$ 1704/MT
- Density: 1.00 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 - 0.014 cm/cm
- Tensile Strength at Break: 25.0 MPa
- Elongation at Break: 7.0 %
$ 2050/MT
- Density: 2.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 0.70 %
$ 1519/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 - 0.017 cm/cm
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 10 %
$ 1526/MT
- Density: 1.43 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 - 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.014 cm/cm
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 1.0 %
$ 1478/MT
- Density: 1.73 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0065 cm/cm
- Tensile Strength at Break: 35.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 45.0 MPa @Temperature 120 °C
$ 1574/MT
- Density: 1.38 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0065 cm/cm
- Tensile Strength at Break: 20.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 25.0 MPa @Temperature 120 °C
$ 1851/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0065 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 9.0 %
$ 1690/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0060 cm/cm
- Elongation at Break: >= 100 %
- Elongation at Yield: 2.2 %
$ 1583/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0060 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 3.5 %
$ 1578/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0090 cm/cm
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 2.2 %
$ 1780/MT
- Density: 1.21 g/cc
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0075 cm/cm
- Tensile Strength at Break: 23.0 MPa @Temperature 120 °C
- Tensile Strength at Break: 25.0 MPa @Temperature 90.0 °C
$ 1679/MT
- Density: 1.58 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 50.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 60.0 MPa @Temperature 120 °C
$ 1483/MT
- Density: 1.44 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0015 - 0.0025 cm/cm
- Tensile Strength at Break: 70.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 85.0 MPa @Temperature 120 °C
$ 1812/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0085 - 0.010 cm/cm
- Tensile Strength at Break: 70.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 80.0 MPa @Temperature 120 °C
$ 1855/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.00050 - 0.0025 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 100 MPa @Temperature 150 °C
- Tensile Strength at Break: 155 MPa @Temperature 120 °C
$ 1772/MT
- Density: 1.65 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.010 cm/cm
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 0.50 %
$ 1618/MT
- Density: 0.970 g/cc
- Linear Mold Shrinkage, Flow: 0.0135 - 0.0165 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 - 0.017 cm/cm
- Tensile Strength at Break: 25.0 MPa
- Elongation at Break: 25 % @Temperature 23.0 °C
$ 1574/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 85.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 100 MPa @Temperature 120 °C
$ 1512/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0105 - 0.0135 cm/cm
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 6.5 %
$ 1811/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0105 - 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0115 - 0.0135 cm/cm
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 8.0 %
$ 1466/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0095 cm/cm
- Tensile Strength at Break: 200 MPa
- Elongation at Break: 2.5 %
$ 1471/MT
- Density: 1.44 g/cc
- Linear Mold Shrinkage, Flow: 0.020 - 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0205 - 0.0225 cm/cm
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 20 %
$ 1802/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.010 cm/cm
- Tensile Strength at Break: 40.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 50.0 MPa @Temperature 120 °C
$ 1948/MT
- Density: 1.58 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0095 - 0.0125 cm/cm
- Tensile Strength at Break: 40.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 50.0 MPa @Temperature 120 °C
$ 1704/MT
- Density: 1.419 g/cc
- Linear Mold Shrinkage, Flow: 0.020 - 0.0235 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0205 - 0.0225 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 10 %
$ 1786/MT
- Density: 1.55 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 135 MPa
- Elongation at Break: 1.7 %
$ 2570/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0095 cm/cm
- Elongation at Break: >= 100 % @Temperature 23.0 °C
- Elongation at Break: >= 100 % @Temperature 60.0 °C
$ 1466/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0075 cm/cm
- Tensile Strength at Break: 55.0 MPa
- Elongation at Break: 10 %
$ 1915/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 70.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 85.0 MPa @Temperature 120 °C
$ 2097/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0095 - 0.0125 cm/cm
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 3.8 %
$ 1837/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0055 - 0.085 cm/cm
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 2.5 % @Temperature 23.0 °C
$ 1780/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage, Flow: 0.0095 - 0.0125 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.013 cm/cm
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 35 % @Temperature 23.0 °C
$ 1595/MT
- Density: 1.63 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.013 cm/cm
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 10 %
$ 1820/MT
- Density: 1.75 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0065 cm/cm
- Tensile Strength at Break: 35.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 45.0 MPa @Temperature 120 °C
$ 1585/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 190 MPa
- Elongation at Break: 2.0 %
$ 1525/MT
- Density: 1.64 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0090 cm/cm
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 0.50 %
$ 1621/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0075 cm/cm
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 12 %
$ 1484/MT
- Density: 1.66 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0055 - 0.0075 cm/cm
- Tensile Strength at Break: 40.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 50.0 MPa @Temperature 120 °C
$ 1557/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.0105 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm
- Tensile Strength at Break: 5.00 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 15.0 MPa @Temperature 60.0 °C
$ 1475/MT
- Density: 1.53 g/cc
- Linear Mold Shrinkage, Flow: 0.0185 - 0.0215 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0185 - 0.021 cm/cm
- Tensile Strength at Break: 30.0 MPa @Temperature 60.0 °C
- Tensile Strength at Break: 45.0 MPa @Temperature 23.0 °C
$ 2008/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 160 MPa
- Elongation at Break: 3.0 % @Temperature 23.0 °C
$ 2197/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.00050 - 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0045 cm/cm
- Tensile Strength at Break: 200 MPa @Temperature 150 °C
- Tensile Strength at Break: 230 MPa @Temperature 120 °C
$ 2565/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0075 cm/cm
- Tensile Strength at Break: 35.0 MPa
- Elongation at Break: 0.80 %
$ 2095/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0080 cm/cm
- Tensile Strength at Break: 30.0 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 45.0 MPa @Temperature 60.0 °C
$ 1565/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0075 - 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 7.00 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 10.0 MPa @Temperature 60.0 °C
$ 1502/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0155 - 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0165 - 0.020 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 6.0 %
$ 2039/MT
- Density: 1.50 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0055 - 0.0085 cm/cm
- Tensile Strength at Break: 110 MPa @Temperature 150 °C
