LATI Latene® 22H2 MX/25 PP Homopolymer, Heat Stabilized price 1484 per MT

Physical Properties
Density
1.11 g/cc
Linear Mold Shrinkage, Flow
0.011 - 0.014 cm/cm
Linear Mold Shrinkage, Transverse
0.0115 - 0.0145 cm/cm

Mechanical Properties
Tensile Strength at Break
18.0 MPa
Elongation at Break
>= 100 % @Temperature 23.0 °C
Elongation at Break
>= 100 % @Temperature 60.0 °C
Elongation at Break
>= 100 % @Temperature 90.0 °C
Elongation at Yield
6.0 % @Temperature 23.0 °C
Elongation at Yield
8.5 % @Temperature 60.0 °C
Elongation at Yield
9.0 % @Temperature 90.0 °C
Tensile Modulus
0.650 GPa @Temperature 90.0 °C
Tensile Modulus
1.10 GPa @Temperature 60.0 °C
Tensile Modulus
2.60 GPa @Temperature 23.0 °C
Charpy Impact Unnotched
1.50 J/cm² @Temperature -20.0 °C
Charpy Impact Unnotched
6.50 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.100 J/cm² @Temperature -20.0 °C
Charpy Impact, Notched
0.350 J/cm² @Temperature 23.0 °C

Thermal Properties
Maximum Service Temperature, Air
120 °C
Deflection Temperature at 0.46 MPa (66 psi)
105 °C
Deflection Temperature at 1.8 MPa (264 psi)
55.0 °C
Vicat Softening Point
95.0 °C @Load 5.00 kg
Flammability, UL94
2.00 @Thickness 1.50 mm
Flammability, UL94
2.00 @Thickness 0.750 mm
Oxygen Index
24 %
Glow Wire Test
750 °C @Thickness 1.00 mm
Glow Wire Test
750 °C @Thickness 2.00 mm

Electrical Properties
Comparative Tracking Index
600 V

Processing Properties
Melt Temperature
200 - 240 °C
Mold Temperature
40.0 - 60.0 °C
Drying Temperature
80.0 - 90.0 °C @Time 10800 sec

Descriptive Properties
ISO Shrinkage - Pressure
60 MPa

Alternative products

BASF Ultradur B 6550 PBT accurate 44%

$ 1788/MT

Density: 1.30 g/cc
Water Absorption: 0.50 %
Moisture Absorption at Equilibrium: 0.25 %
Viscosity Test: 160 cm³/g
Linear Mold Shrinkage, Flow: 0.015 cm/cm

Covestro Makroblend® DP UT3905 Polycarbonate + PBT, Impact Grade accurate 44%

$ 1832/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 260 °C
Water Absorption: 0.50 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 45 g/10 min @Load 5.00 kg, Temperature 260 °C

Covestro Makroblend® DP UT3907 Polycarbonate + PBT, Impact Grade accurate 44%

$ 1489/MT

Density: 1.20 g/cc
Density: 1.02 g/cc @Temperature 260 °C
Water Absorption: 0.50 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 45 g/10 min @Load 5.00 kg, Temperature 260 °C

Thermal Ceramics Cerafelt accurate 54%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

LATI Latene® EP 22UVH2 MX/25 PP Copolymer, Mineral Reinforced accurate 44%

$ 1837/MT

Density: 1.13 g/cc
Linear Mold Shrinkage, Flow: 0.011 - 0.014 cm/cm
Linear Mold Shrinkage, Transverse: 0.0115 - 0.0145 cm/cm
Elongation at Break: >= 100 % @Temperature 23.0 °C
Elongation at Break: >= 100 % @Temperature 60.0 °C

DuPont Performance Polymers Zytel® EFE1068 NC010T Nylon 66 (Unverified Data**) accurate 44%

$ 1623/MT

Density: 0.950 g/cc
Density: 1.14 g/cc
Water Absorption: 8.5 % @Thickness 2.00 mm
Moisture Absorption: 2.80 % @Thickness 2.00 mm
Linear Mold Shrinkage, Flow: 0.015 cm/cm

LATI Latene® 7-V2 PP Homopolymer, Flame Retardant accurate 54%

$ 1871/MT

Density: 0.940 g/cc
Linear Mold Shrinkage, Flow: 0.014 - 0.017 cm/cm
Linear Mold Shrinkage, Transverse: 0.0145 - 0.0175 cm/cm
Elongation at Break: >= 100 % @Temperature 23.0 °C
Elongation at Break: >= 100 % @Temperature 60.0 °C

LATI Latene® EP 7-V2HF PP Copolymer, Flame Retardant accurate 54%

$ 1818/MT

Density: 0.950 g/cc
Linear Mold Shrinkage, Flow: 0.0135 - 0.0165 cm/cm
Linear Mold Shrinkage, Transverse: 0.0135 - 0.0165 cm/cm
Tensile Strength at Break: 8.00 MPa @Temperature 90.0 °C
Tensile Strength at Break: 10.0 MPa @Temperature 60.0 °C

LATI Later 4 PBT accurate 44%

$ 1581/MT

Density: 1.32 g/cc
Linear Mold Shrinkage, Flow: 0.017 - 0.020 cm/cm
Linear Mold Shrinkage, Transverse: 0.017 - 0.020 cm/cm
Elongation at Break: >= 100 % @Temperature 23.0 °C
Elongation at Break: >= 100 % @Temperature 60.0 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, freight ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

5 prices for LATI Latene® 22H2 MX/25 PP Homopolymer, Heat Stabilized

Seller from Houston – 2021-03-04:

Seller from Houston work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2533 per MT

Seller from Brasília – 2021-07-27:

Seller from Brasília work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2453 per MT

Seller from Houston – 2021-07-10:

Seller from Houston work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1752 per MT

Seller from Toronto – 2021-04-02:

Seller from Toronto work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2290 per MT

Seller from Hanoi – 2021-07-15:

Seller from Hanoi work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1484 per MT