LATI Latamid 66 E21 G/15 PA 66, 15% Glass Fiber Reinforced price 1914 per MT

Physical Properties
Density
1.14 g/cc
Linear Mold Shrinkage, Flow
0.0050 - 0.0080 cm/cm
Linear Mold Shrinkage, Transverse
0.010 - 0.013 cm/cm

Mechanical Properties
Tensile Strength at Break
30.0 MPa @Temperature 150 °C
Tensile Strength at Break
35.0 MPa @Temperature 120 °C
Tensile Strength at Break
45.0 MPa @Temperature 90.0 °C
Tensile Strength at Break
65.0 MPa @Temperature 60.0 °C
Tensile Strength at Break
90.0 MPa @Temperature 23.0 °C
Elongation at Break
5.0 % @Temperature 23.0 °C
Elongation at Break
7.5 % @Temperature 60.0 °C
Elongation at Break
8.6 % @Temperature 90.0 °C
Elongation at Break
9.3 % @Temperature 120 °C
Elongation at Break
9.5 % @Temperature 150 °C
Elongation at Yield
3.0 % @Temperature 23.0 °C
Elongation at Yield
4.8 % @Temperature 60.0 °C
Elongation at Yield
6.1 % @Temperature 90.0 °C
Elongation at Yield
6.6 % @Temperature 120 °C
Elongation at Yield
6.9 % @Temperature 150 °C
Tensile Modulus
1.70 GPa @Temperature 150 °C
Tensile Modulus
1.90 GPa @Temperature 120 °C
Tensile Modulus
2.50 GPa @Temperature 90.0 °C
Tensile Modulus
3.40 GPa @Temperature 60.0 °C
Tensile Modulus
4.80 GPa @Temperature 23.0 °C
Charpy Impact Unnotched
7.50 J/cm² @Temperature 23.0 °C
Charpy Impact Unnotched
8.00 J/cm² @Temperature -20.0 °C
Charpy Impact, Notched
1.50 J/cm² @Temperature -20.0 °C
Charpy Impact, Notched
2.00 J/cm² @Temperature 23.0 °C

Thermal Properties
Maximum Service Temperature, Air
90.0 °C
Deflection Temperature at 0.46 MPa (66 psi)
255 °C
Deflection Temperature at 1.8 MPa (264 psi)
230 °C
Vicat Softening Point
230 °C @Load 5.00 kg

Processing Properties
Melt Temperature
260 - 290 °C
Mold Temperature
60.0 - 80.0 °C
Drying Temperature
90.0 - 100 °C @Time 10800 sec

Descriptive Properties
ISO Shrinkage - Pressure
60 MPa

Alternative products

SABIC Innovative Plastics LNP STAT-KON RE0069S PA 66 accurate 70%

$ 1804/MT

Specific Gravity: 1.49 g/cc
Density: 1.49 g/cc
Density: 1.50 g/cc
Moisture Absorption: 0.400 %
Moisture Absorption: 0.560 %

SABIC Innovative Plastics LNP VERTON RV008ES PA 66 accurate 70%

$ 1456/MT

Density: 1.47 g/cc
Density: 1.48 g/cc
Moisture Absorption: 0.700 %
Linear Mold Shrinkage, Flow: 0.0029 cm/cm @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec

Thermal Ceramics Cerafelt accurate 70%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

LATI Latamid 66 H2E21 G/13 PA 66, 13% Glass Fiber Reinforced accurate 99%

$ 1677/MT

Density: 1.20 g/cc
Linear Mold Shrinkage, Flow: 0.0055 - 0.0085 cm/cm
Linear Mold Shrinkage, Transverse: 0.0105 - 0.0135 cm/cm
Tensile Strength at Break: 35.0 MPa @Temperature 150 °C
Tensile Strength at Break: 45.0 MPa @Temperature 120 °C

LATI Latamid 66 MDT03-01 PA 66 accurate 70%

$ 1899/MT

Density: 1.28 g/cc
Linear Mold Shrinkage, Flow: 0.0060 - 0.010 cm/cm
Linear Mold Shrinkage, Transverse: 0.0060 - 0.010 cm/cm
Tensile Strength at Break: 60.0 MPa @Temperature 23.0 °C
Elongation at Break: 18 % @Temperature 23.0 °C

LATI Latamid 66 H2 G/25-V0KB PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant accurate 85%

$ 1462/MT

Density: 1.36 g/cc
Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
Linear Mold Shrinkage, Transverse: 0.0085 - 0.0115 cm/cm
Tensile Strength at Break: 60.0 MPa @Temperature 150 °C
Tensile Strength at Break: 70.0 MPa @Temperature 120 °C

SABIC Innovative Plastics LNP THERMOCOMP RF0069XZ PA 66 accurate 70%

$ 2101/MT

Specific Gravity: 1.69 g/cc
Density: 1.68 g/cc
Density: 1.69 g/cc
Moisture Absorption: 0.360 %
Moisture Absorption: 0.540 %

SABIC Innovative Plastics LNP VERTON RVL28 PA 66 accurate 70%

$ 1865/MT

Density: 1.57 g/cc
Density: 1.58 g/cc
Moisture Absorption: 0.500 %
Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0033 cm/cm @Time 86400 sec

LATI Laticonther 80 GR/50 PPS, 50% Graphite Reinforced accurate 70%

$ 2035/MT

Density: 1.71 g/cc
Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm
Tensile Strength at Break: 60.0 MPa
Elongation at Break: 0.60 % @Temperature 23.0 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, oil chemical tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

5 prices for LATI Latamid 66 E21 G/15 PA 66, 15% Glass Fiber Reinforced

Seller from Atlanta – 2021-06-18:

Seller from Atlanta work with company: Celanese Corporation, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2390 per MT

Seller from Miami – 2021-05-13:

Seller from Miami work with company: 3M, PolyOne Corporation, Exxon Chemical, SABIC Innovative Plastics (GE Plastics)

Price: $2342 per MT

Seller from Hanoi – 2021-05-08:

Seller from Hanoi work with company: 3M, Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $2529 per MT

Seller from Phoenix – 2021-04-27:

Seller from Phoenix work with company: Solvay, Exxon Chemical, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1914 per MT

Seller from Shenzhen – 2021-06-12:

Seller from Shenzhen work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co.

Price: $2132 per MT