- Tensile Strength at Break: 135 MPa @Temperature 120 °C
$ 2100/MT
- Density: 1.87 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0060 cm/cm
- Tensile Strength at Break: 30.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 35.0 MPa @Temperature 120 °C
$ 2047/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0145 - 0.0185 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0145 - 0.0185 cm/cm
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: >= 100 %
$ 1486/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0145 - 0.0185 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0145 - 0.0185 cm/cm
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: >= 100 %
$ 1828/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0145 - 0.0185 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0145 - 0.0185 cm/cm
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: >= 100 %
$ 1807/MT
- Density: 1.74 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0090 cm/cm
- Tensile Strength at Break: 45.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 55.0 MPa @Temperature 120 °C
$ 1786/MT
- Density: 1.38 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0090 cm/cm
- Tensile Strength at Break: 105 MPa @Temperature 150 °C
- Tensile Strength at Break: 125 MPa @Temperature 120 °C
$ 1665/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0090 cm/cm
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 2.3 %
$ 1694/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 90.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 105 MPa @Temperature 120 °C
$ 1561/MT
- Density: 1.50 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0025 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0045 cm/cm
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 1.5 %
$ 1955/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 - 0.018 cm/cm
- Tensile Strength at Break: 25.0 MPa
- Elongation at Break: 6.0 %
$ 1495/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage, Flow: 0.018 - 0.021 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 - 0.0205 cm/cm
- Elongation at Break: >= 100 % @Temperature 23.0 °C
- Elongation at Break: >= 100 % @Temperature 60.0 °C
$ 1905/MT
- Density: 0.970 g/cc
- Linear Mold Shrinkage, Flow: 0.014 - 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0145 - 0.0175 cm/cm
- Tensile Strength at Break: 10.0 MPa
- Elongation at Break: 95 %
$ 1495/MT
- Density: 1.43 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 80.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 100 MPa @Temperature 120 °C
$ 1804/MT
- Density: 1.50 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.013 cm/cm
- Tensile Strength at Break: 65.0 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 100 MPa @Temperature 60.0 °C
$ 1788/MT
- Density: 1.63 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 70.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 130 MPa @Temperature 120 °C
$ 2148/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 0.70 %
$ 2463/MT
- Density: 1.62 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0090 cm/cm
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 2.0 %
$ 2013/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength at Break: 25.0 MPa @Temperature 120 °C
- Tensile Strength at Break: 45.0 MPa @Temperature 90.0 °C
$ 1977/MT
- Density: 1.50 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0090 cm/cm
- Tensile Strength at Break: 110 MPa @Temperature 150 °C
- Tensile Strength at Break: 135 MPa @Temperature 120 °C
$ 1488/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0055 - 0.0075 cm/cm
- Tensile Strength at Break: 20.0 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 45.0 MPa @Temperature 60.0 °C
$ 1453/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 40.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 65.0 MPa @Temperature 120 °C
$ 1938/MT
- Density: 1.28 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 - 0.015 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 2.0 %
$ 1539/MT
- Density: 2.96 g/cc
- Linear Mold Shrinkage, Flow: 0.0065 - 0.0085 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0085 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 1.4 %
$ 1882/MT
- Density: 0.970 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 - 0.018 cm/cm
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 150 % @Temperature 23.0 °C
$ 2091/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0065 cm/cm
- Tensile Strength at Break: 35.0 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 60.0 MPa @Temperature 60.0 °C
$ 2515/MT
- Density: 2.55 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0040 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 0.50 %
$ 1613/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.013 cm/cm
- Tensile Strength at Break: 25.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 55.0 MPa @Temperature 120 °C
$ 1475/MT
- Density: 1.55 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 170 MPa
- Elongation at Break: 2.2 %
$ 1529/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 - 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.014 cm/cm
- Tensile Strength at Break: 75.0 MPa
- Elongation at Break: 30 %
$ 2172/MT
- Density: 1.55 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength at Break: 55.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 65.0 MPa @Temperature 120 °C
$ 2167/MT
- Density: 1.43 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 70.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 100 MPa @Temperature 120 °C
$ 2113/MT
- Density: 1.52 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.013 cm/cm
- Tensile Strength at Break: 45.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 50.0 MPa @Temperature 120 °C
$ 1961/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0030 cm/cm
- Tensile Strength at Break: 50.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 70.0 MPa @Temperature 120 °C
$ 2093/MT
- Density: 1.44 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 3.0 %
$ 1451/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0090 cm/cm
- Tensile Strength at Break: 105 MPa
- Elongation at Break: 2.3 %
$ 1495/MT
- Density: 1.50 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0045 cm/cm
- Tensile Strength at Break: 170 MPa
- Elongation at Break: 0.50 %
$ 1940/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.0165 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 - 0.016 cm/cm
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 15 %
$ 1653/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0085 - 0.0115 cm/cm
- Tensile Strength at Break: 55.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 75.0 MPa @Temperature 120 °C
$ 1719/MT
- Density: 1.60 g/cc
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0080 cm/cm
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 1.0 %
$ 1741/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0055 - 0.0085 cm/cm
- Tensile Strength at Break: 65.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 80.0 MPa @Temperature 120 °C
$ 1499/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Elongation at Break: >= 100 % @Temperature 23.0 °C
- Elongation at Yield: >= 100 % @Temperature 23.0 °C
$ 1530/MT
- Density: 1.59 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0090 cm/cm
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 2.0 %
$ 2320/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.0095 cm/cm
- Tensile Strength at Break: 70.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 75.0 MPa @Temperature 120 °C
$ 2132/MT
- Density: 1.61 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0055 - 0.0075 cm/cm
- Tensile Strength at Break: 30.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 35.0 MPa @Temperature 120 °C
$ 1575/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0115 - 0.0145 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0125 - 0.015 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 80 %
$ 1527/MT
- Density: 1.59 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 85.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 105 MPa @Temperature 120 °C
