-08-07:

Seller from Monterrey work with company: 3M, Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $2457 per MT