LATI LARTON G/40 40% Glass Fiber Filled Polyphenylene sulfide (PPS)  (Unverified Data**)

Seller in Philadelphia price: $1772 per MT
Seller in Chongqing price: $1618 per MT

LATI LARTON G/40 40% Glass Fiber Filled Polyphenylene sulfide (PPS)  (Unverified Data**) in Polymer, Thermoplastic, Polyphenylene Sulfide (PPS), Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler

  • Physical Properties
  • Density
  • 1.65 g/cc
  • Water Absorption
  • 0.010 %
  • Linear Mold Shrinkage
  • 0.0025 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.0060 cm/cm
  • Mechanical Properties
  • Hardness, Rockwell M
  • >= 100
  • Tensile Strength, Ultimate
  • 135 MPa
  • Tensile Strength, Ultimate
  • 100 MPa @Temperature 120 °C
  • Tensile Strength, Ultimate
  • 118 MPa @Temperature 90.0 °C
  • Tensile Strength, Ultimate
  • 128 MPa @Temperature 60.0 °C
  • Flexural Modulus
  • 13.0 GPa
  • Flexural Modulus
  • 8.00 GPa @Temperature 120 °C
  • Flexural Modulus
  • 10.5 GPa @Temperature 90.0 °C
  • Flexural Modulus
  • 13.0 GPa @Temperature 60.0 °C
  • Izod Impact, Notched
  • 0.850 J/cm @Temperature -20.0 °C
  • Izod Impact, Notched
  • 0.850 J/cm @Temperature 23.0 °C
  • Izod Impact, Notched
  • 0.850 J/cm @Temperature -40.0 °C
  • Charpy Impact Unnotched
  • 2.00 J/cm² @Temperature -20.0 °C
  • Charpy Impact Unnotched
  • 2.00 J/cm² @Temperature -40.0 °C
  • Charpy Impact Unnotched
  • 2.00 J/cm² @Temperature 23.0 °C
  • Thermal Properties
  • CTE, linear
  • 27.0 µm/m-°C @Temperature 20.0 °C
  • Deflection Temperature at 0.46 MPa (66 psi)
  • 279 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 265 °C
  • Vicat Softening Point
  • 246 °C
  • Flammability, UL94
  • V-0 @Thickness 0.890 mm
  • Oxygen Index
  • 44 %
  • Glow Wire Test
  • 960 °C @Thickness 2.00 mm
  • Glow Wire Test
  • 960 °C @Thickness 1.00 mm
  • Electrical Properties
  • Dielectric Strength
  • 18.0 kV/mm @Thickness 2.00 mm
  • Comparative Tracking Index
  • 125 V
  • Processing Properties
  • Melt Temperature
  • 280 - 300 °C
  • Mold Temperature
  • 130 - 140 °C
  • Drying Temperature
  • 130 - 140 °C
  • Dry Time
  • >= 3 hour
  • Descriptive Properties
  • Heat Resistance - Ball Test (125°C)
  • Y
  • Heat Resistance - Ball Test (165°C)
  • Y
  • Injection Speed
  • medium - high
  • Needle Burner Test
  • Y
  • Needle Burner Test
  • Y

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, dredging ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for LATI LARTON G/40 40% Glass Fiber Filled Polyphenylene sulfide (PPS)  (Unverified Data**)

Seller from Philadelphia – 2021-04-01:

Seller from Philadelphia work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1772 per MT

Seller from Chongqing – 2021-06-10:

Seller from Chongqing work with company: Celanese Corporation, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1618 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell LATI LARTON G/40 40% Glass Fiber Filled Polyphenylene sulfide (PPS)  (Unverified Data**)?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Digital printer in Singapore open-nearme.com