$ 2444/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.013 cm/cm
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 3.5 %
$ 1916/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0075 cm/cm
- Tensile Strength at Break: 25.0 MPa @Temperature 60.0 °C
- Tensile Strength at Break: 45.0 MPa @Temperature 23.0 °C
$ 1460/MT
- Density: 1.73 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0065 cm/cm
- Tensile Strength at Break: 150 MPa @Temperature 150 °C
- Tensile Strength at Break: 170 MPa @Temperature 120 °C
$ 2380/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.0115 cm/cm
- Tensile Strength at Break: 65.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 75.0 MPa @Temperature 120 °C
$ 1745/MT
- Density: 1.65 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.011 cm/cm
- Tensile Strength at Break: 85.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 110 MPa @Temperature 120 °C
$ 1644/MT
- Density: 1.238 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.0165 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 - 0.0165 cm/cm
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 2.7 %
$ 1678/MT
- Density: 1.59 g/cc
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 - 0.014 cm/cm
- Tensile Strength at Break: 55.0 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 85.0 MPa @Temperature 60.0 °C
$ 1557/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0080 cm/cm
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 1.2 %
$ 1591/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0165 - 0.0195 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0175 - 0.021 cm/cm
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 7.5 %
$ 1824/MT
- Density: 1.78 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm
- Tensile Strength at Break: 30.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 40.0 MPa @Temperature 120 °C
$ 1695/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0090 cm/cm
- Tensile Strength at Break: 80.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 90.0 MPa @Temperature 120 °C
$ 1904/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.020 - 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0205 - 0.0225 cm/cm
- Tensile Strength at Break: 55.0 MPa
- Elongation at Break: 80 % @Temperature 23.0 °C
$ 1460/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 2.5 %
$ 1452/MT
- Density: 1.43 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 - 0.015 cm/cm
- Tensile Strength at Break: 40.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 45.0 MPa @Temperature 120 °C
$ 1785/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 - 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0095 - 0.013 cm/cm
- Tensile Strength at Break: 55.0 MPa
- Elongation at Break: 45 %
$ 1645/MT
- Density: 0.950 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0155 - 0.0185 cm/cm
- Tensile Strength at Break: 35.0 MPa
- Elongation at Break: 3.5 %
$ 1723/MT
- Density: 1.78 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0065 cm/cm
- Tensile Strength at Break: 100 MPa @Temperature 150 °C
- Tensile Strength at Break: 165 MPa @Temperature 120 °C
$ 1446/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 200 MPa
- Elongation at Break: 2.0 %
$ 1554/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0125 - 0.0155 cm/cm
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 30 %
$ 1707/MT
- Density: 1.28 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0060 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 4.5 %
$ 1613/MT
- Density: 1.28 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0065 cm/cm
- Tensile Strength at Break: 40.0 MPa @Temperature 120 °C
- Tensile Strength at Break: 65.0 MPa @Temperature 90.0 °C
$ 2344/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0105 - 0.0135 cm/cm
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 2.0 %
$ 1882/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 2.8 %
$ 1737/MT
- Density: 1.192 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0035 - 0.0050 cm/cm
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 1.0 %
$ 1518/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.013 cm/cm
- Tensile Strength at Break: 25.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 35.0 MPa @Temperature 120 °C
$ 1466/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.010 cm/cm
- Tensile Strength at Break: 160 MPa
- Elongation at Break: 3.0 %
$ 2466/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0085 - 0.010 cm/cm
- Elongation at Break: >= 100 % @Temperature 23.0 °C
- Elongation at Break: >= 100 % @Temperature 60.0 °C
$ 2473/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0055 - 0.0075 cm/cm
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 1.5 %
$ 1467/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0060 cm/cm
- Tensile Strength at Break: 70.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 80.0 MPa @Temperature 120 °C
$ 2026/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0095 cm/cm
- Tensile Strength at Break: 90.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 105 MPa @Temperature 120 °C
$ 1622/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 60.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 75.0 MPa @Temperature 120 °C
$ 1468/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0105 - 0.0135 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0115 - 0.014 cm/cm
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 2.5 %
$ 1741/MT
- Density: 1.21 g/cc
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0075 cm/cm
- Tensile Strength at Break: 35.0 MPa @Temperature 60.0 °C
- Tensile Strength at Break: 55.0 MPa @Temperature 23.0 °C
$ 1849/MT
- Density: 1.55 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0090 cm/cm
- Tensile Strength at Break: 95.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 150 MPa @Temperature 120 °C
$ 1755/MT
- Density: 0.780 g/cc
- Linear Mold Shrinkage, Flow: 0.0125 - 0.0155 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 - 0.015 cm/cm
- Tensile Strength at Break: 5.00 MPa
- Elongation at Break: 20 %
$ 2019/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0075 cm/cm
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 2.3 %
$ 1499/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0125 - 0.0145 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0135 - 0.0165 cm/cm
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 5.0 %
$ 1952/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.00050 - 0.0025 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 190 MPa @Temperature 150 °C
- Tensile Strength at Break: 215 MPa @Temperature 120 °C
$ 2575/MT
- Density: 1.68 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0085 cm/cm
- Tensile Strength at Break: 75.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 100 MPa @Temperature 120 °C
$ 1478/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0090 cm/cm
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 30 %
$ 1529/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0055 - 0.0080 cm/cm
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 1.2 %
$ 2377/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.013 cm/cm
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 2.8 %
$ 1643/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 55.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 65.0 MPa @Temperature 120 °C
$ 1490/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.00050 - 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0055 cm/cm
- Tensile Strength at Break: 140 MPa @Temperature 150 °C
- Tensile Strength at Break: 190 MPa @Temperature 120 °C
$ 2156/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 - 0.018 cm/cm
- Tensile Strength at Break: 20.0 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 35.0 MPa @Temperature 60.0 °C
$ 1488/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0025 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0040 cm/cm
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 1.5 %
$ 1758/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0125 - 0.0155 cm/cm
- Tensile Strength at Break: 30.0 MPa
- Elongation at Break: 7.5 %
$ 1595/MT
