LATI Latamid 66 H2 G/35-V0HF1 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant price 2008 per MT

Physical Properties
Density
1.49 g/cc
Linear Mold Shrinkage, Flow
0.0035 - 0.0060 cm/cm
Linear Mold Shrinkage, Transverse
0.0070 - 0.010 cm/cm

Mechanical Properties
Tensile Strength at Break
160 MPa
Elongation at Break
3.0 % @Temperature 23.0 °C
Tensile Modulus
11.5 GPa
Charpy Impact Unnotched
7.00 J/cm²
Charpy Impact, Notched
0.880 J/cm²

Thermal Properties
Maximum Service Temperature, Air
125 °C
Deflection Temperature at 0.46 MPa (66 psi)
255 °C
Deflection Temperature at 1.8 MPa (264 psi)
235 °C
Vicat Softening Point
245 °C @Load 5.00 kg
Flammability, UL94
V-0 @Thickness 3.00 mm
Flammability, UL94
V-0 @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 0.750 mm
Oxygen Index
32 %
Glow Wire Test
775 °C @Thickness 1.00 mm
Glow Wire Test
775 °C @Thickness 2.00 mm
Glow Wire Test
960 °C @Thickness 1.00 mm
Glow Wire Test
960 °C @Thickness 2.00 mm

Electrical Properties
Comparative Tracking Index
600 V

Processing Properties
Melt Temperature
270 - 290 °C
Mold Temperature
70.0 - 100 °C
Drying Temperature
90.0 - 100 °C @Time 10800 sec

Descriptive Properties
ISO Shrinkage - Pressure
60 MPa

Alternative products

Eurostar Starflam AFR682B1 PA66, Mineral Reinforced, Flame Retardant, Injection Molding accurate 42%

$ 1498/MT

Density: 1.56 g/cc
Moisture Absorption: 0.600 % @Temperature 23.0 °C
Water Absorption at Saturation: 5.0 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Hardness, Rockwell R: 118

LATI Latamid 66 H2 G/25-V0HF1 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant accurate 70%

$ 2380/MT

Density: 1.40 g/cc
Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
Linear Mold Shrinkage, Transverse: 0.0080 - 0.0115 cm/cm
Tensile Strength at Break: 65.0 MPa @Temperature 150 °C
Tensile Strength at Break: 75.0 MPa @Temperature 120 °C

LATI Latamid 66 H2 G/25-V0KB1 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant accurate 42%

$ 1643/MT

Density: 1.32 g/cc
Linear Mold Shrinkage, Flow: 0.0035 - 0.0065 cm/cm
Linear Mold Shrinkage, Transverse: 0.0075 - 0.0105 cm/cm
Tensile Strength at Break: 55.0 MPa @Temperature 150 °C
Tensile Strength at Break: 65.0 MPa @Temperature 120 °C

LATI Latamid 6 H2 G/30-V0HF1 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant accurate 49%

$ 1732/MT

Density: 1.40 g/cc
Linear Mold Shrinkage, Flow: 0.0035 - 0.0055 cm/cm
Linear Mold Shrinkage, Transverse: 0.0065 - 0.0090 cm/cm
Tensile Strength at Break: 65.0 MPa @Temperature 150 °C
Tensile Strength at Break: 75.0 MPa @Temperature 120 °C

LATI Latamid 66 H2 G/35-V0KB1 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant accurate 42%

$ 2442/MT

Density: 1.45 g/cc
Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm
Linear Mold Shrinkage, Transverse: 0.0075 - 0.010 cm/cm
Tensile Strength at Break: 75.0 MPa @Temperature 150 °C
Tensile Strength at Break: 85.0 MPa @Temperature 120 °C

LATI Latamid 66 H2 G/50-V0HF1 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant accurate 49%

$ 1899/MT

Density: 1.68 g/cc
Linear Mold Shrinkage, Flow: 0.0025 - 0.0060 cm/cm
Linear Mold Shrinkage, Transverse: 0.0075 - 0.011 cm/cm
Tensile Strength at Break: 80.0 MPa @Temperature 150 °C
Tensile Strength at Break: 90.0 MPa @Temperature 120 °C

LATI Latamid 66 H2 G/50-V0KB1 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant accurate 42%

$ 2006/MT

Density: 1.56 g/cc
Linear Mold Shrinkage, Flow: 0.0025 - 0.0055 cm/cm
Linear Mold Shrinkage, Transverse: 0.0065 - 0.0095 cm/cm
Tensile Strength at Break: 65.0 MPa @Temperature 150 °C
Tensile Strength at Break: 80.0 MPa @Temperature 120 °C

LATI Latamid 66 H2 G/25-V0KB4 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant accurate 56%

$ 1712/MT

Density: 1.33 g/cc
Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
Linear Mold Shrinkage, Transverse: 0.0105 - 0.013 cm/cm
Tensile Strength at Break: 35.0 MPa @Temperature 150 °C
Tensile Strength at Break: 40.0 MPa @Temperature 120 °C

Eurostar Starflam AFR682A1 PA66, Mineral Reinforced, Flame Retardant, Injection Molding accurate 42%

$ 1488/MT

Density: 1.60 g/cc
Moisture Absorption: 0.600 % @Temperature 23.0 °C
Water Absorption at Saturation: 5.0 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm
Hardness, Rockwell R: 118

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng carrier vessel for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for LATI Latamid 66 H2 G/35-V0HF1 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant

Seller from Montréal – 2021-07-15:

Seller from Montréal work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2215 per MT

Seller from Rangoon – 2021-05-14:

Seller from Rangoon work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2008 per MT