LATI LARIL 13 G/30-V1 30% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1) (Unverified Data**) price 1602 per MT

Physical Properties
Density
1.29 g/cc
Water Absorption
0.040 %
Linear Mold Shrinkage
0.0020 cm/cm
Linear Mold Shrinkage, Transverse
0.0020 cm/cm

Mechanical Properties
Hardness, Rockwell M
93
Tensile Strength, Ultimate
108 MPa
Tensile Strength, Ultimate
51.0 MPa @Temperature 120 °C
Tensile Strength, Ultimate
72.0 MPa @Temperature 90.0 °C
Tensile Strength, Ultimate
85.0 MPa @Temperature 60.0 °C
Flexural Modulus
7.85 GPa
Flexural Modulus
5.00 GPa @Temperature 120 °C
Flexural Modulus
6.50 GPa @Temperature 90.0 °C
Flexural Modulus
7.00 GPa @Temperature 60.0 °C
Izod Impact, Notched
0.650 J/cm @Temperature -40.0 °C
Izod Impact, Notched
0.670 J/cm @Temperature -20.0 °C
Izod Impact, Notched
0.850 J/cm @Temperature 23.0 °C
Charpy Impact Unnotched
1.90 J/cm² @Temperature -20.0 °C
Charpy Impact Unnotched
1.90 J/cm² @Temperature -40.0 °C
Charpy Impact Unnotched
2.00 J/cm² @Temperature 23.0 °C

Thermal Properties
CTE, linear
30.0 µm/m-°C @Temperature 20.0 °C
Deflection Temperature at 0.46 MPa (66 psi)
132 °C
Deflection Temperature at 1.8 MPa (264 psi)
128 °C
Vicat Softening Point
135 °C
Flammability, UL94
V-1 @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 6.00 mm
Oxygen Index
31 %
Glow Wire Test
960 °C @Thickness 2.00 mm

Electrical Properties
Dielectric Strength
23.0 kV/mm @Thickness 2.00 mm
Comparative Tracking Index
225 V

Processing Properties
Melt Temperature
260 - 280 °C
Mold Temperature
80.0 - 100 °C
Drying Temperature
100 - 110 °C
Dry Time
>= 3 hour

Descriptive Properties
Heat Resistance - Ball Test (125°C)
Y
Heat Resistance - Ball Test (165°C)
N
Injection Speed
medium
Needle Burner Test
Y
Needle Burner Test
Y

Alternative products

Covestro Makrolon® 2865 Polycarbonate, Flame Retardant Grade accurate 45%

$ 1672/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 300 °C
Water Absorption: 0.30 %
Moisture Absorption at Equilibrium: 0.12 %
Linear Mold Shrinkage, Flow: 0.0070 cm/cm

LATI LARIL 13 G/20-V1 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1) (Unverified Data**) accurate 61%

$ 2333/MT

Density: 1.23 g/cc
Water Absorption: 0.050 %
Linear Mold Shrinkage: 0.0040 cm/cm
Linear Mold Shrinkage, Transverse: 0.0040 cm/cm
Hardness, Rockwell M: 93

LATI LARIL 13 G/20 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (Unverified Data**) accurate 53%

$ 1875/MT

Density: 1.21 g/cc
Water Absorption: 0.050 %
Linear Mold Shrinkage: 0.0040 cm/cm
Linear Mold Shrinkage, Transverse: 0.0040 cm/cm
Hardness, Rockwell M: 91

Covestro Makrolon® KU1-1230* Polycarbonate accurate 45%

$ 1726/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 300 °C
Water Absorption: 0.30 %
Moisture Absorption at Equilibrium: 0.12 %
Linear Mold Shrinkage, Flow: 0.0070 cm/cm

Celanese FORTRON 1131L4 ITT PPS, 30% Glass Reinforced (Unverified Data**) accurate 45%

$ 2078/MT

Specific Gravity: 1.40 g/cc
Specific Gravity: 1.41 g/cc
Density: 1.40 g/cc
Density: 1.56 g/cc
Water Absorption: 0.020 %

Covestro Makrolon® 1248 Polycarbonate, Impact Grade accurate 45%

$ 1459/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 300 °C
Water Absorption: 0.40 %
Moisture Absorption at Equilibrium: 0.12 %
Linear Mold Shrinkage, Flow: 0.0080 cm/cm

Celanese FORTRON 214 PPS (Unverified Data**) accurate 53%

$ 2311/MT

Specific Gravity: 1.35 g/cc
Specific Gravity: 1.36 g/cc
Density: 1.35 g/cc
Density: 1.35 g/cc
Density of Compound: 1.15 g/cc

BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Dry) (discontinued **) accurate 45%

$ 1782/MT

Density: 1.16 g/cc
Density: 1.34 g/cc
Water Absorption: 0.90 %
Moisture Absorption at Equilibrium: 1.5 %
Water Absorption at Saturation: 5.5 %

LATI LARIL 13 G/30 30% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (Unverified Data**) accurate 45%

$ 1644/MT

Density: 1.27 g/cc
Water Absorption: 0.040 %
Linear Mold Shrinkage: 0.0025 cm/cm
Linear Mold Shrinkage, Transverse: 0.0025 cm/cm
Hardness, Rockwell M: 93

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale norway. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

5 prices for LATI LARIL 13 G/30-V1 30% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1) (Unverified Data**)

Seller from Hechi – 2021-06-01:

Seller from Hechi work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2292 per MT

Seller from Chennai – 2021-03-28:

Seller from Chennai work with company: 3M, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1957 per MT

Seller from Santiago – 2021-08-04:

Seller from Santiago work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2069 per MT

Seller from Phoenix – 2021-07-20:

Seller from Phoenix work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1602 per MT

Seller from Guadalajara – 2021-04-25:

Seller from Guadalajara work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2517 per MT