- Density: 1.43 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0065 cm/cm
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 2.5 %
$ 2468/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.020 - 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0205 - 0.0225 cm/cm
- Tensile Strength at Break: 55.0 MPa
- Elongation at Break: 5.0 %
$ 1587/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 - 0.015 cm/cm
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 20 %
$ 1465/MT
- Density: 1.48 g/cc
- Linear Mold Shrinkage, Flow: 0.0065 - 0.0105 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.013 cm/cm
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 2.5 %
$ 1583/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 60.0 MPa @Temperature 120 °C
- Tensile Strength at Break: 70.0 MPa @Temperature 90.0 °C
$ 1896/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0085 - 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm
- Tensile Strength at Break: 45.0 MPa @Temperature 60.0 °C
- Tensile Strength at Break: 70.0 MPa @Temperature 23.0 °C
$ 2328/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.012 cm/cm
- Tensile Strength at Break: 45.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 55.0 MPa @Temperature 120 °C
$ 1858/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0105 cm/cm
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 1.8 %
$ 2417/MT
- Density: 1.64 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0070 cm/cm
- Tensile Strength at Break: 95.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 155 MPa @Temperature 120 °C
$ 1631/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.012 cm/cm
- Tensile Strength at Break: 90.0 MPa @Temperature 120 °C
- Tensile Strength at Break: 120 MPa @Temperature 90.0 °C
$ 1546/MT
- Density: 1.67 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0075 cm/cm
- Tensile Strength at Break: 135 MPa
- Elongation at Break: 1.7 %
$ 2370/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 - 0.014 cm/cm
- Tensile Strength at Break: 95.0 MPa
- Elongation at Break: 4.2 %
$ 1504/MT
- Density: 1.82 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm
- Tensile Strength at Break: 75.0 MPa
- Elongation at Break: 2.4 % @Temperature 23.0 °C
$ 1549/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 - 0.0125 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0095 - 0.0135 cm/cm
- Tensile Strength at Break: 75.0 MPa
- Elongation at Break: 6.0 %
$ 1880/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0035 - 0.0060 cm/cm
- Tensile Strength at Break: 160 MPa @Temperature 150 °C
- Tensile Strength at Break: 185 MPa @Temperature 120 °C
$ 1574/MT
- Density: 1.325 g/cc
- Linear Mold Shrinkage, Flow: 0.017 - 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 - 0.020 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 10 %
$ 1529/MT
- Density: 1.91 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0015 - 0.0030 cm/cm
- Tensile Strength at Break: 60.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 75.0 MPa @Temperature 120 °C
$ 1739/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0055 - 0.0080 cm/cm
- Tensile Strength at Break: 75.0 MPa
- Elongation at Break: 2.0 %
$ 1651/MT
- Density: 1.80 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0015 - 0.0040 cm/cm
- Tensile Strength at Break: 35.0 MPa
- Elongation at Break: 3.5 %
$ 1450/MT
- Density: 1.61 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0105 - 0.0135 cm/cm
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 2.7 %
$ 1598/MT
- Density: 2.96 g/cc
- Linear Mold Shrinkage, Flow: 0.0065 - 0.0085 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0085 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 1.4 %
$ 1603/MT
- Density: 2.96 g/cc
- Linear Mold Shrinkage, Flow: 0.0065 - 0.0085 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0085 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 1.4 %
$ 1692/MT
- Density: 2.96 g/cc
- Linear Mold Shrinkage, Flow: 0.0065 - 0.0085 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0085 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 1.4 %
$ 1667/MT
- Density: 3.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0065 - 0.0085 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0085 cm/cm
- Tensile Strength at Break: 35.0 MPa @Temperature 23.0 °C
- Elongation at Break: 0.80 % @Temperature 23.0 °C
$ 1524/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.010 cm/cm
- Tensile Strength at Break: 55.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 80.0 MPa @Temperature 120 °C
$ 2136/MT
- Density: 3.27 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0090 cm/cm
- Tensile Strength at Break: 35.0 MPa
- Elongation at Break: 1.0 % @Temperature 23.0 °C
$ 2488/MT
- Density: 4.50 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 0.60 % @Temperature 23.0 °C
$ 1518/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm
- Tensile Strength at Break: 35.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 50.0 MPa @Temperature 120 °C
$ 2207/MT
- Density: 2.14 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0055 cm/cm
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 0.60 %
$ 2021/MT
- Density: 2.96 g/cc
- Linear Mold Shrinkage, Flow: 0.0065 - 0.0085 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0085 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 1.4 %
$ 1541/MT
- Density: 2.93 g/cc
- Thickness: 140 microns
- Thickness: 560 microns
- Linear Mold Shrinkage, Flow: 0.0075 - 0.0095 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0095 cm/cm
$ 1622/MT
- Density: 8.58 g/cc
- Thickness: 340 microns
- Thickness: 660 microns
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0090 cm/cm
$ 2127/MT
- Density: 10.85 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0090 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 0.80 %
$ 1577/MT
- Density: 2.96 g/cc
- Linear Mold Shrinkage, Flow: 0.0065 - 0.0085 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0085 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 1.4 %
$ 1552/MT
- Density: 1.28 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 2.0 %
$ 1628/MT
- Density: 1.00 g/cc
- Linear Mold Shrinkage, Flow: 0.010 - 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.012 cm/cm
- Tensile Strength at Break: 25.0 MPa
- Elongation at Break: 0.70 %
$ 1531/MT
- Density: 3.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.010 cm/cm
- Tensile Strength at Break: 25.0 MPa
- Elongation at Break: 0.60 %
$ 1648/MT
- Density: 8.10 g/cc
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0085 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0055 - 0.0085 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 1.3 %
$ 1511/MT
- Density: 3.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 2.5 %
$ 2221/MT
- Density: 2.96 g/cc
- Linear Mold Shrinkage, Flow: 0.0065 - 0.0085 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0085 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 1.4 %
$ 2118/MT
- Density: 2.96 g/cc
- Linear Mold Shrinkage, Flow: 0.0065 - 0.0085 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0085 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 1.4 %
$ 1641/MT
- Density: 11.0 g/cc
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0085 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0055 - 0.0085 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 0.70 %
$ 1826/MT
- Density: 4.25 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0060 cm/cm
- Tensile Strength at Break: 35.0 MPa
- Elongation at Break: 0.70 %
$ 1736/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.0115 - 0.0145 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0125 - 0.015 cm/cm
- Elongation at Break: >= 100 % @Temperature 23.0 °C
- Elongation at Break: >= 100 % @Temperature 60.0 °C
$ 1587/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0055 - 0.0080 cm/cm
- Tensile Strength at Break: 10.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 20.0 MPa @Temperature 120 °C
$ 1685/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm
- Tensile Strength at Break: 70.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 80.0 MPa @Temperature 120 °C
