LATI Latamid 66 H2E21 G/13 PA 66, 13% Glass Fiber Reinforced

Seller in Barcelona price: $2480 per MT
Seller in Xi’an price: $2512 per MT
Seller in Singapore price: $1677 per MT

LATI Latamid 66 H2E21 G/13 PA 66, 13% Glass Fiber Reinforced in Polymer, Thermoplastic, Nylon, Nylon 66, 10% Glass Fiber Filled

  • Physical Properties
  • Density
  • 1.20 g/cc
  • Linear Mold Shrinkage, Flow
  • 0.0055 - 0.0085 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.0105 - 0.0135 cm/cm
  • Mechanical Properties
  • Tensile Strength at Break
  • 35.0 MPa @Temperature 150 °C
  • Tensile Strength at Break
  • 45.0 MPa @Temperature 120 °C
  • Tensile Strength at Break
  • 50.0 MPa @Temperature 90.0 °C
  • Tensile Strength at Break
  • 70.0 MPa @Temperature 60.0 °C
  • Tensile Strength at Break
  • 100 MPa @Temperature 23.0 °C
  • Elongation at Break
  • 4.0 % @Temperature 23.0 °C
  • Elongation at Break
  • 6.5 % @Temperature 60.0 °C
  • Elongation at Break
  • 10 % @Temperature 150 °C
  • Elongation at Break
  • 12 % @Temperature 90.0 °C
  • Elongation at Break
  • 12 % @Temperature 120 °C
  • Elongation at Yield
  • 3.0 % @Temperature 23.0 °C
  • Elongation at Yield
  • 4.0 % @Temperature 60.0 °C
  • Elongation at Yield
  • 7.0 % @Temperature 150 °C
  • Elongation at Yield
  • 7.5 % @Temperature 90.0 °C
  • Elongation at Yield
  • 8.0 % @Temperature 120 °C
  • Tensile Modulus
  • 1.50 GPa @Temperature 150 °C
  • Tensile Modulus
  • 1.70 GPa @Temperature 120 °C
  • Tensile Modulus
  • 2.10 GPa @Temperature 90.0 °C
  • Tensile Modulus
  • 3.70 GPa @Temperature 60.0 °C
  • Tensile Modulus
  • 4.60 GPa @Temperature 23.0 °C
  • Charpy Impact Unnotched
  • 5.50 J/cm² @Temperature -20.0 °C
  • Charpy Impact Unnotched
  • 6.50 J/cm² @Temperature 23.0 °C
  • Charpy Impact, Notched
  • 0.400 J/cm² @Temperature -20.0 °C
  • Charpy Impact, Notched
  • 1.00 J/cm² @Temperature 23.0 °C
  • Thermal Properties
  • Maximum Service Temperature, Air
  • 90.0 °C
  • Deflection Temperature at 0.46 MPa (66 psi)
  • 255 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 230 °C
  • Vicat Softening Point
  • 235 °C @Load 5.00 kg
  • Processing Properties
  • Melt Temperature
  • 270 - 290 °C
  • Mold Temperature
  • 70.0 - 90.0 °C
  • Drying Temperature
  • 90.0 - 100 °C @Time 10800 sec
  • Descriptive Properties
  • ISO Shrinkage - Pressure
  • 60 MPa

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, bulk ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for LATI Latamid 66 H2E21 G/13 PA 66, 13% Glass Fiber Reinforced

Seller from Barcelona – 2021-03-01:

Seller from Barcelona work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2480 per MT

Seller from Xi’an – 2021-03-29:

Seller from Xi’an work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $2512 per MT

Seller from Singapore – 2021-05-27:

Seller from Singapore work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1677 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell LATI Latamid 66 H2E21 G/13 PA 66, 13% Glass Fiber Reinforced?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Walk-in clinic in Singapore open-nearme.com