LATI Latamid 12 H2 G/30 PA 12, 30% Glass Fiber Reinforced, Heat Stabilized price 1518 per MT

Physical Properties
Density
1.23 g/cc
Linear Mold Shrinkage, Flow
0.0040 - 0.0070 cm/cm
Linear Mold Shrinkage, Transverse
0.0080 - 0.011 cm/cm

Mechanical Properties
Tensile Strength at Break
35.0 MPa @Temperature 150 °C
Tensile Strength at Break
50.0 MPa @Temperature 120 °C
Tensile Strength at Break
60.0 MPa @Temperature 90.0 °C
Tensile Strength at Break
75.0 MPa @Temperature 60.0 °C
Tensile Strength at Break
100 MPa @Temperature 23.0 °C
Elongation at Break
8.0 % @Temperature 23.0 °C
Elongation at Break
11 % @Temperature 60.0 °C
Elongation at Break
12 % @Temperature 90.0 °C
Elongation at Break
14 % @Temperature 120 °C
Elongation at Break
16 % @Temperature 150 °C
Elongation at Yield
6.5 % @Temperature 23.0 °C
Elongation at Yield
>= 10 % @Temperature 60.0 °C
Elongation at Yield
>= 10 % @Temperature 90.0 °C
Elongation at Yield
>= 10 % @Temperature 120 °C
Elongation at Yield
>= 10 % @Temperature 150 °C
Tensile Modulus
2.10 GPa @Temperature 150 °C
Tensile Modulus
2.70 GPa @Temperature 120 °C
Tensile Modulus
3.20 GPa @Temperature 90.0 °C
Tensile Modulus
4.00 GPa @Temperature 60.0 °C
Tensile Modulus
6.60 GPa @Temperature 23.0 °C
Charpy Impact Unnotched
7.00 J/cm² @Temperature 23.0 °C
Charpy Impact Unnotched
8.00 J/cm² @Temperature -20.0 °C
Charpy Impact, Notched
1.00 J/cm² @Temperature -20.0 °C
Charpy Impact, Notched
1.50 J/cm² @Temperature 23.0 °C

Thermal Properties
Maximum Service Temperature, Air
120 °C
Deflection Temperature at 0.46 MPa (66 psi)
180 °C
Deflection Temperature at 1.8 MPa (264 psi)
175 °C
Vicat Softening Point
170 °C @Load 5.00 kg

Processing Properties
Melt Temperature
210 - 230 °C
Mold Temperature
70.0 - 90.0 °C
Drying Temperature
70.0 - 90.0 °C @Time 10800 sec

Descriptive Properties
ISO Shrinkage - Pressure
60 MPa

Alternative products

SABIC Innovative Plastics Valox® 7062 PBT+PET (Europe-Africa-Middle East) accurate 70%

$ 2487/MT

Density: 1.81 g/cc
Linear Mold Shrinkage, Flow: 0.012 - 0.019 cm/cm @Thickness 3.20 mm
Melt Index of Compound: 21 g/10 min @Load 1.20 kg, Temperature 265 °C
Hardness, H358/30: 140 MPa
Tensile Strength at Break: 60.0 MPa

DuPont Performance Polymers Crastin® FG6130 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)< accurate 56%

$ 2085/MT

Density: 1.12 g/cc
Density: 1.30 g/cc
Water Absorption: 0.40 % @Thickness 2.00 mm
Moisture Absorption: 0.200 % @Thickness 2.00 mm
Viscosity Test: 130 cm³/g

LATI Later 4-V0 PBT, Flame Retardant accurate 56%

$ 2156/MT

Density: 1.42 g/cc
Linear Mold Shrinkage, Flow: 0.015 - 0.018 cm/cm
Linear Mold Shrinkage, Transverse: 0.015 - 0.018 cm/cm
Tensile Strength at Break: 20.0 MPa @Temperature 90.0 °C
Tensile Strength at Break: 35.0 MPa @Temperature 60.0 °C

SABIC Innovative Plastics Valox® 7062HP PBT (Europe-Africa-Middle East) accurate 56%

$ 1601/MT

Specific Gravity: 1.81 g/cc
Density: 1.81 g/cc
Moisture Absorption: 0.0700 %
Water Absorption at Saturation: 0.070 %
Linear Mold Shrinkage, Flow: 0.012 - 0.019 cm/cm @Thickness 3.20 mm

LATI Latamid 12 G/50 PA 12, 50% Glass Fiber Reinforced accurate 56%

$ 1524/MT

Density: 1.45 g/cc
Linear Mold Shrinkage, Flow: 0.0035 - 0.0055 cm/cm
Linear Mold Shrinkage, Transverse: 0.0075 - 0.010 cm/cm
Tensile Strength at Break: 55.0 MPa @Temperature 150 °C
Tensile Strength at Break: 80.0 MPa @Temperature 120 °C

SABIC Innovative Plastics LNP THERMOCOMP RF002ES PA 66 accurate 70%

$ 1715/MT

Density: 1.22 g/cc
Density: 1.224 g/cc
Moisture Absorption: 1.26 %
Moisture Absorption: 1.94 %
Linear Mold Shrinkage, Flow: 0.0077 cm/cm @Time 86400 sec

LATI Lasulf G/15 PSU, 15% Glass Fiber Reinforced accurate 70%

$ 1656/MT

Density: 1.34 g/cc
Linear Mold Shrinkage, Flow: 0.0020 - 0.0045 cm/cm
Linear Mold Shrinkage, Transverse: 0.0065 - 0.0085 cm/cm
Tensile Strength at Break: 50.0 MPa @Temperature 150 °C
Tensile Strength at Break: 65.0 MPa @Temperature 120 °C

SABIC Innovative Plastics LNP THERMOCOMP HF008 PA 11 (Asia Pacific) accurate 56%

$ 1914/MT

Density: 1.37 g/cc
Density: 1.37 g/cc
Moisture Absorption: 0.100 %
Moisture Absorption: 0.190 %
Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec

LATI Latiblend 6252 H2 G/30 PA6/PP Homopolymer accurate 56%

$ 1583/MT

Density: 1.24 g/cc
Linear Mold Shrinkage, Flow: 0.0035 - 0.0050 cm/cm
Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm
Tensile Strength at Break: 27.0 MPa @Temperature 150 °C
Tensile Strength at Break: 40.0 MPa @Temperature 120 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale norway. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for LATI Latamid 12 H2 G/30 PA 12, 30% Glass Fiber Reinforced, Heat Stabilized

Seller from Bengalūru – 2021-06-15:

Seller from Bengalūru work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2243 per MT

Seller from Lima – 2021-05-05:

Seller from Lima work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), BASF

Price: $2050 per MT

Seller from Madrid – 2021-03-24:

Seller from Madrid work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $1518 per MT

Seller from Lahore – 2021-07-23:

Seller from Lahore work with company: Celanese Corporation, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $2116 per MT