$ 1998/MT
- Density: 1.54 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength at Break: 40.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 50.0 MPa @Temperature 120 °C
$ 1732/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0090 cm/cm
- Tensile Strength at Break: 65.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 75.0 MPa @Temperature 120 °C
$ 1711/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm
- Tensile Strength at Break: 80.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 90.0 MPa @Temperature 120 °C
$ 2374/MT
- Density: 1.62 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength at Break: 105 MPa @Temperature 150 °C
- Tensile Strength at Break: 120 MPa @Temperature 120 °C
$ 2289/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0055 - 0.0075 cm/cm
- Tensile Strength at Break: 65.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 75.0 MPa @Temperature 120 °C
$ 1565/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0105 - 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0115 - 0.0145 cm/cm
- Tensile Strength at Break: 50.0 MPa @Temperature 60.0 °C
- Tensile Strength at Break: 70.0 MPa @Temperature 23.0 °C
$ 1707/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0085 - 0.0115 cm/cm
- Tensile Strength at Break: 55.0 MPa @Temperature 60.0 °C
- Tensile Strength at Break: 80.0 MPa @Temperature 23.0 °C
$ 1914/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.013 cm/cm
- Tensile Strength at Break: 30.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 35.0 MPa @Temperature 120 °C
$ 1574/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0095 cm/cm
- Tensile Strength at Break: 75.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 95.0 MPa @Temperature 120 °C
$ 1934/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.0165 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 - 0.016 cm/cm
- Elongation at Break: >= 100 % @Temperature 23.0 °C
- Elongation at Break: >= 100 % @Temperature 60.0 °C
$ 1911/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.105 cm/cm
- Tensile Strength at Break: 80.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 90.0 MPa @Temperature 120 °C
$ 2442/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.010 cm/cm
- Tensile Strength at Break: 75.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 85.0 MPa @Temperature 120 °C
$ 1955/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.010 cm/cm
- Tensile Strength at Break: 45.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 55.0 MPa @Temperature 120 °C
$ 1865/MT
- Density: 1.56 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0095 cm/cm
- Tensile Strength at Break: 100 MPa @Temperature 150 °C
- Tensile Strength at Break: 120 MPa @Temperature 120 °C
$ 1618/MT
- Density: 1.58 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.012 cm/cm
- Tensile Strength at Break: 80.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 90.0 MPa @Temperature 120 °C
$ 1899/MT
- Density: 1.68 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.011 cm/cm
- Tensile Strength at Break: 80.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 90.0 MPa @Temperature 120 °C
$ 2006/MT
- Density: 1.56 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0095 cm/cm
- Tensile Strength at Break: 65.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 80.0 MPa @Temperature 120 °C
$ 1491/MT
- Density: 1.69 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0090 cm/cm
- Tensile Strength at Break: 95.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 110 MPa @Temperature 120 °C
$ 1658/MT
- Density: 1.28 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0055 - 0.0085 cm/cm
- Tensile Strength at Break: 100 MPa @Temperature 150 °C
- Tensile Strength at Break: 120 MPa @Temperature 120 °C
$ 1690/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0070 cm/cm
- Tensile Strength at Break: 105 MPa @Temperature 150 °C
- Tensile Strength at Break: 125 MPa @Temperature 120 °C
$ 1731/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0035 - 0.0055 cm/cm
- Tensile Strength at Break: 100 MPa @Temperature 150 °C
- Tensile Strength at Break: 125 MPa @Temperature 120 °C
$ 1677/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0085 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0105 - 0.0135 cm/cm
- Tensile Strength at Break: 35.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 45.0 MPa @Temperature 120 °C
$ 2051/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0115 - 0.0145 cm/cm
- Tensile Strength at Break: 40.0 MPa @Temperature 60.0 °C
- Tensile Strength at Break: 50.0 MPa @Temperature 23.0 °C
$ 1802/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0105 - 0.0135 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0105 - 0.014 cm/cm
- Tensile Strength at Break: 50.0 MPa @Temperature 60.0 °C
- Tensile Strength at Break: 70.0 MPa @Temperature 23.0 °C
$ 1607/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 85.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 100 MPa @Temperature 120 °C
$ 1899/MT
- Density: 1.28 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.010 cm/cm
- Tensile Strength at Break: 60.0 MPa @Temperature 23.0 °C
- Elongation at Break: 18 % @Temperature 23.0 °C
$ 1561/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0125 - 0.0155 cm/cm
- Tensile Strength at Break: 95.0 MPa
- Elongation at Break: 30 % @Temperature 23.0 °C
$ 1995/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 65.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 70.0 MPa @Temperature 120 °C
$ 1879/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 70.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 85.0 MPa @Temperature 120 °C
$ 1594/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0105 - 0.0135 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0115 - 0.014 cm/cm
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 30 % @Temperature 23.0 °C
$ 1568/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0095 cm/cm
- Tensile Strength at Break: 55.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 65.0 MPa @Temperature 120 °C
$ 1791/MT
- Density: 1.39 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0085 cm/cm
- Tensile Strength at Break: 20.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 35.0 MPa @Temperature 120 °C
$ 1664/MT
- Density: 1.56 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength at Break: 100 MPa @Temperature 150 °C
- Tensile Strength at Break: 115 MPa @Temperature 120 °C
$ 1547/MT
- Density: 1.74 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0025 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0045 cm/cm
- Tensile Strength at Break: 95.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 105 MPa @Temperature 120 °C
$ 1521/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.0145 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 - 0.015 cm/cm
- Tensile Strength at Break: 25.0 MPa @Temperature 60.0 °C
- Tensile Strength at Break: 35.0 MPa @Temperature 23.0 °C
$ 1473/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 - 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.0125 cm/cm
- Tensile Strength at Break: 20.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 25.0 MPa @Temperature 120 °C
$ 1858/MT
- Density: 1.52 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 40.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 50.0 MPa @Temperature 120 °C
$ 1878/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 105 MPa
- Elongation at Break: 2.0 %
$ 1577/MT
- Density: 1.53 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0070 cm/cm
- Tensile Strength at Break: 65.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 125 MPa @Temperature 120 °C
$ 1837/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0115 - 0.0145 cm/cm
- Elongation at Break: >= 100 % @Temperature 23.0 °C
- Elongation at Break: >= 100 % @Temperature 60.0 °C
$ 1700/MT
- Density: 1.80 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0070 cm/cm
- Tensile Strength at Break: 45.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 65.0 MPa @Temperature 120 °C
$ 1864/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0125 - 0.0155 cm/cm
- Tensile Strength at Break: 75.0 MPa
- Elongation at Break: 2.7 %
$ 2395/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.020 - 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0205 - 0.0225 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 50 % @Temperature 23.0 °C
$ 1515/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0045 cm/cm
- Tensile Strength at Break: 25.0 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 60.0 MPa @Temperature 60.0 °C
$ 2245/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0030 cm/cm
- Tensile Strength at Break: 45.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 65.0 MPa @Temperature 120 °C
$ 1920/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0085 - 0.0115 cm/cm
- Tensile Strength at Break: 80.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 90.0 MPa @Temperature 120 °C
$ 2400/MT
- Density: 1.50 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0015 - 0.0025 cm/cm
- Tensile Strength at Break: 100 MPa @Temperature 150 °C
- Tensile Strength at Break: 120 MPa @Temperature 120 °C
$ 1463/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 - 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.014 cm/cm
- Tensile Strength at Break: 22.0 MPa
- Elongation at Break: 1.0 %
$ 1473/MT
- Density: 1.92 g/cc
- Linear Mold Shrinkage, Flow: 0.016 - 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 - 0.019 cm/cm
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 2.5 %
$ 1623/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0115 - 0.0155 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 - 0.0155 cm/cm
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 35 %
$ 1573/MT
- Density: 1.44 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 4.0 %
$ 1857/MT
- Density: 1.60 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 - 0.016 cm/cm
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 1.8 %
$ 2051/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.023 - 0.027 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0235 - 0.0275 cm/cm
- Tensile Strength at Break: 35.0 MPa
- Elongation at Break: >= 100 % @Temperature 23.0 °C
$ 1780/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0090 cm/cm
- Tensile Strength at Break: 50.0 MPa
- Elongation at Yield: 4.5 %
$ 2509/MT
- Density: 1.55 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.013 cm/cm
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 1.5 %
$ 1558/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength at Break: 20.0 MPa @Temperature 120 °C
- Tensile Strength at Break: 40.0 MPa @Temperature 90.0 °C
$ 1742/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0085 - 0.0115 cm/cm
- Tensile Strength at Break: 170 MPa
- Elongation at Break: 3.0 %
$ 1448/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 - 0.014 cm/cm
- Tensile Strength at Break: 20.0 MPa @Temperature 60.0 °C
- Tensile Strength at Break: 30.0 MPa @Temperature 23.0 °C
$ 1616/MT
- Density: 1.57 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 1.5 %
$ 2442/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0035 - 0.0050 cm/cm
- Tensile Strength at Break: 45.0 MPa @Temperature 23.0 °C
- Elongation at Break: 50 % @Temperature 23.0 °C
$ 2403/MT
- Density: 1.59 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0095 cm/cm
- Tensile Strength at Break: 220 MPa
- Elongation at Break: 2.5 %
$ 1961/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0055 - 0.0075 cm/cm
- Tensile Strength at Break: 15.0 MPa @Temperature 120 °C
- Tensile Strength at Break: 35.0 MPa @Temperature 90.0 °C
$ 1882/MT
- Density: 4.50 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0060 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 0.40 %
$ 1770/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0085 cm/cm
- Tensile Strength at Break: 15.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 20.0 MPa @Temperature 120 °C
$ 1564/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.010 - 0.0125 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0105 - 0.0135 cm/cm
- Tensile Strength at Break: 20.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 25.0 MPa @Temperature 120 °C
$ 1789/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.010 cm/cm
- Tensile Strength at Break: 70.0 MPa @Temperature 23.0 °C
- Elongation at Break: 5.0 % @Temperature 23.0 °C
$ 1487/MT
- Density: 1.59 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0035 - 0.0060 cm/cm
- Tensile Strength at Break: 20.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 25.0 MPa @Temperature 120 °C
$ 1832/MT
- Density: 1.56 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0065 cm/cm
- Tensile Strength at Break: 35.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 50.0 MPa @Temperature 120 °C
$ 1496/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0070 cm/cm
- Tensile Strength at Break: 25.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 30.0 MPa @Temperature 120 °C
$ 1556/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0065 - 0.0085 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0090 cm/cm
- Tensile Strength at Break: 35.0 MPa
- Elongation at Break: 3.5 %
$ 1840/MT
- Density: 1.78 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 - 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.014 cm/cm
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 1.6 %
$ 1755/MT
- Density: 1.62 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0075 cm/cm
- Tensile Strength at Break: 130 MPa @Temperature 150 °C
- Tensile Strength at Break: 150 MPa @Temperature 120 °C
$ 1847/MT
- Density: 1.38 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 165 MPa
- Elongation at Break: 3.1 %
$ 1576/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0060 cm/cm
- Tensile Strength at Break: 55.0 MPa
- Elongation at Break: 4.5 %
$ 2015/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0060 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 1.3 %
$ 2094/MT
- Density: 1.56 g/cc
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.0125 cm/cm
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 2.0 %
$ 1679/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0025 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.012 cm/cm
- Tensile Strength at Break: 45.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 60.0 MPa @Temperature 120 °C
$ 1462/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0085 - 0.0115 cm/cm
- Tensile Strength at Break: 60.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 70.0 MPa @Temperature 120 °C
$ 1766/MT
- Density: 1.55 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 1.5 %
$ 1881/MT
- Density: 1.99 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0065 cm/cm
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 0.60 %
$ 2273/MT
- Density: 1.85 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0025 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0015 - 0.0030 cm/cm
- Tensile Strength at Break: 85.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 100 MPa @Temperature 120 °C
$ 1863/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0095 - 0.0125 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.0135 cm/cm
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 20 %
$ 2372/MT
- Density: 1.48 g/cc
- Linear Mold Shrinkage, Flow: 0.0195 - 0.0225 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0195 - 0.022 cm/cm
- Tensile Strength at Break: 30.0 MPa @Temperature 60.0 °C
- Tensile Strength at Break: 45.0 MPa @Temperature 23.0 °C
$ 1483/MT
- Density: 1.812 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 0.50 %
$ 1740/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.010 cm/cm
- Tensile Strength at Break: 165 MPa
- Elongation at Break: 2.9 %
$ 2019/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 - 0.018 cm/cm
- Tensile Strength at Break: 12.0 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 25.0 MPa @Temperature 60.0 °C
$ 1586/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0075 cm/cm
- Tensile Strength at Break: 55.0 MPa
- Elongation at Break: 8.0 %
$ 2074/MT
- Density: 1.58 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0095 cm/cm
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 2.4 %
$ 1875/MT
- Density: 1.93 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 100 MPa @Temperature 150 °C
- Tensile Strength at Break: 115 MPa @Temperature 120 °C
$ 1822/MT
- Density: 1.28 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0035 - 0.0055 cm/cm
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 1.8 %
$ 1589/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0075 - 0.0095 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0090 cm/cm
- Tensile Strength at Break: 10.0 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 15.0 MPa @Temperature 60.0 °C
$ 2425/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 70.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 90.0 MPa @Temperature 120 °C
$ 1870/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0085 - 0.0105 cm/cm
- Tensile Strength at Break: 13.0 MPa @Temperature 60.0 °C
- Tensile Strength at Break: 25.0 MPa @Temperature 23.0 °C
$ 1642/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 - 0.015 cm/cm
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 20 % @Temperature 23.0 °C
$ 1871/MT
- Density: 0.940 g/cc
- Linear Mold Shrinkage, Flow: 0.014 - 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0145 - 0.0175 cm/cm
- Elongation at Break: >= 100 % @Temperature 23.0 °C
- Elongation at Break: >= 100 % @Temperature 60.0 °C
$ 1988/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 - 0.018 cm/cm
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 9.0 % @Temperature 23.0 °C
$ 1484/MT
- Density: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0115 - 0.0145 cm/cm
- Tensile Strength at Break: 18.0 MPa
- Elongation at Break: >= 100 % @Temperature 23.0 °C
$ 1670/MT
- Density: 1.02 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0135 - 0.0165 cm/cm
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 60 % @Temperature 23.0 °C
$ 1532/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0095 cm/cm
- Tensile Strength at Break: 30.0 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 45.0 MPa @Temperature 60.0 °C
$ 2371/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0080 cm/cm
- Tensile Strength at Break: 40.0 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 55.0 MPa @Temperature 60.0 °C
$ 1680/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 25.0 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 35.0 MPa @Temperature 60.0 °C
$ 1650/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
- Tensile Strength at Break: 40.0 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 65.0 MPa @Temperature 60.0 °C
$ 1818/MT
- Density: 0.950 g/cc
- Linear Mold Shrinkage, Flow: 0.0135 - 0.0165 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0135 - 0.0165 cm/cm
- Tensile Strength at Break: 8.00 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 10.0 MPa @Temperature 60.0 °C
$ 2405/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage, Flow: 0.0105 - 0.0135 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 - 0.014 cm/cm
- Tensile Strength at Break: 10.0 MPa @Temperature 60.0 °C
- Tensile Strength at Break: 20.0 MPa @Temperature 23.0 °C
$ 2020/MT
- Density: 2.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0090 cm/cm
- Tensile Strength at Break: 75.0 MPa
- Elongation at Break: 1.1 %
$ 1575/MT
- Density: 1.29 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 20.0 MPa @Temperature 23.0 °C
- Elongation at Break: 8.5 % @Temperature 23.0 °C
$ 1499/MT
- Density: 1.28 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0035 cm/cm
- Tensile Strength at Break: 65.0 MPa @Temperature 120 °C
- Tensile Strength at Break: 90.0 MPa @Temperature 90.0 °C
$ 1699/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage, Flow: 0.0105 - 0.0135 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.013 cm/cm
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: >= 100 %
$ 2486/MT
- Density: 1.72 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0025 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 160 MPa
- Elongation at Break: 1.5 %
$ 1943/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 - 0.017 cm/cm
- Tensile Strength at Break: 75.0 MPa
- Elongation at Break: 5.0 %
$ 1712/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0105 - 0.013 cm/cm
- Tensile Strength at Break: 35.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 40.0 MPa @Temperature 120 °C
$ 2214/MT
- Density: 2.56 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 1.5 %
$ 1939/MT
- Density: 5.38 g/cc
- Thickness: 520 microns
- Thickness: 680 microns
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0090 cm/cm
$ 1742/MT
- Density: 1.82 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0055 cm/cm
- Tensile Strength at Break: 160 MPa @Temperature 150 °C
- Tensile Strength at Break: 180 MPa @Temperature 120 °C
$ 1999/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0085 - 0.0105 cm/cm
- Tensile Strength at Break: 30.0 MPa
- Elongation at Break: 3.0 %
$ 1790/MT
- Density: 1.38 g/cc
- Linear Mold Shrinkage, Flow: 0.00050 - 0.0015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0015 - 0.0030 cm/cm
- Tensile Strength at Break: 75.0 MPa @Temperature 120 °C
- Tensile Strength at Break: 100 MPa @Temperature 90.0 °C
$ 1451/MT
- Density: 1.38 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm
- Tensile Strength at Break: 55.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 70.0 MPa @Temperature 120 °C
$ 1562/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0090 cm/cm
- Elongation at Break: >= 100 % @Temperature 23.0 °C
- Elongation at Break: >= 100 % @Temperature 60.0 °C
$ 1722/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 - 0.105 cm/cm
- Tensile Strength at Break: 85.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 130 MPa @Temperature 120 °C
$ 2124/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0035 cm/cm
- Tensile Strength at Break: 60.0 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 85.0 MPa @Temperature 60.0 °C
$ 2115/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage, Flow: 0.0115 - 0.0145 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 - 0.015 cm/cm
- Tensile Strength at Break: 45.0 MPa @Temperature 60.0 °C
- Tensile Strength at Break: 55.0 MPa @Temperature 23.0 °C
$ 2035/MT
- Density: 1.71 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 0.60 % @Temperature 23.0 °C
$ 2129/MT
- Density: 2.80 g/cc
- Linear Mold Shrinkage, Flow: 0.0145 - 0.0175 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 - 0.018 cm/cm
- Tensile Strength at Break: 8.00 MPa
- Elongation at Break: 3.0 %
$ 1631/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.0135 cm/cm
- Tensile Strength at Break: 185 MPa
- Elongation at Break: 2.5 %
$ 1499/MT
- Density: 1.29 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0085 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0095 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 2.2 %
$ 1650/MT
- Density: 1.50 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 1.2 %
$ 1456/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0065 cm/cm
- Tensile Strength at Break: 40.0 MPa @Temperature 120 °C
- Tensile Strength at Break: 60.0 MPa @Temperature 90.0 °C
$ 2249/MT
- Density: 1.57 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0075 cm/cm
- Tensile Strength at Break: 20.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 25.0 MPa @Temperature 120 °C
$ 1598/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 - 0.016 cm/cm
- Tensile Strength at Break: 10.0 MPa
- Elongation at Break: >= 100 %
$ 1546/MT
- Density: 1.44 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0095 - 0.012 cm/cm
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 2.5 %
$ 1717/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.020 - 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0205 - 0.0225 cm/cm
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 20 %
$ 1842/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0090 cm/cm
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 2.5 %
$ 1545/MT
- Density: 2.95 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength at Break: 30.0 MPa @Temperature 23.0 °C
- Elongation at Break: 0.40 % @Temperature 23.0 °C
$ 1890/MT
- Density: 1.66 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0080 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 1.8 %
$ 1497/MT
- Density: 1.60 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0075 cm/cm
- Tensile Strength at Break: 10.0 MPa @Temperature 120 °C
- Tensile Strength at Break: 90.0 MPa @Temperature 150 °C
$ 1513/MT
- Density: 1.76 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0045 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 0.30 %
$ 1718/MT
- Density: 1.97 g/cc
- Linear Mold Shrinkage, Flow: 0.010 - 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.015 cm/cm
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 1.2 %
$ 1511/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.00050 - 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0045 cm/cm
- Tensile Strength at Break: 110 MPa @Temperature 150 °C
- Tensile Strength at Break: 155 MPa @Temperature 120 °C
$ 1494/MT
- Density: 1.48 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.012 cm/cm
- Tensile Strength at Break: 160 MPa
- Elongation at Break: 2.5 %
$ 1649/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 8.00 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 15.0 MPa @Temperature 60.0 °C
$ 1725/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0065 cm/cm
- Tensile Strength at Break: 8.00 MPa @Temperature 90.0 °C
- Tensile Strength at Break: 15.0 MPa @Temperature 60.0 °C
$ 1871/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.012 cm/cm
- Tensile Strength at Break: 30.0 MPa
- Elongation at Break: 85 %
$ 1602/MT
- Density: 1.44 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0035 - 0.0055 cm/cm
- Tensile Strength at Break: 50.0 MPa @Temperature 120 °C
- Tensile Strength at Break: 70.0 MPa @Temperature 90.0 °C
$ 1941/MT
- Density: 2.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0065 cm/cm
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 0.90 %
$ 1638/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0125 - 0.0155 cm/cm
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 11 %
$ 1608/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.010 - 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0095 - 0.0125 cm/cm
- Tensile Strength at Break: 22.0 MPa
- Elongation at Break: 1.2 %
$ 1928/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0095 - 0.0125 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0105 - 0.0135 cm/cm
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 3.5 %
$ 2291/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0075 cm/cm
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 25 %
$ 1658/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0225 - 0.0265 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0225 - 0.0265 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 90 % @Temperature 23.0 °C
$ 2351/MT
- Density: 2.70 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.013 cm/cm
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 7.0 %
$ 1772/MT
- Density: 2.56 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 1.5 %
$ 1592/MT
- Density: 2.77 g/cc
- Linear Mold Shrinkage, Flow: 0.0075 - 0.0125 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.012 cm/cm
- Tensile Strength at Break: 30.0 MPa
- Elongation at Break: 40 %
$ 1592/MT
- Density: 1.97 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0015 - 0.0030 cm/cm
- Tensile Strength at Break: 90.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 105 MPa @Temperature 120 °C
$ 1656/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 - 0.0085 cm/cm
- Tensile Strength at Break: 50.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 65.0 MPa @Temperature 120 °C
$ 1809/MT
- Density: 1.91 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0070 cm/cm
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 2.0 %
$ 1461/MT
- Density: 1.77 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0025 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0045 cm/cm
- Tensile Strength at Break: 70.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 130 MPa @Temperature 120 °C
$ 2042/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.012 cm/cm
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 2.5 %
$ 1583/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm
- Tensile Strength at Break: 27.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 40.0 MPa @Temperature 120 °C
$ 2202/MT
- Density: 1.58 g/cc
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0085 cm/cm
- Tensile Strength at Break: 25.0 MPa
- Elongation at Break: 0.60 %
$ 1820/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.0095 cm/cm
- Tensile Strength at Break: 65.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 85.0 MPa @Temperature 120 °C
$ 1481/MT
- Density: 0.780 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.011 cm/cm
- Tensile Strength at Break: 8.00 MPa
- Elongation at Break: 2.0 %
$ 1578/MT
- Density: 0.780 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.011 cm/cm
- Tensile Strength at Break: 8.00 MPa
- Elongation at Break: 2.0 %
$ 1473/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 - 0.018 cm/cm
- Tensile Strength at Break: 5.00 MPa
- Elongation at Break: >= 100 %
$ 1740/MT
- Density: 2.05 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0125 - 0.0155 cm/cm
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 1.0 %
$ 1581/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.017 - 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 - 0.020 cm/cm
- Elongation at Break: >= 100 % @Temperature 23.0 °C
- Elongation at Break: >= 100 % @Temperature 60.0 °C
$ 1633/MT
- Density: 0.850 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0125 - 0.0155 cm/cm
- Tensile Strength at Break: 8.00 MPa
- Elongation at Break: 55 %
$ 1513/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 50.0 MPa @Temperature 120 °C
- Tensile Strength at Break: 60.0 MPa @Temperature 90.0 °C
$ 2433/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 50.0 MPa @Temperature 120 °C
- Tensile Strength at Break: 60.0 MPa @Temperature 90.0 °C
$ 2168/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.018 - 0.021 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 - 0.0205 cm/cm
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 8.0 %
$ 2391/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0085 - 0.0125 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0095 - 0.0135 cm/cm
- Tensile Strength at Break: 30.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 50.0 MPa @Temperature 120 °C
$ 1479/MT
- Density: 0.970 g/cc
- Linear Mold Shrinkage, Flow: 0.014 - 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 - 0.017 cm/cm
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 20 %
$ 1748/MT
- Density: 1.57 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0095 - 0.0125 cm/cm
- Tensile Strength at Break: 45.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 50.0 MPa @Temperature 120 °C
$ 2577/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0045 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 1.2 %
$ 2091/MT
- Density: 1.39 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 - 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.012 cm/cm
- Tensile Strength at Break: 25.0 MPa @Temperature 150 °C
- Tensile Strength at Break: 30.0 MPa @Temperature 120 °C
$ 2522/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.017 - 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 - 0.020 cm/cm
- Tensile Strength at Break: 30.0 MPa
- Elongation at Break: >= 100 %
$ 1476/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0035 - 0.0055 cm/cm
- Tensile Strength at Break: 170 MPa
- Elongation at Break: 1.0 %
$ 2536/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.020 - 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0205 - 0.0225 cm/cm
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 40 % @Temperature 23.0 °C
Delivery Polymer LATI
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cargo ship for sale in turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.